CN113925967A - 一种生物光素及其制备方法和应用 - Google Patents
一种生物光素及其制备方法和应用 Download PDFInfo
- Publication number
- CN113925967A CN113925967A CN202111201813.3A CN202111201813A CN113925967A CN 113925967 A CN113925967 A CN 113925967A CN 202111201813 A CN202111201813 A CN 202111201813A CN 113925967 A CN113925967 A CN 113925967A
- Authority
- CN
- China
- Prior art keywords
- parts
- jade
- superfine
- zinc oxide
- biological light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种生物光素及其制备方法和应用,属于医用保健品技术领域。本发明提供的生物光素,按质量份数计,包括以下组分:玉石15~35份,砭石20~40份,二氧化硅矿石20~35份和氧化锌10~25份。本发明加入的氧化锌有良好的生物相容性和较高的生物活性,与玉石、砭石和二氧化硅配合使用后,能够起到协同作用,提高了对于金黄色葡萄球菌、大肠杆菌和白色念珠菌等细菌的杀菌抑菌效果,同时提高了生物光素的消臭效果。实施例的结果显示,本发明提供的生物光素对于金黄色葡萄球菌的抑菌率≥99%,对大肠杆菌的抑菌率≥70%,对白色念珠菌的抑菌率≥99%,洗后10次消臭率≥70%,远红外辐射率≥0.87。
Description
技术领域
本发明涉及医用保健品技术领域,尤其涉及一种生物光素及其制备方法和应用。
背景技术
生物光素是一种全新的医用生物功能性复合材料,是生物医用光量子非晶体等多种技术的结晶产物,能调节人体的机能。在祖国传统的医学宝库里,玉石可入药,它性平味甘,有除烦止渴,养神明目,定心定睛,滋长毛发,助声喉等功能。据矿物医学研究证明:玉石具有高强度的电子,电子衍射能释放出足以影响人体的生物电,刺激内分泌,调节新陈代谢的巨大能量,玉石还具有特殊的光电效应,在切削、研磨和抛光过程中形成一个电磁场,这些效应集蓄而形成一个谐振器,能与人体发生谐振,使人体各部分更加协调运转。同时玉石还含有锌、铜、锗、钴、镍、锰、硒等各种有益的微量元素,具有能够平衡生理机能的功效。因此,现有技术通常会使用玉石制作生物光素,同时为了提高生物光素的功效,通常选择加入珍珠粉、甲壳素和钻石等。由于珍珠粉、甲壳素和钻石等成本高,导致生物光素的价格高昂,同时生物光素具有促进微循环的作用,促进有机质的排出和皮肤表面出汗,很容易引起细菌和微生物的生长,导致生物光素用于医疗止痛膏贴时难以抑制炎症,需要加入其他的消炎成分,用于纺织品后容易使得纺织品产生异味,极大的限制了生物光素的推广和应用。因此,需要提供一种成本低且杀菌抑菌效果优异的生物光素。
发明内容
本发明的目的在于提供一种生物光素及其制备方法和应用,本发明提供的生物光素具有很好的杀菌抑菌效果,能够用于医疗止痛膏贴和纺织品中起到很好的医疗保健效果,且生产成本较低。
为了实现上述发明目的,本发明提供以下技术方案:
本发明提供了一种生物光素,按质量份数计,包括以下组分:玉石15~35份,砭石20~40份,二氧化硅矿石20~35份和氧化锌10~25份。
优选地,按质量份数计,包括以下组分:玉石20~25份,砭石30~40份,二氧化硅矿石25~30份和氧化锌10~25份。
优选地,所述玉石、砭石、二氧化硅矿石和氧化锌的粒径独立地为D50≤1μm。
优选地,所述玉石、砭石和二氧化硅矿石的纯度≥95wt.%。
优选地,所述玉石的密度为2.4~4.2kg/L。
优选地,所述砭石的密度为2.6~2.9kg/L。
优选地,所述二氧化硅矿石的密度为2.5~2.9kg/L。
本发明提供了上述技术方案所述生物光素的制备方法,包括以下步骤:
(1)分别将玉石、砭石和二氧化硅矿石依次进行粉碎、湿法球磨和超细粉碎,得到超细玉石、超细砭石和超细二氧化硅矿石;
(2)将氧化锌和部分所述步骤(1)得到的超细玉石混合进行超细粉碎,得到超细混合料;
(3)将所述步骤(1)得到的超细砭石、超细二氧化硅矿石和剩余的超细玉石与所述步骤(2)得到的超细混合料混合,得到生物光素。
优选地,所述步骤(2)中氧化锌和部分超细玉石的质量比为5:(1~2)。
本发明提供了上述技术方案所述生物光素或上述技术方案所述制备方法制备的生物光素在医用膏贴和纺织品中的应用。
本发明提供了一种生物光素,按质量份数计,包括以下组分:玉石15~35份,砭石20~40份,二氧化硅矿石20~35份和氧化锌10~25份。本发明中玉石具有高强度的电子,可以刺激人体内分泌,调节新陈代谢,同时刺激人体穴位,起到治疗作用;二氧化硅作为远红外材料,具有吸收外界光能、热能,并将其转化为远红外光的作用,对人体产生光化学作用、光热作用和光电离作用,促使皮下深层的温度上升,并使微血管扩张,促进血液循环,清除淤血等妨碍新陈代谢的障碍;砭石产生的远红外线可以促进血液微循环,具有安神、调理气血、疏通经络的作用,通过微晶红外、脉冲达到一些治疗和保健功能;氧化锌有良好的生物相容性和较高的生物活性,能够起到一定的杀菌抑菌效果,但是难以满足要求,与玉石、砭石和二氧化硅配合使用后,能够起到协同作用,提高了对于金黄色葡萄球菌、大肠杆菌和白色念珠菌等细菌的杀菌抑菌效果,同时提高了生物光素的消臭效果。实施例的结果显示,本发明提供的生物光素加入到纺织品中时,添加量为2~5%,对于金黄色葡萄球菌的抑菌率≥99%,对于大肠杆菌的抑菌率≥70%,对于白色念珠菌的抑菌率≥99%,洗后10次消臭率≥70%,远红外辐射率≥0.85,生物光素加入到医疗止痛膏贴中时,添加量为5~20%,远红外辐射率≥0.87。
具体实施方式
本发明提供了一种生物光素,按质量份数计,包括以下组分:玉石15~35份,砭石20~40份,二氧化硅矿石20~35份和氧化锌10~25份。
按质量份数计,本发明提供的生物光素包括玉石15~35份,优选为20~25份,更优选为23份。本发明对所述玉石的种类没有特殊的限定,采用本领域技术人员熟知的市售产品即可。在本发明中,所述玉石具有高强度的电子,电子衍射能释放出足以影响人体的生物电,可以刺激内分泌,调节新陈代谢;同时宝玉石具有特殊的光电效应,在切削,研磨和抛光过程中形成一个电磁场,这些效应集蓄而形成一个谐振器,能与人体发生谐振,使人体各部分更加协调运转;且玉石含有锌、铜、锗、钴、镍、锰和硒等各种有益的微量元素,微量元素浸润进入人体内,可以平衡生理机能,起到保健的功效;此外,玉石能发出萤光和彩光,刺激人体穴位,起到治疗和保健的作用。
在本发明中,所述玉石的粒径优选为D50≤1μm,更优选为D50≤0.8μm;所述玉石的纯度优选为≥95wt.%,更优选为≥96wt.%,进一步优选为≥97wt.%;所述玉石的密度优选为2.4~4.2kg/L,更优选为2.6~4.0kg/L,进一步优选为3.0~3.9kg/L。本发明将玉石的参数限定在上述范围内,可以充分发挥玉石的光电效应,进一步提高生物光素的保健效果。
以玉石的质量份数为15~35份计,本发明提供的生物光素包括砭石20~40份,优选为30~40份,更优选为35份。在本发明中,所述砭石产生的远红外线可以促进血液微循环,具有安神、调理气血、疏通经络的作用,通过微晶红外、脉冲达到一些治疗和保健功能。
在本发明中,所述砭石的粒径优选为D50≤1μm,更优选为D50≤0.8μm;所述砭石的纯度优选为≥95wt.%,更优选为≥96wt.%,进一步优选为≥97wt.%;所述砭石的密度优选为2.5~2.9kg/L,更优选为2.6~2.85kg/L,进一步优选为2.8kg/L。本发明将砭石的参数限定在上述范围内,可以进一步提高砭石的功效。
以玉石的质量份数为15~35份计,本发明提供的生物光素包括二氧化硅矿石20~35份,优选为25~30份,更优选为28份。在本发明中,所述二氧化硅矿石为远红外材料,具有放射性、共振吸收性和渗透性,可以吸收外界光能、热能,并将其转化为远红外光,对人体产生光化学作用、光热作用和光电离作用,红外线能够深入皮肤和皮下组织,引发原子和分子的振动,再通过共鸣吸收,形成热反应,促使皮下深层的温度上升,并使微血管扩张,促进血液循环,清楚淤血等妨碍新陈代谢的障碍,使组织焕发活力,促进酵素生成,经过新陈代谢后将原本滞留在体内的老旧物和有害的蓄积物等,由汗腺排出体外;同时,二氧化硅还具有综合生物学效应,即电磁波效应、微量元素效应、热效应和酶效应,可以改善人体微循环。
在本发明中,所述二氧化硅矿石的粒径优选为D50≤1μm,更优选为D50≤0.8μm;所述二氧化硅矿石的纯度优选为≥95wt.%,更优选为≥96wt.%,进一步优选为≥97wt.%;所述二氧化硅矿石的密度优选为2.5~2.9kg/L,更优选为2.6~2.8kg/L,进一步优选为2.65kg/L。本发明将二氧化硅矿石的参数限定在上述范围内,可以进一步提高二氧化硅矿石的远红外辐射效率。
以玉石的质量份数为15~35份计,本发明提供的生物光素包括氧化锌10~25份,优选为15~20份,更优选为18份。在本发明中,所述氧化锌具有良好的生物相容性和较高的生物活性,对金黄色葡萄球菌的抑菌率为80%,对大肠杆菌的抑菌率为70%,对白色念珠菌的抑菌率为60%,消臭率为65%,与玉石、砭石和二氧化硅配合使用后,能够起到协同作用,大幅度提高了对于金黄色葡萄球菌、大肠杆菌和白色念珠菌等细菌的杀菌抑菌效果,同时提高了生物光素的消臭效果。
在本发明中,所述氧化锌的粒径优选为D50≤1μm,更优选为D50≤0.8μm本发明将氧化锌的参数限定在上述范围内,可以进一步提高氧化锌杀菌抑菌效果和除臭效率。
本发明提供的生物光素具有抗菌、美容、调节生理机能和促进微循环等多种保健功能。
本发明还提供了上述技术方案所述生物光素的制备方法,包括以下步骤:
(1)分别将玉石、砭石和二氧化硅矿石依次进行粉碎、湿法球磨和超细粉碎,得到超细玉石、超细砭石和超细二氧化硅矿石;
(2)将氧化锌和部分所述步骤(1)得到的超细玉石混合进行超细粉碎,得到超细混合料;
(3)将所述步骤(1)得到的超细砭石、超细二氧化硅矿石和剩余的超细玉石与所述步骤(2)得到的超细混合料混合,得到生物光素。
本发明分别将玉石、砭石和二氧化硅矿石依次进行粉碎、湿法球磨和超细粉碎,得到超细玉石、超细砭石和超细二氧化硅矿石。
粉碎前,本发明优选分别对玉石、砭石和二氧化硅矿石进行选矿。本发明通过对玉石、砭石和二氧化硅矿石进行选矿,能够去除原料中的杂质,使玉石、砭石和二氧化硅矿石的纯度≥95wt.%,进一步提高生物光素的效果。
在本发明中,所述粉碎优选在雷蒙磨中进行。在本发明中,所述粉碎的产物的粒度优选为≥300目。本发明对所述雷蒙磨的具体型号没有特殊的限定,采用本领域技术人员熟知的市售产品即可。本发明通过对原料进行粉碎处理,可以初步降低原料的粒径,便于后续的进一步加工。
在本发明中,所述湿法球磨优选在球磨机中进行。在本发明中,所述湿法球磨的产物的粒径优选为D50≤1μm。本发明对所述球磨机的具体型号没有特殊的限定,采用本领域技术人员熟知的市售产品即可。本发明采用湿法球磨处理物料,能够进一步降低原料的粒径。
湿法球磨结束后,本发明优选对湿法球磨的产物进行干燥处理。本发明对所述干燥的方式没有特殊的限定,能够使物料干燥即可。
在本发明中,所述超细粉碎优选在气流粉碎机中进行。本发明对所述气流粉碎机的具体型号没有特殊的限定,采用本领域技术人员熟知的市售产品即可。本发明通过采用超细粉碎的方式,可以使球磨后的产物彻底分散。
得到超细玉石、超细砭石和超细二氧化硅矿石后,本发明将氧化锌和部分超细玉石混合进行超细粉碎,得到超细混合料。
在本发明中,所述氧化锌和部分超细玉石的质量比优选为5:(1~2),更优选为5:1。本发明通过将氧化锌和超细玉石混合后进行粉碎,可以克服由于氧化锌的团聚性和粘性所带来的分散性差,无法单独加工的问题,提高了氧化锌的分散性。
在本发明中,所述超细混合料的粒径优选为D50≤1μm,更优选为D50≤0.8μm。在本发明中,所述超细粉碎优选在气流粉碎机中进行。本发明对所述气流粉碎机的具体型号没有特殊的限定,采用本领域技术人员熟知的市售产品即可。本发明通过采用超细粉碎的方式,可以使氧化锌的粒径满足使用要求。
得到超细混合料后,本发明将所述超细砭石、超细二氧化硅矿石和剩余的超细玉石与所述超细混合料混合,得到生物光素。
在本发明中,所述混合优选在气流粉碎机中进行。本发明对所述气流粉碎机的具体型号没有特殊的限定,采用本领域技术人员熟知的市售产品即可。本发明通过采用超细粉碎的方式进行,有利于各组分混合均匀。
本发明提供的制备方法简单,采用现有的设备即可完成,同时可以克服氧化锌分散性差的问题,有利于进一步提高生物光素的医疗保健效果。
本发明提供了上述技术方案所述生物光素或上述技术方案所述制备方法制备的生物光素在医用膏贴和纺织品中的应用。
在本发明中,所述生物光素应用于医用膏贴时,所述生物光素在医用膏贴中的质量百分含量优选为5~20%,更优选为10~15%。本发明将生物光素的用量限定在上述范围内,可以保证医用膏贴具有良好的杀菌抑菌效果,同时远红外辐射率高。
在本发明中,所述生物光素应用于纺织品时,所述生物光素在纺织品中的质量百分含量优选为2~5%,更优选为3~4%。在本发明中,所述纺织品优选包括袜子、内衣和床上用品。本发明将生物光素的用量限定在上述范围内,既可以避免生物光素用量过多,对纺织品的力学性能产生负面影响,同时可以保证具有良好的杀菌抑菌效果和较高的除臭效果。
本发明提供的生物光素用于医用膏贴和纺织品中,具有很好的杀菌抑菌效果,较高的除臭率,同时远红外辐射率高。
下面将结合本发明中的实施例,对本发明中的技术方案进行清楚、完整地描述。显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
一种生物光素,按质量份数计,由以下组分组成:玉石20份,砭石35份,二氧化硅矿石30份和氧化锌15份;
所述生物光素的制备方法,由以下步骤组成:
(1)分别对玉石、砭石和二氧化硅矿石进行选矿,使玉石、砭石和二氧化硅矿石的纯度≥95wt.%,然后分别将玉石、砭石和二氧化硅矿石放入雷蒙磨中粉碎至粒度≥300目,在放入到球磨机中进行湿法球磨至粒径D50≤1μm,干燥后放入气流粉碎机中进行超细粉碎,得到超细玉石、超细砭石和超细二氧化硅矿石;
(2)将氧化锌和部分所述步骤(1)得到的超细玉石混合进行超细粉碎,得到粒径D50≤1μm的超细混合料;所述氧化锌和部分超细玉石的质量比为5:1;
(3)将所述步骤(1)得到的超细砭石、超细二氧化硅矿石和剩余的超细玉石与所述步骤(2)得到的超细混合料混合,得到生物光素。
实施例2
一种生物光素,按质量份数计,由以下组分组成:玉石30份,砭石25份,二氧化硅矿石20份和氧化锌25份;制备方法与实施例1相同。
实施例3
一种生物光素,按质量份数计,由以下组分组成:玉石35份,砭石20份,二氧化硅矿石35份和氧化锌10份;制备方法与实施例1相同。
应用例1
添加了实施例2制备的生物光素的氨纶面料,氨纶面料中生物光素的质量百分含量为3%。
应用例2
将应用例1中的氨纶面料洗涤10次之后。
应用例3
将应用例1中的氨纶面料洗涤50次之后。
应用例4
将实施例3制备的生物光素添加到医用药膏中,医用药膏中生物光素的质量百分含量为10%。
对比例1
未添加生物光素的氨纶面料。
对应用例1~2和对比例1提供的氨纶面料的氨气去除性能进行测试,采用SEK标志纤维产品认证标准规定的方法测试氨气去除性能评价试验,其结果如表1所示:
表1对应用例1~2和对比例1提供的氨纶面料的氨气去除性能
初始浓度/ppm | 2h后的浓度/ppm | 减少率% | |
应用例1 | 100 | 14 | 83 |
应用例2 | 100 | 22 | 73 |
对比例1 | 100 | 82 | -- |
表1中的减少了计算公式为:
减少率=(2h后的空白浓度-2h后的浓度)/2h后的浓度;
其中,2h后的空白浓度为对比例1中2h后的浓度,2h后的浓度为应用例中2h后的浓度。
对应用例3提供的氨纶面料的抗菌抑菌性能进行测试,其结果如表2所示:
表2应用例3提供的氨纶面料的抗菌抑菌性能测试结果
细菌种类 | 单位 | 技术要求AAA | 检测结果 | 单项判定 |
金黄色葡萄球菌(ATCC6538) | % | ≥80 | >99 | 合格 |
大肠杆菌(ATCC25922) | % | ≥70 | 70 | 合格 |
白色念珠菌(ATCC10231) | % | ≥60 | 99 | 合格 |
由表1可以看出,添加了本发明提供的生物光素后的氨纶面料对于氨气的去除率高达83%,即使经过10次的洗涤之后,对于氨气的去除率依然能够达到73%,远远超过为添加生物光素的氨纶面料的去除效果,说明本发明提供的生物光素具有很好的除臭效果。
由表2可以看出,添加了本发明提供的生物光素后的氨纶面料对于金黄色葡萄球菌、大肠杆菌和白色念珠菌都具有很好的抑制效果,即使洗涤50次,依然能够大幅度超过技术要求,说明本发明提供的生物光素具有很好的杀菌抑菌效果,同时说明了氧化锌与玉石、砭石和二氧化硅配合使用后,能够起到协同作用,提高对金黄色葡萄球菌、大肠杆菌和白色念珠菌等细菌的杀菌抑菌效果,同时提高其消臭效果。
对应用例1提供的氨纶面料的远红外辐射率进行测试,经过检测,氨纶面料的远红外辐射率≥0.85,说明本发明提供的生物光素具有较高的远红外辐射率,加入到纺织物中能够大幅度提高纺织物的远红外辐射率。
对应用例4提供的医用药膏的远红外辐射率进行测试,经过检测,医用药膏的远红外辐射率≥0.87,说明本发明提供的生物光素具有较高的远红外辐射率,加入到医用药膏中能够大幅度提高纺织物的远红外辐射率。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种生物光素,按质量份数计,包括以下组分:玉石15~35份,砭石20~40份,二氧化硅矿石20~35份和氧化锌10~25份。
2.根据权利要求1所述的生物光素,其特征在于,按质量份数计,包括以下组分:玉石20~25份,砭石30~40份,二氧化硅矿石25~30份和氧化锌10~25份。
3.根据权利要求1或2所述的生物光素,其特征在于,所述玉石、砭石、二氧化硅矿石和氧化锌的粒径独立地为D50≤1μm。
4.根据权利要求1或2所述的生物光素,其特征在于,所述玉石、砭石和二氧化硅矿石的纯度≥95wt.%。
5.根据权利要求1或2所述的生物光素,其特征在于,所述玉石的密度为2.4~4.2kg/L。
6.根据权利要求1或2所述的生物光素,其特征在于,所述砭石的密度为2.6~2.9kg/L。
7.根据权利要求1或2所述的生物光素,其特征在于,所述二氧化硅矿石的密度为2.5~2.9kg/L。
8.权利要求1~7任意一项所述生物光素的制备方法,包括以下步骤:
(1)分别将玉石、砭石和二氧化硅矿石依次进行粉碎、湿法球磨和超细粉碎,得到超细玉石、超细砭石和超细二氧化硅矿石;
(2)将氧化锌和部分所述步骤(1)得到的超细玉石混合进行超细粉碎,得到超细混合料;
(3)将所述步骤(1)得到的超细砭石、超细二氧化硅矿石和剩余的超细玉石与所述步骤(2)得到的超细混合料混合,得到生物光素。
9.根据权利要求8所述的制备方法,其特征在于,所述步骤(2)中氧化锌和部分超细玉石的质量比为5:(1~2)。
10.权利要求1~8任意一项所述生物光素或权利要求9所述制备方法制备的生物光素在医用膏贴和纺织品中的应用。