CN113998987A - 一种陶瓷艺术品的制作方法 - Google Patents

一种陶瓷艺术品的制作方法 Download PDF

Info

Publication number
CN113998987A
CN113998987A CN202110047379.1A CN202110047379A CN113998987A CN 113998987 A CN113998987 A CN 113998987A CN 202110047379 A CN202110047379 A CN 202110047379A CN 113998987 A CN113998987 A CN 113998987A
Authority
CN
China
Prior art keywords
product
parts
clay
mud
mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110047379.1A
Other languages
English (en)
Inventor
朴守帆
罗明敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Business College
Original Assignee
Zhejiang Business College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Business College filed Critical Zhejiang Business College
Priority to CN202110047379.1A priority Critical patent/CN113998987A/zh
Publication of CN113998987A publication Critical patent/CN113998987A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种陶瓷艺术品的制作方法，包括以下步骤：a、配料：取黏土原料制成黏土，为A品；b、柔泥：取A品进行揉制，形成含水率为15‑24％的B品；c、压泥：采用压泥板将B品压制成泥板，为C品；d、爆破：将C品进行爆破，在泥板上形成凹陷和/或放射状纹路，得D品；e、修整：将D品进行修整成需要的样式，得E品；f、烧制：将E品在1150‑1400℃下进行烧制，得成品。本发明不仅具有立体感强、强度高的特点，而且工艺简单的特点。

Description

一种陶瓷艺术品的制作方法
技术领域
本发明涉及一种陶瓷制作方法，特别是一种陶瓷艺术品的制作方法。
背景技术
陶瓷是以粘士以及各种天然矿物经过粉碎泪炼、成型和锻烧制得的材料为主要原料的各种制品。中国陶瓷制品很早以前就在世界上享有盛誉。在长期的生产实践中，我国人民生产制造出了大量的形状多种多样、图案色彩千变万化的陶瓷制品，有许多产品具有非常珍贵的艺术价值和收藏价值。但是在绝大多数的陶瓷产品和陶瓷艺术品中，其图案和色彩都是在成型后的坯胎表面，利用施釉、绘画、雕刻、贴塑或贴花纸等方法形成的。按照这种方法，只能在产品的表面形成花纹和/或图案，而在产品的内部则没有花纹和/或图案，或者是只有原料本身固有的花纹和/或图案，立体感不强；而且陶瓷制品本身易脆，强度不高，耐久性较差。
因此，现有的陶瓷制品，存在立体感不强、强度不高的问题。
发明内容
本发明的目的在于，提供一种陶瓷艺术品的制作方法。本发明不仅具有立体感强、强度高的特点，而且工艺简单的特点。
本发明的技术方案：一种陶瓷艺术品的制作方法，包括以下步骤：
a、配料：取黏土原料制成黏土，为A品；
b、柔泥：取A品进行揉制，形成含水率为15-24％的B品；
c、压泥：采用压泥板将B品压制成泥板，为C品；
d、爆破：将C品进行爆破，在泥板上形成凹陷和/或放射状纹路，得D品；
e、修整：将D品进行修整成需要的样式，得E品；
f、烧制：将E品在1150-1400℃下进行烧制，得成品。
前述的陶瓷艺术品的制作方法中，所述步骤a中，黏土包括以下重量份数的原料：高温陶土30-40份、中温瓷土20-30份、高岭土30-40份、叶蜡石10-15份、金属粉末5-8份、石英砂6-10份、玄武岩纤维5-10份、碳纤维4-8份、石油树脂5-8份、水20-50份。
前述的陶瓷艺术品的制作方法中，黏土还包括氧化铁3-5份、长石3-8份、氧化铜2-5份。
前述的陶瓷艺术品的制作方法中，所述步骤a中，将高温陶土、中温瓷土、高岭土、叶蜡石、金属粉末、石英砂、玄武岩纤维、碳纤维粉碎，过100-150目筛后混合、加水搅拌，再过200-300目筛，制成黏土。
前述的陶瓷艺术品的制作方法中，所述步骤b中，在揉制过程中，加入氧化铁、长石和氧化铜中的一种或者多种的组合。
前述的陶瓷艺术品的制作方法中，所述步骤c中，泥板的厚度为1.5-2cm；所述步骤d中，凹陷的深度为0.5-1cm，凹陷的底部面积为1-10cm2。
前述的陶瓷艺术品的制作方法中，所述步骤c中，在压泥时，将B品置于模具内，模具的底部设有模腔，模腔的外围设有一圈接水槽，模腔底部铺设有吸水纸，模具的侧面设有观察窗以及与模腔连通的点火口，模具的顶部设有覆盖模腔的上盖，上盖的一端与模具铰接，上盖的另一端设有扣环，模具上转动连接有与扣环配合连接的旋钮；点火口的外部设有两道滑道，两道滑道之间滑动连接有覆盖点火口的移动板。
前述的陶瓷艺术品的制作方法中，所述步骤c中，压制的压力为10-15MPa，保压时间为15-30s。
前述的陶瓷艺术品的制作方法中，所述步骤d中，爆破的方式包括炸药爆破、气体爆破，其中炸药爆破为表面爆破或者埋设爆破。
前述的陶瓷艺术品的制作方法中，步骤f具体为，烧制：将E品先在1150-1250℃下进行烧制3-5h，然后以50-100℃/h的速度上升至1320-1400℃烧制5-8h，得成品。
与现有技术相比，本发明以高温陶土、中温瓷土和高岭土为主原料，增加高岭土的比例，优化黏土原料成分和比例，形成网络状黏连、粘度较高的结构，提高了其结构强度，可以保证在一定范围内爆破的同时，避免其余地方的开裂，并配合一定的叶蜡石，使得黏土泥板密度均一、抗火抗水性能佳；采用了少量的金属粉末和石英砂，增加摩擦力，提高材料的稳定性和强度、耐久性好；利用玄武岩纤维和碳纤维，使得制得的陶瓷产品具有良好的柔韧性，并减少由于爆破在爆破区外产生的裂纹；利用石油树脂作为增韧剂，使得不同成分的原料混合更加均匀，保证泥浆在模具内不易产生龟裂，制得柔韧性好、不易断裂的泥板，便于后期的爆破处理。进一步采用的氧化铁、石英、长石和氧化铜，可以根据实际需求，加入所需的材料，丰富产品外观。
在制备过程中，利用独特的爆破的方式，在泥板上爆破出凹陷的放射状纹路，工艺简单，能够根据实际需求，制造不同样式的爆破形式，制作和生产出具有抽象和变形风格装饰的各种陶瓷制品，凹凸鲜明、立体感强烈，形成独特的艺术形态，视觉效果新颖，独具韵味。制得的产品可作为现代装饰材料运用到环境装饰、室内背景墙等批量生产研发。且配合黏土成分，烧制温度偏高，保证烧制的稳定性。
因此，本发明不仅具有立体感强、强度高的特点，而且工艺简单的特点。
附图说明
图1是本发明制得的陶瓷工艺品图；
图2是本发明制得的产品作为室内背景墙的结构示意图；
图3是本发明中模具的结构示意图。
附图中的标记为：1、模具；2、模腔；21、接水槽；3、观察窗；31、点火口；32、上盖；33、扣环；34、旋钮；35、滑道；36、移动板。
具体实施方式
下面结合实施例对本发明作进一步的说明，但并不作为对本发明限制的依据。
实施例1。
a、配料：黏土包括以下重量份数的原料：高温陶土30份、中温瓷土20份、高岭土40份、叶蜡石10份、金属粉末5份、石英砂6份、玄武岩纤维5份、碳纤维4份、石油树脂5份、水20份。
将高温陶土、中温瓷土、高岭土、叶蜡石、金属粉末、石英砂、玄武岩纤维、碳纤维粉碎，过150目筛后混合、加水搅拌，再过300目筛，制成黏土，为A品；
b、柔泥：取A品进行揉制，形成含水率为15％的B品；
c、压泥：采用压泥板将置于模具1内的B品压制成泥板，模具如图3所示，模具1的底部设有模腔2，模腔2的外围设有一圈接水槽21，模腔2底部铺设有吸水纸，模具1的侧面设有观察窗3以及与模腔2连通的点火口31，模具1的顶部设有覆盖模腔2的上盖32，上盖32的一端与模具1铰接，上盖32的另一端设有扣环33，模具1上转动连接有与扣环33配合连接的旋钮34；点火口31的外部设有两道滑道35，两道滑道35之间滑动连接有覆盖点火口31的移动板36。通过点火口31进行点火，提高安全性，填完后迅速盖上上盖32和移动板36，防止外溅，通过接水槽21接收溅出来的多余的水、泥，减少外部污染；泥板的厚度为1.5cm，压制的压力为10MPa，保压时间为15s，得C品；
d、爆破：将C品采用炸药埋设爆破的方式进行爆破，在泥板上形成凹陷和放射状纹路，凹陷的深度为0.5-0.6cm，凹陷的底部面积为2-8cm2得D品；
e、修整：将D品进行修整成需要的样式，得E品；
f、烧制：将E品先在1150℃下进行烧制5h，然后以50℃/h的速度上升至1320℃烧制8h，得成品。成品图如图1所示。作为室内背景墙如图2所示。
实施例2。
a、配料：黏土包括以下重量份数的原料：高温陶土40份、中温瓷土30份、高岭土40份、叶蜡石15份、金属粉末8份、石英砂10份、玄武岩纤维10份、碳纤维8份、石油树脂8份、水50份。
将高温陶土、中温瓷土、高岭土、叶蜡石、金属粉末、石英砂、玄武岩纤维、碳纤维粉碎、过100目筛后混合、加水搅拌，再过200目筛，制成黏土，为A品；
b、柔泥：取A品进行揉制，在揉制过程中，加入氧化铁和长石，形成含水率为24％的B品；
c、压泥：采用压泥板将置于模具1内的B品压制成泥板，模具如图3所示，模具1的底部设有模腔2，模腔2的外围设有一圈接水槽21，模腔2底部铺设有吸水纸，吸收压制时挤出的水分，模具1的侧面设有观察窗3以及与模腔2连通的点火口31，模具1的顶部设有覆盖模腔2的上盖32，上盖32的一端与模具1铰接，上盖32的另一端设有扣环33，模具1上转动连接有与扣环33配合连接的旋钮34；点火口31的外部设有两道滑道35，两道滑道35之间滑动连接有覆盖点火口31的移动板36。泥板的厚度为2cm，压制的压力为15MPa，保压时间为30s，得C品；
d、爆破：将C品采用炸药埋设爆破的方式进行爆破，在泥板上形成凹陷和放射状纹路，凹陷的深度为0.8-1cm，凹陷的底部面积为8-10cm2得D品；
e、修整：将D品进行修整成需要的样式，得E品；
f、烧制：将E品先在1250℃下进行烧制3h，然后以100℃/h的速度上升至1400℃烧制5h，得成品。
实施例3。
a、配料：黏土包括以下重量份数的原料：高温陶土35份、中温瓷土25份、高岭土35份、叶蜡石13份、金属粉末6份、石英砂8份、玄武岩纤维7份、碳纤维6份、石油树脂6份、水30份。
将高温陶土、中温瓷土、高岭土、叶蜡石、金属粉末、石英砂、玄武岩纤维、碳纤维粉碎、过120目筛后混合、加水搅拌，再过250目筛，制成黏土，为A品；
b、柔泥：取A品进行揉制，在揉制过程中，加入氧化铜，形成含水率为20％的B品；
c、压泥：采用压泥板将置于模具1内的B品压制成泥板，模具如图3所示，模具1的底部设有模腔2，模腔2的外围设有一圈接水槽21，模腔2底部铺设有吸水纸，吸收压制时挤出的水分，模具1的侧面设有观察窗3以及与模腔2连通的点火口31，模具1的顶部设有覆盖模腔2的上盖32，上盖32的一端与模具1铰接，上盖32的另一端设有扣环33，模具1上转动连接有与扣环33配合连接的旋钮34；点火口31的外部设有两道滑道35，两道滑道35之间滑动连接有覆盖点火口31的移动板36。泥板的厚度为1.8cm，压制的压力为13MPa，保压时间为20s，得C品；
d、爆破：将C品采用炸药埋设爆破的方式进行爆破，在泥板上形成凹陷和放射状纹路，凹陷的深度为0.6-0.9cm，凹陷的底部面积为3-5cm2得D品；
e、修整：将D品进行修整成需要的样式，得E品；
f、烧制：将E品先在1200℃下进行烧制4h，然后以80℃/h的速度上升至1350℃烧制6h，得成品。

Claims (10)

1.一种陶瓷艺术品的制作方法，其特征在于：包括以下步骤：
a、配料：取黏土原料制成黏土，为A品；
b、柔泥：取A品进行揉制，形成含水率为15-24％的B品；
c、压泥：采用压泥板将B品压制成泥板，为C品；
d、爆破：将C品进行爆破，在泥板上形成凹陷和/或放射状纹路，得D品；
e、修整：将D品进行修整成需要的样式，得E品；
f、烧制：将E品在1150-1400℃下进行烧制，得成品。
2.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤a中，黏土包括以下重量份数的原料：高温陶土30-40份、中温瓷土20-30份、高岭土30-40份、叶蜡石10-15份、金属粉末5-8份、石英砂6-10份、玄武岩纤维5-10份、碳纤维4-8份、石油树脂5-8份、水20-50份。
3.根据权利要求2所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤a中，黏土还包括氧化铁3-5份、长石3-8份、氧化铜2-5份。
4.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤a中，将高温陶土、中温瓷土、高岭土、叶蜡石、金属粉末、石英砂、玄武岩纤维、碳纤维粉碎，过100-150目筛后混合、加水搅拌，再过200-300目筛，制成黏土。
5.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤b中，在揉制过程中，加入氧化铁、长石和氧化铜中的一种或者多种的组合。
6.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤c中，泥板的厚度为1.5-2cm；所述步骤d中，凹陷的深度为0.5-1cm，凹陷的底部面积为1-10cm2。
7.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤c中，在压泥时，将B品置于模具(1)内，模具(1)的底部设有模腔(2)，模腔(2)的外围设有一圈接水槽(21)，模腔(2)底部铺设有吸水纸，模具(1)的侧面设有观察窗(3)以及与模腔(2)连通的点火口(31)，模具(1)的顶部设有覆盖模腔(2)的上盖(32)，上盖(32)的一端与模具(1)铰接，上盖(32)的另一端设有扣环(33)，模具(1)上转动连接有与扣环(33)配合连接的旋钮(34)；点火口(31)的外部设有两道滑道(35)，两道滑道(35)之间滑动连接有覆盖点火口(31)的移动板(36)。
8.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤c中，压制的压力为10-15MPa，保压时间为15-30s。
9.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：所述步骤d中，爆破的方式包括炸药爆破、气体爆破，其中炸药爆破为表面爆破或者埋设爆破。
10.根据权利要求1所述的一种陶瓷艺术品的制作方法，其特征在于：步骤f具体为，烧制：将E品先在1150-1250℃下进行烧制3-5h，然后以50-100℃/h的速度上升至1320-1400℃烧制5-8h，得成品。
CN202110047379.1A 2021-01-14 2021-01-14 一种陶瓷艺术品的制作方法 Pending CN113998987A (zh)