CN113980499A - 一种抗过敏无机内墙儿童漆及其制备方法 - Google Patents
一种抗过敏无机内墙儿童漆及其制备方法 Download PDFInfo
- Publication number
- CN113980499A CN113980499A CN202111214214.5A CN202111214214A CN113980499A CN 113980499 A CN113980499 A CN 113980499A CN 202111214214 A CN202111214214 A CN 202111214214A CN 113980499 A CN113980499 A CN 113980499A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- children
- inorganic
- silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗过敏无机内墙儿童漆及其制备方法，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐150‑400份、净味乳液40‑150份、消泡剂2‑6份、分散剂3‑10份、颜料100‑300份、无机填料0‑400份、增稠剂1‑5份、流平剂5‑20份、耐水剂1‑10份、水80‑350份和稳定剂1‑10份；其中，所述净味乳液选自聚乙烯‑丙烯酸酯乳液和聚苯乙烯‑丙烯酸酯乳液中的至少一种。该抗过敏无机内墙儿童漆解决了现有技术中儿童漆存在的毒性大、易引发过敏的缺陷。
Description
技术领域
本发明涉及儿童漆领域，具体地，涉及一种抗过敏无机内墙儿童漆及其制备方法。
背景技术
在国内的内墙装饰中，乳胶漆具有施工方便，颜色丰富的特点，其市场份额大于80％，儿童房的内墙装饰大多数也使用了乳胶漆。但是常规乳胶漆不具有抗菌作用，市场上儿童房用乳胶漆为了避免细菌、霉菌、藻类的产生，大多数都添加了大量的杀菌剂，这些杀菌剂大多数是CIT、BIT、MIT等一些高分子化合物的混合物或衍生物，毒性相对较大；而无机的银离子抗菌剂、铜离子抗菌剂，活性又低，对环境要求苛刻，需要结合CIT、BIT、MIT等同时使用才能有更好的抗菌效果。
所以大多数乳胶漆里面添加的杀菌剂都具有较大的毒性，当被涂刷在室内墙面上，儿童不小心接触很有可能会引起儿童过敏反应，如哮喘、打喷嚏、起疹子、肠胃炎、反复呼吸道感染、过敏性咳嗽等症状，从而对身体产生危害，影响儿童生长发育。
另外，乳胶漆用的乳液在合成后会有残留单体的存在及释放，同时还要使用成膜助剂、防冻剂等挥发性厉害的助剂，味道大，且非常容易引起过敏反应。
发明内容
本发明的目的是提供一种抗过敏无机内墙儿童漆及其制备方法，以解决现有技术中儿童漆存在的毒性大、易引发过敏的缺陷。
为了实现上述目的，本发明提供了一种抗过敏无机内墙儿童漆，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐150-400份、净味乳液40-150份、消泡剂2-6份、分散剂3-10份、颜料100-300份、无机填料0-400份、增稠剂1-5份、流平剂5-20份、耐水剂1-10份、水80-350份和稳定剂1-10份；
其中，所述净味乳液选自聚乙烯-丙烯酸酯乳液和聚苯乙烯-丙烯酸酯乳液中的至少一种。
本发明还提供了一种如上述的抗过敏无机内墙儿童漆的制备方法，盖制备方法包括：
1)将水、增稠剂、分散剂、消泡剂和稳定剂进行第一混合，以得到第一混合液；
2)将无机填料、所述第一混合液进行第二混合，以得到第二混合液；
3)将消泡剂、所述第二混合液进行第三混合，以得到第三混合液；
4)将净味乳液、硅酸盐、流平剂和耐水剂进行第四混合，以得到所述抗过敏无机内墙儿童漆；
其中，步骤1)中的消泡剂、步骤3)中的消泡剂的重量比为1：1.5-2.5，优选为1：2。
与现有技术进行对比，本发明具有以下优点：
1)未使用可能引起儿童过敏的杀菌剂、防腐剂、防霉剂：
本发明以无机材料硅酸钾为主要成膜物质的涂料，加入各种助剂，制成的硅酸盐无机涂料；不仅与基材有很好的附着力、阻燃性、透气性，而且无机内墙儿童漆具有天然碱的特性，PH值在11以上，能杀灭细菌、苔藓、孢子，再结合其透气性能使建筑物保持干燥，并且纯天然无毒，从而降低儿童接触后的过敏反应。
2)未使用成膜助剂、防冻剂：
以无机材料硅酸钾自身成膜的特性，儿童漆中不含有易挥发的有机化学原料或溶剂，在生产和应用期间，没有任何味道有利于生态环境，不会引发任何过敏反应，非常的安全环保。
本发明的其他特征和优点将在随后的具体实施方式部分予以详细说明。
附图说明
附图是用来提供对本发明的进一步理解，并且构成说明书的一部分，与下面的具体实施方式一起用于解释本发明，但并不构成对本发明的限制。在附图中：
图1是本发明提供的一种抗过敏无机内墙儿童漆的制备方法的操作流程图。
具体实施方式
以下对本发明的具体实施方式进行详细说明。应当理解的是，此处所描述的具体实施方式仅用于说明和解释本发明，并不用于限制本发明。
本发明提供了一种抗过敏无机内墙儿童漆，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐150-400份、净味乳液40-150份、消泡剂2-6份、分散剂3-10份、颜料100-300份、无机填料0-400份、增稠剂1-5份、流平剂5-20份、耐水剂1-10份、水80-350份和稳定剂1-10份；
其中，所述净味乳液选自聚乙烯-丙烯酸酯乳液和聚苯乙烯-丙烯酸酯乳液中的至少一种，所述净味乳液可以提高儿童漆在涂刷上墙24小时以内的的早期耐水性，也可增加漆膜的柔韧度。净味乳液为壳核结构，采用保护胶体，成膜温度底，不需要添加任何成膜助剂，对填料等具有优异的包裹性，延展性好，极少的游离单体，气味较小。
在上述抗过敏无机内墙儿童漆中，各组分的含量可以在宽的范围内选择，但是为了进一步提高该儿童漆的力学性能、抗菌抗霉性能，优选地，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐200-350份、净味乳液40-90份、消泡剂3-5份、分散剂4-8份、颜料100-300份、无机填料150-200份、增稠剂2-5份、流平剂5-10份、耐水剂2-8份、水200-340份、稳定剂2-8份；更优选地，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐300份、净味乳液90份、消泡剂3份、分散剂7份、无机填料200份、增稠剂4份、流平剂5份、耐水剂3份、水173份、稳定剂5份。
在上述实施方式的基础上，为了赋予该抗过敏无机内墙儿童漆具有不同的色彩，优选地，以200-350份硅酸盐为基准，所述颜料的用量为150-250份。
其中，所述颜料的种类可以在宽的范围内选择，但是为了使得该抗过敏无机内墙儿童漆的色彩更加地丰富，优选地，所述颜料为金红石型钛白粉、锐钛型钛白粉中的一种。
在本发明中，对所述硅酸盐的种类不作具体限定，但是为了进一步提高该儿童漆的成膜效果，优选地，所述硅酸盐为氧化改性硅酸钠、氧化改性硅酸钾、氧化改性硅酸锂中的至少一种。如所述硅酸盐为氧化改性高模数硅酸钾水溶液(硅酸钾的模数为3.5-3.7)，常温下自固化，不需要添加任何成膜助剂即能较好成膜，具有优异的抗菌性、透气性，不需要添加成膜助剂、防冻剂，并且在合成的时无残留单体挥发，无气味，安全环保。所述硅酸盐可以以纯物质作为原料，也可以以水溶液的形式提供，水溶液稳定性好，早期耐水，上墙不易脱落，有良好的储存性。其中，改性硅酸钠、改性硅酸钾或改性硅酸锂均是通过以下方式得到：以盐类作为无机源，水玻璃与所述无机源进行皂化反应得到的改性硅酸盐。
在本发明中，对所述消泡剂的具体种类不作具体限定，但是为了提高消泡效果，优选地，所述消泡剂选自纳米聚硅氧烷-聚醚共聚物乳液类消泡剂、聚乙二醇-憎水固体-聚硅氧烷混合物类消泡剂和矿物油基类消泡剂中的至少一种。
在本发明中，所述分散剂的具体种类可以在宽的范围内选择，但是为了进一步提高分散效果，优选地，所述分散剂选自改性聚丙烯酸类分散剂和改性聚羧酸盐类分散剂中的至少一种。
所述改性聚丙烯酸类分散剂和改性聚羧酸盐类分散剂通过以下方法得到：以丙烯酸或羧酸盐为主单体，以马来酸酐、丙烯酰胺、甲基丙烯酸羟乙酯为改性单体，通过氧化还原引发自由基共聚合制备得到。
在上述实施方式中，所述无机填料的种类可以在宽的范围内变化，但是为了进一步提高儿童漆在成膜后的力学强度，优选地，所述无机填料选自重质碳酸钙、绢云母、滑石粉和硅灰石粉中的至少一种。其中，所述重质碳酸钙至少满足：CaCO3的重量分数≥98％，盐酸不溶物含量≤0.2重量％，碱金属及镁含量≤1.0重量％。
在此基础上，为了进一步提高儿童漆在成膜后的力学强度，更优选地，所述无机填料含有重量比为120-160：50：0-40的改性重质碳酸钙、绢云母和硅灰石粉。
在本发明中，所述增稠剂的种类可以在宽的范围内选择，但是为了提高儿童漆的黏度，优选地，所述增稠剂选自羟乙基纤维素、改性膨润土、气相纳米二氧化硅中的至少一种。
改性膨润土是利用蒙脱石的层片状结构及其能在水或有机溶剂中慢慢溶胀的特性，将有机覆盖剂交换插入而制成的，并且具有良好的增稠性、触变性、悬浮稳定性、耐水性等。
在上述实施方式中，对所述流平剂的种类不作具体限定，但是为了使得漆膜更加平整、光滑和均匀，优选地，所述流平剂选自交联型有机硅聚醚-丙烯酸酯类共聚物、二甲基聚硅氧烷乳液和聚硅氧烷-聚醚共聚物中的至少一种。
在上述实施方式中，对所述耐水剂的种类不作具体限定，但是为了使得漆膜具有更强的耐水性能，优选地，所述耐水剂为聚硅氧烷和烷基三乙氧基硅烷的共聚物，属于有机硅改性助剂。
在上述实施方式中，对所述稳定剂的种类不作具体限定，但是为了该儿童漆具有抗老化和防分解的效果，所述稳定剂选自季铵盐类、叔胺盐类、有机硅化物中的至少一种。稳定剂可以保证无机涂料在储存期内粘度稳定，降低涂料干化的风险。
本发明还提供了一种如上述的抗过敏无机内墙儿童漆的制备方法，盖制备方法包括：
1)将水、增稠剂、分散剂、消泡剂和稳定剂进行第一混合，以得到第一混合液；
2)将无机填料、所述第一混合液进行第二混合，以得到第二混合液；
3)将消泡剂、所述第二混合液进行第三混合，以得到第三混合液；
4)将净味乳液、硅酸盐、流平剂和耐水剂进行第四混合，以得到所述抗过敏无机内墙儿童漆；
其中，步骤1)中的消泡剂、步骤3)中的消泡剂的重量比为1：1.5-2.5，优选为1：2。
在上述制备方法中，对所述第一混合的条件不作具体限定，但是为了进一步提高该儿童漆的混合效果，优选地，所述第一混合至少满足以下条件：搅拌速率为200-300转/分钟，混合时间为3-8分钟。
在上述制备方法中，对所述第二混合的条件不作具体限定，但是为了进一步提高该儿童漆的混合效果，优选地，所述第二混合至少满足以下条件：搅拌速率为1500-1700转/分钟，混合时间为10-15分钟。
在上述制备方法中，对所述第三混合的条件不作具体限定，但是为了进一步提高消泡效果，所述第三混合至少满足以下条件：搅拌速率为700-900转/分钟，混合时间为4-10分钟。
在上述制备方法中，对所述第四混合的条件不作具体限定，但是为了进一步提高该儿童漆的混合效果，所述第四混合至少满足以下条件：搅拌速率为500-600转/分钟，混合时间为10-18分钟。
最后，在上述诸多实施方式的基础上，为了使得颜料能够与其他组分充分配合，优选地，所述第二混合还包括：将颜料、所述无机填料、所述第一混合液进行混合。
以下将通过实例对本发明进行详细描述。在以下实例中，硅酸盐溶液1选自澳润化工有限公司生产的K99A，固体含量在29.5±1重量％；硅酸盐溶液2选自佛山市顺德区荷叶化工有限公司生产的777A，固含量在30±1重量％。
净味乳液1选自佛山市顺德区荷叶化工有限公司生产的J-506乳液，固体含量在47±1重量％，玻璃化温度为5℃，最低成膜温度为0℃。净味乳液2选自上海巴德富有限公司的聚苯乙烯-丙烯酸酯乳液RS-837W，固体含量在48.5±1重量％，玻璃化温度为5℃，最低成膜温度为-1℃。
消泡剂1选自德国毕克化学公司生产的BYK024，消泡剂2选自巴斯夫公司生产的ST-2410AG。
分散剂1选自上海澳润化工生产的CROSFECT3600，分散剂2选自法国高泰化学生产ECODIS P30。
颜料为氯化法制得的金红石型钛白粉R-258。
填料选自广福建材的无机专用重钙粉CC-600、广福建材的SC800硅灰石,格锐矿业的绢云母粉GM900。
增稠剂1为浙江宇达化工有限公司的纳米气相二氧化硅粉体，增稠剂2为阿克苏公司生产的EBM3000。
流平剂为陶氏化学生产的流平剂RM-8W。
耐水剂为瓦克化学生产的有机硅耐水剂BS1306。
稳定剂1为上海澳润化工生产的CROSFECT CS1，稳定剂2为佛山市顺德区荷叶化工有限公司生产的WJ-100。
实施例1
A、原料准备：硅酸盐(300g硅酸盐溶液1)、净味乳液(90g净味乳液1)、消泡剂(3g消泡剂2)、分散剂(7g分散剂2)、200g颜料、无机填料(120g重钙粉CC600、50g绢云母粉GM900和40g硅灰石粉SC800)、增稠剂(4g增稠剂2)、5g流平剂、3g耐水剂、173g去离子水、稳定剂(5g稳定剂2)。
B、儿童漆制备：
1)分散机，将转速调到200-300转/分钟的速度，依次缓慢将水和增稠剂、分散剂、1g消泡剂、稳定剂在搅拌状态下加入，边搅拌边加料，加料完成再搅拌5分钟得到混合液。
2)向步骤1)的混合液中依次加入颜料、重钙粉CC600、绢云母粉GM900，和硅灰石粉SC800，加料同时按照浆料粘度逐步提高分散机的转速，全部加完后转速提高到1600转/分钟，分散10-15分钟得到混合液。测试混合液的细度指标，细度小于50um即进入下一步。
3)依次向步骤2)得到的混合液中加入2g消泡剂，并以800转/分钟的转速搅拌5分钟，充分消泡。
4)调整分散机至500-600转/分钟，加入净味乳液，搅拌1分钟混合均匀，再缓慢加入硅酸盐，测PH值大于11，最后加入流平剂、耐水剂，继续搅拌10-15分钟后，即得到抗过敏无机内墙儿童漆。
C、对上述抗过敏无机内墙儿童漆进行检测，检测结果见表1。
表1
实施例2
A、原料准备：硅酸盐(280g硅酸盐溶液2)、净味乳液(80g净味乳液2)、消泡剂(3g消泡剂1)、分散剂(7g分散剂1)、200g颜料、无机填料(120g重钙粉CC600、50g绢云母粉GM900和40g硅灰石粉SC800)、增稠剂(4g增稠剂1)、5g流平剂、3g耐水剂、203g去离子水、稳定剂(5g稳定剂1)。
B、儿童漆制备：
1)分散机，将转速调到200-300转/分钟的速度，依次缓慢将水和增稠剂、分散剂、1g消泡剂、稳定剂在搅拌状态下加入，边搅拌边加料，加料完成再搅拌5分钟得到混合液。
2)向步骤1)的混合液中依次加入颜料、重钙粉CC600、绢云母粉GM900，和硅灰石粉SC800，加料同时按照浆料粘度逐步提高分散机的转速，全部加完后转速提高到1600转/分钟，分散10-15分钟得到混合液。测试混合液的细度指标，细度小于50um即进入下一步。
3)依次向步骤2)得到的混合液中加入2g消泡剂，并以800转/分钟的转速搅拌5分钟，充分消泡。
4)调整分散机至500-600转/分钟，加入净味乳液，搅拌1分钟混合均匀，再缓慢加入硅酸盐，测PH值大于11，最后加入流平剂、耐水剂，继续搅拌10-15分钟后，即得到抗过敏无机内墙儿童漆。
C、对上述抗过敏无机内墙儿童漆进行检测，检测结果见表2。
表2
实施例3
A、原料准备：硅酸盐(280g硅酸盐溶液1)、净味乳液(80g净味乳液1)、消泡剂(3g消泡剂2)、分散剂(6g分散剂2)、190g颜料、无机填料(160g重钙粉CC600、50g绢云母粉GM900)、增稠剂(5g增稠剂2)、5g流平剂、3g耐水剂、214g去离子水、稳定剂(5g稳定剂2)。
B、儿童漆制备：
1)分散机，将转速调到200-300转/分钟的速度，依次缓慢将水和增稠剂、分散剂、1g消泡剂、稳定剂在搅拌状态下加入，边搅拌边加料，加料完成再搅拌5分钟得到混合液。
2)向步骤1)的混合液中依次加入颜料、重钙粉CC600、绢云母粉GM900，和硅灰石粉SC800，加料同时按照浆料粘度逐步提高分散机的转速，全部加完后转速提高到1600转/分钟，分散10-15分钟得到混合液。测试混合液的细度指标，细度小于50um即进入下一步。
3)依次向步骤2)得到的混合液中加入2g消泡剂，并以800转/分钟的转速搅拌5分钟，充分消泡。
4)调整分散机至500-600转/分钟，加入净味乳液，搅拌1分钟混合均匀，再缓慢加入硅酸盐，测PH值大于11，最后加入流平剂、耐水剂，继续搅拌10-15分钟后，即得到抗过敏无机内墙儿童漆。
C、对上述抗过敏无机内墙儿童漆进行检测，检测结果见表3。
表3
实施例4
按照实施例1的方法进行，唯一所不同的是：A、原料准备：硅酸盐(250g硅酸盐溶液2)、净味乳液(60g净味乳液2)、消泡剂(3g消泡剂1)、分散剂(7g分散剂1)、180g颜料、无机填料(160g重钙粉CC600、50g绢云母粉GM900和40g硅灰石粉SC800)、增稠剂(4g增稠剂1)、5g流平剂、3g耐水剂、303g去离子水、稳定剂(5g稳定剂1)；其他步骤相同。
对制得的抗过敏无机内墙儿童漆进行检测，检测结果见表4。
表4
实施例5
按照实施例1的方法进行，唯一所不同的是：A、原料准备：硅酸盐(150g硅酸盐溶液2)、净味乳液(40g净味乳液2)、消泡剂(3g消泡剂1)、分散剂(7g分散剂1)、100g颜料、无机填料(310g重钙粉CC600、50g绢云母粉GM900、40g硅灰石粉SC800)、增稠剂(4g增稠剂1)、5g流平剂、3g耐水剂、283g去离子水、稳定剂(5g稳定剂1)；其他步骤相同。
对制得的抗过敏无机内墙儿童漆进行检测，检测结果见表5。
表5
实施例6
按照实施例1的方法进行，唯一所不同的是：A、原料准备：硅酸盐(400g硅酸盐溶液2)、净味乳液(150g净味乳液2)、消泡剂(5g消泡剂1)、分散剂(10g分散剂1)、300g颜料、增稠剂(4g增稠剂1)、15g流平剂、8g耐水剂、80g去离子水、稳定剂(5g稳定剂1)；其他步骤相同。
对制得的抗过敏无机内墙儿童漆进行检测，检测结果见表6。
表6
对比例1
按照实施例1的方法进行，唯一所不同的是：硅酸盐用量为450g，净味乳液的用量为160g。
对制得的抗过敏无机内墙儿童漆进行检测，检测结果见表7。
表7
实施例1中硅酸钾乳液为300g，净味乳液是90g,钛白粉含量为200g，乳液和钛白粉的含量均是1-5实施例中添加量最高的，因而耐擦洗是10000次，对比率为0.98均是最高的。并且对大肠杆菌和金黄色葡萄球菌的抗菌性能、抗细菌耐久性数值对比实施例2-5也是最高的。
实施例2中的硅酸钾乳液为280g，净味乳液是80g，比实施例1有所下降，但粉料添加是不变的，因而实施例2中的耐擦洗数值为9000次，比实施例1下降1000次，对比率无变化。
实施例3中的硅酸钾乳液为280g，净味乳液是80g，相比较实施例2无变化，但是钛白粉为190g，比实施例2下降10g，测结果显示对比率下降1个值，为0.97，而耐擦洗数值和实施例2一致。
实施例4中硅酸钾溶液250g，比实施例3少30g；净味乳液60g，比实施例3少20g；钛白粉为170g，比实施例3少20g；结果对比率下降到0.96，耐擦洗只有7000次。
实施例5中硅酸钾溶液最低，为220g；净味乳液40g，钛白粉150g，测试结果对比率为0.95，耐擦洗为6000次，刚刚达到GB9756-2018国家标准中规定的优等品，处于临界值。
综合分析1-5实施例可以看出，随着硅酸钾乳液和净味乳液的递减，抗过敏无机内墙儿童漆的耐擦洗性能会有所下降，从10000次下降至6000次，这是因为随着乳液的逐渐递减，对粉料的包裹能力逐渐下降，耐水性也逐渐降低。
同时由于硅酸钾乳液提供抗过敏无机内墙儿童漆的天然碱性，在硅酸钾乳液含量高的实施例中如实施例1中，对大肠杆菌和金黄色葡萄球菌的抗菌性能、抗细菌耐久性数值是最高的，但是从实施例1至实施例5，随着硅酸钾溶液的递减，产品的PH也成递减的趋势，因而实施例5中因为硅酸钾溶液含量最低，产品的PH也最低，对大肠杆菌和金黄色葡萄球菌的抗菌性能、抗细菌耐久性数值是最低的，处于合格临界值。
实施例6中硅酸钾乳液为400g，净味乳液是150g,钛白粉含量为300g，乳液和钛白粉的含量均是1-6实施例中添加量最高的，因而耐擦洗是20000次是最高的，对比率为0.98和实施例1一致。由于大量的加入硅酸钾乳液能显著提高配方的碱性，碱性越强，细菌越难生存，所以对大肠杆菌和金黄色葡萄球菌的抗菌性能、抗细菌耐久性也是很好的。
对比例1是按照实施例1的方法进行，唯一所不同的是：硅酸盐用量为450g，净味乳液的用量为160g。很明显实施例中乳液的增加在一定程度上降低了粉体在整个配方中的浓度，因而虽然颜料含量也升高了，对比率也就下降了只有0.90，已经达不到国家内墙涂料优等品(对比率》0.95)的要求了。耐洗刷性为20000次，实施例1是10000次，因而提高乳液加入量有益于增加耐洗刷性能。同时，由于对比例1中的硅酸盐用量为450，大于实施例1用量150g,整体配方碱性比实施例1高，所以抗菌性能要好于实施例1。
因而，配方的遮盖力(对比例)、耐洗刷性、抗菌性之间是有互相牵制的关系的。一味的提升耐洗刷性，遮盖力就可能下降；降低耐洗刷性，抗菌性可能也下降。所以应综合评估各个原料的加入量，使产品的综合性能得到提升，而不是只提升其中某一项性能。
检测例1
本发明实例所得抗过敏无机内墙儿童漆与市售的两款普通儿童乳胶漆同时测试比较，其中，市售儿童乳胶漆1为一款国内A厂的市售品，市售儿童乳胶漆2为一款国外B厂的市售品。
实验方法：将9个体积为3立方米的透明玻璃仓编号1-9#，1个玻璃仓留一个观察面查看小白鼠的反应，剩余4个面刷上市售普通儿童乳胶漆1、市售儿童乳胶漆2和本发明实例中的抗过敏无机内墙儿童漆。之后分别在各个玻璃仓中分别放入10只幼年小白鼠，体重为40-50克左右，随着玻璃仓漆膜的逐渐干燥，漆膜会释放产品本身的化学气味，2小时后观察玻璃仓中小白鼠的反应，是否有打喷嚏，喘气不匀，精神萎靡，起疹子等症状并记录。24小时后查看小白鼠状态并记录，具体结果见表6。
表6
由此可见：市售儿童漆2个样品在最初2个小时的VOC释放，均引起了部分幼年小白鼠打喷嚏或喘气不匀的症状，在24小时后喘气不匀的小白鼠数量增加，说明在本实验条件下很容易引起过敏反应；而抗过敏无机内墙儿童漆在最初2个小时，由于其无气味环保，并没有小白鼠出现异常症状，在24小时后实施例3玻璃仓中有1只喘气不匀，其它均无症状。因而相比较市售的儿童乳胶漆，抗过敏无机内墙儿童漆具有很好的抗过敏效果。
以上详细描述了本发明的优选实施方式，但是，本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
Claims (10)
1.一种抗过敏无机内墙儿童漆，其特征在于，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐150-400份、净味乳液40-150份、消泡剂2-6份、分散剂3-10份、颜料100-300份、无机填料0-400份、增稠剂1-5份、流平剂5-20份、耐水剂1-10份、水80-350份和稳定剂1-10份；
其中，所述净味乳液选自聚乙烯-丙烯酸酯乳液和聚苯乙烯-丙烯酸酯乳液中的至少一种。
2.根据权利要求1所述的抗过敏无机内墙儿童漆，其特征在于，按重量份计，所述抗过敏无机内墙儿童漆含有：硅酸盐200-350份、净味乳液40-90份、消泡剂3-5份、分散剂4-8份、颜料100-300份、无机填料150-200份、增稠剂2-5份、流平剂5-10份、耐水剂2-8份、水200-340份、稳定剂2-8份。
3.根据权利要求1所述的抗过敏无机内墙儿童漆，其特征在于，以200-350份硅酸盐为基准，所述颜料的用量为150-250份；
优选地，所述颜料为金红石型钛白粉、锐钛型钛白粉中的一种。
4.根据权利要求1-3中任意一项所述的抗过敏无机内墙儿童漆，其特征在于，所述硅酸盐为改性硅酸钠、改性硅酸钾、改性硅酸锂中的至少一种；改性硅酸钠、改性硅酸钾或改性硅酸锂均是通过以下方式得到：以盐类作为无机源，水玻璃与所述无机源进行皂化反应得到的改性硅酸盐；
所述消泡剂选自聚硅氧烷-聚醚共聚物乳液类消泡剂、聚乙二醇-憎水固体-聚硅氧烷混合物类消泡剂和矿物油基类消泡剂中的至少一种。
5.根据权利要求1-3中任意一项所述的抗过敏无机内墙儿童漆，其特征在于，所述分散剂选自改性聚丙烯酸类分散剂和改性聚羧酸盐类分散剂中的至少一种；
所述无机填料选自重质碳酸钙、绢云母、滑石粉和硅灰石粉中的至少一种；
所述重质碳酸钙至少满足：CaCO3的重量分数≥98％，盐酸不溶物含量≤0.2重量％，碱金属及镁含量≤1.0重量％；
优选地，所述无机填料含有重量比为120-160：50：0-40的重质碳酸钙、绢云母和硅灰石粉。
6.根据权利要求1-3中任意一项所述的抗过敏无机内墙儿童漆，其特征在于，所述增稠剂选自羟乙基纤维素、改性膨润土、气相纳米二氧化硅中的至少一种；
所述流平剂选自交联型有机硅聚醚-丙烯酸酯类共聚物、二甲基聚硅氧烷乳液和聚硅氧烷-聚醚共聚物中的至少一种。
7.根据权利要求1-3中任意一项所述的抗过敏无机内墙儿童漆，其特征在于，所述耐水剂为聚硅氧烷和烷基三乙氧基硅烷的共聚物；
所述稳定剂选自季铵盐类、叔胺盐类、有机硅化物中的至少一种。
8.一种如权利要求1-7中任意一项所述的抗过敏无机内墙儿童漆的制备方法，其特征在于，所述制备方法包括：
1)将水、增稠剂、分散剂、消泡剂和稳定剂进行第一混合，以得到第一混合液；
2)将无机填料、所述第一混合液进行第二混合，以得到第二混合液；
3)将消泡剂、所述第二混合液进行第三混合，以得到第三混合液；
4)将净味乳液、硅酸盐、流平剂和耐水剂进行第四混合，以得到所述抗过敏无机内墙儿童漆；
其中，步骤1)中的消泡剂、步骤3)中的消泡剂的重量比为1：1.5-2.5。
9.根据权利要求8所述的制备方法，其特征在于，所述第一混合至少满足以下条件：搅拌速率为200-300转/分钟，混合时间为3-8分钟；
所述第二混合至少满足以下条件：搅拌速率为1500-1700转/分钟，混合时间为10-15分钟；
所述第三混合至少满足以下条件：搅拌速率为700-900转/分钟，混合时间为4-10分钟；
所述第四混合至少满足以下条件：搅拌速率为500-600转/分钟，混合时间为10-18分钟。
10.根据权利要求9或10所述的制备方法，其特征在于，所述第二混合还包括：将颜料、所述无机填料、所述第一混合液进行混合。