CN114249535A - 一种不含硝酸盐的晶质玻璃及其制备方法 - Google Patents
一种不含硝酸盐的晶质玻璃及其制备方法 Download PDFInfo
- Publication number
- CN114249535A CN114249535A CN202210002912.7A CN202210002912A CN114249535A CN 114249535 A CN114249535 A CN 114249535A CN 202210002912 A CN202210002912 A CN 202210002912A CN 114249535 A CN114249535 A CN 114249535A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- nitrate
- glass
- crystalline glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不含硝酸盐的晶质玻璃及其制备方法，所述不含硝酸盐的晶质玻璃包括下述重量份的原料：SiO2 71‑72份、Na2O 11‑12份、K2O 2‑3份、BaO 2‑3份、B2O3 1.5‑2份、Al2O3 1‑1.5份、ZnO 1‑1.5份、Li2O 0.2‑0.4份、CeO2 0.1‑0.2份、Er2O3 0.04‑0.05份。本发明的有益效果为：本发明所述不含硝酸盐的晶质玻璃各原料有机地结合在一起制得的晶质玻璃在不含硝酸盐的条件下，在玻璃色泽、透过率和折射率上均能满足要求。省去了在制备玻璃过程中脱硝设备的应用，提高了生产效率，降低了生产成本。
Description
技术领域
本发明属于玻璃制造技术领域，具体涉及一种不含硝酸盐的晶质玻璃及其制备方法。
背景技术
晶质玻璃是一种艺术玻璃，大部分含氧化铅、氧化钾的量较多无色透明、光泽好，易成型、硬度低，便于机械加工。晶质玻璃与其他玻璃相比雕刻琢磨后棱角清析醒目。碰击时有清脆悦耳的金属声的特点，通常主要用于制作玻璃器皿、工艺品、透镜等，经过造形雕刻琢磨加工制成别具风格的中、高档玻璃制品、或性能优良的透光玻璃制品，可雕刻成各种艺术品和日用器皿。
晶质玻璃在制造过程中，为保证玻璃色泽、透过率、折射率等，需在晶质玻璃的配方中加入一定量的硝酸盐，在晶质玻璃的生产工艺中必须配制脱硝设备来满足环保要求。但这无疑提高了晶质玻璃的生产成本，降低其生产效率。
发明内容
本发明的目的为提供一种在制备过程中无需使用脱硝设备，节省了晶质玻璃的制作成本，提高了晶质玻璃生产效率的不含硝酸盐的晶质玻璃及其制备方法。
为实现本发明的上述目的，本发明采用以下技术方案：
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 70-73份、Na2O11-13份、K2O 2-3.5份、BaO 2-4份、B2O3 1-2.5份、Al2O3 1-2份、ZnO 1-2份、Li2O0.1-0.5份、CeO20.1-0.3份、Er2O3 0.03-0.06份。
上述一种不含硝酸盐的晶质玻璃，作为一种优选的实施方案，包括下述重量份的原料：SiO2 71-72份、Na2O 11-12份、K2O 2-3份、BaO 2-3份、B2O3 1.5-2份、Al2O3 1-1.5份、ZnO 1-1.5份、Li2O 0.2-0.4份、CeO2 0.1-0.2份、Er2O3 0.04-0.05份。
上述一种不含硝酸盐的晶质玻璃，作为一种优选的实施方案，包括下述重量份的原料：SiO2 71份、Na2O 12份、K2O 2.5份、BaO 2.5份、B2O3 1.8份、Al2O3 1.6份、ZnO 1.2份、Li2O 0.3份、CeO2 0.15份、Er2O3 0.04份。
上述一种不含硝酸盐的晶质玻璃，作为一种优选的实施方案，包括下述重量份的原料：SiO2 71.5份、Na2O 11.5份、K2O 2份、BaO 2.5份、B2O3 1.5份、Al2O3 1.2份、ZnO 1.2份、Li2O 0.3份、CeO2 0.15份、Er2O3 0.04份。
SiO2(氧化硅)是一种无机物，硅原子和氧原子长程有序排列形成晶态二氧化硅，短程有序或长程无序排列形成非晶态二氧化硅。二氧化硅晶体中，硅原子位于正四面体的中心，四个氧原子位于正四面体的四个顶角上，许多个这样的四面体又通过顶角的氧原子相连，每个氧原子为两个四面体共有，即每个氧原子与两个硅原子相结合。是纯净的天然二氧化硅晶体，是一种坚硬、脆性、不容的无色透明的固体。熔点为1723℃。
Na2O(氧化钠)是一种无机物，灰白色粉末，熔点为1132℃，常温下为白色无定形片状或粉末。常用来制取钠的化合物，或用作脱氢剂、化学反应的聚合剂、缩合剂等。
K2O(氧化钾)是一种化合物，熔点为350℃，白色结晶性粉末。主要用于无机工业，是制造各种钾盐如硫酸钾、硝酸钾、氯酸钾、红矾钾等的基本原料。
BaO(氧化钡)是一种无机物，熔点1923℃，为无色立方晶体。主要用于玻璃、陶瓷工业、也用于甜菜糖精炼，用于制造过氧化钡和钡盐的原料，也可用作脱水剂和高效干燥剂等。
B2O3(三氧化二硼)是硼最主要的氧化物，是一种白色蜡状固体，一般以无定形的状态存在，很难形成晶体，但在高强度退火后也能结晶。熔融时可以溶解许多碱性的金属氧化物，生成有特征颜色的玻璃状硼酸盐和偏硼酸盐(玻璃)，用于制取元素硼和精细硼化合物。也可与多种氧化物化合制成具有特征颜色的硼玻璃、光学玻璃、耐热玻璃、仪器玻璃及玻璃纤维、光线防护材料等。熔点450℃。
Al2O3(三氧化二铝)是一种无机物，一种高硬度的化合物，熔点为2054℃，用作分析试剂、有机溶剂的脱水、吸附剂、有机反应催化剂、研磨剂、抛光剂、冶炼铝的原料、耐火材料等。
ZnO(氧化锌)是一种无机物，是锌的氧化物，熔点1975℃。是一种常用的化学添加剂，广泛地应用于塑料、硅酸盐制品、合成橡胶、润滑油、油漆涂料、药膏、粘合剂、食品、电池、阻燃剂等产品的制作中。氧化锌的能带隙和激子束缚能较大，透明度高，有优异的常温发光性能，在半导体领域的液晶显示器、薄膜晶体管、发光二极管等产品中均有应用。
Li2O(氧化锂)是锂最常见的氧化物，被广泛用作玻璃的成分。熔点1567℃。常被用作光谱纯试剂、特种玻璃、陶瓷、医药等领域。
CeO2(氧化铈)是一种无机物，淡黄或黄褐色助粉末，熔点2397℃，是有机反应的催化剂，用作玻璃工业添加剂，作板玻璃研磨材料，还可用在化妆品中起到抗紫外线作用。已扩大到眼镜玻璃、光学透镜、显像管的研磨，起脱色、澄清、玻璃的紫外线和电子线的吸收等作用。
Er2O3(氧化铒)是一种粉红色粉末，易吸收湿气和二氧化碳，熔点2387℃，主要用作钇铁柘榴石添加剂和核反应堆控制材料，也用于制造特种发光玻璃和吸收红外线的玻璃，还用作玻璃着色剂。
本发明的第二方面，提供一种不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入熔炉中进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
上述一种不含硝酸盐的晶质玻璃的制备方法，作为一种优选的实施方案，步骤(1)中，熔炉熔化的温度为1450℃-1500℃。
上述一种不含硝酸盐的晶质玻璃的制备方法，作为一种优选的实施方案，步骤(1)中，所述熔炉为电熔炉。
本发明的有益效果为：本发明所述不含硝酸盐的晶质玻璃各原料有机地结合在一起制得的晶质玻璃在不含硝酸盐的条件下，在玻璃色泽、透过率和折射率上均能满足要求。省去了在制备玻璃过程中脱硝设备的应用，提高了生产效率，降低了生产成本。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将对本发明的技术方案进行详细的描述。显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所得到的所有其它实施方式，都属于本发明所保护的范围。
实施例1
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 70重量份、Na2O11重量份、K2O 2重量份、BaO 2重量份、B2O3 1重量份、Al2O3 1重量份、ZnO 1重量份、Li2O 0.1重量份、CeO2 0.1重量份、Er2O3 0.03重量份。
实施例1所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1450℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
实施例2
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 71重量份、Na2O11重量份、K2O 2重量份、BaO 2重量份、B2O3 1.5重量份、Al2O3 1重量份、ZnO1重量份、Li2O 0.2重量份、CeO2 0.1重量份、Er2O3 0.04重量份。
实施例2所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1480℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
实施例3
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 72重量份、Na2O12重量份、K2O 3重量份、BaO 3重量份、B2O3 2重量份、Al2O3 1.5重量份、ZnO1.5重量份、Li2O 0.4重量份、CeO2 0.2重量份、Er2O3 0.05重量份。
实施例3所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1450℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
实施例4
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 71重量份、Na2O12重量份、K2O 2.5重量份、BaO 2.5重量份、B2O3 1.8重量份、Al2O3 1.6重量份、ZnO 1.2重量份、Li2O 0.3重量份、CeO2 0.15重量份、Er2O3 0.04重量份。
实施例4所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1500℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
实施例5
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 71.5重量份、Na2O11.5重量份、K2O 2重量份、BaO 2.5重量份、B2O3 1.5重量份、Al2O3 1.2重量份、ZnO 1.2重量份、Li2O 0.3重量份、CeO2 0.15重量份、Er2O3 0.04重量份。
实施例5所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1480℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
实施例6
一种不含硝酸盐的晶质玻璃，包括下述重量份的原料：SiO2 73重量份、Na2O13重量份、K2O 3.5重量份、BaO 4重量份、B2O3 2.5重量份、Al2O3 2重量份、ZnO2重量份、Li2O 0.5重量份、CeO2 0.3重量份、Er2O3 0.06重量份。
实施例6所述不含硝酸盐的晶质玻璃的制备方法，包括以下步骤：
(1)将上述各原料加入电熔炉中，在熔炉熔化温度为1500℃的条件下进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
采用T340仪器对本实施例熔制窑炉尾气进行检测NOx，事实证明无需脱硝设备也能满足国家环保要求，节约生产成本。
以上所述仅为本申请的优选实施例而已，并不用于限制本申请，对于本领域的技术人员来说，本申请可以有各种更改和变化。凡在本申请的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本申请的保护范围之内。
Claims (7)
1.一种不含硝酸盐的晶质玻璃，其特征在于，包括下述重量份的原料：SiO270-73份、Na2O 11-13份、K2O 2-3.5份、BaO 2-4份、B2O3 1-2.5份、Al2O3 1-2份、ZnO 1-2份、Li2O 0.1-0.5份、CeO2 0.1-0.3份、Er2O3 0.03-0.06份。
2.根据权利要求1所述不含硝酸盐的晶质玻璃，其特征在于，包括下述重量份的原料：SiO2 71-72份、Na2O 11-12份、K2O 2-3份、BaO 2-3份、B2O3 1.5-2份、Al2O3 1-1.5份、ZnO 1-1.5份、Li2O 0.2-0.4份、CeO2 0.1-0.2份、Er2O30.04-0.05份。
3.根据权利要求1所述不含硝酸盐的晶质玻璃，其特征在于，包括下述重量份的原料：SiO2 71份、Na2O 12份、K2O 2.5份、BaO 2.5份、B2O3 1.8份、Al2O31.6份、ZnO 1.2份、Li2O 0.3份、CeO2 0.15份、Er2O3 0.04份。
4.根据权利要求1所述不含硝酸盐的晶质玻璃，其特征在于，包括下述重量份的原料：SiO2 71.5份、Na2O 11.5份、K2O 2份、BaO 2.5份、B2O3 1.5份、Al2O31.2份、ZnO 1.2份、Li2O0.3份、CeO2 0.15份、Er2O3 0.04份。
5.权利要求1-4之一所述不含硝酸盐的晶质玻璃的制备方法，其特征在于，包括以下步骤：
(1)将上述各原料加入熔炉中进行熔化，得玻璃液；
(2)吹制玻璃液得晶质玻璃。
6.根据权利要求5所述不含硝酸盐的晶质玻璃的制备方法，其特征在于，步骤(1)中，熔炉熔化的温度为1450℃-1500℃。
7.根据权利要求5所述不含硝酸盐的晶质玻璃的制备方法，其特征在于，步骤(1)中，所述熔炉为电熔炉。