CN107089823A - 一种陶瓷材料及其制备方法 - Google Patents

一种陶瓷材料及其制备方法 Download PDF

Info

Publication number
CN107089823A
CN107089823A CN201710154518.4A CN201710154518A CN107089823A CN 107089823 A CN107089823 A CN 107089823A CN 201710154518 A CN201710154518 A CN 201710154518A CN 107089823 A CN107089823 A CN 107089823A
Authority
CN
China
Prior art keywords
parts
ceramic material
weight
carborundum
boron nitride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710154518.4A
Other languages
English (en)
Inventor
何珩
张宇军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Bonding Technology Co Ltd
Original Assignee
Anhui Bonding Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Bonding Technology Co Ltd filed Critical Anhui Bonding Technology Co Ltd
Priority to CN201710154518.4A priority Critical patent/CN107089823A/zh
Publication of CN107089823A publication Critical patent/CN107089823A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种陶瓷材料及其制备方法，按重量份计，由以下组分制备而成：高岭土4‑18份、石英砂2‑10份、氯化硅2‑6份、碳化硅2‑5份、二氧化锆4‑12份、氮化硼2‑6份、二氧化钍3‑8份、氧化铝1‑5份、镍粉4‑6份、玄武岩纤维2‑8份，制备方法为：按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件；将毛坯件在1100‑1300℃的条件下煅烧3‑7小时，保温1‑3小时，制备得到半成品；将半成品在850‑1150℃条件下煅烧12‑20小时，保温3‑5小时后，即可。本发明具有耐磨性能好、耐腐蚀性好等优点。

Description

一种陶瓷材料及其制备方法
技术领域
本发明涉及陶瓷加工技术领域，具体来说是一种陶瓷材料及其制备方法。
背景技术
陶瓷是指陶器和瓷器的通称,也就是通过成型和高温烧结所得到的成型烧结体，传统的陶瓷材料主要是指硅铝酸盐，刚开始的时候人们对硅铝酸盐的选择要求不高，纯度不大，颗粒的粒度也不均一，成型压强不高，这时得到陶瓷称为传统陶瓷，后来发展到纯度高，粒度小且均一，成型压强高，进行烧结得到的烧结体叫做精细陶瓷。
陶瓷材料是生产陶瓷的基础，目前，陶瓷材料的种类比较多样，但是现有的陶瓷材料的普遍存在耐磨性差、耐腐蚀性差的缺陷，比较容易损坏，使用寿命也就大大缩短。
发明内容
本发明的目的是为了解决现有技术中的陶瓷材料耐磨性差、耐腐蚀性差的缺陷，提供一种陶瓷材料及其制备方法来解决上述问题。
为了实现上述目的，本发明的技术方案如下：本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4-18份、石英砂2-10份、氯化硅2-6份、碳化硅2-5份、二氧化锆4-12份、氮化硼2-6份、二氧化钍3-8份、氧化铝1-5份、镍粉4-6份、玄武岩纤维2-8份
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4-16份、石英砂2-8份、氯化硅2-4份、碳化硅2-3份、二氧化锆4-11份、氮化硼2-5份、二氧化钍3-7份、氧化铝2-4份、镍粉5-6份、玄武岩纤维2-7份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土11份、石英砂6份、氯化硅4份、碳化硅3份、二氧化锆8份、氮化硼4份、二氧化钍5份、氧化铝3份、镍粉5份、玄武岩纤维5份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土18份、石英砂2份、氯化硅6份、碳化硅2份、二氧化锆12份、氮化硼2份、二氧化钍8份、氧化铝1份、镍粉6份、玄武岩纤维2份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4份、石英砂10份、氯化硅2份、碳化硅5份、二氧化锆4份、氮化硼6份、二氧化钍3份、氧化铝5份、镍粉4份、玄武岩纤维3份。
作为优选，本发明还公开了上述陶瓷材料的制备方法，具体步骤如下：
（1）、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件； （2）、将毛坯件在1100-1300℃的条件下煅烧 3-7小时，保温1-3 小时，制备得到半成品；
（3）、将半成品在850-1150℃条件下煅烧12-20小时，保温3-5小时后，即可。
本发明相比现有技术具有以下优点：
本发明所述的陶瓷材料通过采用氯化硅、碳化硅、二氧化锆、氮化硼、二氧化钍、氧化铝、玄武岩纤维，因此制备而成的陶瓷材料具有高硬度、耐磨性好、韧性强的优点，使用寿命大大延长，而且通过添加镍粉，镍粉具有优异的耐腐蚀性，因此制备的产品的耐腐蚀性效果也比较优异。
具体实施方式
下面对本发明的实施例作详细说明，本实施例在以本发明技术方案为前提下进行实施，给出了详细的实施方式和具体的操作过程，但本发明的保护范围不限于下述的实施例。
本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4-18份、石英砂2-10份、氯化硅2-6份、碳化硅2-5份、二氧化锆4-12份、氮化硼2-6份、二氧化钍3-8份、氧化铝1-5份、镍粉4-6份、玄武岩纤维2-8份
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4-16份、石英砂2-8份、氯化硅2-4份、碳化硅2-3份、二氧化锆4-11份、氮化硼2-5份、二氧化钍3-7份、氧化铝2-4份、镍粉5-6份、玄武岩纤维2-7份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土11份、石英砂6份、氯化硅4份、碳化硅3份、二氧化锆8份、氮化硼4份、二氧化钍5份、氧化铝3份、镍粉5份、玄武岩纤维5份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土18份、石英砂2份、氯化硅6份、碳化硅2份、二氧化锆12份、氮化硼2份、二氧化钍8份、氧化铝1份、镍粉6份、玄武岩纤维2份。
作为优选，本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4份、石英砂10份、氯化硅2份、碳化硅5份、二氧化锆4份、氮化硼6份、二氧化钍3份、氧化铝5份、镍粉4份、玄武岩纤维3份。
作为优选，本发明还公开了上述陶瓷材料的制备方法，具体步骤如下：
（1）、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件； （2）、将毛坯件在1100-1300℃的条件下煅烧 3-7小时，保温1-3 小时，制备得到半成品；
（3）、将半成品在850-1150℃条件下煅烧12-20小时，保温3-5小时后，即可。
实施例1
本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土11份、石英砂6份、氯化硅4份、碳化硅3份、二氧化锆8份、氮化硼4份、二氧化钍5份、氧化铝3份、镍粉5份、玄武岩纤维5份。
本发明还公开了上述陶瓷材料的制备方法，具体步骤如下：
（1）、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件； （2）、将毛坯件在1200℃的条件下煅烧 5小时，保温2 小时，制备得到半成品；
（3）、将半成品在1000℃条件下煅烧15小时，保温4小时后，即可。
实施例2
本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土18份、石英砂2份、氯化硅6份、碳化硅2份、二氧化锆12份、氮化硼2份、二氧化钍8份、氧化铝1份、镍粉6份、玄武岩纤维2份。
本发明还公开了上述陶瓷材料的制备方法，具体步骤如下：
（1）、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件； （2）、将毛坯件在1250℃的条件下煅烧6小时，保温3 小时，制备得到半成品；
（3）、将半成品在1000℃条件下煅烧16小时，保温3小时后，即可。
实施例3
本发明公开了一种陶瓷材料，按重量份计，由以下组分制备而成：高岭土4份、石英砂10份、氯化硅2份、碳化硅5份、二氧化锆4份、氮化硼6份、二氧化钍3份、氧化铝5份、镍粉4份、玄武岩纤维3份。
本发明还公开了上述陶瓷材料的制备方法，具体步骤如下：
（1）、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件； （2）、将毛坯件在1200℃的条件下煅烧 7小时，保温3 小时，制备得到半成品；
（3）、将半成品在1150℃条件下煅烧20小时，保温5小时后，即可。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明的范围内。本发明要求的保护范围由所附的权利要求书及其等同物界定。

Claims (6)

1.一种陶瓷材料，其特征在于：按重量份计，由以下组分制备而成：高岭土4-18份、石英砂2-10份、氯化硅2-6份、碳化硅2-5份、二氧化锆4-12份、氮化硼2-6份、二氧化钍3-8份、氧化铝1-5份、镍粉4-6份、玄武岩纤维2-8份
2.根据权利要求1所述的一种陶瓷材料，其特征在于：按重量份计，由以下组分制备而成：高岭土4-16份、石英砂2-8份、氯化硅2-4份、碳化硅2-3份、二氧化锆4-11份、氮化硼2-5份、二氧化钍3-7份、氧化铝2-4份、镍粉5-6份、玄武岩纤维2-7份。
3.根据权利要求1所述的一种陶瓷材料，其特征在于：按重量份计，由以下组分制备而成：高岭土11份、石英砂6份、氯化硅4份、碳化硅3份、二氧化锆8份、氮化硼4份、二氧化钍5份、氧化铝3份、镍粉5份、玄武岩纤维5份。
4.根据权利要求1所述的一种陶瓷材料，其特征在于：按重量份计，由以下组分制备而成：高岭土18份、石英砂2份、氯化硅6份、碳化硅2份、二氧化锆12份、氮化硼2份、二氧化钍8份、氧化铝1份、镍粉6份、玄武岩纤维2份。
5.根据权利要求1所述的一种陶瓷材料，其特征在于：按重量份计，由以下组分制备而成：高岭土4份、石英砂10份、氯化硅2份、碳化硅5份、二氧化锆4份、氮化硼6份、二氧化钍3份、氧化铝5份、镍粉4份、玄武岩纤维3份。
6.根据权利要求1-5任一所述的一种陶瓷材料的制备方法，其特征在于：具体步骤如下：
(1)、按重量份数称取所有的原料，将所称取的原料混匀注浆成毛坯件；
(2)、将毛坯件在1100-1300℃的条件下煅烧3-7小时，保温1-3小时，制备得到半成品；
(3)、将半成品在850-1150℃条件下煅烧12-20小时，保温3-5小时后，即可。
CN201710154518.4A 2017-03-15 2017-03-15 一种陶瓷材料及其制备方法 Pending CN107089823A (zh)