CN114278049A - Construction method of titanium porcelain water paint terrace - Google Patents
Construction method of titanium porcelain water paint terrace Download PDFInfo
- Publication number
- CN114278049A CN114278049A CN202210035105.5A CN202210035105A CN114278049A CN 114278049 A CN114278049 A CN 114278049A CN 202210035105 A CN202210035105 A CN 202210035105A CN 114278049 A CN114278049 A CN 114278049A
- Authority
- CN
- China
- Prior art keywords
- water paint
- coating
- titanium porcelain
- porcelain water
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a construction method of a titanium porcelain water paint terrace, which belongs to the technical field of terraces and comprises the following steps: the method comprises the following steps: treating a base layer, namely cleaning oil stains, garbage and various impurities on the surface of the concrete base layer, polishing the uneven part of the surface of the base layer, and filling the gap part; step two: rolling and coating a primer, and mixing the titanium porcelain water paint and a curing agent to roll and coat the base layer for the first time after the base layer is treated; step three: rolling and coating finish paint, wherein after rolling and coating the base layer for 30-80min for the first time, rolling and coating titanium porcelain water paint for the first time, and after rolling and coating the titanium porcelain water paint for 8-24h for the first time, rolling and coating a second layer of titanium porcelain water paint uniformly; step four: drawing a line, namely drawing a line on the terrace according to a construction drawing; step five: checking, after the titanium porcelain water paint is completely coated, checking whether the coating is flat or not and whether a skin-cracking phenomenon occurs or not, and if the skin-cracking phenomenon occurs, cleaning and then repeating the second step to the fourth step; step six: and (5) maintaining, namely drying the finish paint in a dry environment for 72 hours and then putting into use.
Description
Technical Field
The invention relates to the technical field of terraces, in particular to a construction method of a titanium porcelain water paint terrace.
Background
The paint is a continuous film which is coated on the surface of a protected or decorated object and can form firm adhesion with the object to be coated, and is a viscous liquid which is prepared by taking resin, oil or emulsion as a main material, adding or not adding pigments and fillers, adding corresponding auxiliary agents and using organic solvent or water. The paint is a material which can be coated on the surface of an object by different construction processes to form a continuous solid film with firm adhesion and certain strength. The film thus formed is generally called a coating film, also called a paint film or a coating. The early coating mostly uses vegetable oil as a main raw material, so the coating is called as 'paint', the traditional coating product using natural substances as raw materials or the coating product using synthetic chemical products as raw materials in modern development belong to organic chemical high polymer materials, and the formed coating film belongs to a high polymer compound type. According to the modern popular classification of chemical products, the coating belongs to fine chemical products.
The existing terrace is generally roll-coated with common paint, and after the common terrace is finished, the wear resistance is poor, the odor volatility is high, toxic and harmful substances are released, and the body health of a user is influenced.
Disclosure of Invention
The invention aims to solve the technical problem of providing a construction method of a titanium porcelain water paint terrace, which can improve the wear resistance of the terrace and prolong the service life of the terrace.
In order to solve the technical problems, the technical scheme of the invention is as follows:
a construction method of a titanium porcelain water paint terrace comprises the following steps:
the method comprises the following steps: treating a base layer, namely cleaning oil stains, garbage and various impurities on the surface of a concrete base layer, polishing the uneven part of the surface of the base layer, filling the gap part, and polishing the concave part after filling the gap part by cement or putty powder;
step two: rolling and coating a primer, and mixing the titanium porcelain water paint and a curing agent to roll and coat the base layer for the first time after the base layer is treated;
step three: rolling and coating finish paint, wherein after rolling and coating the base layer for 30-80min for the first time, rolling and coating titanium porcelain water paint for the first time, and after rolling and coating the titanium porcelain water paint for 8-24h for the first time, rolling and coating a second layer of titanium porcelain water paint uniformly;
step four: drawing a line, namely drawing a line on the terrace according to a construction drawing;
step five: checking, after the titanium porcelain water paint is completely coated, checking whether the coating is flat or not and whether a skin-cracking phenomenon occurs or not, and if the skin-cracking phenomenon occurs, cleaning and then repeating the second step to the fourth step;
step six: and (5) maintaining, namely drying the finish paint in a dry environment for 72 hours and then putting into use.
Preferably, the weight ratio of the titanium porcelain water paint to the curing agent in the second step is 7: and 3, mixing the titanium porcelain water paint and the curing agent, stirring for 15-25min, and standing for 30min after stirring.
Preferably, the titanium porcelain water paint is prepared from the following raw materials in parts by weight: 10-15 parts of nano titanium dioxide, 12-17 parts of nano silicon dioxide, 10-12 parts of nano aluminum oxide, 5-8 parts of rare earth, 3-5 parts of dispersing agent, 15-20 parts of adhesive and 90-95 parts of deionized water.
Preferably, the binder is a silica sol or a resin.
Adopt above-mentioned technical scheme, through having scribbled titanium porcelain water paint on the basic unit again, accomplished the preparation of terrace, had following beneficial effect:
1. the hardness of the terrace can be improved, so that the hardness of the cement surface is improved by 3-5 times;
2. after construction is finished, the paint is non-toxic and tasteless, does not contain formaldehyde, benzene and heavy metals, and is harmless to the health of a human body;
3. the fireproof performance of the terrace is improved;
4. oil-proof, water-proof and water seepage prevention frost cracking;
5. the wear resistance of the terrace is improved.
Detailed Description
The following further describes the embodiments of the present invention. It should be noted that the description of the embodiments is provided to help understanding of the present invention, but the present invention is not limited thereto. In addition, the technical features involved in the embodiments of the present invention described below may be combined with each other as long as they do not conflict with each other.
A construction method of a titanium porcelain water paint terrace comprises the following steps:
the method comprises the following steps: treating a base layer, namely cleaning oil stains, garbage and various impurities on the surface of a concrete base layer, polishing the uneven part of the surface of the base layer, filling the gap part, and polishing the concave part after filling the gap part by cement or putty powder;
the base layer can be a newly-finished concrete layer, when the base layer is treated, dust on the surface can be cleaned up through a dust collector, a concave place is filled with cement or putty powder and then polished to be flat, and the flatness requirement is less than 3 mm;
step two: rolling and coating a primer, and mixing the titanium porcelain water paint and a curing agent to roll and coat the base layer for the first time after the base layer is treated;
after the base layer is treated, the primer is uniformly coated by rolling, and the weight ratio of the titanium porcelain water paint to the curing agent is 7: 3, mixing the titanium porcelain water paint and the curing agent, stirring for 15-25min, standing for 30min after stirring, and mixing the curing agent to improve the curing speed;
step three: rolling and coating finish paint, wherein after rolling and coating the base layer for 30-80min for the first time, rolling and coating titanium porcelain water paint for the first time, and after rolling and coating the titanium porcelain water paint for 8-24h for the first time, rolling and coating a second layer of titanium porcelain water paint uniformly;
after the surface of the primer is dried, repeatedly roll-coating along a certain direction by adopting a roll-coating method, and roll-coating titanium porcelain water paint twice;
step four: drawing a line, namely drawing a line on the terrace according to a construction drawing;
step five: checking, after the titanium porcelain water paint is completely coated, checking whether the coating is flat or not and whether a skin-cracking phenomenon occurs or not, and if the skin-cracking phenomenon occurs, cleaning and then repeating the second step to the fourth step;
step six: maintaining, namely drying the finish paint in a dry environment for 72 hours and then putting into use;
the titanium porcelain water paint has the characteristics of environmental protection, has no emission of formaldehyde, toluene and heavy metals in the production, application and recovery processes, can resist the high temperature of 500-1200 ℃, has corrosion resistance, has super strong tolerance to salt fog and seawater due to a unique Si-O bond structure, has wide applicability, can be sprayed on copper, aluminum, pot paste, wood, plastic, glass fiber reinforced plastic, concrete, GRC and calcium silicate board glass, can directly express the texture of a base material, has the performance of normal temperature curing, has high hardness, has the hardness of 4-9H after being sprayed, is multiple times of that of the traditional paint, has excellent hydrophobic characteristic, is not easy to be stained with dust, can be cleaned after being washed by rainwater, is a semi-permanent material, has tolerance to environmental change and ultraviolet rays within a long time, is not easy to change color and pulverize, and has good antistatic performance, the adsorption of dust on the surface of the coating can be reduced, the self-cleaning performance is better, and the potential safety hazard caused by static electricity can be effectively reduced in the electronic industry and the petrochemical industry;
the titanium porcelain water paint is prepared from the following raw materials in parts by weight: 12 parts of nano titanium dioxide, 15 parts of nano silicon dioxide, 11 parts of nano aluminum oxide, 7 parts of rare earth, 4 parts of dispersing agent, 17 parts of adhesive and 93 parts of deionized water;
in other embodiments of this embodiment, the titanium porcelain enamel can be prepared from the following raw materials in parts by weight: 10 parts of nano titanium dioxide, 12 parts of nano silicon dioxide, 10 parts of nano aluminum oxide, 5 parts of rare earth, 3 parts of dispersing agent, 15 parts of adhesive and 90 parts of deionized water;
in other embodiments of this embodiment, the titanium porcelain water paint may also be prepared from the following raw materials in parts by weight: 15 parts of nano titanium dioxide, 17 parts of nano silicon dioxide, 12 parts of nano aluminum oxide, 8 parts of rare earth, 5 parts of dispersing agent, 20 parts of adhesive and 95 parts of deionized water;
wherein the adhesive is silica sol or resin.
The embodiments of the present invention have been described in detail, but the present invention is not limited to the described embodiments. It will be apparent to those skilled in the art that various changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, and the scope of protection is still within the scope of the invention.
Claims (4)
1. The construction method of the titanium porcelain water paint terrace is characterized by comprising the following steps:
the method comprises the following steps: treating a base layer, namely cleaning oil stains, garbage and various impurities on the surface of a concrete base layer, polishing the uneven part of the surface of the base layer, filling the gap part, and polishing the concave part after filling the gap part by cement or putty powder;
step two: rolling and coating a primer, and mixing the titanium porcelain water paint and a curing agent to roll and coat the base layer for the first time after the base layer is treated;
step three: rolling and coating finish paint, wherein after rolling and coating the base layer for 30-80min for the first time, rolling and coating titanium porcelain water paint for the first time, and after rolling and coating the titanium porcelain water paint for 8-24h for the first time, rolling and coating a second layer of titanium porcelain water paint uniformly;
step four: drawing a line, namely drawing a line on the terrace according to a construction drawing;
step five: checking, after the titanium porcelain water paint is completely coated, checking whether the coating is flat or not and whether a skin-cracking phenomenon occurs or not, and if the skin-cracking phenomenon occurs, cleaning and then repeating the second step to the fourth step;
step six: and (5) maintaining, namely drying the finish paint in a dry environment for 72 hours and then putting into use.
2. The construction method of the titanium porcelain water paint terrace according to the claim 1, characterized in that: in the second step, the weight ratio of the titanium porcelain water paint to the curing agent is 7: and 3, mixing the titanium porcelain water paint and the curing agent, stirring for 15-25min, and standing for 30min after stirring.
3. The construction method of the titanium porcelain water paint terrace according to the claim 1, characterized in that: the titanium porcelain water paint is prepared from the following raw materials in parts by weight: 10-15 parts of nano titanium dioxide, 12-17 parts of nano silicon dioxide, 10-12 parts of nano aluminum oxide, 5-8 parts of rare earth, 3-5 parts of dispersing agent, 15-20 parts of adhesive and 90-95 parts of deionized water.
4. The construction method of the titanium porcelain water paint terrace according to the claim 3, characterized in that: the adhesive is silica sol or resin.