CN113667550A - 一种pet塑胶板清洗剂及其制备方法和使用方法 - Google Patents
一种pet塑胶板清洗剂及其制备方法和使用方法 Download PDFInfo
- Publication number
- CN113667550A CN113667550A CN202111109412.5A CN202111109412A CN113667550A CN 113667550 A CN113667550 A CN 113667550A CN 202111109412 A CN202111109412 A CN 202111109412A CN 113667550 A CN113667550 A CN 113667550A
- Authority
- CN
- China
- Prior art keywords
- pet plastic
- cleaning agent
- plastic board
- percent
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及工业清洗剂的技术领域，更具体地说，它涉及一种PET塑胶板清洗剂及其制备方法和使用方法。PET塑胶板清洗剂包括窄分子量分布古伯特醇聚氧乙烯醚（5EO）、氢氧化钠、柠檬酸、异辛酸、草酸、十二烷基二甲基氯化铵、醇类物质和去离子水。通过先将去离子水、氢氧化钾、柠檬酸、草酸和异辛酸进行搅拌混合，然后依次加入窄分子量分布古伯特醇聚氧乙烯醚（5EO）、十二烷基二甲基氯化铵和醇类物质，再进行搅拌混合的方法得到PET塑胶板清洗剂。使用本发明的PET塑胶板清洗剂不仅不易对产品的品质造成影响，而且提高了安全环保性能。
Description
技术领域
本发明涉及工业清洗剂的技术领域，更具体地说，它涉及一种PET塑胶板清洗剂及其制备方法和使用方法。
背景技术
工业清洗在表面处理中占有着重要的地位，是表面处理中的不可缺少的前后处理工序。合适的工业清洗剂具有优秀的清洁性、不伤基材、易漂洗和高效环保，可以提高生产产能，保证产品质量，降低生产成本。近几年来，由于手机表面处理技术的不断提高，先进表面着色的不断涌现，工艺和工件材料的发展，推动了工业清洗技术的发展。随着PET材料在高端汽车、电子元器件、3C领域的加大投入和人们环保意识的加强，对清洗剂提出了新的要求。
目前，大多数的清洗剂仍以磷酸盐为主，但是，磷酸盐具有高污染性，造成了环境污染、地面水体恶化，威胁着人类健康，同时，采用pH值较高的清洗剂也容易对PET基材及基材着色后的表面造成异色，因此，开发一种环保且不易损害产品品质的PET塑胶板清洗剂是十分有必要的。
发明内容
本发明提供一种PET塑胶板清洗剂及其制备方法和使用方法，不易对产品的品质造成影响的同时，具有安全、环保的优点。
第一方面，本发明提供一种PET塑胶板清洗剂，采用如下的技术方案：一种PET塑胶板清洗剂，包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚(5EO)4％-6％；
氢氧化钠3％-5％；
柠檬酸4％-5％；
异辛酸2％-3％；
草酸2％-3％；
十二烷基二甲基氯化铵2％-3％；
醇类物质3％-5％；
去离子水余量。
本发明的配方中，氢氧化钠为滨化公司生产的99％含量的片碱，其在配方体系中作为碱储备和有机酸中和，柠檬酸与氢氧化钠中和能产生螯合剂，同时能作为体系的缓冲溶液，易于稳定控制体系的pH值。异辛酸和窄分子量分布古伯特醇聚氧乙烯醚(5EO)均为99％含量工业品，十二烷基二甲基氯化铵为50％含量工业品。草酸为工业级草酸，去离子水为RO反渗透过滤膜生产。
本发明通过利用柠檬酸、异辛酸和草酸与氢氧化钠作用得到螯合剂，无需添加传统的螯合剂，采用高品质窄分子量分布古伯特醇聚氧乙烯醚(5EO)的高浊点稳定性和乳化性与螯合剂的钙皂分散能力和耐电解质性能起到协同作用，可以降低在脏污在PET塑胶板的吸附力，不易对产品的品质造成影响的同时，具有安全、环保的优点。
优选的，所述醇类物质包括重量百分比含量为(70-100)％的异己二醇和余量的丁醇。
优选的，所述醇类物质包括重量百分比含量为98％的异己二醇和2％的丁醇。
异己二醇能极好地润湿硬表面，提高乳化剂的去污能力。丁醇是润湿剂，增溶异己二醇并协同异己二醇在清洗过程地润湿作用。
优选的，所述PET塑胶板清洗剂包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚(5EO)4％-5％；
氢氧化钠3％-4％；
柠檬酸4％-4.5％；
异辛酸2％-3％；
草酸2％-2.5％；
十二烷基二甲基氯化铵2％-3％；
醇类物质3％-4％；
去离子水余量。
优选的，所述PET塑胶板清洗剂包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚(5EO)4％；
氢氧化钠3.7％；
柠檬酸4.5％；
异辛酸2.6％；
草酸2.1％；
十二烷基二甲基氯化铵2.7％；
醇类物质4％；
去离子水余量。
优选的，所述柠檬酸为食用级一水柠檬酸。
第二方面，本申请提供一种PET塑胶板清洗剂的制备方法，采用如下的技术方案：
一种PET塑胶板清洗剂的制备方法，包括以下步骤：
步骤A：按重量百分含量计，依次向去离子水中加入氢氧化钾、柠檬酸、草酸和异辛酸，调节反应温度为40～50℃，搅拌混合；
步骤B：在35～40℃下，向步骤A得到的混合物中依次加入窄分子量分布古伯特醇聚氧乙烯醚(5EO)、十二烷基二甲基氯化铵和醇类物质，搅拌混合，得到PET塑胶板清洗剂。
优选的，所述步骤A中，调节pH值为8.0-8.5，搅拌时间为30分钟，搅拌速度为100～200rpm。
优选的，所述步骤B中，搅拌时间为30分钟，搅拌速度为100～200rpm。
第三方面，本申请提供一种PET塑胶板清洗剂的使用方法，采用如下的技术方案：
一种PET塑胶板清洗剂的使用方法，包括以下步骤：在温度为45℃下，将待清洗件浸泡在由权利要求7-9任一项制备得到的PET塑胶板清洗剂中，进行超声波清洗60-120s，超声波频率为20Khz。
利用本发明制备得到的PET塑胶板清洗剂上述的使用方法完成对PET塑胶板表面脏污的清洗，清洗过程无异味，不含磷，无VOC产生，提高生产环境质量。
综上所述，本发明包括以下至少一种有益技术效果：
1.本发明的配方为非传统除油粉除油剂体系，不添加传统含磷螯合剂，废水易处理，COD的产生量低。
2.通过自行配制螯合剂，稳定控制PH值，添加窄分子量分布古伯特醇聚氧乙烯醚(5EO)和十二烷基二甲基氯化铵还有混合醇产生了协同作用，在对PET塑胶板清洗过程中可以高效清洁表面脏污，不对PET塑胶板表面产生异色漂洗后无清洗剂残留，清洗后良率达到99％。
具体实施方式
以下结合实施例对本发明作进一步详细说明。
实施例1
一种PET塑胶板清洗剂，由以下重量百分比含量的组分组成：
窄分子量分布古伯特醇聚氧乙烯醚(5EO)4.6％；
氢氧化钠3.5％；
柠檬酸4.5％；
异辛酸2.2％；
草酸2.3％；
十二烷基二甲基氯化铵2.3％；
醇类物质3.5％；
去离子水余量。
其中，醇类物质由98％的异己二醇和2％的丁醇组成。柠檬酸为一水柠檬酸。
上述PET塑胶板清洗剂的制备方法如下：
步骤A：按重量百分比含量计，依次向去离子水中加入氢氧化钾、柠檬酸、草酸和异辛酸，调节反应温度为40～50℃，调节pH值为8.0-8.5，进行搅拌混合，搅拌时间为30分钟，搅拌速度为100～200rpm。
步骤B：在35～40℃下，向步骤A得到的混合物中依次加入窄分子量分布古伯特醇聚氧乙烯醚(5EO)、十二烷基二甲基氯化铵和醇类物质，搅拌混合，搅拌时间为30分钟，搅拌速度为100～200rpm，得到PET塑胶板清洗剂。
上述PET塑胶板清洗剂的使用方法如下：在温度为45℃下，将待清洗件浸泡在制备得到的PET塑胶板清洗剂中，进行超声波清洗60-120s，超声波频率为20Khz。
实施例2-6
一种PET塑胶板清洗剂，与实施例1的区别在于，PET塑胶板清洗剂各组分的用量不同，具体参见表1。
表1实施例1-6的各组分配比
实施例7
一种PET塑胶板清洗剂，由以下重量百分比含量的组分组成：
窄分子量分布古伯特醇聚氧乙烯醚(5EO)4.8％；
氢氧化钠3.8％；
柠檬酸4.2％；
异辛酸2.5％；
草酸2.4％；
十二烷基二甲基氯化铵2.2％；
醇类物质4.0％；
去离子水余量。
其中，醇类物质为异己二醇的单一组分。
本实施例的PET塑胶板清洗剂的制备方法和使用方法均与实施例2相同，此处不再赘述。
实施例8
一种PET塑胶板清洗剂，与实施例7的区别在于，醇类物质由50％的异己二醇和50％的丁醇组成。
实施例9
一种PET塑胶板清洗剂，与实施例3的区别在于，柠檬酸为工业级柠檬酸。
对比例1
一种PET塑胶板清洗剂，与实施例6的区别在于，采用同用量的苄基三乙基氯化铵替代十二烷基二甲基氯化铵，其余与实施例6均相同，此处不再赘述。
对比例2
一种PET塑胶板清洗剂，与实施例6的区别在于，采用窄分子量分布古伯特醇聚氧乙烯醚(2EO)替代窄分子量分布古伯特醇聚氧乙烯醚(5EO)，其余与实施例6均相同，此处不再赘述。
对比例3
一种PET塑胶板清洗剂，与实施例6的区别在于，采用异辛醇聚氧乙烯醚替代窄分子量分布古伯特醇聚氧乙烯醚(5EO)，其余与实施例6均相同，此处不再赘述。
性能检测试验
原液外观的检测：通过目测的方法观察PET塑胶板清洗剂的外观颜色状态，无出现异物和异色即为合格。具体结果见表2。
表面张力的检测：利用SITA表面张力仪对原液进行表面张力的测试，表面张力值≤30N/m即为合格。具体结果见表2。
相对密度的检测：根据GB/T 1884和GB/T 1885对实施例1-9和对比例1-3制备得到的PET塑胶板清洗剂原液进行相对密度的检测。具体结果见表2。
pH值的检测：利用pH计对原液进行pH值的测试，pH值越接近7.0对PET表面异色影响越小但是清洗去脏污能力会下降，因而8≤pH值≤8.6即为合格。具体结果见表2。
PET不异色良率的检测：将实施例1-9和对比例1-3制备得到的PET塑胶板清洗剂原液配制成质量浓度1％的稀释液，将PET塑胶板分别置于各稀释液中进行超声波浸泡清洗，清洗温度为45℃，清洗时间为2min，超声波频率为20Khz。记录PET塑胶板清洗后的不异色良率数据，具体结果见表2。
PET去脏污良率的检测：测试标准与PET不异色良率的检测标准相同，记录PET塑胶板清洗后的去脏污良率数据，具体结果见表2。
判定当PET不异色良率和PET去脏污良率越高，清洗剂清洗性能越优秀。
表2检测结果数据
根据实施例1-9和对比例1-3并结合表2，可以看出，本发明采用窄分子量分布古伯特醇聚氧乙烯醚(5EO)的高浊点稳定性和乳化性与螯合剂的钙皂分散能力和耐电解质性能的协同作用，制备得到的PET塑胶板清洗剂，配合本发明的超声波清洗方法，能提高对PET塑胶板清洗的效果，PET塑胶板的不异色度良率均能达到95％以上，PET塑胶板的去脏污良率均能达到96％以上。
对比实施例6和对比例1-3并结合表2，可以看出，本发明的PET塑胶板清洗剂配方中，窄分子量分布古伯特醇聚氧乙烯醚(5EO)、十二烷基二甲基氯化铵以及醇类物质之间具有协同作用，当取代了其中一种组分后，其制备得到的PET塑胶板清洗剂对PET塑胶板的清洗效果有显著的下降。
对比实施例1-6并结合表2，可以看出，当采用实施例3的特定配比的配方，其制备得到的PET塑胶板清洗剂在PET不异色良率的检测和PET去脏污良率的检测方面均具有较佳的表现，即清洗效果最佳。
对比实施例2、7-8并结合表2，可以看出，采用特定的配比的异己二醇和丁醇作为醇类物质，提高配方的配伍性，能促进醇类物质与配方体系其他组分的作用，进一步提高PET塑胶板清洗剂对PET塑胶板的清洗效果。
对比实施例3和实施例9并结合表2可以看出，采用特定的食用级一水柠檬酸能提高PET塑胶板清洗剂对PET塑胶板的清洗效果。
本具体实施例仅仅是对本发明的解释，其并不是对本发明的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本发明的权利要求范围内都受到专利法的保护。
Claims (10)
1.一种PET塑胶板清洗剂，其特征在于：包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚（5EO） 4%-6%；
氢氧化钠 3%-5%；
柠檬酸 4%-5%；
异辛酸 2%-3%；
草酸 2%-3%；
十二烷基二甲基氯化铵 2%-3%；
醇类物质 3%-5%；
去离子水余量。
2.根据权利要求1所述的一种PET塑胶板清洗剂，其特征在于：所述醇类物质包括重量百分比含量为（70-100）%的异己二醇和余量的丁醇。
3.根据权利要求2所述的一种PET塑胶板清洗剂，其特征在于：所述醇类物质包括重量百分比含量为98%的异己二醇和2%的丁醇。
4.根据权利要求1-3任一项所述的一种PET塑胶板清洗剂，其特征在于：包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚（5EO） 4%-5%；
氢氧化钠 3%-4%；
柠檬酸 4%-4.5%；
异辛酸 2%-3%；
草酸 2%-2.5%；
十二烷基二甲基氯化铵 2%-3%；
醇类物质 3%-4%；
去离子水余量。
5.根据权利要求4所述的一种PET塑胶板清洗剂，其特征在于：包括以下重量百分比含量的组分：
窄分子量分布古伯特醇聚氧乙烯醚（5EO） 4%；
氢氧化钠 3.7%；
柠檬酸 4.5%；
异辛酸 2.6%；
草酸 2.1%；
十二烷基二甲基氯化铵 2.7%；
醇类物质 4%；
去离子水余量。
6.根据权利要求5所述的一种PET塑胶板清洗剂，其特征在于：所述柠檬酸为食用级一水柠檬酸。
7.一种PET塑胶板清洗剂的制备方法，其特征在于：包括以下步骤：
步骤A：按重量百分含量计，依次向去离子水中加入氢氧化钾、柠檬酸、草酸和异辛酸，调节反应温度为40～50℃，搅拌混合；
步骤B：在35～40℃下，向步骤A得到的混合物中依次加入窄分子量分布古伯特醇聚氧乙烯醚（5EO）、十二烷基二甲基氯化铵和醇类物质，搅拌混合，得到PET塑胶板清洗剂。
8.根据权利要求7所述的一种PET塑胶板清洗剂的制备方法，其特征在于：所述步骤A中，调节pH值为8.0-8.5，搅拌时间为30分钟，搅拌速度为100～200rpm。
9.根据权利要求7或8所述的一种PET塑胶板清洗剂的制备方法，其特征在于：所述步骤B中，搅拌时间为30分钟，搅拌速度为100～200rpm。
10.一种PET塑胶板清洗剂的使用方法，其特征在于：包括以下步骤：在温度为45℃下，将待清洗件浸泡在由权利要求7-9任一项制备得到的PET塑胶板清洗剂中，进行超声波清洗60-120s，超声波频率为20Khz。