CN113416029A - 一种抗压超薄的高强度水泥日用卫浴材料及其制备方法 - Google Patents
一种抗压超薄的高强度水泥日用卫浴材料及其制备方法 Download PDFInfo
- Publication number
- CN113416029A CN113416029A CN202110827705.0A CN202110827705A CN113416029A CN 113416029 A CN113416029 A CN 113416029A CN 202110827705 A CN202110827705 A CN 202110827705A CN 113416029 A CN113416029 A CN 113416029A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- water
- pressure
- strength cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种抗压超薄的高强度水泥日用卫浴材料及其制备方法。该材料按重量份数计，包括如下物质：水泥30~60份、玻璃纤维0.5~5份、填充料30~60份，水性树脂9~40份、金属氧化物1~10份和水7~25份。本发明优选为：水泥55份、玻璃纤维4份、填充料40份，水性树脂25份、金属氧化物6份和水20份。本发明中，在原料中添加的树脂玻璃纤维可以有效提升产品的抗压性能，本申请中的产品可以将卫浴器件做到超薄的水平；本发明制备方法简单，克服传统卫浴需要高温烧制的缺点，本发明的制备方法绿色环保。
Description
技术领域
本发明属于日用卫浴材料领域，具体涉及一种抗压超薄的高强度水泥日用卫浴材料及其制备方法。
背景技术
卫浴材料是一种用于洗手间以及浴室的材料，主要用作洗手盆以及马桶的主要材料。传统的卫浴材料主要是陶瓷材料。陶瓷材料主要是依靠天然矿石，瓷泥等不可再生的物质经过高温温度（通常在1300℃以上）烧制而成。这种烧制方法以及原料决定了，现有的陶瓷材料的日用卫浴材料的缺陷。由于大量需要高温烧制，这个需要消耗大量能源，这样不但对环境造成影响，同时使得最终做出来的成品价格偏高。
本申请中采用新的原料，克服现有卫浴材料需要高温，且大量使用不可再生的原料的缺点。现有技术中，并没有将水泥应用在卫浴材料上的做法。
发明内容
本发明克服现有技术的缺陷，提供一种抗压超薄的高强度水泥日用卫浴材料及其制备方法，该材料具有原料来源广泛，制备方法简单的优点。
本发明技术方案如下。
一种抗压超薄的高强度水泥日用卫浴材料，按重量份数计，包括如下物质：水泥30~60份、玻璃纤维0.5~5份、填充料30~60份，水性树脂9~40份、金属氧化物1~10份和水7~25份。本发明优选为：水泥55份、玻璃纤维4份、填充料40份，水性树脂25份、金属氧化物6份和水20份。
进一步地，所述水性树脂包括氨基树脂、丙烯酸树脂、纤维素衍生物、酚醛树脂中的一种以上。
进一步地，所述金属氧化物包括氧化铁或钛白粉中的一种以上。
进一步地，所述填充料选自石英砂、陶瓷颗粒。
一种抗压超薄的高强度水泥日用卫浴材料，包括如下步骤：
（1）取计量的水泥、玻璃纤维、填充料、水性树脂和金属氧化物，混合后，加入水，搅拌后备用；
（2）将步骤（1）所得的物料注入模具中，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥日用卫浴材料。
本申请中的抗压超薄的高强度水泥日用卫浴材料，具有优异的防水抗压性能，这主要是水泥在固话过程中与树脂（本发明采用水性树脂乳液）的结合，使得产品具有水泥的强度以及在水泥结构缝隙中夹杂着树脂，可以有效解决水分容易从水泥缝隙中渗透的问题，同时提升强度。
与现有技术相比，本发明的优势在于：
（1）本发明中采用水泥作为原料主体，同时结合树脂等原料，可以使得产品具有防水抗压的效果。
（2）经过申请人的研究，在原料中添加的树脂玻璃纤维可以有效提升产品的抗压性能，本申请中的产品可以将卫浴器件做到超薄的水平；
（3）本发明制备方法简单，克服传统卫浴需要高温烧制的缺点，本发明的制备方法绿色环保。
具体实施方式
下面结合具体实施例对本发明作进一步地具体详细描述，但本发明的实施方式不限于此。
实施例1
（1）取水泥55kg、玻璃纤维4kg、石英砂40kg，丙烯酸树脂乳液25kg、钛白粉6kg，混合后，加入20kg水，搅拌后备用；
（2）将步骤（1）所得的物料注入模具中，本实施例中的模具为一个洗浴盆模具，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥洗浴盆，洗浴盆为椭圆形状，其中椭圆形长轴为1.5m，短轴为80cm，盆体高度为60cm，盆壁平均厚度为1cm，盆底的厚度为3cm。
经过测试，本实施例制备得到的盆体放满水后，在200斤重物进入后5天内，未见开裂现象，同时在防水测试中，盆内放满水，5天后未见水分渗出外壁面。
实施例2
（1）取计量的水泥30kg、玻璃纤维5kg、石英砂30kg，氨基树脂乳液9kg、钛白粉5kg，氧化铁色粉5kg，混合后，加入15kg水，搅拌后备用；
（2）将步骤（1）所得的物料注入洗手盆状模具中，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥洗手盆，洗手盆为圆柱形结构，其中底面的直径为45cm，高为18cm，壁面平均厚度为1cm。
实施例3
（1）取计量的泥60kg、玻璃纤维5kg、石英砂50kg，酚醛树脂乳液20kg、钛白粉10kg，混合后，加入25kg水，搅拌后备用；
（2）将步骤（1）所得的物料注入洗手盆状模具中，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥洗手盆，洗手盆为底面为椭圆形的柱形结构，其中底面椭圆形的长轴为为55cm，短轴为30cm，高为20cm，壁面平均厚度为1cm。
实施例4
（1）取计量的水泥50kg、玻璃纤维4kg、200目废弃陶瓷颗粒30kg，氨基树脂乳液35kg、钛白粉5kg份，混合后，加入20kg水，搅拌后备用；
（2）将步骤（1）所得的物料注入淋浴房地砖面板模具中，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，得到淋浴房地砖面板，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥淋浴房地砖面板。该淋浴房地砖面板为80cm*80cm，厚度为5cm的地砖结构。
Claims (6)
1.一种抗压超薄的高强度水泥日用卫浴材料，其特征在于，按重量份数计，包括如下物质：水泥30~60份、玻璃纤维0.5~5份、填充料30~60份，水性树脂9~40份、金属氧化物1~10份和水7~25份。
2.根据权利要求1所述抗压超薄的高强度水泥日用卫浴材料，其特征在于，所述水性树脂包括氨基树脂、丙烯酸树脂、纤维素衍生物、酚醛树脂中的一种以上。
3.根据权利要求1所述抗压超薄的高强度水泥日用卫浴材料，其特征在于，所述金属氧化物包括氧化铁或钛白粉中的一种以上。
4.根据权利要求1所述抗压超薄的高强度水泥日用卫浴材料，其特征在于，所述填充料选自石英砂、陶瓷颗粒。
5.根据权利要求1所述抗压超薄的高强度水泥日用卫浴材料，其特征在于，按重量份数计，包括如下物质：水泥55份、玻璃纤维4份、填充料40份，水性树脂25份、金属氧化物6份和水20份。
6.权利要求1~5任一项所述抗压超薄的高强度水泥日用卫浴材料，其特征在于，包括如下步骤：
（1）取计量的水泥、玻璃纤维、填充料、水性树脂和金属氧化物，混合后，加入水，搅拌后备用；
（2）将步骤（1）所得的物料注入模具中，得到注浆后的产品；
（3）将步骤（2）中所得的产品进行脱模，再喷上防水剂，然后自然干燥，得到抗压超薄的高强度水泥日用卫浴材料。