CN113526936A - 一种新型防火堵料 - Google Patents
一种新型防火堵料 Download PDFInfo
- Publication number
- CN113526936A CN113526936A CN202110772029.1A CN202110772029A CN113526936A CN 113526936 A CN113526936 A CN 113526936A CN 202110772029 A CN202110772029 A CN 202110772029A CN 113526936 A CN113526936 A CN 113526936A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- mixing
- blocking material
- novel fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型防火堵料，包括以下材料组成：二乙基硅油20‑45份、丁基橡胶6‑15份、双磷酸季戊四醇酯密胺盐2‑6份、硅藻土8‑20份、氧化镁15‑25份、松脂岩粉30‑45份、填料20‑50份、氢氧化铝20‑35份、阻燃剂15‑30份、碳纳米管10‑23份；步骤S1：将二乙基硅油、丁基橡胶、硅藻土、氧化镁和填料按比例称取；步骤S2：将所述步骤S1中称取的组分放入搅拌机中，进行混合搅拌7‑16分钟；步骤S3：在所述步骤S2的基础上加入碳纳米管进行混合搅拌；步骤S4：在所述步骤S3的基础上加入松脂碳粉和阻燃剂进行混合搅拌。本发明含有松脂岩粉及碳纳米管可以保持堵料的可塑性，在长时间使用后或者经历火灾后，可塑性依然很强，有利于进行防火布置和布局，也降低了后期的使用以及维护成本。
Description
技术领域
本发明涉及一种防火堵料，特别涉及一种新型防火堵料。
背景技术
防火封堵材料(产品)用于封堵各种贯穿物，如电缆、风管、油管、气管等穿过墙(仓)壁、楼(甲)板时形成的各种开口以及电缆桥架的防火分隔，以免火势通过这些开口及缝隙蔓延，具有优良的防火功能，便于更换；防火封堵材料包括：有机防火堵料、无机防火堵料及阻火包。有机防火堵料是以有机合成树脂为粘接剂，添加防火剂、填料等经辗压而成；无机防火堵料，亦称速固型防火堵料，是以快干胶粘剂为基料，添加防火剂、耐火材料等经研磨、混合均匀而成；阻火包是用不燃或阻燃性的纤维布把耐火材料固定成各种规格的包状体，在施工时可堆砌成各种形态的墙体，可对大的孔洞进行封堵，起到隔热阻火作用。
但是，目前的防火堵料在使用方面，存在一定的缺陷，如在经过长时间的使用之后，会逐渐变得坚硬，可塑性急剧变差，对于后期的防火布置造成很大影响，而且现有的防火堵料在经历火灾后，无法继续发挥作用，也提高了使用成本和维护成本。
发明内容
本发明要解决的技术问题是克服现有技术的缺陷，提供一种新型防火堵料。
为了解决上述技术问题，本发明提供了如下的技术方案：
本发明一种新型防火堵料，包括以下材料组成：
二乙基硅油20-45份、
丁基橡胶6-15份、
双磷酸季戊四醇酯密胺盐2-6份、
硅藻土8-20份、
氧化镁15-25份、
松脂岩粉30-45份、
填料20-50份、
氢氧化铝20-35份、
阻燃剂15-30份、
碳纳米管10-23份。
作为本发明的一种优选技术方案，包括如下加工步骤：
步骤S1：将二乙基硅油、丁基橡胶、硅藻土、氧化镁和填料按比例称取；
步骤S2：将所述步骤S1中称取的组分放入搅拌机中，进行混合搅拌7-16分钟；
步骤S3：在所述步骤S2的基础上加入碳纳米管进行混合搅拌；
步骤S4：在所述步骤S3的基础上加入松脂碳粉和阻燃剂进行混合搅拌；
步骤S5：在所述步骤S4的基础上加入双磷酸季戊四醇酯密胺盐和氢氧化铝进行混合搅拌；
步骤S6：将所述步骤S6得到的混合物放入挤出机，进行挤出，得到防火堵料。
作为本发明的一种优选技术方案，
所述步骤S3中，进行混合搅拌前，至少间隔5-8分钟；
所述步骤S4中，进行混合搅拌前，至少间隔10分钟；
所述步骤S5中，进行混合搅拌前，至少间隔6分钟。
作为本发明的一种优选技术方案，所述填料包括天然硅藻土、高岭土中的一种或多种。
作为本发明的一种优选技术方案，所述阻燃剂包括磷酸三丁酯、三氧化二锑中的一种或多种。
作为本发明的一种优选技术方案，所述碳纳米管内含有15％的盐酸。
本发明所达到的有益效果是：本发明含有松脂岩粉及碳纳米管可以保持堵料的可塑性，在长时间使用后或者经历火灾后，可塑性依然很强，有利于进行防火布置和布局，也降低了后期的使用以及维护成本。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例
本发明提供一种新型防火堵料，包括以下材料组成：
二乙基硅油20-45份、
丁基橡胶6-15份、
双磷酸季戊四醇酯密胺盐2-6份、
硅藻土8-20份、
氧化镁15-25份、
松脂岩粉30-45份、
填料20-50份、
氢氧化铝20-35份、
阻燃剂15-30份、
碳纳米管10-23份。
包括如下加工步骤：
步骤S1：将二乙基硅油、丁基橡胶、硅藻土、氧化镁和填料按比例称取；
步骤S2：将所述步骤S1中称取的组分放入搅拌机中，进行混合搅拌7-16分钟；
步骤S3：在所述步骤S2的基础上加入碳纳米管进行混合搅拌；
步骤S4：在所述步骤S3的基础上加入松脂碳粉和阻燃剂进行混合搅拌；
步骤S5：在所述步骤S4的基础上加入双磷酸季戊四醇酯密胺盐和氢氧化铝进行混合搅拌；
步骤S6：将所述步骤S6得到的混合物放入挤出机，进行挤出，得到防火堵料。
所述步骤S3中，进行混合搅拌前，至少间隔5-8分钟；所述步骤S4中，进行混合搅拌前，至少间隔10分钟；所述步骤S5中，进行混合搅拌前，至少间隔6分钟，混合搅拌的时间间隔，可以保证各组分之间的混合均匀。
所述填料包括天然硅藻土、高岭土中的一种或多种。
所述阻燃剂包括磷酸三丁酯、三氧化二锑中的一种或多种。
所述碳纳米管内含有15％的盐酸，含有盐酸的碳纳米管及松脂岩粉提高了堵料的可塑性及可塑性的耐候性。
具体的，本发明含有松脂岩粉及碳纳米管可以保持堵料的可塑性，在长时间使用后或者经历火灾后，可塑性依然很强，有利于进行防火布置和布局，也降低了后期的使用以及维护成本。
本发明含有松脂岩粉及碳纳米管可以保持堵料的可塑性，在长时间使用后或者经历火灾后，可塑性依然很强，有利于进行防火布置和布局，也降低了后期的使用以及维护成本。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种新型防火堵料，其特征在于，按重量份，包括以下材料组成：
二乙基硅油20-45份、
丁基橡胶6-15份、
双磷酸季戊四醇酯密胺盐2-6份、
硅藻土8-20份、
氧化镁15-25份、
松脂岩粉30-45份、
填料20-50份、
氢氧化铝20-35份、
阻燃剂15-30份、
碳纳米管10-23份。
2.根据权利要求1所述的一种新型防火堵料，其特征在于，包括如下加工步骤：
步骤S1：将二乙基硅油、丁基橡胶、硅藻土、氧化镁和填料按比例称取；
步骤S2：将所述步骤S1中称取的组分放入搅拌机中，进行混合搅拌7-16分钟；
步骤S3：在所述步骤S2的基础上加入碳纳米管进行混合搅拌；
步骤S4：在所述步骤S3的基础上加入松脂碳粉和阻燃剂进行混合搅拌；
步骤S5：在所述步骤S4的基础上加入双磷酸季戊四醇酯密胺盐和氢氧化铝进行混合搅拌；
步骤S6：将所述步骤S6得到的混合物放入挤出机，进行挤出，得到防火堵料。
3.根据权利要求2所述的一种新型防火堵料，其特征在于，
所述步骤S3中，进行混合搅拌前，至少间隔5-8分钟；
所述步骤S4中，进行混合搅拌前，至少间隔10分钟；
所述步骤S5中，进行混合搅拌前，至少间隔6分钟。
4.根据权利要求1所述的一种新型防火堵料，其特征在于，所述填料包括天然硅藻土、高岭土中的一种或多种。
5.根据权利要求1所述的一种新型防火堵料，其特征在于，所述阻燃剂包括磷酸三丁酯、三氧化二锑中的一种或多种。
6.根据权利要求1所述的一种新型防火堵料，其特征在于，所述碳纳米管内含有15％的盐酸。