CN102991024A - Method for laying protection layer on surface of iron storage tank - Google Patents
Method for laying protection layer on surface of iron storage tank Download PDFInfo
- Publication number
- CN102991024A CN102991024A CN2011102676462A CN201110267646A CN102991024A CN 102991024 A CN102991024 A CN 102991024A CN 2011102676462 A CN2011102676462 A CN 2011102676462A CN 201110267646 A CN201110267646 A CN 201110267646A CN 102991024 A CN102991024 A CN 102991024A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- laying
- protective layer
- spreads
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for laying a protection layer on the surface of an iron storage tank. The technical scheme of the invention is characterized in that the method comprises the following steps: carrying out sand blast treatment of the metal surface to make the surface reach an Sa2.5 grade effect, carrying out isodirectional brush coating of a primer resin of the metal surface, allowing the obtained coat to solidify, carrying out isodirectional brush coating of the primer resin again, allowing the obtained new coat to solidify, laying a layer of a resin mortar on the surface of the coat, laying a reinforcement layer obtained through laying glass fiber clothes in an alternated manner to a required thickness of 3-5mm, laying a resin-rich layer, laying a layer of a plastic film on the surface, allowing to solidify, and uncovering the plastic film. The method for laying the protection layer on the surface of the iron storage tank has the characteristics of strong adhesion of the metal and the glass fiber reinforced plastic protection layer, long use time, no cracking, no exfoliation, and flattened and beautiful surface.
Description
?
Technical field
The present invention relates to a kind of iron reservoir surface and spread deposited protective layer method, belong to the chemical equipment field.
Background technology
Iron storage tank is a large amount of containers that are used for holding acid-base medium that use of the industries such as chemical industry, mine, medicine.Because the not acidproof corrosion that waits chemical medium of iron storage tank often needs to carry out anticorrosion to iron storage tank.Be used for now anticorrosion being mainly of storage tank and brush corrosion-resistant paint, inside lining anti-corrosive rubber layer and inner lining glass fiber reinforced plastic etc.But because the metal surface material characteristic, existing vinylite exists the problem with the metal surface poor adhesive force, often occurs flaking, the generation of the quality accidents such as bubbling, layering.
Summary of the invention
Purpose nine of the present invention be often occur flaking for solving iron reservoir surface now, the problem of the quality accidents such as bubbling, layering provides a kind of iron reservoir surface to spread to apply protective layer method.
Technical scheme of the present invention is: a kind of iron reservoir surface spreads applies protective layer method; its method step is: at first to the metal surface blasting treatment; make the surface reach Sa2.5 level effect; then the backing material resin is brushed in the same way in the metal surface; brush again the backing material resin after the curing one time; behind the backing material resin solidification; spread deposited one deck resin-bonded mastic on its surface; the enhancement layer that laggard oozy glass fiber cloth is alternately laid is to desired thickness 3-5mm; then spread and apply resin-rich layer; spread on the surface at last and apply layer of plastic film, throw off after cured.
A kind of iron reservoir surface spreads applies protective layer method, and the formulation by weight of above-mentioned backing material resin is: 100 parts of backing material resins, curing agent 2-4 part, promoter 1-4 part.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned resin-bonded mastic formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt, curing agent 2-4 part, promoter 1-4 part, 120 parts of talcum powder.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned enhancement layer formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt, 50 parts of glass fabrics, curing agent 2-4 part, promoter 1-4 part, 10 parts of white carbons.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned resin-rich layer formulation by weight is as follows: the resin-rich layer formulation by weight is as follows: 100 parts of vinylites, curing agent 2-4 part, promoter 1-4 part.
The invention has the beneficial effects as follows: metal and fiberglass protective layer adhesion are strong, and service time is long, does not ftracture, and do not peel off the characteristics that surfacing is attractive in appearance.
The specific embodiment
Below in conjunction with example the present invention is described in further detail: at first to the metal surface blasting treatment, make the surface reach Sa2.5 level effect, then the backing material resin is brushed in the same way in the metal surface, brush again the backing material resin after the curing one time, behind the backing material resin solidification, spread deposited one deck resin-bonded mastic on its surface, the enhancement layer that laggard oozy glass fiber cloth is alternately laid is to desired thickness 4mm, then spread and apply resin-rich layer, spread on the surface at last and apply layer of plastic film, throw off after cured.
A kind of iron reservoir surface spreads applies protective layer method, and the formulation by weight of above-mentioned backing material resin is: 100 parts of backing material resins, 3 parts in curing agent, 2 parts of promoter.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned resin-bonded mastic formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt, 3 parts in curing agent, 2 parts of promoter, 120 parts of talcum powder.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned enhancement layer formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt, 50 parts of glass fabrics, 3 parts in curing agent, 2 parts of promoter, white carbon: 10 parts.
A kind of iron reservoir surface spreads applies protective layer method, and above-mentioned resin-rich layer formulation by weight is as follows: the resin-rich layer formulation by weight is as follows: 100 parts of vinylites, 3 parts in curing agent, 2 parts of promoter.
Claims (5)
1. an iron reservoir surface spreads and applies protective layer method; it is characterized in that the following methods step: at first to the metal surface blasting treatment; make the surface reach Sa2.5 level effect; then the backing material resin is brushed in the same way in the metal surface; brush again the backing material resin after the curing one time; behind the backing material resin solidification; spread deposited one deck resin-bonded mastic on its surface; the enhancement layer that laggard oozy glass fiber cloth is alternately laid is to desired thickness 3-5MM; then spread and apply resin-rich layer; spread on the surface at last and apply layer of plastic film, throw off after cured.
2. a kind of iron reservoir surface according to claim 1 spreads and applies protective layer method, and it is characterized in that: the formulation by weight of above-mentioned backing material resin is: 100 parts of backing material resins, curing agent 2-4 part.
3. a kind of iron reservoir surface according to claim 1 spreads and applies protective layer method, and it is characterized in that: above-mentioned resin-bonded mastic formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt, curing agent 2-4 part, promoter 1-4 part, 120 parts of talcum powder.
4. a kind of iron reservoir surface according to claim 1 spreads and applies protective layer method, and it is characterized in that: above-mentioned enhancement layer formulation by weight is as follows: 100 parts of vinylites, 20 parts on chopped felt; 50 parts of glass fabrics; curing agent 2-4 part, promoter 1-4 part, 10 parts of white carbons.
5. a kind of iron reservoir surface according to claim 1 spreads and applies protective layer method, and it is characterized in that: above-mentioned resin-rich layer formulation by weight is as follows: 100 parts of vinylites, curing agent 2-4 part, promoter 1-4 part.