CN1134028C - 低温精密测控温热敏电阻器 - Google Patents
低温精密测控温热敏电阻器 Download PDFInfo
- Publication number
- CN1134028C CN1134028C CNB991011341A CN99101134A CN1134028C CN 1134028 C CN1134028 C CN 1134028C CN B991011341 A CNB991011341 A CN B991011341A CN 99101134 A CN99101134 A CN 99101134A CN 1134028 C CN1134028 C CN 1134028C
- Authority
- CN
- China
- Prior art keywords
- temperature
- manganese
- nickel
- lanthanum
- yttrium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种低温精密测控温热敏电阻器，尤其是在低温条件下进行精密温度测量控制的热敏电阻器。该电阻器是由锰、镍、铜氧化物混合物作基料，添加铁、锂、镧、钇四元金属氧化物混合物组成，采用配料、混合、研磨、加入粘合剂制成，电阻体坯体为片状或珠型，用铂金丝钳入坯体中进行烧结，然后在烧结的铂金丝上分别点焊杜美丝外引线，玻璃密封，该电阻器可在-253℃-0℃的不同温度区域内进行精密温度测量控制。
Description
技术领域
本发明涉及一种具有负电阻温度系数的温度敏感元件，尤其是对低温环境或媒体进行精密温度测量或控制的低温热敏电阻器。
背景技术
本发明研制的低温测控温热敏电阻器是一种对低温环境或媒体进行精密温度测量或控制的低温热敏电阻。采用液氢和液氧作为推进剂的运载火箭技术中，需要对低温液体或相关系统的温度参数进行精确测量与控制，因此本发明在经过大量的试验与研究中研制出一种低温精密测控温热敏电阻器。该热敏电阻器灵敏度极高，特别适用于航天技术应用中的低温遥测与控制。同时也适用于运载火箭系统的地面试验以及低温科学试验及其它低温工程技术中进行低温温度的精密测量与控制。
发明内容
本发明目的在于提供一种在低温条件下进行精密温度测量或控制的热敏电阻器。该热敏电阻器是由锰、镍、铜氧化物混合物作基料，添加铁或锂或镧或钇四元金属氧化物混合物组成，采用配料、混合、研磨、加入粘合剂、玻璃密封制成，具有体积小、灵敏度高、性能稳定可靠的特点。根据选用材料配方的不同，制成的低温热敏电阻器可以工作在-253℃-0℃的不同温度区域。
本发明所述的低温精密测控温热敏电阻器是由锰、镍、铜氧化物混合物作基料，添加铁或镧或钇的四元金属氧化物混合物组成，采用配料、混合、研磨、加入粘合剂制成；该热敏电阻器的比例为锰∶镍∶铜∶(铁或锂或镧或钇)，其份量为金属原子比0.5-2.0∶1.0-3.5∶1.0-3.0∶0.1-1.0；该热敏电阻器的制做方法为：将锰、镍、铜氧化物混合物作基料，添加铁或锂或镧或钇，其各比例为金属原子比锰0.5-2.0∶镍1.0-3.5∶铜1.0-3.0∶铁或锂或镧或钇0.1-1.0；混合均匀，在制作中研磨时间为16-32小时，加入聚乙稀醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结后的电阻体铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可；制成的低温热敏电阻器可以工作在-253℃-0℃的不同温度区域。
具体实施方式
实施例1
首先取锰0.5∶镍1.0∶铜1.0金属氧化物混合均匀，研磨16-32小时，加入聚乙烯醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结后的电阻体铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可。所制成的热敏电阻器在-196℃(液氮中)的电阻值为0.5-100kn，在-196℃的电阻温度系数为-6～-10％/℃，可在-196℃～-0℃的温区内工作使用。
实施例2
首先取锰1.0∶镍2.0∶铜1.5∶铁0.1金属氧化物混合均匀，研磨16-32小时，加入聚乙烯醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结后的电阻体铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可。所制成的热敏电阻器在-196℃(液氮中)的电阻值为10-300kn，在-196℃的电阻温度系数为-8～-12％/℃，可在-196℃～-0℃的温区内工作使用。
实施例3
首先取锰1.5∶镍2.5∶铜2.0∶锂0.5金属氧化物混合均匀，研磨16-32小时，加入聚乙烯醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结的铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可。所制成的热敏电阻器在-253℃(液氢中)的电阻值为10-1000kn，在-253℃的电阻温度系数为-30～-60％/℃，可在-253℃～-196℃的温区内工作使用。
实施例4
首先取锰2.0∶镍3.0∶铜3.0∶镧1.0金属氧化物混合均匀，研磨16-32小时，加入聚乙烯醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结的铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可。所制成的热敏电阻器在-253℃(液氢中)的电阻值为10-1000kn，在-253℃的电阻温度系数为-30～-60％/℃，可在-253℃～-196℃的温区内工作使用。
实施例5
首先取锰2.0∶镍1.5∶铜1.5∶钇1.0金属氧化物混合均匀，研磨16-32小时，加入聚乙烯醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结的铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可。所制成的热敏电阻器在-253℃(液氢中)的电阻值为10-1000kn，在-253℃的电阻温度系数为-30～-60％/℃，可在-253℃～-196℃的温区内工作使用。
Claims (2)
1、一种低温精密测控温热敏电阻器，其特征在于该电阻器是由锰、镍、铜氧化物混合物作基料，添加铁或锂或镧或钇的四元金属氧化物混合物组成，采用配料、混合、研磨、加入粘合剂制成；该热敏电阻器的比例为锰∶镍∶铜∶铁或锂或镧或钇，其份量为金属原子比0.5-2.0∶1.0-3.5∶1.0-3.0∶0.1-1.0；
2、根据权利要求1所述的低温精密测控温热敏电阻器的制做方法，其特征在于将锰、镍、铜氧化物混合物作基料，添加铁或锂或镧或钇，其各比例为金属原子比锰0.5-2.0∶镍1.0-3.5∶铜1.0-3.0∶铁或锂或镧或钇0.1-1.0；混合均匀，在制作中研磨时间为16-32小时，加入聚乙稀醇粘合剂进行成型，电阻体坯体为片状或珠型，用铂金丝钳入坯体中，在1000-1200℃温度下保温0.5-1小时进行烧结，然后在烧结后的电阻体铂金丝上分别点焊杜美丝外引线，玻璃密封，在100-250℃温度下老化200-500小时即可；制成的低温热敏电阻器可以工作在-253℃-0℃的不同温度区域。