CN114045058A - 一种舰船用高耐盐雾性膨胀型防火阻燃涂料 - Google Patents
一种舰船用高耐盐雾性膨胀型防火阻燃涂料 Download PDFInfo
- Publication number
- CN114045058A CN114045058A CN202111596843.9A CN202111596843A CN114045058A CN 114045058 A CN114045058 A CN 114045058A CN 202111596843 A CN202111596843 A CN 202111596843A CN 114045058 A CN114045058 A CN 114045058A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- retardant coating
- fog
- salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种舰船用高耐盐雾性膨胀型防火阻燃涂料。包括如下重量份数的组分：金属氧化物50‑100份、植物提取物30‑80份、乳化剂20‑40份、成膜剂15‑30份、阻燃剂10‑20份、有机溶剂150‑250份。本发明制备的防火阻燃涂料，具有良好的防火阻燃性能，组分中桉树皮提取物和槭树皮提取物的组合使用，提高了材料的耐盐雾性能和拉拔附着力，组合使用协同增效。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种舰船用高耐盐雾性膨胀型防火阻燃涂料。
背景技术
舰船用材料一般采用不锈钢，因具有良好的力学、耐腐蚀和焊接性能广泛应用于造船。不锈钢良好的耐腐蚀性能主要依赖于在大气环境下形成致密的钝化膜，但是在海洋大气下，风携带着含有氯化物悬浮颗粒的空气传输到钢表面，氯化物通过潮解释放出的氯离子，易造成不锈钢表面钝化膜的破裂，引发较为严重的局部腐蚀。
专利CN 108250347 A公开了一种耐盐雾的磷酸酯改性丙烯酸核壳乳液，用于制备涂料。其壳层上含有长链烷基-丙烯酸酯磷酸双酯功能基团；其成分有丙烯酸酯软硬单体、丙烯酸、长链烷基-丙烯酸酯磷酸双酯、中和剂、引发剂、乳化剂和水；长链烷基-丙烯酸酯磷酸酯由羟基丙烯酸酯单体、R6-10OH和五氧化二磷通过反应制得。该核壳乳液制备方法比较复杂，制备成本高，难以满足人们的需求。
发明内容
本发明的目的在于提供一种舰船用高耐盐雾性膨胀型防火阻燃涂料。
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：金属氧化物50-100份、植物提取物30-80份、乳化剂20-40份、成膜剂15-30份、阻燃剂10-20份、有机溶剂150-250份。
所述金属氧化物为二氧化钛、氧化铁、氧化钇、三氧化二铈中的一种或几种。
所述乳化剂为脂肪醇聚氧乙烯醚、环氧丙醇、N-羟甲基丙烯酰胺、丙烯酰胺、醋酸丁酯、丙二醇甲醚醋酸酯中的一种或几种。
所述成膜剂为聚甲基硅倍半氧烷、聚乙烯醇、硝酸纤维、戊二醇单异氰酸酯中的一种或几种。
所述有机溶剂为乙醇、丙醇、异丙醇、醋酸乙酯、苯乙烯中的一种或几种。
所述植物提取物为桉树皮提取物和槭树皮提取物按照质量比1：1混合的混合物。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过60-100目筛，CO2超临界萃取1-4小时，得到桉树皮提取物；所述CO2超临界萃取的压力为20-30MPa，分离釜I的温度为40-45℃，压力为12-16MPa，分离釜II的温度为35-38℃，压力为8-10MPa。
所述槭树为青枫、三角枫、复叶槭、五角枫中的一种或几种。
所述槭树皮提取物的提取方法为：取槭树皮，晒干，粉碎，过60-80目筛，CO2超临界萃取1-3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为25-35MPa，分离釜I的温度为40-45℃，压力为10-15MPa，分离釜II的温度为30-35℃，压力为10-15MPa。
所述阻燃剂为聚磷酸铵、硼砂、水滑石、氧化石墨烯、三聚氰胺中的一种或几种。
本发明的有益效果：本发明制备的防火阻燃涂料，具有良好的防火阻燃性能，组分中桉树皮提取物和槭树皮提取物的组合使用，提高了材料的耐盐雾性能和拉拔附着力，组合使用协同增效。
具体实施方式
为了便于理解本发明，下面将对本发明进行更全面的描述。但是，本发明可以以许多不同的形式来实现，并不限于本文所描述的实施例。相反地，提供这些实施例的目的是使对本发明的公开内容的理解更加透彻全面。
实施例1
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：二氧化钛80份、植物提取物60份、脂肪醇聚氧乙烯醚30份、聚甲基硅倍半氧烷20份、聚磷酸铵15份、乙醇200份；所述植物提取物为桉树皮提取物和青枫皮提取物按照质量比1：1混合的混合物。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过80目筛，CO2超临界萃取3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为25MPa，分离釜I的温度为42℃，压力为15MPa，分离釜II的温度为36℃，压力为9MPa。
所述青枫皮提取物的提取方法为：取青枫皮，晒干，粉碎，过70目筛，CO2超临界萃取2小时，得到桉树皮提取物；所述CO2超临界萃取的压力为30MPa，分离釜I的温度为42℃，压力为12MPa，分离釜II的温度为32℃，压力为12MPa。
实施例2
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：氧化铁30份、氧化钇30份、植物提取物40份、环氧丙醇10份、N-羟甲基丙烯酰胺10份、聚乙烯醇15份、硼砂6份、三聚氰胺6份、丙醇160份；所述植物提取物为桉树皮提取物和三角枫皮提取物按照质量比1：1混合的混合物。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过60目筛，CO2超临界萃取2小时，得到桉树皮提取物；所述CO2超临界萃取的压力为21MPa，分离釜I的温度为42℃，压力为12MPa，分离釜II的温度为35℃，压力为8MPa。
所述三角枫皮提取物的提取方法为：取三角枫皮，晒干，粉碎，过60目筛，CO2超临界萃取1小时，得到桉树皮提取物；所述CO2超临界萃取的压力为25MPa，分离釜I的温度为40℃，压力为10MPa，分离釜II的温度为30℃，压力为10MPa。
实施例3
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：三氧化二铈100份、植物提取物80份、丙烯酰胺20份、醋酸丁酯20份、戊二醇单异氰酸酯30份、水滑石10份、氧化石墨烯10份、异丙醇250份；所述植物提取物为桉树皮提取物和复叶槭皮提取物按照质量比1：1混合的混合物。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过100目筛，CO2超临界萃取4小时，得到桉树皮提取物；所述CO2超临界萃取的压力为30MPa，分离釜I的温度为45℃，压力为16MPa，分离釜II的温度为38℃，压力为10MPa。
所述复叶槭皮提取物的提取方法为：取复叶槭皮，晒干，粉碎，过80目筛，CO2超临界萃取3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为35MPa，分离釜I的温度为45℃，压力为15MPa，分离釜II的温度为35℃，压力为15MPa。
实施例4
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：二氧化钛60份、氧化钇25份、植物提取物60份、丙二醇甲醚醋酸酯40份、硝酸纤维30份、氧化石墨烯10份、三聚氰胺10份、苯乙烯250份；所述植物提取物为桉树皮提取物和五角枫皮提取物按照质量比1：1混合的混合物。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过80目筛，CO2超临界萃取3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为22MPa，分离釜I的温度为43℃，压力为12MPa，分离釜II的温度为35℃，压力为10MPa。
所述五角枫皮提取物的提取方法为：取五角枫皮，晒干，粉碎，过80目筛，CO2超临界萃取2小时，得到桉树皮提取物；所述CO2超临界萃取的压力为28MPa，分离釜I的温度为42℃，压力为12MPa，分离釜II的温度为32℃，压力为12MPa。
对比例1
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：二氧化钛80份、桉树皮提取物60份、脂肪醇聚氧乙烯醚30份、聚甲基硅倍半氧烷20份、聚磷酸铵15份、乙醇200份。
所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过80目筛，CO2超临界萃取3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为25MPa，分离釜I的温度为42℃，压力为15MPa，分离釜II的温度为36℃，压力为9MPa。
对比例2
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：二氧化钛80份、青枫皮提取物60份、脂肪醇聚氧乙烯醚30份、聚甲基硅倍半氧烷20份、聚磷酸铵15份、乙醇200份。
所述青枫皮提取物的提取方法为：取青枫皮，晒干，粉碎，过70目筛，CO2超临界萃取2小时，得到桉树皮提取物；所述CO2超临界萃取的压力为30MPa，分离釜I的温度为42℃，压力为12MPa，分离釜II的温度为32℃，压力为12MPa。
对比例3
一种舰船用高耐盐雾性膨胀型防火阻燃涂料，包括如下重量份数的组分：二氧化钛80份、脂肪醇聚氧乙烯醚30份、聚甲基硅倍半氧烷20份、聚磷酸铵15份、乙醇200份。
实验例1：
按照ISO 9227:2017(人工大气中的腐蚀试验.盐雾试验)测试标准的要求及方法，测定实施例1-4及对比例1-3制备的涂料的耐盐雾性能，测试结果见表1：
表1
注：*代表与实施例1组比较P<0.05；**代表P<0.01。
实验例2：
按照ASTM D4541《用便携式粘合试验仪测定涂层剥离强度的标准试验方法》的规定，测定实施例1-4及对比例1-3制备的涂料的拉拔附着力(MPa)，测试结果见表2：
表2
注：*代表与实施例1组比较P<0.05；**代表P<0.01。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，包括如下重量份数的组分：金属氧化物50-100份、植物提取物30-80份、乳化剂20-40份、成膜剂15-30份、阻燃剂10-20份、有机溶剂150-250份。
2.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述金属氧化物为二氧化钛、氧化铁、氧化钇、三氧化二铈中的一种或几种。
3.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述乳化剂为脂肪醇聚氧乙烯醚、环氧丙醇、N-羟甲基丙烯酰胺、丙烯酰胺、醋酸丁酯、丙二醇甲醚醋酸酯中的一种或几种。
4.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述成膜剂为聚甲基硅倍半氧烷、聚乙烯醇、硝酸纤维、戊二醇单异氰酸酯中的一种或几种。
5.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述有机溶剂为乙醇、丙醇、异丙醇、醋酸乙酯、苯乙烯中的一种或几种。
6.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述植物提取物为桉树皮提取物和槭树皮提取物按照质量比1：1混合的混合物。
7.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述桉树皮提取物的提取方法为：取桉树皮，晒干，粉碎，过60-100目筛，CO2超临界萃取1-4小时，得到桉树皮提取物；所述CO2超临界萃取的压力为20-30MPa，分离釜I的温度为40-45℃，压力为12-16MPa，分离釜II的温度为35-38℃，压力为8-10MPa。
8.根据权利要求6所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述槭树为青枫、三角枫、复叶槭、五角枫中的一种或几种。
9.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述槭树皮提取物的提取方法为：取槭树皮，晒干，粉碎，过60-80目筛，CO2超临界萃取1-3小时，得到桉树皮提取物；所述CO2超临界萃取的压力为25-35MPa，分离釜I的温度为40-45℃，压力为10-15MPa，分离釜II的温度为30-35℃，压力为10-15MPa。
10.根据权利要求1所述舰船用高耐盐雾性膨胀型防火阻燃涂料，其特征在于，所述阻燃剂为聚磷酸铵、硼砂、水滑石、氧化石墨烯、三聚氰胺中的一种或几种。