CN114316846A - 一种含有聚苯乙烯微球的胶膜组合物及其制备方法和用途 - Google Patents
一种含有聚苯乙烯微球的胶膜组合物及其制备方法和用途 Download PDFInfo
- Publication number
- CN114316846A CN114316846A CN202111643146.4A CN202111643146A CN114316846A CN 114316846 A CN114316846 A CN 114316846A CN 202111643146 A CN202111643146 A CN 202111643146A CN 114316846 A CN114316846 A CN 114316846A
- Authority
- CN
- China
- Prior art keywords
- adhesive film
- hydroxy
- parts
- silane coupling
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种含有聚苯乙烯微球的胶膜组合物及其制备方法和用途。以重量份计所述胶膜组合物包括基体树脂80～98份、聚苯乙烯微球1～20份、主交联剂0.2～2份、助交联剂0.2～1份和硅烷偶联剂0.05～1份；所述硅烷偶联剂包括硅烷偶联剂单体和硅烷偶联剂低聚物的组合。所述胶膜组合物通过在基体树脂中加入聚苯乙烯微球，配合其他助剂的使用，在保证胶膜的机械性能的基础之上，能够提高胶膜的透过率，并且能够使所述胶膜呈现不同颜色；使得包括所述胶膜组合物的光伏组件发电功率高且美观。
Description
技术领域
本发明属于光伏组件技术领域，具体涉及一种含有聚苯乙烯微球的胶膜组合物及其制备方法和用途。
背景技术
光伏建筑一体化(BIVP)是一种将太阳能发电(光伏)产品集成到建筑上的技术。随着新能源的不断发展和城市节能减排、绿色环保需求的日益增加，太阳能光伏建筑一体化越来越成为太阳能应用发电的新潮流。
为了美观，越来越多的BIPV用组件不只选择以前的黑色，还会有其他各种颜色，而现有技术中多通过在胶膜中添加染料或颜料来提供颜色。CN204375770U公开了一种彩色封装胶膜，包括依次设置的透明乙烯-醋酸乙烯酯(EVA)胶膜层、彩色聚对苯二甲酸乙二醇酯(PET)膜层和透明EVA胶膜层，所述彩色聚对苯二甲酸乙二醇酯(PET)膜层通过添加不同颜色的色母粒制备得到，满足建筑装饰美化要求，也使得组件具有优异耐冲击强度和粘合力，延长组件使用寿命。但是，所述胶膜的透过率低且彩色胶膜会随着时间老化而使颜色变色。
CN102585715A公开了一种彩色EVA夹层胶片，所述胶片包括EVA、EVA载体色母、3-异丁烯丙基三乙氧基硅烷、十八烷基-3,5-双(1,1-二甲基乙基)-4-羟基苯丙酸酯、2-(2-羟基-5-叔辛基苯基)苯并三唑以及双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯；所述彩色EVA胶片耐冲击性能好，具有非常好的耐候性和长期保存性。但是所述胶片的透过率低且颜色单一。
CN202651156U公开了一种用于光伏建筑一体化的新型太阳能组件，包括正面玻璃层，正面玻璃层下方设置正面夹胶膜层，正面夹胶膜层与背面夹胶膜层中间设置光电组件层，背面夹胶膜层下方设置背面玻璃层，背面玻璃层为由颜料、乳浊剂和夜光粉混合制成的混合层。但是，所述组件通过添加颜料来制备彩色组件，存在褪色问题。
因此，开发一种透过率高、不会褪色且机械强度优异的彩色胶膜是本领域亟待解决的问题。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种含有聚苯乙烯微球的胶膜组合物及其制备方法和用途，所述胶膜组合物通过在基体树脂中加入聚苯乙烯微球，配合其他助剂的使用，在保证胶膜的机械性能的基础之上，能够提高胶膜的透过率，并且能够使所述胶膜呈现不同颜色。
为达此目的，本发明采用以下技术方案：
第一方面，本发明提供一种含有聚苯乙烯微球的胶膜组合物，以重量份计所述胶膜组合物包括基体树脂80～98份、聚苯乙烯微球1～20份、主交联剂0.2～2份、助交联剂0.2～1份和硅烷偶联剂0.05～1份；所述硅烷偶联剂包括硅烷偶联剂单体和硅烷偶联剂低聚物的组合。
本发明中，在所述胶膜组合物中加入聚苯乙烯微球，聚苯乙烯微球能够折射入射光，使肉眼看上去胶膜表现为彩色，同时使得胶膜的透过率提高，从而使得包括所述胶膜组合物的光伏组件的功率升高，并且通过聚苯乙烯微球和基体树脂、其他助剂的配合使用，使得所述胶膜组合物具有优异的机械性能和加工性能。
优选地，以重量份计所述含有聚苯乙烯微球的胶膜组合物包括基体树脂80～98份，例如可以为80份、82份、84份、86份、88份、90份、92份、94份、96份、98份等。
优选地，以重量份计所述含有聚苯乙烯微球的胶膜组合物包括聚苯乙烯微球1～20份，例如可以为2份、4份、6份、8份、10份、12份、14份、16份、18份、20份等。
本发明中，所述聚苯乙烯微球含量太多，不能加工成胶膜。
优选地，以重量份计所述含有聚苯乙烯微球的胶膜组合物包括主交联剂0.2～2份，例如可以为0.2份、0.4份、0.6份、0.8份、1份、1.2份、1.4份、1.6份、1.8份、2份等。
优选地，以重量份计所述含有聚苯乙烯微球的胶膜组合物包括助交联剂0.2～1份，例如可以为0.2份、0.3份、0.4份、0.5份、0.6份、0.7份、0.8份、0.9份、1份等。
优选地，以重量份计所述含有聚苯乙烯微球的胶膜组合物包括硅烷偶联剂0.05～1份，例如可以为0.06份、0.1份、0.2份、0.3份、0.4份、0.5份、0.6份、0.7份、0.8份、0.9份、1份等。
优选地，所述基体树脂包括乙烯-醋酸乙烯酯共聚物、乙烯-α-烯烃共聚物、乙烯-丙烯酸共聚物、乙烯-丙烯酸乙酯共聚物、乙烯-甲基丙烯酸甲酯共聚物、乙基-甲基丙烯酸酯共聚物、乙烯-丙烯酸丁酯共聚物、聚乙烯醇缩丁醛、离子聚合物或聚氨酯中的任意一种或至少两种的组合。
优选地，所述聚苯乙烯微球的粒径为100～800nm，例如可以为120nm、160nm、200nm、240nm、280nm、300nm、320nm、360nm、400nm、440nm、460nm、500nm、550nm、600nm、650nm、700nm、750nm等。
优选地，所述聚苯乙烯微球的折射率为0.1～3，例如可以为0.2、0.4、0.6、0.8、1、1.4、1.8、2、2.4、2.8等。
本发明中，可通过添加不同折射率的聚苯乙烯微球，从而使胶膜呈现不同颜色。
优选地，所述主交联剂包括过氧类交联剂。
优选地，所述过氧类交联剂包括过氧化2-乙基己基碳酸叔丁酯、过氧化2-乙基己基碳酸叔戊酯、2,5-二甲基-2,5-双(过氧化叔丁基)己烷、过氧化-3,5,5-三甲基己酸叔丁酯、二(4-甲基苯甲酰)过氧化物、过氧化二苯甲酰、1,1-二(叔丁基过氧)环己烷、叔丁基过氧化碳酸-2-乙基己酯、丁基-4,4-双(叔丁过氧基)戊酸酯、过氧化二异丙苯或α,α′-双(叔丁基过氧化)-1,3-二异丙苯中的任意一种或至少两种的组合。
优选地，所述助交联剂包括丙烯酸酯类交联剂和/或三烯丙基异氰脲酸酯。
优选地，所述丙烯酸酯酯类交联剂包括三羟甲基丙烷三丙烯酸酯、乙氧基化三羟甲基丙烷三丙烯酸酯或乙氧基化季戊四醇四丙烯酸酯中的任意一种或至少两种的组合。
优选地，所述硅烷偶联剂单体与硅烷偶联剂低聚物的质量比为1:(0.2～0.5)，例如可以为1:0.2、1:0.3、1:0.4、1:0.5等。
本发明中，所述硅烷偶联剂选用硅烷偶联剂单体和低聚物的组合，有助于提高胶膜的加工性能和抗老化性能；硅烷偶联剂单体与硅烷偶联剂低聚物的质量比大于1:0.2，所述胶膜的耐老化性能差，剥离力低；小于1:0.5，层压时胶膜的交联度低，胶膜的机械性能差。
优选地，所述硅烷偶联剂单体包括乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三(β-甲氧基乙氧基)硅烷、N-(2-氨乙基-3-氨丙基)三甲氧基硅烷、3-(2,3-环氧丙氧)丙基甲基二乙氧基硅烷、3-(甲基丙烯酰氯)丙基三甲基氧基硅烷、甲基丙氨丙烯氧丙基三甲氧基硅烷或3-(甲基丙烯酰氧基)丙基三甲氧基硅烷中的任意一种或至少两种的组合。
优选地，所述硅烷偶联剂低聚物的数均分子量为100～5000，例如可以为150、200、300、400、600、800、1000、2000、3000、4000、4500等。
优选地，所述硅烷偶联剂低聚物包括乙烯基三甲氧基硅烷低聚物、乙烯基三乙氧基硅烷低聚物、乙烯基三(β-甲氧基乙氧基)硅烷低聚物或3-(甲基丙烯酰氧基)丙基三甲氧基硅烷低聚物中的任意一种或至少两种的组合。
优选地，以重量份计所述胶膜组合物还包括0.05～5.5份光稳定剂，例如可以为0.08份、0.1份、0.5份、1份、1.5份、2份、2.5份、3份、3.5份、4份、4.5份、5份等。
优选地，所述光稳定剂包括紫外吸收剂和/或其它光稳定剂。
优选地，以重量份计所述光稳定剂包括0.01～0.4份紫外吸收剂，例如可以为0.01份、0.05份、0.1份、0.15份、0.2份、0.25份、0.3份、0.35份、0.4份等。
优选地，所述紫外吸收剂包括双(1-辛氧基-2,2,6,6-四甲基-4-哌啶基)癸二酸酯、双(1,2,2,6,6,-五甲基哌啶基)癸二酸酯、聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯或聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-[(2,2,6,6,-四甲基-哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)亚氨基]}中的任意一种或至少两种的组合。
优选地，以重量份计所述光稳定剂包括0.05～5份其它光稳定剂，例如可以为0.08份、0.1份、0.5份、1份、1.5份、2份、2.、5份、3份、3.5份、4份、4.5份、5份等。
优选地，所述其它光稳定剂包括2,2'-四亚甲基双(3,1-苯并噁嗪-4-酮)、2-羟基-4-甲氧基-2'-羧基二苯甲酮、2,2'-二羟基-4,4'-二甲氧基二苯甲酮、2-羟基-4-苯甲酰基氧基二苯甲酮、2,2',4,4'-四羟基二苯甲酮、2,2'-二羟基-4,4'-二甲氧基二苯甲酮、2-羟基-5-氯二苯甲酮、2-(2'-羟基-5'-叔丁基苯基)苯并三唑、2-(2'-羟基-5'-氨苯基)苯并三唑、双水杨酸双酚A酯、2-(2-羟基-3,5-二叔戊基苯基)苯并三唑、2-(2'-甲基-4'-羟基苯基)苯并三唑、双-(2-甲氧基-4-羟基-5-苯甲酰基苯基)甲烷、2-(2'-羟基-5-甲基苯基)苯并三唑、2-(2'-羟基-5-甲基苯基)-5-羧酸丁基酯苯并三唑、2-羟基-4-烷氧基二苯甲酮、3,5-二叔丁基-4-羟基-苯甲酸十六烷基酯、三(1,2,2,6,6-五甲基-4-哌啶基)亚磷酸酯、癸二酸双-2,2,6,6-四甲基哌啶醇酯、丁二酸与4-羟基-2,2,6,6-四甲基-1-哌啶醇的聚合物或N,N'-双(2,2,6,6-四甲基-4-哌啶基)-1,6-己二胺和2,4-二氯-6-(1,1,3,3-四甲基丁基)氨基-1,3,5-三嗪的聚合物中的任意一种或至少两种的组合。
第二方面，本发明提供一种胶膜，所述胶膜包括根据第一方面所述的含有聚苯乙烯微球的胶膜组合物。
优选地，所述胶膜的厚度为0.4～0.8mm，例如可以为0.4mm、0.45mm、0.5mm、0.55mm、0.6mm、0.65mm、0.7mm、0.75mm、0.8mm等。
第三方面，本发明提供一种根据第二方面所述的胶膜的制备方法，所述制备方法包括：
将胶膜组合物挤出、流延，得到所述胶膜。
优选地，所述挤出的设备为挤出流延膜机。
优选地，所述挤出的温度为50～110℃，例如可以为50℃、55℃、60℃、65℃、70℃、75℃、80℃、85℃、90℃、95℃、100℃、105℃等。
作为本发明优选的技术方案，所述胶膜的制备方法具体包括：按配方量，将基体树脂、聚苯乙烯微球、主交联剂、助交联剂、硅烷偶联剂和光稳定剂混合，加入到挤出流延膜机中，在温度为50～110℃的条件下挤出、流延冷却，得到所述胶膜。
第四方面，本发明提供一种光伏组件，所述光伏组件包括如第一方面所述的含有聚苯乙烯微球的胶膜组合物和/或如第二方面所述的胶膜。
本发明所述的数值范围不仅包括上述列举的点值，还包括没有列举出的上述数值范围之间的任意的点值，限于篇幅及出于简明的考虑，本发明不再穷尽列举所述范围包括的具体点值。
与现有技术相比，本发明的有益效果为：
本发明提供的含有聚苯乙烯微球的胶膜组合物，通过在基体树脂中加入聚苯乙烯微球，使得胶膜具有较高的透过率且可以呈现出不同颜色；通过聚苯乙烯微球与基体树脂及其他助剂的协同使用，使得所述胶膜具有优异的机械性能和加工性能。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
本发明中实施例和对比例提供的含有聚苯乙烯微球的胶膜组合物用到的材料如下：
乙烯-醋酸乙烯酯共聚物：购自韩华的282；
主交联剂：叔丁基过氧化碳酸-2-乙基己酯(TBEC)；
助交联剂：三烯丙基异氰脲酸酯(TAIC)；
硅烷偶联剂单体：乙烯基三甲氧基硅烷；
硅烷偶联剂低聚物：乙烯基三甲氧基硅烷低聚物；
紫外吸收剂：UV944；
其它光稳定剂：双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯。
实施例1
本实施例提供一种含有聚苯乙烯微球的胶膜组合物，以重量份计所述胶膜组合物包括94份乙烯-醋酸乙烯共聚物、3份聚苯乙烯微球、1份主交联剂、1份助交联剂、0.5份硅烷偶联剂单体、0.1份硅烷偶联剂低聚物、0.2份紫外吸收剂和0.2份其它光稳定剂。
本实施例提供一种胶膜，所述胶膜包括所述胶膜组合物，具体制备方法包括：
按配方量，将乙烯-醋酸乙烯共聚物、聚苯乙烯微球、主交联剂、助交联剂、硅烷偶联剂单体、硅烷偶联剂低聚物、紫外吸收剂和其它光稳定剂混合，在温度为80℃下，挤出流延，得到所述胶膜。
实施例2
本实施例提供一种含有聚苯乙烯微球的胶膜组合物，以重量份计所述胶膜组合物包括80份乙烯-醋酸乙烯共聚物、1份聚苯乙烯微球、0.2份主交联剂、0.2份助交联剂、0.05份硅烷偶联剂单体、0.01份硅烷偶联剂低聚物、0.05份紫外吸收剂和0.1份其它光稳定剂。
本实施例提供一种胶膜，所述胶膜包括所述胶膜组合物，具体制备方法与实施例1相同。
实施例3
本实施例提供一种含有聚苯乙烯微球的胶膜组合物，以重量份计所述胶膜组合物包括98份乙烯-醋酸乙烯共聚物、5份聚苯乙烯微球、2份主交联剂、1份助交联剂、0.6份硅烷偶联剂单体、0.3份硅烷偶联剂低聚物、0.4份紫外吸收剂和5份其它光稳定剂。
本实施例提供一种胶膜，所述胶膜包括所述胶膜组合物，具体制备方法与实施例1相同。
对比例1
本对比例提供一种胶膜组合物，其与实施例1的区别仅在于，将所述聚苯乙烯微球替换为等重量份的彩色母粒(上海精颜化工的5001)，其它原料、用量均与实施例1相同。
本对比例提供一种胶膜，所述胶膜包括对比例1提供的胶膜组合物，具体制备方法与实施例1相同。
对比例2
一种透明胶膜，所述透明胶膜为常州百佳薄膜科技有限生产的透明EVA胶膜。
应用例
一种光伏组件，所述光伏组件包括高效晶体硅太阳能电池片、超白布纹钢化玻璃、胶膜、透明背板以及铝合金边框；所述胶膜为实施例1～3、对比例1～2提供的胶膜。
性能测试
(1)胶膜的透过率：采用GB29848方法进行测试；
(2)光伏组件的正面发电功率：采用IEC61215标准进行测试。
具体测试结果如表1所示：
表1
由上表可知，本发明提供的胶膜组合物，通过在基体树脂中加入聚苯乙烯微球，以及通过所述胶膜组合物各组分间的配合使用，使得所述胶膜具有高的透过率，且能呈现不同颜色；使得包括所述胶膜的光伏组件发电功率高。
由实施例1～3可知，所述胶膜的透过率大于87％，包括所述胶膜的光伏组件的正面发电功率大于73W；由实施例1与对比例1比较可知，所述胶膜中采用彩色母粒替换聚苯乙烯微球时，胶膜的透过率和光伏组件的发电功率下降；由实施例1与对比例2比较可知，本发明提供的胶膜的透过率以及光伏组件的发电功率与透明膜相比相差不多，说明本发明提供的胶膜通过添加聚苯乙烯微球不仅能保持胶膜高的透过率和光伏组件的发电功率，而且还能够使得所述胶膜呈彩色，美观实用。
综上所述，本发明提供的胶膜组合物，通过聚苯乙烯微球和基体树脂、交联剂和偶联剂的协同作用，使得所述胶膜透过率高，且可制备不同颜色的胶膜，包括所述胶膜的光伏组件具有较高的发电功率。
以上所述的具体实施例，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种含有聚苯乙烯微球的胶膜组合物，其特征在于，以重量份计所述胶膜组合物包括基体树脂80～98份、聚苯乙烯微球1～20份、主交联剂0.2～2份、助交联剂0.2～1份和硅烷偶联剂0.05～1份；
所述硅烷偶联剂包括硅烷偶联剂单体和硅烷偶联剂低聚物的组合。
2.根据权利要求1所述的含有聚苯乙烯微球的胶膜组合物，其特征在于，所述基体树脂包括乙烯-醋酸乙烯酯共聚物、乙烯-α-烯烃共聚物、乙烯-丙烯酸共聚物、乙烯-丙烯酸乙酯共聚物、乙烯-甲基丙烯酸甲酯共聚物、乙基-甲基丙烯酸酯共聚物、乙烯-丙烯酸丁酯共聚物、聚乙烯醇缩丁醛、离子聚合物或聚氨酯中的任意一种或至少两种的组合。
3.根据权利要求1或2所述的含有聚苯乙烯微球的胶膜组合物，其特征在于，所述聚苯乙烯微球的粒径为100～800nm；
优选地，所述聚苯乙烯微球的折射率为0.1～3；
优选地，所述主交联剂包括过氧类交联剂；
优选地，所述过氧类交联剂包括过氧化2-乙基己基碳酸叔丁酯、过氧化2-乙基己基碳酸叔戊酯、2,5-二甲基-2,5-双(过氧化叔丁基)己烷、过氧化-3,5,5-三甲基己酸叔丁酯、二(4-甲基苯甲酰)过氧化物、过氧化二苯甲酰、1,1-二(叔丁基过氧)环己烷、叔丁基过氧化碳酸-2-乙基己酯、丁基-4,4-双(叔丁过氧基)戊酸酯、过氧化二异丙苯或α,α′-双(叔丁基过氧化)-1,3-二异丙苯中的任意一种或至少两种的组合；
优选地，所述助交联剂包括丙烯酸酯类交联剂和/或三烯丙基异氰脲酸酯；
优选地，所述丙烯酸酯酯类交联剂包括三羟甲基丙烷三丙烯酸酯、乙氧基化三羟甲基丙烷三丙烯酸酯或乙氧基化季戊四醇四丙烯酸酯中的任意一种或至少两种的组合。
4.根据权利要求1～3任一项所述的含有聚苯乙烯微球的胶膜组合物，其特征在于，所述硅烷偶联剂单体与硅烷偶联剂低聚物的质量比为1:(0.2～0.5)；
优选地，所述硅烷偶联剂单体包括乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三(β-甲氧基乙氧基)硅烷、N-(2-氨乙基-3-氨丙基)三甲氧基硅烷、3-(2,3-环氧丙氧)丙基甲基二乙氧基硅烷、3-(甲基丙烯酰氯)丙基三甲基氧基硅烷或3-(甲基丙烯酰氧基)丙基三甲氧基硅烷中的任意一种或至少两种的组合；
优选地，所述硅烷偶联剂低聚物的数均分子量为100～5000；
优选地，所述硅烷偶联剂低聚物包括乙烯基三甲氧基硅烷低聚物、乙烯基三乙氧基硅烷低聚物、乙烯基三(β-甲氧基乙氧基)硅烷低聚物或3-(甲基丙烯酰氧基)丙基三甲氧基硅烷低聚物中的任意一种或至少两种的组合。
5.根据权利要求1～4任一项所述的含有聚苯乙烯微球的胶膜组合物，其特征在于，以重量份计所述胶膜组合物还包括0.05～5.5份光稳定剂；
优选地，所述光稳定剂包括紫外吸收剂和/或其它光稳定剂；
优选地，以重量份计所述光稳定剂包括0.01～0.4份紫外吸收剂；
优选地，所述紫外吸收剂包括双(1-辛氧基-2,2,6,6-四甲基-4-哌啶基)癸二酸酯、双(1,2,2,6,6,-五甲基哌啶基)癸二酸酯、聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯或聚{[6-[(1,1,3,3-四甲基丁基)氨基]]-1,3,5-三嗪-2,4-[(2,2,6,6,-四甲基-哌啶基)亚氨基]-1,6-己二撑[(2,2,6,6-四甲基-4-哌啶基)亚氨基]}中的任意一种或至少两种的组合；
优选地，以重量份计所述光稳定剂包括0.05～5份其它光稳定剂；
优选地，所述其它光稳定剂包括2,2'-四亚甲基双(3,1-苯并噁嗪-4-酮)、2-羟基-4-甲氧基-2'-羧基二苯甲酮、2,2'-二羟基-4,4'-二甲氧基二苯甲酮、2-羟基-4-苯甲酰基氧基二苯甲酮、2,2',4,4'-四羟基二苯甲酮、2,2'-二羟基-4,4'-二甲氧基二苯甲酮、2-羟基-5-氯二苯甲酮、2-(2'-羟基-5'-叔丁基苯基)苯并三唑、2-(2'-羟基-5'-氨苯基)苯并三唑、双水杨酸双酚A酯、2-(2-羟基-3,5-二叔戊基苯基)苯并三唑、2-(2'-甲基-4'-羟基苯基)苯并三唑、双-(2-甲氧基-4-羟基-5-苯甲酰基苯基)甲烷、2-(2'-羟基-5-甲基苯基)苯并三唑、2-(2'-羟基-5-甲基苯基)-5-羧酸丁基酯苯并三唑、2-羟基-4-烷氧基二苯甲酮、3,5-二叔丁基-4-羟基-苯甲酸十六烷基酯、三(1,2,2,6,6-五甲基-4-哌啶基)亚磷酸酯、癸二酸双-2,2,6,6-四甲基哌啶醇酯、丁二酸与4-羟基-2,2,6,6-四甲基-1-哌啶醇的聚合物或N,N'-双(2,2,6,6-四甲基-4-哌啶基)-1,6-己二胺和2,4-二氯-6-(1,1,3,3-四甲基丁基)氨基-1,3,5-三嗪的聚合物中的任意一种或至少两种的组合。
6.一种胶膜，其特征在于，所述胶膜包括根据权利要求1～5任一项所述的含有聚苯乙烯微球的胶膜组合物。
7.根据权利要求6所述的胶膜，其特征在于，所述胶膜的厚度为0.4～0.8mm。
8.一种根据权利要求6或7所述的胶膜的制备方法，其特征在于，所述制备方法包括：
将胶膜组合物挤出、流延，得到所述胶膜。
9.根据权利要求8所述的制备方法，其特征在于，所述挤出的设备为挤出流延膜机；
优选地，所述挤出的温度为50～110℃。
10.一种光伏组件，其特征在于，所述光伏组件包括如权利要求1～5任一项所述的含有聚苯乙烯微球的胶膜组合物和/或如权利要求6或7所述的胶膜。