CN114409948A - Wormwood latex material and manufacturing method thereof, mattress, pillow and insole - Google Patents
Wormwood latex material and manufacturing method thereof, mattress, pillow and insole Download PDFInfo
- Publication number
- CN114409948A CN114409948A CN202210041626.1A CN202210041626A CN114409948A CN 114409948 A CN114409948 A CN 114409948A CN 202210041626 A CN202210041626 A CN 202210041626A CN 114409948 A CN114409948 A CN 114409948A
- Authority
- CN
- China
- Prior art keywords
- latex
- wormwood
- layer
- mixed solution
- latex material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of latex products and application, and discloses a method for manufacturing a wormwood latex material, which comprises the steps of putting latex into a stirring barrel, and sequentially adding hard gum, soap, potassium pyrophosphate, potassium hydroxide and siloxane to form a mixed solution; adding a vulcanizing agent into the mixed solution and stirring for 1 minute; continuously adding calcium powder into the mixed solution and uniformly stirring; continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution; adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product; and conveying the foamed latex product into an oven through a conveyer belt for drying, wherein the temperature of the oven is controlled to be 120-150 ℃, and the finished wormwood latex material is obtained. And applying the wormwood latex material to mattresses, pillows and insoles. The invention can enable the latex material to have the health-care function of the wormwood, and simplifies the difficulty of applying the latex material to household products.
Description
Technical Field
The invention belongs to the technical field of latex products and application, and particularly relates to a wormwood latex material, a manufacturing method thereof, a mattress, a pillow and an insole.
Background
The latex is also called latex, the material is soft and skin-friendly, has high elasticity, the mattress made of the material can provide good support for each contact part, has good sleep experience feeling, is accepted by more and more people, more and more latex products enter common people, the latex is used as a high-grade material and can be used as an inner material in the mattress, the latex mattress can also be made into the latex mattress by adopting a mould processing mode to provide a healthy and comfortable sleep environment for a user, more and more consumers pay more attention to the experience of health care household products while pursuing the healthy and comfortable sleep experience, functional materials such as bamboo charcoal latex, green tea latex and the like and latex products are appeared in the latex product market at present, so the development of the products can better meet the demands of the public, and the latex material contributes and breaks through in the field of the latex material, the existing latex material cannot meet the requirements of stronger health care function and more requirements.
Disclosure of Invention
The invention aims to provide a wormwood latex material, a manufacturing method thereof, a mattress, a pillow and an insole, which can enable the wormwood latex material to have the health care function of wormwood and simplify the difficulty of applying the wormwood latex material to household products.
The embodiment of the invention is realized as follows:
a method for manufacturing a wormwood latex material comprises the following steps:
preparing raw materials: moxa powder, latex, ebonite, soap, potassium pyrophosphate, potassium hydroxide, siloxane, a vulcanizing agent, calcium powder and water;
putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and drying the foamed latex product, and controlling the temperature of an oven at 120-150 ℃ to obtain the finished wormwood latex material.
A manufacturing method of a wormwood latex material specifically comprises the following steps:
drying adult folium artemisiae argyi in a drying chamber at 100 ℃ for 12 hours to enable the folium artemisiae argyi to be naturally dehydrated, controlling the water content within 1%, roughly crushing the dried folium artemisiae argyi by using a common straw crusher, grinding the roughly crushed folium artemisiae argyi for 3 times by using a stone mill to separate mesophyll, petiole and vein of the folium artemisiae argyi, separating leaf skin and fluff of the folium artemisiae argyi by using an electric vibrating screen under the vibration of 30 times per minute after crushing, secondarily removing impurities of the separated fluff by using a centrifugal fan, wherein a first fan adopts a 50-mesh sieve, a second fan adopts a 100-mesh sieve, and the separated fluff is screened according to the proportion of 1: 5, namely 1 part of fluff to 5 parts of water, grinding for 2 times by using a stone mill to shorten the fluff, filtering the ground fluff liquid for 5 times by using a sieve to retain fluff solids, scattering the fluff solids, and drying in a drying chamber at 80 ℃ for 24 hours to naturally dehydrate the fluff solids to form moxa powder;
putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding for 1 minute to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring for 1 minute to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and conveying the foamed latex product into an oven through a conveyer belt for drying, wherein the temperature of the oven is controlled to be 120-150 ℃, and the finished wormwood latex material is obtained.
Furthermore, the wormwood latex material obtained by the manufacturing method is applied.
A mattress applying a wormwood latex material comprises a wormwood latex layer made of wormwood latex material.
Further, the mattress includes the basic unit, basic unit upper portion is equipped with in proper order chinese mugwort grass emulsion layer and pleat cotton precoat, pleat cotton precoat contains 3D screen cloth layer, top layer chinese mugwort grass emulsion layer and top layer bed cloth layer.
Further, the base layer comprises a spring layer and a hard cotton layer.
Further, the wormwood latex layer is 5CM thick sheet-shaped latex.
Furthermore, the pleating cotton fabric layer is divided into an upper pleating cotton layer, a lower pleating cotton layer and a peripheral pleating cotton surrounding strip layer, wherein the surface layer moxa emulsion layer is in a shape of a coil with the thickness of 1CM, the periphery of the upper pleating cotton fabric layer and the periphery of the pleating cotton surrounding strip layer are sewn with a 40MM wide braid by sewing, and the fabric layer and the surrounding strip layer are fixed to form a finished mattress product.
A pillow using a wormwood latex material comprises a wormwood latex layer made of wormwood latex material.
An insole applying a wormwood latex material comprises a wormwood latex layer made of wormwood latex material.
According to the embodiment of the invention, the manufactured wormwood latex material is applied to household products, and the health care function is realized by utilizing the effect of moxa. The moxa has pure natural plant essence and aromatic smell, has the effects of repelling mosquitoes and preventing mites, refreshing brain, improving eyesight, soothing nerves and helping sleep, removing rheumatism, dispelling cold and relieving pain, preserving health and protecting health, clearing and activating the channels and collaterals, promoting tissue regeneration and preventing miscarriage, relieving asthma and cough, resisting bacteria and viruses, and can effectively improve the immunity of a human body. The moxa wool component is added into the wormwood latex material, and the moxa wool component directly or indirectly contacts a human body for a long time in daily application, so that the wormwood latex material has a good physical therapy effect. The structure of the mattress is added with a large amount of wormwood latex, so that the wormwood latex not only has the effects of repelling mosquitoes and mites, calming the nerves, restoring consciousness and improving human immunity, but also has the effects of warming and activating qi and blood, strengthening body resistance, eliminating evil, preventing and treating diseases, regulating human immunity and enhancing physique, can be applied to the fields of pillows, insoles and the like, is wide in application and has great market value.
Drawings
Fig. 1 is a schematic structural view of a wormwood latex mattress according to the present invention.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is described in further detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
The following detailed description of specific implementations of the present invention is provided in conjunction with specific embodiments:
a method for manufacturing a wormwood latex material is characterized by comprising the following steps:
preparing raw materials: moxa powder, latex, ebonite, soap, potassium pyrophosphate, potassium hydroxide, siloxane, a vulcanizing agent, calcium powder and water;
putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and drying the foamed latex product, and controlling the temperature of an oven at 120-150 ℃ to obtain the finished wormwood latex material.
A manufacturing method of a wormwood latex material specifically comprises the following steps: drying adult folium artemisiae argyi in a drying chamber at 100 ℃ for 12 hours to enable the folium artemisiae argyi to be naturally dehydrated, controlling the water content within 1%, roughly crushing the dried folium artemisiae argyi by using a common straw crusher, grinding the roughly crushed folium artemisiae argyi for 3 times by using a stone mill to separate mesophyll, petiole and vein of the folium artemisiae argyi, separating leaf skin and fluff of the folium artemisiae argyi by using an electric vibrating screen under the vibration of 30 times per minute after crushing, secondarily removing impurities of the separated fluff by using a centrifugal fan, wherein a first fan adopts a 50-mesh sieve, a second fan adopts a 100-mesh sieve, and the separated fluff is screened according to the proportion of 1: 5, namely 1 part of fluff to 5 parts of water, grinding for 2 times by using a stone mill to shorten the fluff, filtering the ground fluff liquid for 5 times by using a sieve to retain fluff solids, scattering the fluff solids, and drying in a drying chamber at 80 ℃ for 24 hours to naturally dehydrate the fluff solids to form moxa powder;
preparing materials: 50 wt% of latex, 4.5 wt% of soap, 9 wt% of vulcanizing agent, 30 wt% of calcium powder, 3 wt% of moxa powder, 2.4 wt% of hard rubber, 0.5 wt% of potassium pyrophosphate, 0.4 wt% of potassium hydroxide, 0.2 wt% of siloxane and 2 wt% of water; it should be emphasized that the ratio of the components of the preparation material in this embodiment can be any ratio, and the wormwood latex material of the present invention can be produced.
Putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding for 1 minute to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring for 1 minute to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and conveying the foamed latex product into an oven through a conveyer belt for drying, wherein the temperature of the oven is controlled to be 120-150 ℃, and the finished wormwood latex material is obtained.
Furthermore, the wormwood latex material obtained by the manufacturing method is applied,
as shown in fig. 1, a mattress using a moxa latex material comprises a moxa latex layer 2 made of the moxa latex material.
Further, the mattress includes the basic unit, basic unit upper portion is equipped with in proper order chinese mugwort grass emulsion layer 2 and pleat cotton fabric layer 1, pleat cotton fabric layer contains 3D screen cloth layer, top layer chinese mugwort grass emulsion layer and top layer bed cloth layer.
Further, the base layer comprises a spring layer 5 and a hard cotton layer 4, and in the figure, a foam layer 3 is further arranged between the hard cotton layer 4 and the wormwood latex layer 2.
Further, the wormwood latex layer is 5CM thick sheet-shaped latex.
Further, the pleating cotton fabric layer is divided into an upper pleating cotton layer 1 and a lower pleating cotton surrounding strip layer 6, wherein the surface layer wormwood latex layer is in a shape of a coil with the thickness of 1CM, the peripheries of the upper pleating cotton fabric layer and the lower pleating cotton surrounding strip layer are sewn with the pleating cotton surrounding strip layer through a 40MM wide braid, and the fabric layer and the surrounding strip layer are fixed to form a finished mattress product.
The mattress can be arranged in a symmetrical structure or an asymmetrical structure on the upper surface and the lower surface of the base layer, and can be customized according to the specific positioning of a product and the selection of a user as shown in the figure.
A pillow using a wormwood latex material comprises a wormwood latex layer made of wormwood latex material.
An insole applying a wormwood latex material comprises a wormwood latex layer made of wormwood latex material.
According to the embodiment of the invention, the manufactured wormwood latex material is applied to household products, and the health care function is realized by utilizing the effect of moxa. The moxa has pure natural plant essence and aromatic smell, has the effects of repelling mosquitoes and preventing mites, refreshing brain, improving eyesight, soothing nerves and helping sleep, removing rheumatism, dispelling cold and relieving pain, preserving health and protecting health, clearing and activating the channels and collaterals, promoting tissue regeneration and preventing miscarriage, relieving asthma and cough, resisting bacteria and viruses, and can effectively improve the immunity of a human body. The moxa wool component is added into the wormwood latex material, and the moxa wool component directly or indirectly contacts a human body for a long time in daily application, so that the wormwood latex material has a good physical therapy effect. The structure of the mattress is added with a large amount of wormwood latex, so that the wormwood latex not only has the effects of repelling mosquitoes and mites, calming the nerves, restoring consciousness and improving human immunity, but also has the effects of warming and activating qi and blood, strengthening body resistance, eliminating evil, preventing and treating diseases, regulating human immunity and enhancing physique, can be applied to the fields of pillows, insoles and the like, can also be used as other household products, has wide application and has great market value.
The above description is only exemplary of the present invention and should not be taken as limiting the invention, as any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (10)
1. A method for manufacturing a wormwood latex material is characterized by comprising the following steps:
preparing raw materials: moxa powder, latex, ebonite, soap, potassium pyrophosphate, potassium hydroxide, siloxane, a vulcanizing agent, calcium powder and water;
putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and drying the foamed latex product, and controlling the temperature of an oven at 120-150 ℃ to obtain the finished wormwood latex material.
2. The manufacturing method of the wormwood latex material as claimed in claim 1, wherein the method specifically comprises:
drying adult folium artemisiae argyi in a drying chamber at 100 ℃ for 12 hours to enable the folium artemisiae argyi to be naturally dehydrated, controlling the water content within 1%, roughly crushing the dried folium artemisiae argyi by using a common straw crusher, grinding the roughly crushed folium artemisiae argyi for 3 times by using a stone mill to separate mesophyll, petiole and vein of the folium artemisiae argyi, separating leaf skin and fluff of the folium artemisiae argyi by using an electric vibrating screen under the vibration of 30 times per minute after crushing, secondarily removing impurities of the separated fluff by using a centrifugal fan, wherein a first fan adopts a 50-mesh sieve, a second fan adopts a 100-mesh sieve, and the separated fluff is screened according to the proportion of 1: 5, namely 1 part of fluff to 5 parts of water, grinding for 2 times by using a stone mill to shorten the fluff, filtering the ground fluff liquid for 5 times by using a sieve to retain fluff solids, scattering the fluff solids, and drying in a drying chamber at 80 ℃ for 24 hours to naturally dehydrate the fluff solids to form moxa powder;
putting the latex into a stirring barrel, sequentially adding the ebonite, the soap, the potassium pyrophosphate, the potassium hydroxide and the siloxane, and stirring while adding for 1 minute to form a mixed solution;
adding a vulcanizing agent into the mixed solution, and stirring for 1 minute to mix;
continuously adding calcium powder into the mixed solution and uniformly stirring;
continuously adding the moxa powder and the water into the mixed solution and uniformly stirring to form a final mixed solution;
adding the final mixed solution into a foaming machine, foaming by the foaming machine and adjusting to the required density, namely the required hardness, so as to form a foamed latex product;
and conveying the foamed latex product into an oven through a conveyer belt for drying, wherein the temperature of the oven is controlled to be 120-150 ℃, and the finished wormwood latex material is obtained.
3. The moxa latex material obtained by the production method according to claim 1.
4. A mattress using the wormwood latex material of claim 3, wherein: the mattress comprises a wormwood latex layer made of wormwood latex material.
5. The mattress of claim 4, wherein: the mattress includes the basic unit, basic unit upper portion is equipped with in proper order chinese mugwort grass emulsion layer and pleat cotton precoat, pleat cotton precoat contains 3D screen cloth layer, top layer chinese mugwort grass emulsion layer and top layer bed cloth layer.
6. The mattress of claim 5, wherein: the base layer comprises a spring layer and a hard cotton layer.
7. The mattress of claim 1, wherein: the wormwood latex layer is sheet latex with the thickness of 5 CM.
8. The mattress of claim 5, wherein: the pleating cotton fabric layer is divided into an upper pleating cotton layer, a lower pleating cotton layer and a peripheral pleating cotton surrounding strip layer, wherein the surface layer wormwood latex layer is in a shape of a coil with the thickness of 1CM, the periphery of the upper pleating cotton fabric layer and the periphery of the pleating cotton surrounding strip layer are sewn with a 40MM wide braid, and the fabric layer and the surrounding strip layer are fixed to form a finished mattress product.
9. A pillow using the wormwood latex material of claim 3, wherein: the pillow comprises a wormwood latex layer made of wormwood latex material.
10. An insole using the wormwood latex material of claim 3, wherein: the insole comprises a wormwood latex layer made of wormwood latex material.