CN114369414A - 一种版缝胶带及其制备方法 - Google Patents
一种版缝胶带及其制备方法 Download PDFInfo
- Publication number
- CN114369414A CN114369414A CN202111504330.0A CN202111504330A CN114369414A CN 114369414 A CN114369414 A CN 114369414A CN 202111504330 A CN202111504330 A CN 202111504330A CN 114369414 A CN114369414 A CN 114369414A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- coating resin
- adhesive tape
- base film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种版缝胶带，包括本体，本体包括PET基膜和粘接层，PET基膜上设有电晕层，粘接层设置在电晕层上，粘接层通过涂料树脂制备而成，使用粘贴时版缝胶带需经高温使涂料树脂溶解，且高温溶解的温度为140～180℃，本发明的优点：通过纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和离子水混合而成的涂料树脂，不仅使涂料树脂具有良好的耐水、耐热、隔热和抗压性能，而且还具备较强的防腐和抗氧化性能，从而提升产品的质量，减少了成品膜的报废，另外，本发明还提供了一种版缝胶带的制备方法，用于制备上述所述的版缝胶带。
Description
技术领域
本发明涉及一种版缝胶带及其制备方法。
背景技术
全息模压是把经电铸形成的具有全息图案的镍版包覆在版辊上，然后加热版辊，将涂有信息层的塑料薄膜通过模压机的版辊和压辊之间，由模压机的压合装置和传动装置把镍版上的全息图案压印在塑料薄膜上，形成全息膜，模压版辊的版缝处需要粘贴胶带，而现有的胶带容易折皱、鼓起，从而造成成品膜报废。
发明内容
本发明所要达到的目的就是提供一种版缝胶带，能提高胶带与版缝结合力，提升产品的质量。
为了解决上述技术问题，本发明是通过以下技术方案实现的：一种版缝胶带，包括本体，所述本体包括PET基膜和粘接层，所述PET基膜上设有电晕层，所述粘接层设置在电晕层上，所述粘接层通过涂料树脂制备而成，所述涂料树脂包括以下重量份的组份组成：35～50重量份的纳米远红外陶瓷粉、3～5.5重量份的硅酸钠、8～16重量份的酚醛树脂、1～1.5重量份的酸铵、5～8重量份的丙二醇、2～5.5重量份的硫酸钴碳酸钙、10～15重量份的聚异丁酯、1～3重量份的羟乙基纤维素、0.5～1重量份的香茅草粉末、0.5～1重量份的艾草粉末、1～5重量份的亚麻油、50～60重量份的去离子水，使用粘贴时版缝胶带需经高温使涂料树脂溶解，且高温溶解的温度为140～180℃。
优选的，所述涂料树脂包括以下重量份的组份组成：50重量份的纳米远红外陶瓷粉、3重量份的硅酸钠、8重量份的酚醛树脂、1重量份的酸铵、5重量份的丙二醇、2重量份的硫酸钴碳酸钙、10重量份的聚异丁酯、1重量份的羟乙基纤维素、0.5重量份的香茅草粉末、0.5重量份的艾草粉末、1重量份的亚麻油、50重量份的去离子水。
优选的，所述涂料树脂包括以下重量份的组份组成：45重量份的纳米远红外陶瓷粉、4.7重量份的硅酸钠、12.5重量份的酚醛树脂、1.25重量份的酸铵、7重量份的丙二醇、4重量份的硫酸钴碳酸钙、13重量份的聚异丁酯、2重量份的羟乙基纤维素、0.75重量份的香茅草粉末、0.7重量份的艾草粉末、3重量份的亚麻油、55重量份的去离子水。
优选的，所述涂料树脂包括以下重量份的组份组成：35重量份的纳米远红外陶瓷粉、5.5重量份的硅酸钠、16重量份的酚醛树脂、1.5重量份的酸铵、8重量份的丙二醇、5.5重量份的硫酸钴碳酸钙、15重量份的聚异丁酯、3重量份的羟乙基纤维素、1重量份的香茅草粉末、1重量份的艾草粉末、5重量份的亚麻油、60重量份的去离子水。
优选的，每一平方米的所述电晕层上所述涂料树脂的重量为0.8～1.1g。
优选的，所述PET基膜的厚度等于8～12μm。
本发明还提供了一种版缝胶带的制备方法，用于制备上述所述的版缝胶带，制备方法依次包括以下步骤：
步骤一：获取由纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和去离子水混合而成的涂料树脂；
步骤二：将步骤一获取的涂料树脂均匀的涂覆在PET基膜的电晕层上，并将其分切成版缝胶带。
优选的，步骤二中所述版缝胶带通过分切机进行分切，且所述版缝胶带的宽度为6～8mm。
综上所述，本发明的优点：通过纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和离子水混合而成的涂料树脂，不仅使涂料树脂具有良好的耐水、耐热、隔热和抗压性能，而且还具备较强的防腐和抗氧化性能，从而提升产品的质量，减少了成品膜的报废，而且该涂料树脂只需涂覆一次即可完成PET内电晕薄膜与涂料树脂分子间的交联反应，完美结合模压高温耐压的特殊性能要求，操作方便，大大提高生产效率，涂料树脂只需涂覆一次然后分切即可使用，从而有效的降低了使用成本，其次，本发明制备的版缝胶带在使用时需高温溶解，从而使版缝胶带有利于保存，减少了正常温度下版缝胶带的损坏，最后，在PET基膜上设有电晕层，能提高整个PET基膜的抗拉强度≥160MPa，伸长率≥80％，提高整体的抗张强度和抗冲击强度，使其具有优良的耐热、耐寒性和良好的耐化学药品性和耐油性。
具体实施方式
实施例一
一种版缝胶带，包括本体，所述本体包括PET基膜和粘接层，所述PET基膜上设有电晕层，所述粘接层设置在电晕层上，所述粘接层通过涂料树脂制备而成，所述涂料树脂包括以下重量份的组份组成：35～50重量份的纳米远红外陶瓷粉、3～5.5重量份的硅酸钠、8～16重量份的酚醛树脂、1～1.5重量份的酸铵、5～8重量份的丙二醇、2～5.5重量份的硫酸钴碳酸钙、10～15重量份的聚异丁酯、1～3重量份的羟乙基纤维素、0.5～1重量份的香茅草粉末、0.5～1重量份的艾草粉末、1～5重量份的亚麻油、50～60重量份的去离子水，使用粘贴时版缝胶带需经高温使涂料树脂溶解，且高温溶解的温度为140～180℃。
通过纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和离子水混合而成的涂料树脂，不仅使涂料树脂具有良好的耐水、耐热、隔热和抗压性能，而且还具备较强的防腐和抗氧化性能，从而提升产品的质量，减少了成品膜的报废，而且该涂料树脂只需涂覆一次即可完成PET内电晕薄膜与涂料树脂分子间的交联反应，完美结合模压高温耐压的特殊性能要求，操作方便，大大提高生产效率，涂料树脂只需涂覆一次然后分切即可使用，从而有效的降低了使用成本，其次，本发明制备的版缝胶带在使用时需高温溶解，从而使版缝胶带有利于保存，减少了正常温度下版缝胶带的损坏，最后，在PET基膜上设有电晕层，能提高整个PET基膜的抗拉强度≥160MPa，伸长率≥80％，提高整体的抗张强度和抗冲击强度，使其具有优良的耐热、耐寒性和良好的耐化学药品性和耐油性。
每一平方米的所述电晕层上所述涂料树脂的重量为0.8～1.1g，能减少涂料树脂的排布量，降低了使用成本，所述PET基膜的厚度等于8～12μm，使PET基膜具有抗拉强度≥160MPa，伸长率≥80％，有优良的耐热、耐寒性和良好的耐化学药品性和耐油性。
实施例二
所述涂料树脂包括以下重量份的组份组成：50重量份的纳米远红外陶瓷粉、3重量份的硅酸钠、8重量份的酚醛树脂、1重量份的酸铵、5重量份的丙二醇、2重量份的硫酸钴碳酸钙、10重量份的聚异丁酯、1重量份的羟乙基纤维素、0.5重量份的香茅草粉末、0.5重量份的艾草粉末、1重量份的亚麻油、50重量份的去离子水。
实施例三
所述涂料树脂包括以下重量份的组份组成：45重量份的纳米远红外陶瓷粉、4.7重量份的硅酸钠、12.5重量份的酚醛树脂、1.25重量份的酸铵、7重量份的丙二醇、4重量份的硫酸钴碳酸钙、13重量份的聚异丁酯、2重量份的羟乙基纤维素、0.75重量份的香茅草粉末、0.7重量份的艾草粉末、3重量份的亚麻油、55重量份的去离子水。
实施例四
所述涂料树脂包括以下重量份的组份组成：35重量份的纳米远红外陶瓷粉、5.5重量份的硅酸钠、16重量份的酚醛树脂、1.5重量份的酸铵、8重量份的丙二醇、5.5重量份的硫酸钴碳酸钙、15重量份的聚异丁酯、3重量份的羟乙基纤维素、1重量份的香茅草粉末、1重量份的艾草粉末、5重量份的亚麻油、60重量份的去离子水。
实施例五
一种版缝胶带的制备方法，用于制备实施例一、二、三和四所述的版缝胶带，制备方法依次包括以下步骤：
步骤一：获取由纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和去离子水混合而成的涂料树脂；
步骤二：将步骤一获取的涂料树脂均匀的涂覆在PET基膜的电晕层上，并通过分切机进行分切成版缝胶带，且所述版缝胶带的宽度为6～8mm。
除上述优选实施例外，本发明还有其他的实施方式，本领域技术人员可以根据本发明作出各种改变和变形，只要不脱离本发明的精神，均应属于本发明所附权利要求所定义的范围。
Claims (8)
1.一种版缝胶带，包括本体，其特征在于：所述本体包括PET基膜和粘接层，所述PET基膜上设有电晕层，所述粘接层设置在电晕层上，所述粘接层通过涂料树脂制备而成，所述涂料树脂包括以下重量份的组份组成：35～50重量份的纳米远红外陶瓷粉、3～5.5重量份的硅酸钠、8～16重量份的酚醛树脂、1～1.5重量份的酸铵、5～8重量份的丙二醇、2～5.5重量份的硫酸钴碳酸钙、10～15重量份的聚异丁酯、1～3重量份的羟乙基纤维素、0.5～1重量份的香茅草粉末、0.5～1重量份的艾草粉末、1～5重量份的亚麻油、50～60重量份的去离子水，使用粘贴时版缝胶带需经高温使涂料树脂溶解，且高温溶解的温度为140～180℃。
2.根据权利要求1所述的一种版缝胶带，其特征在于：所述涂料树脂包括以下重量份的组份组成：50重量份的纳米远红外陶瓷粉、3重量份的硅酸钠、8重量份的酚醛树脂、1重量份的酸铵、5重量份的丙二醇、2重量份的硫酸钴碳酸钙、10重量份的聚异丁酯、1重量份的羟乙基纤维素、0.5重量份的香茅草粉末、0.5重量份的艾草粉末、1重量份的亚麻油、50重量份的去离子水。
3.根据权利要求1所述的一种版缝胶带，其特征在于：所述涂料树脂包括以下重量份的组份组成：45重量份的纳米远红外陶瓷粉、4.7重量份的硅酸钠、12.5重量份的酚醛树脂、1.25重量份的酸铵、7重量份的丙二醇、4重量份的硫酸钴碳酸钙、13重量份的聚异丁酯、2重量份的羟乙基纤维素、0.75重量份的香茅草粉末、0.7重量份的艾草粉末、3重量份的亚麻油、55重量份的去离子水。
4.根据权利要求1所述的一种版缝胶带，其特征在于：所述涂料树脂包括以下重量份的组份组成：35重量份的纳米远红外陶瓷粉、5.5重量份的硅酸钠、16重量份的酚醛树脂、1.5重量份的酸铵、8重量份的丙二醇、5.5重量份的硫酸钴碳酸钙、15重量份的聚异丁酯、3重量份的羟乙基纤维素、1重量份的香茅草粉末、1重量份的艾草粉末、5重量份的亚麻油、60重量份的去离子水。
5.根据权利要求1至4任一项所述的一种版缝胶带，其特征在于：每一平方米的所述电晕层上所述涂料树脂的重量为0.8～1.1g。
6.根据权利要求1至4任一项所述的一种版缝胶带，其特征在于：所述PET基膜的厚度等于8～12μm。
7.一种版缝胶带的制备方法，其特征在于：用于制备权利要求1-6任一项所述的版缝胶带，制备方法依次包括以下步骤：
步骤一：获取由纳米远红外陶瓷粉、硅酸钠、酚醛树脂、酸铵、丙二醇、硫酸钴碳酸钙、聚异丁酯、羟乙基纤维素、香茅草粉末、艾草粉末、亚麻油和去离子水混合而成的涂料树脂；
步骤二：将步骤一获取的涂料树脂均匀的涂覆在PET基膜的电晕层上，并将其分切成版缝胶带。
8.根据权利要求7所述的一种版缝胶带的制备方法，其特征在于：步骤二中所述版缝胶带通过分切机进行分切，且所述版缝胶带的宽度为6～8mm。