CN105370013A - Epoxy floor and laying method thereof - Google Patents
Epoxy floor and laying method thereof Download PDFInfo
- Publication number
- CN105370013A CN105370013A CN201510854916.8A CN201510854916A CN105370013A CN 105370013 A CN105370013 A CN 105370013A CN 201510854916 A CN201510854916 A CN 201510854916A CN 105370013 A CN105370013 A CN 105370013A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- layer
- epoxide terrace
- laying method
- cloth layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention specifically relates to an epoxy floor and a laying method thereof, and belongs to the technical field of epoxy floor. The epoxy floor sequentially comprises, from bottom to top, an epoxy primer layer, a carbon fiber cloth layer, a mortar filling layer, and an epoxy finish paint coating. The laying method comprises the steps of processing the base surface, applying primer, laying a carbon fiber cloth layer, filling expansion joints and breaks with epoxy mortar, and applying and curing epoxy finish paint. The epoxy floor laid by the laying method of the invention has the advantages of being resistant to corrosion, impact, abrasion, and the like.
Description
Technical field
The invention belongs to epoxide terrace technical field, be specifically related to a kind of epoxide terrace and laying method thereof.
Background technology
Epoxide terrace is a kind of high strength, floor wear-resistant, attractive in appearance, advantages such as having without seam, quality is solid, resistance to chemical reagents is good, anticorrosion, dust-proof, easy maintenance, maintenance cost are cheap.Epoxide terrace roughly can be divided into: epoxy resin grinding stone terrace, epoxy resin color sand pressure sandy ground level ground, epoxy resin gravity flow self-leveling floor, epoxy resin mortar type terrace, epoxy resin put down painting type terrace.
Epoxide terrace is from the outset for functional terrace: as anticorrosion, wear-resisting, anti-skidding, develops into general general industry terrace; Except having functional requirement, also there is good ornamental effect.At present, epoxide terrace, due to the performance of its excellence, is widely used in the fields such as electronic apparatus, food, medicine, chemical industry, but itself still there is the deficiencies such as rotproofness, weatherability, shock resistance and stretch-proof performance.Conventional improving one's methods mainly coats anticorrosion surface layer on epoxide terrace surface, and the corrosion resistance of the epoxide terrace that this improvement is formed obtains certain lifting, but still has much room for improvement in shock resistance and stretch-proof aspect of performance.
The present invention aims to provide a kind of corrosion-resistant, epoxide terrace that anti-impact force is strong.
Summary of the invention
The object of the invention is to provide a kind of epoxide terrace and laying method thereof, this epoxide terrace paint has corrosion resistance, the advantage such as shock-resistant, wear-resisting.
The technical solution used in the present invention is as follows:
A kind of epoxide terrace, is followed successively by epoxy primer layer from top to bottom, carbon fibre cloth layer, mortar fills up layer and epoxy finish coating.
Described carbon fibre cloth layer is that carbon fiber and polypropylene spinning thermo-compression bonding form.
Further, described epoxy finish coating is twice, adds lemonade during brushing.
The laying method of above-described a kind of epoxide terrace, comprises the steps:
(1) process basal plane, polishing is cleaned out;
(2) be coated with priming, close basal layer;
(3) carbon fiber and polypropylene spinning thermo-compression bonding are formed carbon fibre cloth layer, and at two sides brushing primer;
(4) with epoxy paint and quartz sand modulation epoxy mortar, shrinkage joint and breakage is filled up;
(5) brush epoxy finish and treat that it solidifies, and carry out maintenance.
Further, the roller coating of priming wool cylinder is coated with in described step (2).
Beneficial effect of the present invention is: the epoxide terrace that the present invention lays has the advantages such as corrosion-resistant, shock-resistant, wear-resisting, wherein carbon fibre cloth layer strengthens its impact resistance especially, can be widely used in the Workplace of the industries such as electronics, precision instrument, medicine.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail, but should not be construed as limitation of the present invention.The raw material used in the present invention unless otherwise noted, all by commercial acquisition.
Embodiment 1
A kind of epoxide terrace, is followed successively by epoxy primer layer from top to bottom, carbon fibre cloth layer, mortar fills up layer and epoxy finish coating.Described carbon fibre cloth layer is that carbon fiber and polypropylene spinning thermo-compression bonding form.
Described epoxy finish coating is twice, thickness 2-5mm, adds lemonade during brushing.
The laying method of above-described a kind of epoxide terrace, comprises the steps:
(1) process basal plane, polishing is cleaned out;
(2) be coated with priming, close basal layer;
(3) carbon fiber and polypropylene spinning thermo-compression bonding are formed carbon fibre cloth layer, and at two sides brushing primer;
(4) with epoxy paint and quartz sand modulation epoxy mortar, shrinkage joint and breakage is filled up;
(5) brush epoxy finish and treat that it solidifies, and carry out maintenance.
The roller coating of priming wool cylinder is coated with in described step (2).
Embodiment 2
A kind of epoxide terrace, is followed successively by epoxy primer layer from top to bottom, carbon fibre cloth layer, mortar fills up layer and epoxy finish coating.Described carbon fibre cloth layer is that carbon fiber and polypropylene spinning thermo-compression bonding form.
Described epoxy finish coating is together, and thickness 1-2.5mm adds lemonade during brushing.
The laying method of above-described a kind of epoxide terrace, comprises the steps:
(1) process basal plane, polishing is cleaned out;
(2) be coated with priming, close basal layer;
(3) carbon fiber and polypropylene spinning thermo-compression bonding are formed carbon fibre cloth layer, and at two sides brushing primer;
(4) with epoxy paint and quartz sand modulation epoxy mortar, shrinkage joint and breakage is filled up;
(5) brush epoxy finish and treat that it solidifies, and carry out maintenance.
The roller coating of priming wool cylinder is coated with in described step (2).
Reference examples
A kind of epoxide terrace, is followed successively by epoxy primer layer from top to bottom, layer is filled up by mortar and epoxy finish coating.
Described epoxy finish coating is twice, thickness 2-5mm.
The laying method of above-described a kind of epoxide terrace, comprises the steps:
(1) process basal plane, polishing is cleaned out;
(2) be coated with priming, close basal layer;
(3) with epoxy paint and quartz sand modulation epoxy mortar, shrinkage joint and breakage is filled up;
(4) brush epoxy finish and treat that it solidifies, and carry out maintenance.
The roller coating of priming wool cylinder is coated with in described step (2).
Performance test
Carry out performance test to the epoxide terrace that embodiment of the present invention 1-2 and reference examples lay, result is as following table:
Table 1 properties of product test data
| Embodiment 1 | Embodiment 2 | Reference examples | |
| Impact resistance, MPa | 138 | 124 | 76 |
| Acid resistance (20%H 2SO 4) | ＞48h | ＞48h | ＞48h |
| Alkali resistance (20%NaOH) | ＞72h | ＞72h | ＞72h |
| Abrasion resistance, mg/1000 time | 0.3 | 0.4 | 0.5 |
| Armaticity | Have | Have | Nothing |
As seen from the above table, the epoxide terrace that the present invention lays has corrosion resistance, shock-resistant, wear-resisting, fragrant advantage.
Claims (5)
1. an epoxide terrace, is characterized in that, is followed successively by epoxy primer layer from top to bottom, carbon fibre cloth layer, mortar fill up layer and epoxy finish coating.
2. a kind of epoxide terrace according to claim 1, is characterized in that, described carbon fibre cloth layer is that carbon fiber and polypropylene spinning thermo-compression bonding form.
3. a kind of epoxide terrace according to claim 1, is characterized in that, described epoxy finish coating is twice, adds lemonade during brushing.
4. the laying method of a kind of epoxide terrace according to claim 1, is characterized in that, comprise the steps:
(1) process basal plane, polishing is cleaned out;
(2) be coated with priming, close basal layer;
(3) carbon fiber and polypropylene spinning thermo-compression bonding are formed carbon fibre cloth layer, and at two sides brushing primer;
(4) with epoxy paint and quartz sand modulation epoxy mortar, shrinkage joint and breakage is filled up;
(5) brush epoxy finish and treat that it solidifies, and carry out maintenance.
5. the laying method of a kind of epoxide terrace according to claim 4, is characterized in that, is coated with the roller coating of priming wool cylinder in described step (2).