CN113926675A - UV (ultraviolet) colorful series curtain coating bright surface coating construction process for decorative plate - Google Patents
UV (ultraviolet) colorful series curtain coating bright surface coating construction process for decorative plate Download PDFInfo
- Publication number
- CN113926675A CN113926675A CN202111327120.9A CN202111327120A CN113926675A CN 113926675 A CN113926675 A CN 113926675A CN 202111327120 A CN202111327120 A CN 202111327120A CN 113926675 A CN113926675 A CN 113926675A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- weight
- construction process
- adopting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a decorative plate UV dazzling color series spray coating bright and clear surface coating construction process, which belongs to the technical field of coating construction. The bright clear finish comprises a coupling agent, silicone-acrylic emulsion, epoxy resin, pearl powder and inorganic pigment, wherein the pearl powder and the inorganic pigment are used jointly, so that the finish surface can present metal luster, can generate multi-level reflection when being irradiated by sunlight, and the reflected light interacts to present soft and dazzling or colorful luster and color.
Description
Technical Field
The invention relates to the technical field of coating construction, in particular to a UV colorful series curtain coating bright surface coating construction process for a decorative plate.
Background
At present, the bright coating effect of decorative plates on the market mainly comprises UV (ultraviolet) spraying bright clear surfaces and PET (polyethylene terephthalate) film flatly pasted on the surfaces of the decorative plates. The UV flow-coating bright clear top coat paint film has high plumpness, but has high requirements on paint and coating environment, and the paint film is thick, has easy edge breakage. The PET film with the flat-pasted board surface has strong anti-sinking capability, but the glue is not environment-friendly due to the use of the glue component, and is easy to delaminate and not resistant to yellowing after a long time.
In the prior published documents, much attention is paid to the pursuit of the style and appearance of the decorative board, particularly the color of the decorative board, most of the prior arts mix pigment into the raw material of the decorative board, the color of the panel material prepared by the method is dull due to processing reasons, and the pigment is distributed in the whole decorative board, so the use amount of the pigment is large, and the color is generally monochromatic, and the monochromatic decorative board cannot meet the color requirement of consumers.
Disclosure of Invention
The invention provides a UV dazzling color series spray coating bright surface coating construction process for a decorative plate, which aims to solve the technical problem that the color of the decorative plate is single in the prior art.
The embodiment of the invention adopts the following technical scheme: a decorative board UV dazzles various series and drenches and scribbles clear surface application construction technology, its technical point lies in: the method comprises the following steps:
firstly, sticking dark triamine paper on two sides of a base material with the thickness of 18mm, performing edge grinding treatment on the base material stuck with the dark triamine paper, slightly polishing the surface, and then performing board surface dust removal;
step two, coating a single-roller UV (ultraviolet) adhesion primer on the base material stuck with the dark triamine paper in the step one, wherein the coating weight is 10-15g/m2Drying by adopting an ultraviolet lamp to make the paint film semi-dry;
step three, on the basis of the step two, the coating weight of the mixture of the single-roller UV primer and the color-changing flash silver powder is 10-20g/m2Drying by adopting an ultraviolet lamp to make a paint film semi-dry, wherein the mass ratio of the UV primer to the color-changing flash silver powder is (3-5): 1;
step four, on the basis of the step three, double-roller UV sanding primer with the coating weight of 30-50g/m2Drying by adopting an ultraviolet lamp to dry a paint film;
step five, sequentially adopting 320-mesh, 400-mesh and 600-mesh sand paper for sanding;
sixthly, rolling UV pre-spraying roller primer on the base material subjected to sanding treatment in a coating amount of 8-10g/m2Drying by adopting an ultraviolet lamp;
step seven, adopting a curtain coating machine to curtain and coat the bright clear finish paint, wherein the coating weight is 120-140g/m2After leveling, drying by adopting an ultraviolet lamp to completely dry a paint film, wherein the bright clear finish paint comprises 3-8 parts by weight of coupling agent, 10-20 parts by weight of silicone-acrylic emulsion, 5-10 parts by weight of epoxy resin, 3-4 parts by weight of pearl powder and 1-3 parts by weight of inorganic pigment;
and step eight, finally, coating a protective film and packaging to finish production.
In some embodiments of the present invention, in the first step of the UV glare series curtain coating and bright top-clear coating construction process for the decorative board of the present invention, the base material is any one of a medium density fiberboard and a particle board.
In some embodiments of the invention, in the first step of the decorative board UV glare color series flow coating bright surface finish coating construction process, the dark triamine paper is any one of pure black dark triamine paper or dark grey triamine paper.
In some embodiments of the invention, the UV sanding primer in the fourth step comprises the following raw materials in parts by weight: 30-40 parts of bisphenol A epoxy acrylate, 30-35 parts of tripropylene glycol diacrylate, 2-3 parts of tripropylene glycol diacrylate, 4-5 parts of benzophenone, 2-3 parts of active ammonia, 0.05-1 part of dispersing agent, 10-15 parts of filler, 1-3 parts of flatting agent, 0.6-0.7 part of defoaming agent and 1-2 parts of grinding aid.
In some embodiments of the present invention, the particle size of the pearlescent powder in the step seven is 100-200 nm.
In some embodiments of the present invention, in the step seven, the inorganic pigment is at least one of titanium dioxide, black iron oxide, black copper-chromium black, black manganese-iron, yellow iron oxide, titanium yellow, red iron oxide, cobalt blue, cobalt green and iron green oxide.
In some embodiments of the present invention, the coupling agent in the seventh step is at least one of a silane coupling agent and a titanate coupling agent.
In a further embodiment of the present invention, the silicone-acrylic emulsion in step seven has a solid content of 40-50% and a viscosity of 9-15 pas.
The embodiment of the invention adopts at least one technical scheme which can achieve the following beneficial effects:
the UV colorful series curtain coating bright surface coating construction process for the decorative plate comprises the steps of pretreatment, single-roller UV attaching primer, single-roller UV primer and color-changing flashing silver powder, double-roller UV sanding primer, sanding treatment, roller UV sanding primer and curtain coating bright surface paint. The bright clear finish comprises a coupling agent, silicone-acrylic emulsion, epoxy resin, pearl powder and inorganic pigment, wherein the pearl powder and the inorganic pigment are used jointly, so that the finish surface can present metal luster, can generate multi-level reflection when being irradiated by sunlight, and the reflected light interacts to present soft and dazzling or colorful luster and color.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the technical solutions of the present invention will be clearly and completely described below with reference to the specific embodiments of the present invention. It is to be understood that the described embodiments are merely exemplary of the invention, and not restrictive of the full scope of the invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
A UV dazzling color series curtain coating bright surface coating construction process for a decorative plate comprises the following steps:
firstly, sticking dark triamine paper on two sides of a base material with the thickness of 18mm, performing edge grinding treatment on the base material stuck with the dark triamine paper, slightly polishing the surface, and then performing board surface dust removal;
step two, coating the base material stuck with the dark triamine paper in the step oneRoller UV adhesion primer coating weight of 20g/m2Drying by adopting an ultraviolet lamp to make the paint film semi-dry;
step three, on the basis of the step two, the coating weight of the mixture of the single-roller UV primer and the color-changing flash silver powder is 15g/m2And drying by adopting an ultraviolet lamp to make the paint film semi-dry, wherein the mass ratio of the UV primer to the color-changing flash silver powder is 4: 1;
step four, on the basis of the step three, double-roller UV sanding primer with the coating weight of 40g/m2Drying by adopting an ultraviolet lamp to dry a paint film;
step five, sequentially adopting 320-mesh, 400-mesh and 600-mesh sand paper for sanding;
sixthly, rolling UV pre-spraying roller primer on the base material subjected to sanding treatment in a coating amount of 9g/m2Drying by adopting an ultraviolet lamp;
step seven, adopting a curtain coating machine to coat the bright clear finish paint in a curtain coating way, wherein the coating weight is 130g/m2After leveling, drying by adopting an ultraviolet lamp to ensure that a paint film is completely dry, wherein the bright clear finish paint comprises 5.5 parts by weight of coupling agent, 15 parts by weight of silicone-acrylic emulsion, 7.5 parts by weight of epoxy resin, 3.5 parts by weight of pearl powder and 2 parts by weight of inorganic pigment;
and step eight, finally, coating a protective film and packaging to finish production.
In the first step of the UV dazzling color series flow coating bright surface clear coating construction process for the decorative plate, the base material is a medium density fiberboard.
In the first step of the UV dazzling color series flow coating bright surface clear coating construction process for the decorative plate, the dark triamine paper is pure black dark triamine paper.
The UV sanding primer comprises the following raw materials in parts by weight: 35 parts by weight of bisphenol A epoxy acrylate, 32.5 parts by weight of tripropylene glycol diacrylate, 2.5 parts by weight of tripropylene glycol diacrylate, 4.5 parts by weight of benzophenone, 2.5 parts by weight of active ammonia, 0.5 part by weight of a dispersant, 12.5 parts by weight of a filler, 2 parts by weight of a leveling agent, 0.65 part by weight of an antifoaming agent and 1.5 parts by weight of a grinding aid.
Wherein, the modified organic silicon wetting and leveling agent is adopted to carry out wetting before curtain coating in the fourth step.
Wherein, the particle size of the pearly luster powder in the seventh step is 150 nm.
And the inorganic pigment in the seventh step is titanium dioxide.
Wherein, the coupling agent in the seventh step is a silane coupling agent.
Wherein, the solid content of the silicone-acrylate emulsion in the seventh step is 45 percent, and the viscosity is 12 pas.
Example 2
A UV dazzling color series curtain coating bright surface coating construction process for a decorative plate comprises the following steps:
firstly, sticking dark triamine paper on two sides of a base material with the thickness of 18mm, performing edge grinding treatment on the base material stuck with the dark triamine paper, slightly polishing the surface, and then performing board surface dust removal;
step two, coating a single-roller UV adhesion primer on the base material stuck with the dark triamine paper in the step one, wherein the coating weight is 12.5g/m2Drying by adopting an ultraviolet lamp to make the paint film semi-dry;
step three, on the basis of the step two, the coating weight of the mixture of the single-roller UV primer and the color-changing flash silver powder is 10g/m2And drying by adopting an ultraviolet lamp to make the paint film semi-dry, wherein the mass ratio of the UV primer to the color-changing flash silver powder is 3: 1;
step four, on the basis of the step three, double-roller UV sanding primer with the coating weight of 30g/m2Drying by adopting an ultraviolet lamp to dry a paint film;
step five, sequentially adopting 320-mesh, 400-mesh and 600-mesh sand paper for sanding;
sixthly, rolling UV pre-spraying roller primer on the base material subjected to sanding treatment in a coating amount of 8g/m2Drying by adopting an ultraviolet lamp;
step seven, adopting a curtain coating machine to curtain and coat the bright clear finish paint, wherein the coating weight is 120g/m2After leveling, drying by adopting an ultraviolet lampThe varnish film is completely dry, and the glossy clear finish paint comprises 3 parts by weight of coupling agent, 10 parts by weight of silicone-acrylic emulsion, 5 parts by weight of epoxy resin, 3 parts by weight of pearl powder and 1 part by weight of inorganic pigment;
and step eight, finally, coating a protective film and packaging to finish production.
In the first step of the UV dazzling color series curtain coating bright surface coating construction process for the decorative plate, the base material is a shaving board.
In the first step of the UV dazzling color series flow coating bright surface coating construction process for the decorative plate, the dark triamine paper is dark gray triamine paper.
The UV sanding primer comprises the following raw materials in parts by weight: 30 parts by weight of bisphenol A epoxy acrylate, 30 parts by weight of tripropylene glycol diacrylate, 2 parts by weight of tripropylene glycol diacrylate, 4 parts by weight of benzophenone, 2 parts by weight of active ammonia, 0.05 part by weight of a dispersant, 10 parts by weight of a filler, 1 part by weight of a leveling agent, 0.6 part by weight of an antifoaming agent, and 1 part by weight of a grinding aid.
Wherein, the modified organic silicon wetting and leveling agent is adopted to carry out wetting before curtain coating in the fourth step.
Wherein, the particle size of the pearly luster powder in the seventh step is 100 nm.
Wherein, the inorganic pigment in the seventh step is iron oxide black.
Wherein, the coupling agent in the seventh step is titanate coupling agent.
Wherein, the solid content of the silicone-acrylate emulsion in the seventh step is 40 percent, and the viscosity is 9 pas.
Example 3
A UV dazzling color series curtain coating bright surface coating construction process for a decorative plate comprises the following steps:
firstly, sticking dark triamine paper on two sides of a base material with the thickness of 18mm, performing edge grinding treatment on the base material stuck with the dark triamine paper, slightly polishing the surface, and then performing board surface dust removal;
step two, in the step oneThe single-roll UV adhesion primer is coated on the base material stuck with the dark triamine paper, and the coating weight is 10g/m2Drying by adopting an ultraviolet lamp to make the paint film semi-dry;
step three, on the basis of the step two, coating weight of a mixture of single-roller UV primer and color-changing flash silver powder is 20g/m2Drying by adopting an ultraviolet lamp to make a paint film semi-dry, wherein the mass ratio of the UV primer to the color-changing flash silver powder is 5: 1;
step four, on the basis of the step three, double-roller UV sanding primer with the coating weight of 50g/m2Drying by adopting an ultraviolet lamp to dry a paint film;
step five, sequentially adopting 320-mesh, 400-mesh and 600-mesh sand paper for sanding;
sixthly, rolling UV pre-spraying roller primer on the base material subjected to sanding treatment in a coating amount of 10g/m2Drying by adopting an ultraviolet lamp;
step seven, adopting a curtain coating machine to curtain and coat the bright clear finish paint, wherein the coating weight is 140g/m2After leveling, drying by adopting an ultraviolet lamp to completely dry a paint film, wherein the bright clear finish paint comprises 8 parts by weight of coupling agent, 20 parts by weight of silicone-acrylic emulsion, 10 parts by weight of epoxy resin, 4 parts by weight of pearl powder and 3 parts by weight of inorganic pigment;
and step eight, finally, coating a protective film and packaging to finish production.
In the first step of the UV dazzling color series flow coating bright surface clear coating construction process for the decorative plate, the base material is a medium density fiberboard.
In the first step of the UV dazzling color series flow coating bright surface clear coating construction process for the decorative plate, the dark triamine paper is pure black dark triamine paper.
The UV sanding primer comprises the following raw materials in parts by weight: 40 parts by weight of bisphenol A epoxy acrylate, 35 parts by weight of tripropylene glycol diacrylate, 3 parts by weight of tripropylene glycol diacrylate, 5 parts by weight of benzophenone, 3 parts by weight of active ammonia, 1 part by weight of a dispersant, 15 parts by weight of a filler, 3 parts by weight of a leveling agent, 0.7 part by weight of an antifoaming agent and 2 parts by weight of a grinding aid.
Wherein, the modified organic silicon wetting and leveling agent is adopted to carry out wetting before curtain coating in the fourth step.
Wherein, the particle size of the pearly luster powder in the seventh step is 200 nm.
Wherein, the inorganic pigment in the seventh step is copper chromium black.
Wherein, the coupling agent in the seventh step is a mixture of a silane coupling agent and a titanate coupling agent, wherein the weight ratio of the silane coupling agent to the titanate coupling agent is 1: 1.
wherein, the solid content of the silicone-acrylate emulsion in the seventh step is 50 percent, and the viscosity is 15 Pa.s.
Examples of the experiments
According to the construction process of the UV dazzling series curtain coating bright surface clear coating of the decorative plate in the embodiment 1-3, the performance of the obtained product is detected, and the detection result is as follows:
TABLE 1
| Apparent Properties | |
| Example 1 | Bright and uniform color and clear level |
| Example 2 | Bright and uniform color and clear level |
| Example 3 | Bright and uniform color and clear level |
| Comparative example 1 No addition of pearlescent powder | Dull color and gradation on the surface |
| Comparative example 2 No inorganic pigment addition | Bright and uneven color |
As can be seen from Table 1, the product of the process of the present invention has gorgeous color, distinct color difference gradation and uniform color distribution.
The above description is only an example of the present invention, and is not intended to limit the present invention. Various modifications and alterations to this invention will become apparent to those skilled in the art. Any modification, equivalent replacement, improvement, etc. made within the spirit and principle of the present invention should be included in the scope of the claims of the present invention.
Claims (8)
1. The utility model provides a decorative board UV dazzles various series drenches and scribbles clear surface application construction technology which characterized in that: the method comprises the following steps:
firstly, sticking dark triamine paper on two sides of a base material with the thickness of 18mm, performing edge grinding treatment on the base material stuck with the dark triamine paper, slightly polishing the surface, and then performing board surface dust removal;
step two, coating a single-roller UV (ultraviolet) adhesion primer on the base material stuck with the dark triamine paper in the step one, wherein the coating weight is 10-15g/m2Drying by adopting an ultraviolet lamp to make the paint film semi-dry;
step three, on the basis of the step two, the coating weight of the mixture of the single-roller UV primer and the color-changing flash silver powder is 10-20g/m2Drying by adopting an ultraviolet lamp to make a paint film semi-dry, wherein the mass ratio of the UV primer to the color-changing flash silver powder is (3-5): 1;
step four, on the basis of the step three, double-roller UV sanding primer with the coating weight of 30-50g/m2Drying by adopting an ultraviolet lamp to dry a paint film;
step five, sequentially adopting 320-mesh, 400-mesh and 600-mesh sand paper for sanding;
sixthly, rolling UV pre-spraying roller primer on the base material subjected to sanding treatment in a coating amount of 8-10g/m2Drying by adopting an ultraviolet lamp;
step seven, adopting a curtain coating machine to curtain and coat the bright clear finish paint, wherein the coating weight is 120-140g/m2After leveling, drying by adopting an ultraviolet lamp to completely dry a paint film, wherein the bright clear finish paint comprises 3-8 parts by weight of coupling agent, 10-20 parts by weight of silicone-acrylic emulsion, 5-10 parts by weight of epoxy resin, 3-4 parts by weight of pearl powder and 1-3 parts by weight of inorganic pigment;
and step eight, finally, coating a protective film and packaging to finish production.
2. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: in the first step, the base material is any one of a medium density fiberboard and a flakeboard.
3. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: in the first step, the dark triamine paper is any one of pure black dark triamine paper or dark grey triamine paper.
4. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: the UV sanding primer in the fourth step comprises the following raw materials in parts by weight: 30-40 parts of bisphenol A epoxy acrylate, 30-35 parts of tripropylene glycol diacrylate, 2-3 parts of tripropylene glycol diacrylate, 4-5 parts of benzophenone, 2-3 parts of active ammonia, 0.05-1 part of dispersing agent, 10-15 parts of filler, 1-3 parts of flatting agent, 0.6-0.7 part of defoaming agent and 1-2 parts of grinding aid.
5. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: the particle size of the pearlescent powder in the seventh step is 100-200 nm.
6. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: and the inorganic pigment in the seventh step is at least one of titanium dioxide, black iron oxide, copper chromium black, manganese iron black, iron oxide yellow, titanium yellow, iron oxide red, cobalt blue, cobalt green and iron oxide green.
7. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: and in the seventh step, the coupling agent is at least one of silane coupling agent and titanate coupling agent.
8. The decorative board UV dazzling series curtain coating bright surface coating construction process according to claim 1, characterized in that: the solid content of the silicone-acrylate emulsion in the seventh step is 40-50%, and the viscosity is 9-15 Pa.s.