CN114230264A - Method for manufacturing inorganic mineral ecological environment-friendly wall material - Google Patents
Method for manufacturing inorganic mineral ecological environment-friendly wall material Download PDFInfo
- Publication number
- CN114230264A CN114230264A CN202010940243.9A CN202010940243A CN114230264A CN 114230264 A CN114230264 A CN 114230264A CN 202010940243 A CN202010940243 A CN 202010940243A CN 114230264 A CN114230264 A CN 114230264A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall material
- oxide
- ecological environment
- inorganic mineral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an inorganic mineral ecological environment-friendly wall material, which comprises the following components: 2-4 parts of hexacyclic ring stone powder; 2-6 parts of medical stone powder; 3-5 parts of tourmaline powder; 3-5 parts of bauxite; 2-4 parts of boron oxide; 2-4 parts of magnesium oxide; 0.05-0.07 part of ferric oxide; 0.8-3 parts of sodium oxide; 0.2-1 part of potassium oxide; 3-5 parts of silica sand; 1-3 parts of lignocellulose and 20-30 parts of diatomite; 20-30 parts of sierozem powder; 25-40 parts of heavy calcium carbonate powder; 5-15 parts of white cement. The manufacturing method of the inorganic mineral ecological environment-friendly wall material overcomes the defects of weak capability of decomposing harmful substances and weak antibacterial capability of the existing common diatom ooze wall material, can spontaneously release negative oxygen ions, has a strong sterilization function, and can directly decompose pollutants such as formaldehyde, toluene and the like into nontoxic and odorless carbon dioxide and water by the negative oxygen ions so as to achieve the purposes of purifying air and eliminating the pollutants.
Description
Technical Field
The invention relates to the technical field of interior decoration materials, in particular to a method for manufacturing an inorganic mineral ecological environment-friendly wall material.
Background
With the development of society and the progress of science and technology, people increasingly pay more attention to the quality of life, which is reflected in the aspect of indoor decoration, mainly turns to the comprehensive attention to various factors such as daily life environmental comfort, safety, environmental protection and the like from the single perspective of only paying attention to beauty in the past. Most of the currently used decoration materials are organic chemical coatings, generally contain volatile substances such as formaldehyde, benzene, xylene, ammonia, TVOC and the like which are extremely harmful to human health, and generally adopt a windowing ventilation method to discharge harmful gases and peculiar smell, or adopt methods such as an adsorbent and flower and grass cultivation to reduce indoor pollution, but the methods can not fundamentally eliminate pollution, and have low efficiency and troublesome operation.
Negative oxygen ion can be direct with pollutants such as formaldehyde, toluene decompose into nontoxic tasteless carbon dioxide and water, decompose indoor pollution, there is apparent influence to the purification of air, negative oxygen ion is known as "air vitamin" moreover, medical research shows that negative oxygen ion makes the oxygen content increase in the blood, be favorable to blood oxygen to carry, absorb and utilize, have the effect that promotes human metabolism, improve human immunity, strengthen human flesh ability, adjust the balanced effect of organism function. According to the examination, the negative oxygen ions have the effects of inhibiting, relieving and assisting in treating 7 systems of the human body, nearly 30 diseases, and particularly have more obvious health-care effect on the human body. Therefore, the purification of indoor pollution through negative oxygen ions is a new trend, and therefore, a manufacturing method of an inorganic mineral ecological environment-friendly wall material is provided.
Disclosure of Invention
The invention aims to provide a method for manufacturing an inorganic mineral ecological environment-friendly wall material, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: the manufacturing method of the inorganic mineral ecological environment-friendly wall material comprises the following components: 2-4 parts of hexacyclic ring stone powder; 2-6 parts of medical stone powder; 3-5 parts of tourmaline powder; 3-5 parts of bauxite; 2-4 parts of boron oxide; 2-4 parts of magnesium oxide; 0.05-0.07 part of ferric oxide; 0.8-3 parts of sodium oxide; 0.2-1 part of potassium oxide; 3-5 parts of silica sand; 1-3 parts of lignocellulose and 20-30 parts of diatomite; 20-30 parts of sierozem powder; 25-40 parts of heavy calcium carbonate powder; 5-15 parts of white cement.
Preferably, the fineness of the hexacyclic ring stone powder is 800 meshes.
Preferably, the fineness of the medical stone powder is 800 meshes.
Preferably, the fineness of the tourmaline powder is 800 meshes.
Preferably, the bauxite contains more than 86% of aluminum oxide by mass and has whiteness of more than 90 degrees,
the fineness is 800 meshes.
Preferably, the whiteness of the potassium oxide is more than 90 degrees, and the fineness is 1250 meshes.
Preferably, the mass content of calcium oxide in the sierozem powder is more than 80%, the fineness is 150-1250 meshes, and the whiteness is 75-98 degrees.
Preferably, the weight content of calcium carbonate in the heavy calcium carbonate is more than 75 percent, the fineness is 150-800 meshes, and the whiteness is 78-98 degrees.
Compared with the prior art, the invention has the beneficial effects that: the manufacturing method of the inorganic mineral ecological environment-friendly wall material,
1. the problem that the existing common diatom ooze wall material is weak in capability of decomposing harmful substances and weak in antibacterial capability is solved, negative oxygen ions can be spontaneously released, the negative oxygen ions have a strong sterilization function, and the negative oxygen ions can directly decompose pollutants such as formaldehyde and toluene into nontoxic and odorless carbon dioxide and water, so that the purposes of purifying air and eliminating the pollutants are achieved.
2. Through the synergistic effect of the hexacyclic stone, the medical stone, the tourmaline, the aluminum consolidated soil, the boron oxide, the magnesium oxide, the iron oxide, the sodium oxide and the potassium oxide, a large amount of negative oxygen ions are continuously induced, the release amount of the negative oxygen ions is 10000 per cubic centimeter, the purification effect is good, the purification efficiency is high, one part of the released negative oxygen ions is used for eliminating pollutants and purifying air, and the other part of the released negative oxygen ions is used for the health care function of a human body.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides a technical scheme that: the manufacturing method of the inorganic mineral ecological environment-friendly wall material comprises the following components: 2-4 parts of hexacyclic ring stone powder; 2-6 parts of medical stone powder; 3-5 parts of tourmaline powder; 3-5 parts of bauxite; 2-4 parts of boron oxide; 2-4 parts of magnesium oxide; 0.05-0.07 part of ferric oxide; 0.8-3 parts of sodium oxide; 0.2-1 part of potassium oxide; 3-5 parts of silica sand; 1-3 parts of lignocellulose and 20-30 parts of diatomite; 20-30 parts of sierozem powder; 25-40 parts of heavy calcium carbonate powder; 5-15 parts of white cement;
the fineness of the hexacyclic ring stone powder is 800 meshes; the fineness of the medical stone powder is 800 meshes; the fineness of the tourmaline powder is 800 meshes; the bauxite contains more than 86% of aluminum oxide by mass, the whiteness is more than 90 degrees, and the fineness is 800 meshes; the whiteness of the potassium oxide is over 90 degrees, and the fineness of the potassium oxide is 1250 meshes; the mass content of calcium oxide in the sierozem powder is more than 80 percent, the fineness is 150-1250 meshes, and the whiteness is 75-98 degrees; the weight content of calcium carbonate in the heavy calcium carbonate is more than 75 percent, the fineness is 150-800 meshes, and the whiteness is 78-98 degrees.
1000 g of wall material prepared from the raw material according to example 1 was uniformly spread out and sealed in a sealed box for 24 hours, and the wall material was measured every I hours by using an AIC-1000 negative oxygen ion detector manufactured by Alphalab, USA, and 20 data were taken each time, and the average value of each data was 8356/cm3。
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. The manufacturing method of the inorganic mineral ecological environment-friendly wall material is characterized by comprising the following components: 2-4 parts of hexacyclic ring stone powder; 2-6 parts of medical stone powder; 3-5 parts of tourmaline powder; 3-5 parts of bauxite; 2-4 parts of boron oxide; 2-4 parts of magnesium oxide; 0.05-0.07 part of ferric oxide; 0.8-3 parts of sodium oxide; 0.2-1 part of potassium oxide; 3-5 parts of silica sand; 1-3 parts of lignocellulose and 20-30 parts of diatomite; 20-30 parts of sierozem powder; 25-40 parts of heavy calcium carbonate powder; 5-15 parts of white cement.
2. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the fineness of the hexacyclic ring stone powder is 800 meshes.
3. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the fineness of the medical stone powder is 800 meshes.
4. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the fineness of the tourmaline powder is 800 meshes.
5. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the bauxite contains more than 86% of aluminum oxide by mass, the whiteness is more than 90 degrees, and the fineness is 800 meshes.
6. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the whiteness of the potassium oxide is over 90 degrees, and the fineness is 1250 meshes.
7. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the mass content of calcium oxide in the sierozem powder is more than 80 percent, the fineness is 150-1250 meshes, and the whiteness is 75-98 degrees.
8. The manufacturing method of the inorganic mineral ecological environment-friendly wall material according to claim 1, characterized in that: the weight content of calcium carbonate in the heavy calcium carbonate is more than 75 percent, the fineness is 150-800 meshes, and the whiteness is 78-98 degrees.