CN104481116A - Epoxy colored-stone floor - Google Patents
Epoxy colored-stone floor Download PDFInfo
- Publication number
- CN104481116A CN104481116A CN201410680209.7A CN201410680209A CN104481116A CN 104481116 A CN104481116 A CN 104481116A CN 201410680209 A CN201410680209 A CN 201410680209A CN 104481116 A CN104481116 A CN 104481116A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- colored
- coating
- aggregate
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an epoxy colored-stone floor. The epoxy colored-stone floor comprises a base layer, a base coating and a face coating and is characterized in that patterns are drawn on the surface of the base coating, then EVA foam sponge adhesive tapes are adhered along drawn pattern lines to form the patterns, each color area block is filled with graded aggregate, then epoxy resin coating is injected to enable the aggregate to be cured completely, and the EVA foam sponge adhesive tapes are dismounted. After the patterns are completed, background color is made, finally surface grinding and polishing are performed by using a laser grinding machine, and the epoxy colored-stone floor has mirror smooth face effect. Epoxy colored-stone floor materials of different patterns and different colors can be designed according to different application sites and can be attractive and practical.
Description
Technical field
The present invention relates to a kind of epoxy colored-stone terrace.
Background technology
Epoxide terrace can not have ash, integral seamless, non-leakage, easily cleans, and can not stockpile dust and bacterium; Mechanical strength is high, wear-resistant, shock-resistant; The characteristics such as chemicals such as acid and alkali resistance, salt, gasoline, machine oil diesel oil, make epoxide terrace be widely used.But current integral seamless epoxide terrace mainly contains the gravity flow flat pattern etc. of 0.2 ~ 0.5mm scumbling type, 1 ~ 5mm mortar (comprising color sand) type, 1 ~ 3mm.These terraces all adopt the mode of successively constructing, and the color of same plane layer is single, lack enjoying value and aesthetic effect.Therefore need exploitation badly and a kind ofly different patterns and the epoxy colored-stone terrace of color can be set according to different application place, make it more both artistic and practical.
Summary of the invention
single for improving existing epoxy colored-stone terrace color, lack enjoying value and aesthetic effect, the invention provides a kind of epoxy colored-stone terrace, different patterns and the epoxy colored-stone terrace of color can be set according to different application places, make epoxy colored-stone terrace more both artistic and practical.
The present invention realizes by the following technical solutions:
Epoxy colored-stone terrace of the present invention, comprises basic unit, scratch coat and finishing coat;
Described basic unit is the ground that grinding process is crossed;
In described substrate surface roller coating or batch to scrape epoxy primer and form scratch coat;
Draw a design at described base coating surface, then paste along drawn pattern line with eva foam sponge adhesive tape, form pattern, during the color lump having color to distinguish bonding eva foam sponge adhesive tape, closed block should be sticked into; The aggregate that level prepares is inserted in each block, and compacting, epoxy coating is mixed up according to pattern color, insert in aggregate by the mode of grouting, form saturated shape, make populated its completion of cure of epoxy coating relief of each block in pattern, then eva foam sponge adhesive tape is wherein removed; After pattern completes, start to do background colour, first fill the aggregate that level prepares, and then fill with epoxy coating, identical with pattern manipulation steps, after its completion of cure, use laser mill machine in surface grinding polishing again, finally make epoxy colored-stone terrace present mirror smooth effect.
Described epoxy coating is made up of the component of following percentage by weight:
Epoxy resin 10-20%, flexibilizer 2-6%, mineral filler 60-80%, thinner 5-10%, mill base 0-2%, curing compound 5-10%, above-mentioned percentage sum is 100%.
Described eva foam sponge adhesive tape is the eva foam sponge adhesive tape of 1cm*1cm.
Described aggregate is colored chicken girt, cobble, shell, glass sand or resin particle, and aggregate size is 4 ~ 10 orders.
Described scratch coat is formed through criticizing to scrape with cylinder roller coating or scraper by epoxy primer.
The thickness of described scratch coat is 80-100um.
Compared with prior art, the present invention has the following advantages: the pattern of epoxy colored-stone terrace can design in advance according to embody rule occasion, and pattern is various, makes epoxy colored-stone terrace more both artistic and practical; Structure of the present invention is simple, can shorten the engineering time of the epoxide terrace of pattern requirement of the same race.
Detailed description of the invention
Epoxy colored-stone terrace, comprises basic unit, scratch coat and finishing coat; Described basic unit is the ground that grinding process is crossed; Spray in described substrate surface or criticize and scrape epoxy primer formation scratch coat; Draw a design at described base coating surface, then use 1cm wide, the eva foam sponge adhesive tape that 1cm is thick is pasted along drawn pattern line, forms pattern, should stick into closed block during the color lump having color to distinguish bonding eva foam sponge adhesive tape.The aggregate (aggregate size is 4 ~ 10 orders, and aggregate can be colored chicken girt, cobble, shell, glass sand, resin particle etc.) that level prepares is inserted in each block, and compacting.Epoxy coating is mixed up according to the color of pattern, insert in aggregate by the mode of grouting, form saturated shape, two color watershed areas should careful operation when being in the milk, and prevents from polluting, if color separation region area is less, suggestion gradation is done, first do a kind of color, after its completion of cure, do the color on side again, can ensure that adjacent two colors are not contaminated mutually.Aggregate and resin altogether thickness are 1cm.The same operation, makes populated its completion of cure of epoxy coating relief in each region in pattern, then eva foam sponge adhesive tape is wherein removed.After pattern completes, start to do background colour, first fill graded aggregate, and then fill with epoxy resin, the same, after its completion of cure, then (laser mill machine can be levelling by laser teaching display stand at grinding and polishing above to use laser mill machine, the object of laser mill machine is used to be improve the final planeness aesthetics of grinding stone layer), finally make epoxy colored-stone terrace present mirror smooth effect.
Described epoxy coating is made up of the component of following percentage by weight:
Epoxy resin 20-30%, flexibilizer 2-6%, mineral filler 40-60%, thinner 5-10%, mill base 0-4%, curing compound 10-15%, above-mentioned percentage sum is 100%.
Described epoxy resin is preferably at least one in resin E44 and resin E51.
The preferred acrylonitrile-butadiene rubber of described flexibilizer.
At least one in described mineral filler preferably talc powder, quartz sand, quartz powder.
Described curing compound preferred polyamide class curing compound.
Described thinner is preferably butyl glycidyl ether.
Scratch coat is formed through cylinder roller coating by epoxy primer in an embodiment of the present invention.
In an embodiment of the present invention, described epoxy coating is made up of the component of following percentage by weight: epoxy resin 30%, flexibilizer 2%, mineral filler 40%, thinner 9%, mill base 4%, curing compound 15%.
Preferably the thickness of scratch coat is 80-100um.
Preferably epoxy coating is made up of the component of following percentage by weight: epoxy resin 25%, flexibilizer 5%, mineral filler 50%, thinner 8%, curing compound 12%.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (6)
1. epoxy colored-stone terrace, is characterized in that: comprise basic unit, scratch coat and finishing coat;
Described basic unit is the ground that grinding process is crossed;
In described substrate surface roller coating or batch to scrape epoxy primer and form scratch coat;
Draw a design at described base coating surface, then paste along drawn pattern line with eva foam sponge adhesive tape, form pattern, during the color lump having color to distinguish bonding eva foam sponge adhesive tape, closed block should be sticked into; The aggregate that level prepares is inserted in each block, and compacting, epoxy coating is mixed up according to pattern color, insert in aggregate by the mode of grouting, form saturated shape, make populated its completion of cure of epoxy coating relief of each block in pattern, then eva foam sponge adhesive tape is wherein removed; After pattern completes, start to do background colour, first fill the aggregate that level prepares, and then fill with epoxy coating, identical with pattern manipulation steps, after its completion of cure, use laser mill machine in surface grinding polishing again, finally make epoxy colored-stone terrace present mirror smooth effect.
2. epoxy colored-stone terrace according to claim 1, is characterized in that: described epoxy coating is made up of the component of following percentage by weight:
Epoxy resin 10-20%, flexibilizer 2-6%, mineral filler 60-80%, thinner 5-10%, mill base 0-2%, curing compound 5-10%, above-mentioned percentage sum is 100%.
3. epoxy colored-stone terrace according to claim 1, described in is characterized in that: described eva foam sponge adhesive tape is the eva foam sponge adhesive tape of 1cm*1cm.
4. epoxy colored-stone terrace according to claim 1, is characterized in that: described aggregate is colored chicken girt, cobble, shell, glass sand or resin particle, and aggregate size is 4-10 order.
5. epoxy colored-stone terrace according to claim 1, is characterized in that: described scratch coat is formed through criticizing to scrape with cylinder roller coating or scraper by epoxy primer.
6. epoxy colored-stone terrace according to claim 1, is characterized in that: the thickness of described scratch coat is 80-100um.