CN113831566A - 一种防雾抗菌pet片材 - Google Patents
一种防雾抗菌pet片材 Download PDFInfo
- Publication number
- CN113831566A CN113831566A CN202111241255.3A CN202111241255A CN113831566A CN 113831566 A CN113831566 A CN 113831566A CN 202111241255 A CN202111241255 A CN 202111241255A CN 113831566 A CN113831566 A CN 113831566A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- agent
- master batch
- surfactant
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防雾抗菌PET片材，由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；本发明的有益效果是：纳米二氧化钛可以杀死细菌，分解甲醛，分解乙醛，分解乙烯，通过材料的改性、复配，进行组合，防雾，杀菌，分解乙烯，抑制呼吸，把这五个功能整合在一起，形成新型保鲜技术，新型功能包装材料；包装材料和保鲜技术一体化，这种材料应用的非常方便，解决了产品的简单快捷低成本的保鲜方法，可以解决农产品产地保鲜能力不足的缺点，解决过去解决不了的问题。
Description
技术领域
本发明属于膜技术领域，具体涉及一种防雾抗菌PET片材。
背景技术
传统的抽真空来阻隔空气；市面上的薄膜是组合型的薄膜，通过这种方式来阻隔空气，包装的同时、起到阻隔作用，来延长食品的保质期。蔬菜水果储运销售过程中会挥发出大量的水汽，凝结至包装物内表面，形成水汽，再流向蔬果导致蔬果加速腐烂，增加细菌滋生，导致水分大量流失，腐烂变质。
为了解决农产品产地保鲜能力不足的缺点，防雾，杀菌、分解乙烯，抑制呼吸，为此我们提出一种防雾抗菌PET片材。
发明内容
本发明的目的在于提供一种防雾抗菌PET片材，解决农产品产地保鲜能力不足的缺点，防雾，杀菌、分解乙烯，抑制呼吸。
为实现上述目的，本发明提供如下技术方案：一种防雾抗菌PET片材，由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％。
作为本发明的一种优选的技术方案，所述防雾表面活性剂由FS1330表面活性剂、聚甘油酯、聚氧乙烯醚组成。
作为本发明的一种优选的技术方案，所述润滑剂为硅酮粉、硅酮母粒中的一种。
作为本发明的一种优选的技术方案，所述脱模剂为聚四氟乙烯、氟化乙烯丙烯共聚物中的一种。
作为本发明的一种优选的技术方案，所述增韧剂为聚乙烯醇缩丁醛、聚醋酸乙烯中的一种。
作为本发明的一种优选的技术方案，所述抗静电剂为聚醚酯酰胺、聚醚酯乙酰胺、聚氧化乙烯中的一种。
作为本发明的一种优选的技术方案，所述抗菌母粒为纳米二氧化钛光触酶抗菌母粒。
作为本发明的一种优选的技术方案，所述抗菌PET片材的制备方法如下：
步骤一：材料准备：材料包括PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；
步骤二：干燥：将步骤一的材料置于干燥箱中进行干燥；
步骤三：拌合：干燥后的材料置于拌合机中，并进行拌合；
步骤四：加热挤出：拌合后的混合料进行加热至230-250℃，并挤出；
步骤五：拉片：挤出后进行拉片；
步骤六：卷取：拉片后的材料通过卷取机进行卷取；
步骤七：包装、入库：合格品进行包装、并入库。
与现有技术相比，本发明的有益效果是：
(1)纳米二氧化钛可以杀死细菌，分解甲醛，分解乙醛，分解乙烯，通过材料的改性、复配，进行组合，防雾，杀菌，分解乙烯，抑制呼吸，把这五个功能整合在一起，形成新型保鲜技术，新型功能包装材料；
(2)包装材料和保鲜技术一体化，这种材料应用的非常方便，解决了产品的简单快捷低成本的保鲜方法，可以解决农产品产地保鲜能力不足的缺点，解决过去解决不了的问题。
附图说明
图1为本发明的PET片材的制备方法流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
请参阅图1，本发明提供一种技术方案：一种防雾抗菌PET片材，由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％。
本实施例中，优选的，防雾表面活性剂由FS1330表面活性剂、聚甘油酯、聚氧乙烯醚组成；FS1330具有耐高温性能，能在300℃的环境下保持稳定，不挥发；FS1330是一款阴离子型氟碳表面活性剂，具有极强的提高表面张力能力、同时具有优良的化学稳定性和热稳定性，可应用于涂料油墨、聚合乳液、塑料/橡胶加工、清洁剂领域；本产品无毒害，于阴凉通风处保存，本产品若长期存放可能出现分层的现象，使用前混合均匀即可，不会影响本产品的性能；表面活性剂的特点一端亲油，另一端亲水，亲油的会跟塑料分子结合在一起，亲水的会迁移到表面上来吸收薄膜的水分，同时来提高薄膜表面的张力；当吸收到包装袋内水果蔬菜呼吸的水分之后会在薄膜内表面形成一个薄膜的水膜，这个水膜借助表面张力的提升就有很好的发散作用，蔬菜水果在呼吸出来的水分到袋子上就不会在凝结成水雾了；使得蔬菜水果表面干燥，减少微生物滋生；密封保持，正常含水量水分不流失，保鲜、保值、保重量。
本实施例中，优选的，润滑剂为硅酮粉；硅酮粉具有良好的热稳定性和耐迁移性，可用于高加工温度的工程塑料，如PPS、PPA；产品具有润滑性、脱模性和流动性，降低螺杆扭矩，降低能耗；充模容易，降低制品不良率；明显降低制品表面的摩擦系数，提高爽滑性，增进表面丝质触感，提高产品的耐刮伤性；提高增强或填充体系制品的表面光泽度；提高阻燃性，降低烟密度。
本实施例中，优选的，脱模剂为聚四氟乙烯；脱模剂的使用可以让成型部件快速轻易脱落，减少制造周期，因而有助于降低生产成本，提高效益。
本实施例中，优选的，增韧剂为聚乙烯醇缩丁醛；增韧剂是具有降低复合材料脆性和提高复合材料抗冲击性能的一类助剂，可分为活性增韧剂与非活性增韧剂两类，活性增韧剂是指其分子链上含有能与基体树脂反应的活性基团，它能形成网络结构，增加一部分柔性链，从而提高复合材料的抗冲击性能，非活性增韧剂则是一类与基体树脂很好相溶、但不参与化学反应的增韧剂。
本实施例中，优选的，抗静电剂为聚醚酯酰胺。
本实施例中，优选的，抗菌母粒为纳米二氧化钛光触酶抗菌母粒，纳米二氧化钛另一个名称光触酶抗菌剂，当有微弱光照的情况下纳米二氧化钛就会产生出电子和空穴，电子和空穴遇到氧气和水，就会产生羟基自由基和超氧化离子，它们能够有效杀死细菌，固化细菌的蛋白质，把细菌的细胞分解变成二氧化碳和水；纳米二氧化钛可以分解甲醛，分解乙醛，分解乙烯。
本实施例中，优选的，抗菌PET片材的制备方法如下：
步骤一：材料准备：材料包括PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；
步骤二：干燥：将步骤一的材料置于干燥箱中进行干燥；
步骤三：拌合：干燥后的材料置于拌合机中，并进行拌合；
步骤四：加热挤出：拌合后的混合料进行加热至230℃，并挤出；
步骤五：拉片：挤出后进行拉片；
步骤六：卷取：拉片后的材料通过卷取机进行卷取；
步骤七：包装、入库：合格品进行包装、并入库。
实施例2
请参阅图1，本发明提供一种技术方案：一种防雾抗菌PET片材，由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％。
本实施例中，优选的，防雾表面活性剂由FS1330表面活性剂、聚甘油酯、聚氧乙烯醚组成；FS1330具有耐高温性能，能在300℃的环境下保持稳定，不挥发；FS1330是一款阴离子型氟碳表面活性剂，具有极强的提高表面张力能力、同时具有优良的化学稳定性和热稳定性，可应用于涂料油墨、聚合乳液、塑料/橡胶加工、清洁剂领域；本产品无毒害，于阴凉通风处保存，本产品若长期存放可能出现分层的现象，使用前混合均匀即可，不会影响本产品的性能；表面活性剂的特点一端亲油，另一端亲水，亲油的会跟塑料分子结合在一起，亲水的会迁移到表面上来吸收薄膜的水分，同时来提高薄膜表面的张力；当吸收到包装袋内水果蔬菜呼吸的水分之后会在薄膜内表面形成一个薄膜的水膜，这个水膜借助表面张力的提升就有很好的发散作用，蔬菜水果在呼吸出来的水分到袋子上就不会在凝结成水雾了；使得蔬菜水果表面干燥，减少微生物滋生；密封保持，正常含水量水分不流失，保鲜、保值、保重量。
本实施例中，优选的，润滑剂为硅酮母粒；硅酮母粒产品润滑性、脱模性和流动性好，降低螺杆扭矩，降低能耗，充模容易，减少成型周期期；降低制品不良率，降低成本；明显降低制品表面的摩擦系数，提高爽滑性，增进表面丝质触感，提高产品的耐刮伤性；良好的稳定性和耐迁移性，无表面喷霜，对后处理操作(如喷涂、印刷)无影响。
本实施例中，优选的，脱模剂为氟化乙烯丙烯共聚物；脱模剂的使用可以让成型部件快速轻易脱落，减少制造周期，因而有助于降低生产成本，提高效益。
本实施例中，优选的，增韧剂为聚醋酸乙烯；增韧剂是具有降低复合材料脆性和提高复合材料抗冲击性能的一类助剂，可分为活性增韧剂与非活性增韧剂两类，活性增韧剂是指其分子链上含有能与基体树脂反应的活性基团，它能形成网络结构，增加一部分柔性链，从而提高复合材料的抗冲击性能，非活性增韧剂则是一类与基体树脂很好相溶、但不参与化学反应的增韧剂。
本实施例中，优选的，抗静电剂为聚醚酯乙酰胺。
本实施例中，优选的，抗菌母粒为光触酶抗菌剂，纳米二氧化钛另一个名称光触酶抗菌剂，当有微弱光照的情况下纳米二氧化钛就会产生出电子和空穴，电子和空穴遇到氧气和水，就会产生羟基自由基和超氧化离子，它们能够有效杀死细菌，固化细菌的蛋白质，把细菌的细胞分解变成二氧化碳和水；纳米二氧化钛可以分解甲醛，分解乙醛，分解乙烯。
本实施例中，优选的，抗菌PET片材的制备方法如下：
步骤一：材料准备：材料包括PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；
步骤二：干燥：将步骤一的材料置于干燥箱中进行干燥；
步骤三：拌合：干燥后的材料置于拌合机中，并进行拌合；
步骤四：加热挤出：拌合后的混合料进行加热至240℃，并挤出；
步骤五：拉片：挤出后进行拉片；
步骤六：卷取：拉片后的材料通过卷取机进行卷取；
步骤七：包装、入库：合格品进行包装、并入库。
实施例3
请参阅图1，本发明提供一种技术方案：一种防雾抗菌PET片材，由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％。
本实施例中，优选的，防雾表面活性剂由FS1330表面活性剂、聚甘油酯、聚氧乙烯醚组成；FS1330具有耐高温性能，能在300℃的环境下保持稳定，不挥发；FS1330是一款阴离子型氟碳表面活性剂，具有极强的提高表面张力能力、同时具有优良的化学稳定性和热稳定性，可应用于涂料油墨、聚合乳液、塑料/橡胶加工、清洁剂领域；本产品无毒害，于阴凉通风处保存，本产品若长期存放可能出现分层的现象，使用前混合均匀即可，不会影响本产品的性能；表面活性剂的特点一端亲油，另一端亲水，亲油的会跟塑料分子结合在一起，亲水的会迁移到表面上来吸收薄膜的水分，同时来提高薄膜表面的张力；当吸收到包装袋内水果蔬菜呼吸的水分之后会在薄膜内表面形成一个薄膜的水膜，这个水膜借助表面张力的提升就有很好的发散作用，蔬菜水果在呼吸出来的水分到袋子上就不会在凝结成水雾了；使得蔬菜水果表面干燥，减少微生物滋生；密封保持，正常含水量水分不流失，保鲜、保值、保重量。
本实施例中，优选的，润滑剂为硅酮粉；硅酮粉主要成分为高分子量聚硅氧烷，用做热塑性材料的加工助剂和表面改性剂，提高产品的加工流动性和光泽度，降低摩擦系数，改善手感；硅酮粉具有良好的热稳定性和耐迁移性，可用于高加工温度的工程塑料，如PPS、PPA；产品具有润滑性、脱模性和流动性，降低螺杆扭矩，降低能耗；充模容易，降低制品不良率；明显降低制品表面的摩擦系数，提高爽滑性，增进表面丝质触感，提高产品的耐刮伤性；提高增强或填充体系制品的表面光泽度；提高阻燃性，降低烟密度。
本实施例中，优选的，脱模剂为聚四氟乙烯；脱模剂的使用可以让成型部件快速轻易脱落，减少制造周期，因而有助于降低生产成本，提高效益。
本实施例中，优选的，增韧剂为聚乙烯醇缩丁醛；增韧剂是具有降低复合材料脆性和提高复合材料抗冲击性能的一类助剂，可分为活性增韧剂与非活性增韧剂两类，活性增韧剂是指其分子链上含有能与基体树脂反应的活性基团，它能形成网络结构，增加一部分柔性链，从而提高复合材料的抗冲击性能，非活性增韧剂则是一类与基体树脂很好相溶、但不参与化学反应的增韧剂。
本实施例中，优选的，抗静电剂为聚氧化乙烯。
本实施例中，优选的，抗菌母粒为光触酶抗菌剂，纳米二氧化钛另一个名称光触酶抗菌剂，当有微弱光照的情况下纳米二氧化钛就会产生出电子和空穴，电子和空穴遇到氧气和水，就会产生羟基自由基和超氧化离子，它们能够有效杀死细菌，固化细菌的蛋白质，把细菌的细胞分解变成二氧化碳和水；纳米二氧化钛可以分解甲醛，分解乙醛，分解乙烯。
本实施例中，优选的，抗菌PET片材的制备方法如下：
步骤一：材料准备：材料包括PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；
步骤二：干燥：将步骤一的材料置于干燥箱中进行干燥；
步骤三：拌合：干燥后的材料置于拌合机中，并进行拌合；
步骤四：加热挤出：拌合后的混合料进行加热至250℃，并挤出；
步骤五：拉片：挤出后进行拉片；
步骤六：卷取：拉片后的材料通过卷取机进行卷取；
步骤七：包装、入库：合格品进行包装、并入库。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种防雾抗菌PET片材，其特征在于：由PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒组成，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％。
2.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述防雾表面活性剂由FS1330表面活性剂、聚甘油酯、聚氧乙烯醚组成。
3.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述润滑剂为硅酮粉、硅酮母粒中的一种。
4.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述脱模剂为聚四氟乙烯、氟化乙烯丙烯共聚物中的一种。
5.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述增韧剂为聚乙烯醇缩丁醛、聚醋酸乙烯中的一种。
6.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述抗静电剂为聚醚酯酰胺、聚醚酯乙酰胺、聚氧化乙烯中的一种。
7.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述抗菌母粒为纳米二氧化钛光触酶抗菌母粒。
8.根据权利要求1所述的一种防雾抗菌PET片材，其特征在于：所述抗菌PET片材的制备方法如下：
步骤一：材料准备：材料包括PET树脂、防雾表面活性剂、润滑剂、脱模剂、增韧剂、抗静电剂、抗菌母粒，其组分按百分比计为：PET树脂85％、防雾表面活性剂5％、润滑剂1％、脱模剂1％、增韧剂3％、抗静电剂3％、抗菌母粒5％；
步骤二：干燥：将步骤一的材料置于干燥箱中进行干燥；
步骤三：拌合：干燥后的材料置于拌合机中，并进行拌合；
步骤四：加热挤出：拌合后的混合料进行加热至230-250℃，并挤出；
步骤五：拉片：挤出后进行拉片；
步骤六：卷取：拉片后的材料通过卷取机进行卷取；
步骤七：包装、入库：合格品进行包装、并入库。