CN113565277A - 具有吸附并清除甲醛功能的印花墙布及其生产方法 - Google Patents
具有吸附并清除甲醛功能的印花墙布及其生产方法 Download PDFInfo
- Publication number
- CN113565277A CN113565277A CN202110759936.2A CN202110759936A CN113565277A CN 113565277 A CN113565277 A CN 113565277A CN 202110759936 A CN202110759936 A CN 202110759936A CN 113565277 A CN113565277 A CN 113565277A
- Authority
- CN
- China
- Prior art keywords
- content
- cotton
- glass fiber
- antibacterial
- alkali glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了具有吸附并清除甲醛功能的印花墙布及其生产方法,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,所述合成树脂的份额为16~23%,所述PP棉的份额为6~12%,所述碱玻璃纤维材料的份额为35~46%,所述可剥离强力粘合胶的份额为11~17%,所述活性炭棉的份额为16~26%。本发明所述的具有吸附并清除甲醛功能的印花墙布及其生产方法,使用结构更加多样化,采用活性炭棉对空气中的甲醛进行吸附与清除,具有空气净化的效果,增加使用性能,设置加强型环保复合材料,增加墙布的使用强度,不易出现破损的情况,环保性能更为优异,使用寿命更长,带来更好的使用前景。
Description
技术领域
本发明涉及印花墙布制备领域,特别涉及具有吸附并清除甲醛功能的印花墙布及其生产方法。
背景技术
印花墙布及其生产方法是一种进行印花墙布加工制作的支撑方法,在进行装修的时候,印花墙布是一种进行墙面装饰的贴合布料,直接贴合在墙面上,装饰效果更为优异,质感上比墙纸更胜一筹,随着科技的不断发展,人们对于印花墙布及其生产方法的制造工艺要求也越来越高。
现有的印花墙布及其生产方法在使用时存在一定的弊端,首先,在进行使用的时候使用结构较为单一,功能性少,不能很好的吸附与清楚空气中的甲醛,不利于人们的使用,还有,在进行使用的时候使用强度较低,环保性能较差,给人们的使用过程带来了一定的不利影响,为此,我们提出具有吸附并清除甲醛功能的印花墙布及其生产方法。
发明内容
(一)解决的技术问题
针对现有技术的不足,本发明提供了具有吸附并清除甲醛功能的印花墙布及其生产方法,使用结构更加多样化,采用活性炭棉对空气中的甲醛进行吸附与清除,具有空气净化的效果,增加使用性能,设置加强型环保复合材料,增加墙布的使用强度,不易出现破损的情况,环保性能更为优异,使用寿命更长,可以有效解决背景技术中的问题。
(二)技术方案
为实现上述目的,本发明采取的技术方案为:具有吸附并清除甲醛功能的印花墙布,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,所述合成树脂的份额为16~23%,所述PP棉的份额为6~12%,所述碱玻璃纤维材料的份额为35~46%,所述可剥离强力粘合胶的份额为11~17%,所述活性炭棉的份额为16~26%。
作为一种优选的技术方案,所述合成树脂的份额为20%,所述PP棉的份额为10%,所述碱玻璃纤维材料的份额为38%,所述可剥离强力粘合胶的份额为14%,所述活性炭棉的份额为18%。
作为一种优选的技术方案,所述合成树脂的份额为19%,所述PP棉的份额为9%,所述碱玻璃纤维材料的份额为40%,所述可剥离强力粘合胶的份额为15%,所述活性炭棉的份额为17%。
具有吸附并清除甲醛功能的印花墙布的生产方法,包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,所述碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,所述合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,所述活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,所述PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,所述加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
作为一种优选的技术方案,所述S3步骤中粘合材料的份额为18~28%,所述离子抗菌聚合物的份额为14~25%,所述复合纤维材料的份额为32~45%,所述抗菌薄膜的份额为10~20%,所述银离子抗菌材料的份额为13~29%。
作为一种优选的技术方案,所述粘合材料的份额为19%,所述离子抗菌聚合物的份额为16%,所述复合纤维材料的份额为35%,所述抗菌薄膜的份额为 12%,所述银离子抗菌材料的份额为18%。
作为一种优选的技术方案,所述粘合材料的份额为18%,所述离子抗菌聚合物的份额为15%,所述复合纤维材料的份额为37%,所述抗菌薄膜的份额为 13%,所述银离子抗菌材料的份额为17%。
(三)有益效果
与现有技术相比,本发明提供了具有吸附并清除甲醛功能的印花墙布及其生产方法,具备以下有益效果:该具有吸附并清除甲醛功能的印花墙布及其生产方法,使用结构更加多样化,采用活性炭棉对空气中的甲醛进行吸附与清除,具有空气净化的效果,增加使用性能,设置加强型环保复合材料,增加墙布的使用强度,不易出现破损的情况,环保性能更为优异,使用寿命更长,挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化,挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP 棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用,制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成,将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小,将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合,将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成,整个印花墙布及其生产方法结构简单,操作方便,使用的效果相对于传统方式更好。
具体实施方式
下面将结合具体实施方式对本发明的技术方案进行清楚、完整地描述,但是本领域技术人员将会理解,下列所描述的实施例是本发明一部分实施例,而不是全部的实施例,仅用于说明本发明,而不应视为限制本发明的范围。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
实施例一:
具有吸附并清除甲醛功能的印花墙布,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,合成树脂的份额为16~23%,PP棉的份额为6~12%,碱玻璃纤维材料的份额为35~46%,可剥离强力粘合胶的份额为11~17%,活性炭棉的份额为16~26%。
合成树脂的份额为19%,PP棉的份额为9%,碱玻璃纤维材料的份额为40%,可剥离强力粘合胶的份额为15%,活性炭棉的份额为17%。
具有吸附并清除甲醛功能的印花墙布的生产方法,包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
S3步骤中粘合材料的份额为18~28%,离子抗菌聚合物的份额为14~25%,复合纤维材料的份额为32~45%,抗菌薄膜的份额为10~20%,银离子抗菌材料的份额为13~29%。
粘合材料的份额为18%,离子抗菌聚合物的份额为15%,复合纤维材料的份额为37%,抗菌薄膜的份额为13%,银离子抗菌材料的份额为17%。
实施例二:
在实施例一的基础上,具有吸附并清除甲醛功能的印花墙布,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,合成树脂的份额为16~23%,PP棉的份额为6~12%,碱玻璃纤维材料的份额为35~46%,可剥离强力粘合胶的份额为11~17%,活性炭棉的份额为16~26%。
合成树脂的份额为20%,PP棉的份额为10%,碱玻璃纤维材料的份额为 38%,可剥离强力粘合胶的份额为14%,活性炭棉的份额为18%。
具有吸附并清除甲醛功能的印花墙布的生产方法,包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
S3步骤中粘合材料的份额为18~28%,离子抗菌聚合物的份额为14~25%,复合纤维材料的份额为32~45%,抗菌薄膜的份额为10~20%,银离子抗菌材料的份额为13~29%。
粘合材料的份额为19%,离子抗菌聚合物的份额为16%,复合纤维材料的份额为35%,抗菌薄膜的份额为12%,银离子抗菌材料的份额为18%。
实施例三:
在实施例二的基础上,具有吸附并清除甲醛功能的印花墙布,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,合成树脂的份额为16~23%,PP棉的份额为6~12%,碱玻璃纤维材料的份额为35~46%,可剥离强力粘合胶的份额为11~17%,活性炭棉的份额为16~26%。
合成树脂的份额为19%,PP棉的份额为9%,碱玻璃纤维材料的份额为40%,可剥离强力粘合胶的份额为15%,活性炭棉的份额为17%。
具有吸附并清除甲醛功能的印花墙布的生产方法,包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
S3步骤中粘合材料的份额为18~28%,离子抗菌聚合物的份额为14~25%,复合纤维材料的份额为32~45%,抗菌薄膜的份额为10~20%,银离子抗菌材料的份额为13~29%。
粘合材料的份额为19%,离子抗菌聚合物的份额为16%,复合纤维材料的份额为35%,抗菌薄膜的份额为12%,银离子抗菌材料的份额为18%。
实施例四:
在实施例三的基础上,具有吸附并清除甲醛功能的印花墙布,包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,合成树脂的份额为16~23%,PP棉的份额为6~12%,碱玻璃纤维材料的份额为35~46%,可剥离强力粘合胶的份额为11~17%,活性炭棉的份额为16~26%。
合成树脂的份额为20%,PP棉的份额为10%,碱玻璃纤维材料的份额为 38%,可剥离强力粘合胶的份额为14%,活性炭棉的份额为18%。
具有吸附并清除甲醛功能的印花墙布的生产方法,包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
S3步骤中粘合材料的份额为18~28%,离子抗菌聚合物的份额为14~25%,复合纤维材料的份额为32~45%,抗菌薄膜的份额为10~20%,银离子抗菌材料的份额为13~29%。
粘合材料的份额为18%,离子抗菌聚合物的份额为15%,复合纤维材料的份额为37%,抗菌薄膜的份额为13%,银离子抗菌材料的份额为17%。
工作原理:挑选一定量的碱玻璃纤维材料,碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化,挑选一定量的活性炭棉,活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用,制备加强型环保复合材料,加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成,将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小,将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合,将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
需要说明的是,在本文中,诸如第一和第二(一号、二号)等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来,而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且,术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含,从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素,而且还包括没有明确列出的其他要素,或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下,由语句“包括一个……”限定的要素,并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.具有吸附并清除甲醛功能的印花墙布,其特征在于:包括以下份额的原材料:合成树脂、PP棉、碱玻璃纤维材料、可剥离强力粘合胶、活性炭棉,所述合成树脂的份额为16~23%,所述PP棉的份额为6~12%,所述碱玻璃纤维材料的份额为35~46%,所述可剥离强力粘合胶的份额为11~17%,所述活性炭棉的份额为16~26%。
2.根据权利要求1所述的具有吸附并清除甲醛功能的印花墙布,其特征在于:所述合成树脂的份额为20%,所述PP棉的份额为10%,所述碱玻璃纤维材料的份额为38%,所述可剥离强力粘合胶的份额为14%,所述活性炭棉的份额为18%。
3.根据权利要求1所述的具有吸附并清除甲醛功能的印花墙布,其特征在于:所述合成树脂的份额为19%,所述PP棉的份额为9%,所述碱玻璃纤维材料的份额为40%,所述可剥离强力粘合胶的份额为15%,所述活性炭棉的份额为17%。
4.具有吸附并清除甲醛功能的印花墙布的生产方法,其特征在于:包括以下操作步骤:
S1:挑选一定量的碱玻璃纤维材料,所述碱玻璃纤维材料是一种性能优异的无机非金属材料,绝缘性好,耐热性强;挑选一定量的合成树脂,所述合成树脂采用聚氨酯弹性体TPU材料,耐水解、耐老化;
S2:挑选一定量的活性炭棉,所述活性炭棉采用活性炭过滤棉的材质,采用吸附法进行空气过滤;挑选一定量的PP棉,所述PP棉采用PP材质,具有固液分离效果;挑选一定量的可剥离强力粘合胶,备用;
S3:制备加强型环保复合材料,所述加强型环保复合材料包括复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料,以复合纤维材料为基材,抗菌薄膜、离子抗菌聚合物、银离子抗菌材料与粘合材料进行层压操作制成;
S4:将碱玻璃纤维材料纺织成布,将制成的布料进行染整操作,得到想要的颜色,碱玻璃纤维布料初步完成,将碱玻璃纤维布料裁切成想要的形状与大小;
S5:将合成树脂、PP棉、可剥离强力粘合胶、活性炭棉裁切成碱玻璃纤维布料相同的大小,通过缝纫装置以及层压装置进行复合操作,可剥离强力粘合胶设置在最外层,可以剥离进行粘合;
S6:将复合纤维材料、抗菌薄膜、离子抗菌聚合物、银离子抗菌材料通过粘合材料进行粘合,并通过层压装置进行复合操作,得到加强型环保复合材料,裁切到碱玻璃纤维布料一样的大小,进行重叠复合,在最外侧通过图案绘制机绘制指定的图案,印花墙布即可制作完成。
5.根据权利要求4所述的具有吸附并清除甲醛功能的印花墙布的生产方法,其特征在于:所述S3步骤中粘合材料的份额为18~28%,所述离子抗菌聚合物的份额为14~25%,所述复合纤维材料的份额为32~45%,所述抗菌薄膜的份额为10~20%,所述银离子抗菌材料的份额为13~29%。
6.根据权利要求5所述的具有吸附并清除甲醛功能的印花墙布的生产方法,其特征在于:所述粘合材料的份额为19%,所述离子抗菌聚合物的份额为16%,所述复合纤维材料的份额为35%,所述抗菌薄膜的份额为12%,所述银离子抗菌材料的份额为18%。
7.根据权利要求5所述的具有吸附并清除甲醛功能的印花墙布的生产方法,其特征在于:所述粘合材料的份额为18%,所述离子抗菌聚合物的份额为15%,所述复合纤维材料的份额为37%,所述抗菌薄膜的份额为13%,所述银离子抗菌材料的份额为17%。