CN114035361A - 一种高辉度抗刮伤抗落球的增亮膜 - Google Patents
一种高辉度抗刮伤抗落球的增亮膜 Download PDFInfo
- Publication number
- CN114035361A CN114035361A CN202111330199.0A CN202111330199A CN114035361A CN 114035361 A CN114035361 A CN 114035361A CN 202111330199 A CN202111330199 A CN 202111330199A CN 114035361 A CN114035361 A CN 114035361A
- Authority
- CN
- China
- Prior art keywords
- parts
- brightness
- enhancement film
- brightness enhancement
- ball
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的棱镜层，所述棱镜层由涂料组合物形成；所述涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯5‑30重量份、苯氧基苄基丙烯酸酯5‑20重量份、聚氨酯树脂10‑30重量份、乙氧基化双酚芴二丙烯酸酯10‑50重量份、有机‑无机杂化丙烯酸树脂10‑50重量份、引发剂1‑5重量份、有机硅助剂0.1‑1重量份。采用多种高折射率的单体，可提高涂料组合物的折射率和增亮膜的辉度；乙氧基化双酚芴丙烯酸酯单体可以提高涂层的柔韧性，添加有机‑无机杂化丙烯酸树脂，结合了有机聚合物和无机纳米粒子的性能优点，固化后能够改善棱镜力学性能。本发明的增亮膜具有辉度高、抗刮伤和抗落球的特点。
Description
技术领域
本发明涉及增亮膜技术领域，具体涉及一种高辉度抗刮伤抗落球的增亮膜。
背景技术
增亮膜又称为棱镜片，广泛应用于液晶显示器的背光模组中，以提高整个背光模组的发光效率。增亮膜包括棱镜结构，利用增亮膜特殊的棱镜结构，通过折射、全反射、光积累等光学原理，可以使各方向的光线向中心视角集中，进而提升液晶显示器的亮度和控制可视角度。
一般地，在组装成背光模组的过程中，随着增亮膜的辉度增加，增亮膜的棱镜结构抗刮伤抗落球效果变差，容易出现刮伤。
发明内容
针对现有技术中的不足，本发明提供一种高辉度、抗刮伤、抗落球的增亮膜，解决高辉度增亮膜中棱镜结构容易刮伤、抗落球效果差的问题。
为了解决上述技术问题，本发明采用下述技术方案：
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的棱镜层，所述棱镜层由涂料组合物形成；
所述涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯5-30重量份、苯氧基苄基丙烯酸酯5-20重量份、聚氨酯树脂10-30重量份、乙氧基化双酚芴二丙烯酸酯10-50重量份、有机-无机杂化丙烯酸树脂10-50重量份、引发剂1-5重量份、有机硅助剂0.1-1重量份。
进一步地，所述有机-无机杂化丙烯酸酯为纳米二氧化硅有机-无机杂化丙烯酸酯、纳米二氧化钛有机-无机杂化丙烯酸酯、纳米氧化锆有机-无机杂化丙烯酸酯中的一种或几种。
进一步地，所述乙氧基双酚芴二丙烯酸酯为2(乙氧基)双酚芴二丙烯酸酯、6(乙氧基)双酚芴二丙烯酸酯、10(乙氧基)双酚芴二丙烯酸酯、15(乙氧基)双酚芴二丙烯酸酯、20(乙氧基)双酚芴二丙烯酸酯、30(乙氧基)双酚芴二丙烯酸酯中的一种或几种。
进一步地，所述引发剂为2-羟基-2-甲基-苯基丙酮-1、1-羟基环己基苯甲酮、2,4,6-三甲基苯甲酰基二苯基氧化膦、双(2,4,6-三甲基苯甲酰基)苯基氧化膦中的一种或几种。
进一步地，所述PET基底层的厚度是25μm-150μm。
进一步地，所述棱镜层由多个棱镜形成。
进一步地，所述棱镜的高度是5μm-50μm。
进一步地，相邻两个所述棱镜的顶峰间距是10-100μm。
本发明的有益效果是：
本发明的增亮膜，折射率高、抗刮伤、抗落球。
本发明采用多种高折射率的单体，可提高涂料组合物的折射率和增亮膜的辉度；乙氧基化双酚芴丙烯酸酯单体可以提高涂层的柔韧性，从而达到抗刮伤、抗落球的性能。
本发明添加有机-无机杂化丙烯酸树脂，结合了有机聚合物和无机纳米粒子的性能优点，固化后能够改善棱镜力学性能，提高棱镜的硬度、抗刮伤性，纳米粒子分散在高分子链之间，起到增强增韧的作用，同时能够显著提高棱镜的折射率和抗刮伤性。
附图说明
图1本发明的增亮膜结构。
其中：1-PET基底层，2-棱镜层。
具体实施方式
为了进一步理解本发明，下面结合实施例对本发明优选实施方案进行描述，但是应当理解，这些描述只是为进一步说明本发明的特征和优点，而不是对本发明权利要求的限制。
本发明所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
实施例1
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的多个棱镜形成的棱镜层，棱镜层由涂料组合物形成，涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯5重量份、苯氧基苄基丙烯酸酯15重量份、聚氨酯树脂25重量份、2(乙氧基)双酚芴二丙烯酸酯15重量份、10(乙氧基)双酚芴二丙烯酸酯15重量份、纳米二氧化硅有机-无机杂化丙烯酸酯22重量份、2,4,6-三甲基苯甲酰基二苯基氧化膦1重量份、1重量份的2-羟基-2-甲基-苯基丙酮-1、有机硅助剂0.5重量份。
其中，PET基底层的厚度是100μm，棱镜的高度是12μm，相邻两个棱镜的顶峰间距是24μm。
实施例2
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的多个棱镜形成的棱镜层，棱镜层由涂料组合物形成，涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯30重量份、苯氧基苄基丙烯酸酯5重量份、聚氨酯树脂10重量份、30(乙氧基)双酚芴二丙烯酸酯10重量份、纳米二氧化钛有机-无机杂化丙烯酸酯50重量份、1-羟基环己基苯甲酮1重量份、有机硅助剂0.1重量份。
其中，PET基底层的厚度是25μm，棱镜的高度是5μm，相邻两个棱镜的顶峰间距是10μm。
实施例3
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的多个棱镜形成的棱镜层，棱镜层由涂料组合物形成，涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯15重量份、苯氧基苄基丙烯酸酯20重量份、聚氨酯树脂30重量份、6(乙氧基)双酚芴二丙烯酸酯10重量份、15(乙氧基)双酚芴二丙烯酸酯20重量份、20(乙氧基)双酚芴二丙烯酸酯20重量份、纳米氧化锆有机-无机杂化丙烯酸酯25重量份、双(2,4,6-三甲基苯甲酰基)苯基氧化膦4重量份、有机硅助剂1重量份。
其中，PET基底层的厚度是150μm，棱镜的高度是50μm，相邻两个棱镜的顶峰间距是100μm。
对比例1
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的多个棱镜形成的棱镜层，棱镜层由涂料组合物形成，涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯30重量份、苯氧基苄基丙烯酸酯40重量份、聚氨酯树脂30重量份、2,4,6-三甲基苯甲酰基二苯基氧化膦1重量份、1重量份的2-羟基-2-甲基-苯基丙酮-1、有机硅助剂1重量份。
其中，PET基底层的厚度是100μm，棱镜的高度是12μm，相邻两个棱镜的顶峰间距是24μm。
对比例2
一种高辉度抗刮伤抗落球的增亮膜，包括PET基底层和层叠在PET基底层上的多个棱镜形成的棱镜层，棱镜层由涂料组合物形成，涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯28重量份、苯氧基苄基丙烯酸酯30重量份、聚氨酯树脂30重量份、有机-无机杂化丙烯酸酯20重量份、2,4,6-三甲基苯甲酰基二苯基氧化膦1重量份、1重量份的2-羟基-2-甲基-苯基丙酮-1、有机硅助剂1重量份。
其中，PET基底层的厚度是100μm，棱镜的高度是12μm，相邻两个棱镜的顶峰间距是24μm。
对实施例1-3和对比例1-2中的增亮膜进行光学测试：
(1)辉度测试方法：
采用尺寸大小118*65mm的待测样品，测试仪器为CF600，9点测试取平均值。
(2)厚度测试方法：
用厚度规(精确至0.001mm)测试增亮膜三个不同位置，取平均值。
(3)折射率测试方法：
折射率的测量参照国家标准GB/T614-2006《化学试剂折光率测定通用方法》测定，用阿贝折光仪测定。
(4)抗刮测试方法：
将待测样品以棱镜方向0°贴附在大理石平台上，并用胶带固定，使用25mm宽增光(上增光膜)与待测样品棱镜方向垂直90°，从最大重量500g开始测试。固定位置匀速并同方向，将上增光膜与待测样品进行摩擦，拉5次。
测试结束后，将待测样品放置背光上点亮并多视角观察膜片白雾状刮伤情况。如有刮伤，则更换小一点的砝码继续测试，直到出现无刮伤时，此砝码重量为测试OK，否则判定NG。
(5)落球测试方法：
将待测样品组装在6寸大小背光上，且盖上0.8mm厚盖板，在背光板下放置37mm厚的垫木板治具，并点亮背光；将16.7g钢球放置落球测试平台上，从第一阶段高度25cm处开始进行测试、依每次5cm下调，测试模组5点区域。
落球测试1min后从多视角观察膜材，若有白斑痕迹出现则降低高度，直到无白斑痕迹，此高度即为测试OK之高度，否则判定NG。
| 折射率 | 辉度 | 辉度增益 | 棱镜厚度 | 抗刮伤 | 抗小球 | |
| 无增光膜 | / | 2283.72 | / | / | / | / |
| 实施例1 | 1.5715 | 7845.38 | 0.00％ | 12μm | 500g | 25cm |
| 实施例2 | 1.5878 | 8083.12 | 3.03％ | 12μm | 500g | 25cm |
| 实施例3 | 1.6205 | 8162.37 | 4.04％ | 12μm | 300g | 25cm |
| 对比例1 | 1.5735 | 7810.39 | -0.45％ | 12μm | 50g | 5cm |
| 对比例2 | 1.6015 | 8029.48 | 2.35％ | 12μm | 50g | 5cm |
由实施例1-3和对比例1-2增亮膜的测试结果可知，本发明的增亮膜具有辉度高、抗刮伤和抗落球的特点。
根据上述说明书的揭示，本发明所属领域的技术人员还可以对上述实施方式进行适当的变更和修改。因此，本发明并不局限于上面揭示和描述的具体实施方式，对本发明的一些修改和变更也应当落入本发明的权利要求的保护范围内。此外，尽管本说明书中使用了一些特定的术语，但这些术语只是为了方便说明，并不对本发明构成任何限制。
Claims (8)
1.一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述增亮膜包括PET基底层和层叠在PET基底层上的棱镜层，所述棱镜层由涂料组合物形成；
所述涂料组合物包括如下组分：邻苯基苯氧乙基丙烯酸酯5-30重量份、苯氧基苄基丙烯酸酯5-20重量份、聚氨酯树脂10-30重量份、乙氧基化双酚芴二丙烯酸酯10-50重量份、有机-无机杂化丙烯酸树脂10-50重量份、引发剂1-5重量份、有机硅助剂0.1-1重量份。
2.根据权利要求1所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述有机-无机杂化丙烯酸酯为纳米二氧化硅有机-无机杂化丙烯酸酯、纳米二氧化钛有机-无机杂化丙烯酸酯、纳米氧化锆有机-无机杂化丙烯酸酯中的一种或几种。
3.根据权利要求1所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述乙氧基双酚芴二丙烯酸酯为2(乙氧基)双酚芴二丙烯酸酯、6(乙氧基)双酚芴二丙烯酸酯、10(乙氧基)双酚芴二丙烯酸酯、15(乙氧基)双酚芴二丙烯酸酯、20(乙氧基)双酚芴二丙烯酸酯、30(乙氧基)双酚芴二丙烯酸酯中的一种或几种。
4.根据权利要求1所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述引发剂为2-羟基-2-甲基-苯基丙酮-1、1-羟基环己基苯甲酮、2,4,6-三甲基苯甲酰基二苯基氧化膦、双(2,4,6-三甲基苯甲酰基)苯基氧化膦中的一种或几种。
5.根据权利要求1所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于，所述PET基底层的厚度是25μm-150μm。
6.根据权利要求1所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述棱镜层由多个棱镜形成。
7.根据权利要求6所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：所述棱镜的高度是5μm-50μm。
8.根据权利要求7所述的一种高辉度抗刮伤抗落球的增亮膜，其特征在于：相邻两个所述棱镜的顶峰间距是10-100μm。