CN114380526A - 一种大体积混凝土用多功能添加剂及其制备方法 - Google Patents
一种大体积混凝土用多功能添加剂及其制备方法 Download PDFInfo
- Publication number
- CN114380526A CN114380526A CN202111656274.2A CN202111656274A CN114380526A CN 114380526 A CN114380526 A CN 114380526A CN 202111656274 A CN202111656274 A CN 202111656274A CN 114380526 A CN114380526 A CN 114380526A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- additive
- multifunctional additive
- mass concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及混凝土添加剂领域，具体是公开了一种大体积混凝土用多功能添加剂及其制备方法，所述添加剂包括如下重量份数的原料：减水剂10~20份、柠檬酸渣3~10份、聚乙烯醇纤维5~10份、SJ‑2型引气剂3~5份；所述减水剂是以甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠、丙烯酸复合引发，采用水溶液自由基聚合法合成，再经真空干燥制得。本发明提供的混凝土添加剂能在增强混凝土流动性、增加凝结时间的同时，降低混凝土绝热温升、提高其抗压强度，提升大体积混凝土多方面性能，延长建筑物的使用寿命，降低建筑物的维修成本，具有良好的工程及经济效益。
Description
技术领域
本发明涉及混凝土添加剂技术领域，具体是一种大体积混凝土用多功能添加剂及其制备方法。
背景技术
大体积混凝土是指混凝土结构物实体最小几何尺寸不小于1m的大体量混凝土，或预计会因混凝土中胶凝材料水化引起的温度变化和收缩而导致有害裂缝产生的混凝土，称之为大体积混凝土。现代建筑中时常涉及到大体积混凝土，如高层楼房基础、大型设备基础、水利大坝等。大体积混凝土结构的施工一般具有结构厚、体形大、钢筋密、混凝土数量多、工程条件复杂和施工技术要求高的特点。在实际工程中，大体积混凝土经常暴露在严酷的外部环境中，大大影响了混凝土的使用寿命。因此，需要在大体积混凝土中使用添加剂来增强混凝土的综合性能，起到保护作用。
目前混凝土添加剂品种繁多，包括减水剂、缓凝剂、减缩剂、引气剂等。添加剂功能各不相同，例如减水剂可以降低混凝土单位用水量，降低绝热温升；缓凝剂可以抑制胶凝材料的水化进程，增长凝结时间；减缩剂能有效减小混凝土的自收缩和干燥收缩等。现有的混凝土添加剂功能单一，对混凝土综合性能的提升效果不明显。
以上背景技术内容的公开仅用于辅助理解本发明的发明构思及技术方案，其并不必然属于本专利申请的现有技术，在没有明确的证据表明上述内容在本专利申请的申请日已经公开的情况下，上述背景技术不应当用于评价本申请的新颖性和创造性。
发明内容
本发明针对现有混凝土添加剂功能单一的问题，提供一种大体积混凝土用多功能添加剂及其制备方法。本发明提供的混凝土添加剂能在增强混凝土流动性、增加凝结时间的同时，降低混凝土绝热温升、提高其抗压强度，提升大体积混凝土多方面性能，延长建筑物的使用寿命，降低建筑物的维修成本，具有良好的工程及经济效益。
为了实现以上目的，本发明是通过如下技术方案实现：
一种大体积混凝土用多功能添加剂，包括如下重量份数的原料：减水剂10～20份、柠檬酸渣3～10份、聚乙烯醇纤维5～10份、SJ-2型引气剂3～5份；所述减水剂是以甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠、丙烯酸复合引发，采用水溶液自由基聚合法合成，再经真空干燥制得。
作为本发明方案的进一步优化：所述减水剂中甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠和丙烯酸的质量比为30:20:12:5:3:15。
作为本发明方案的进一步优化：所述水溶液是在40～50℃下发生聚合合成反应。
作为本发明方案的进一步优化：所述柠檬酸渣为生产柠檬酸时产生的工业废渣，主要成分为硫酸钙，含水率为20％。
作为本发明方案的进一步优化：所述聚乙烯醇纤维的直径为40μm，长度为12mm。
作为本发明方案的进一步优化：所述真空干燥是在温度为60～80℃下干燥48～72h。
本发明所述大体积混凝土用多功能添加剂的制备方法，包括如下步骤：
S1:先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；
S2:再加入与混合料等体积量的去离子水，加热搅拌1.0-1.5h后，将混合物取出，再经过干燥，研磨，即得大体积混凝土用多功能添加剂。
作为本发明方案的进一步优化：步骤S2所述加热温度为50-60℃，所述干燥是在温度为60-70℃下进行。
作为本发明方案的进一步优化：本发明所述的添加剂在大体积混凝土的应用，其所述大体积混凝土包括如下重量份数的原料：水泥250份、砂790份、碎石1240份、添加剂10份和水125份。
与现有技术相比，本发明的优点及有益效果包括：
1、本发明能在增强混凝土流动性、增加凝结时间的同时，降低混凝土绝热温升、提高其抗压强度，提升大体积混凝土多方面性能，延长建筑物的使用寿命，降低建筑物的维修成本，具有良好的工程及经济效益。
2、本发明提供的减水剂以甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠和丙烯酸复合引发，采用水溶液自由基聚合法合成。该减水剂合成方法简单，便于制作。且合成的减水剂成品能够在增强混凝土流动性的同时，改善水泥水化的放热性能，降低混凝土的绝热温升。
3、本发明以自制减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂作为大体积混凝土的添加剂。柠檬酸渣是食品化工业采用石灰法制取柠檬酸时的一种化学沉积物，其中残留少量的柠檬酸，在硅酸三钙表面形成不溶性钙盐层，产生缓凝作用；掺入聚乙烯醇纤维能有效抑制早期塑性收缩裂缝，起到减缩的效果；SJ-2型引气剂的主要成分是植物中的三萜皂甙，三萜皂甙是一个既含亲水基团又含憎水基团的两性分子，具有引气作用。各组分协同作用，有效提升大体积混凝土的多方性能。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂20份、柠檬酸渣6份、聚乙烯醇纤维10份、SJ-2型引气剂6份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在45℃下采用水溶液自由基聚合法合成，在70℃下真空干燥36h制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，在温度为45℃加热搅拌1.0h后，将混合物取出，在温度为60℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
实施例2
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂15份、柠檬酸渣5份、聚乙烯醇纤维8份、SJ-2型引气剂4份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在50℃下采用水溶液自由基聚合法合成，在60℃下真空干燥72h制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，在温度为40℃加热搅拌1.5h后，将混合物取出，在温度为70℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
实施例3
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂20份、柠檬酸渣10份、聚乙烯醇纤维9份、SJ-2型引气剂5份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在40℃下采用水溶液自由基聚合法合成，在75℃真空干燥60制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，在温度为55℃加热搅拌1.0h后，将混合物取出，在温度为70℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
实施例4
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂16份、柠檬酸渣6份、聚乙烯醇纤维7份、SJ-2型引气剂5份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在45℃下采用水溶液自由基聚合法合成，在70℃真空干燥72h制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，加热搅拌1.0h后，将混合物取出，在温度为60℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
实施例5
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂13份、柠檬酸渣4份、聚乙烯醇纤维7份、SJ-2型引气剂4份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在50℃下采用水溶液自由基聚合法合成，在70℃真空干燥68制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，在50℃下加热搅拌1.5h后，将混合物取出，在温度为65℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
实施例6
一种大体积混凝土用多功能添加剂，由如下重量份数的原料组成：减水剂18份、柠檬酸渣8份、聚乙烯醇纤维9份、SJ-2型引气剂5份。所述是由甲基烯丙基聚氧乙烯醚30份、丙烯磺酸钠20份、马来酸酐12份为单体，用双氧水5份、硫代硫酸钠3份、丙烯酸15份复合引发，在50℃下采用水溶液自由基聚合法合成，在60℃真空干燥72h制得。所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20％。所述聚乙烯醇纤维的直径为40μm，长度为12mm。
所述大体积混凝土用多功能添加剂的制备方法如下：先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；再加入与混合料等体积量的去离子水，在40℃下加热搅拌1.0h后，将混合物取出，在温度为70℃下干燥，干燥完成后用球磨机研磨半小时，即得大体积混凝土用多功能添加剂。
将上述实施例1-6制得的混凝土用添加剂按照如下方法应用在大体积混凝土，所述大体积混凝土由如下重量份数的原料按照常规方法制成：水泥250份、砂790份、碎石1240份、添加剂10份和水125份。
为了进一步说明本发明方案的有益效果，以不使用添加剂的大体积混凝土以及只使用普通PCA减水剂的大体积混凝土进行对比。
对照例1
一种大体积混凝土，由如下重量分数的原料制成：水泥250份、砂790份、碎石1240份和水125份。
对照例2
一种大体积混凝土，由如下重量份数的原料制成：水泥250份、砂790份、石1240份、减水剂10份、水125份。所述减水剂为市场上购买的普通PCA减水剂。
以上实施例和对照例中所用的水泥、砂、碎石和水都相同，所述水泥为PO42.5普通硅酸盐水泥，砂为普通人工砂(细度模数为2.93,表观密度为2630kg/m3)，碎石为普通碎石(粒径为20～40mm，表观密度为2720kg/m3,压碎值为11.1％)，水为自来水。
根据《水工混凝土试验规程》(SL/T 352-2020)，制备上述实施例与对照例的大体积混凝土并测定混凝土坍落度、凝结时间、1d绝热温升、28d抗压强度，测试结果如表1所示。
表1：本发明添加剂应用在大体积混凝土的性能测试结果
从上述测试结果得知，本发明实施例的强度等级可以达到C30。使用大体积混凝土用多功能添加剂的混凝土整体流动性好，凝结时间长，绝热温升低，抗压强度大，综合性能好。
以上内容是结合具体的/优选的实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，其还可以对这些已描述的实施例做出若干替代或变型，而这些替代或变型方式都应视为属于本发明的保护范围。
Claims (9)
1.一种大体积混凝土用多功能添加剂，其特征在于：所述添加剂包括如下重量份数的原料：减水剂10~20份、柠檬酸渣3~10份、聚乙烯醇纤维5~10份、SJ-2型引气剂3~5份；所述减水剂是以甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠、丙烯酸复合引发，采用水溶液自由基聚合法合成，再经真空干燥制得。
2.根据权利要求1所述的减水剂中甲基烯丙基聚氧乙烯醚、丙烯磺酸钠、马来酸酐为单体，用双氧水、硫代硫酸钠和丙烯酸的质量比为30:20:12:5:3:15。
3.根据权利要求1所述的大体积混凝土用多功能添加剂，其特征在于：所述水溶液是在40~50℃下发生聚合合成反应。
4.根据权利要求1所述的大体积混凝土用多功能添加剂，其特征在于：所述柠檬酸渣为生产柠檬酸时产生的工业废渣，含水率为20%。
5.根据权利要求1所述的大体积混凝土用多功能添加剂，其特征在于：所述聚乙烯醇纤维的直径为40μm，长度为12mm。
6.根据权利要求1所述的大体积混凝土用多功能添加剂，其特征在于：所述真空干燥是在温度为60~80℃下干燥48~72h。
7.如权利要求1-6任一项所述一种大体积混凝土用多功能添加剂的制备方法，其特征在于：包括如下步骤：
S1:先将上述配比称取将减水剂、柠檬酸渣、聚乙烯醇纤维、SJ-2型引气剂，混合均匀，得混合料；
S2:再加入与混合料等体积量的去离子水，加热搅拌1.0~1.5h后，将混合物取出，再经过干燥，研磨，即得大体积混凝土用多功能添加剂。
8.根据权利要求7所述的大体积混凝土用多功能添加剂的制备方法，其特征在于：步骤S2所述加热温度为50~60℃，所述干燥是在温度为60~70℃下进行。
9.如权利要求1-8任一项所述的添加剂在大体积混凝土的应用，其特征在于：所述大体积混凝土包括如下重量份数的原料：水泥250份、砂790份、碎石1240份、添加剂10份和水125份。