CN113354285A - Dry particle glaze material for replacing digital ink with matt rock plate - Google Patents
Dry particle glaze material for replacing digital ink with matt rock plate Download PDFInfo
- Publication number
- CN113354285A CN113354285A CN202110767773.2A CN202110767773A CN113354285A CN 113354285 A CN113354285 A CN 113354285A CN 202110767773 A CN202110767773 A CN 202110767773A CN 113354285 A CN113354285 A CN 113354285A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- matt
- digital ink
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The embodiment of the invention discloses a dry particle glaze material for replacing digital ink with a matt rock plate, which comprises the following components in parts by weight: 20-50 parts of glaze powder, 50-80 parts of dry particles, 80-100 parts of suspension dispersion liquid and 20-50 parts of water. The ink can realize lower price than digital ink, thicker glaze layer and stronger wear resistance, and can be applied to scenes with high wearing degree such as ground and the like besides common use.
Description
Technical Field
The invention relates to the field of rock plates, in particular to a dry particle glaze material for replacing digital ink by a matt rock plate.
Background
Rock plate, also called ceramic rock plate, means sintered stone. The rock plate is very similar to the ceramic tile, the process and the material are also similar, the raw material difference is that the rock plate generally adopts the powder of stone, the ceramic tile adopts materials such as clay, and the process difference is that the pressure and the temperature requirement are all different.
The matt brick is one of ceramic tiles, and compared with a polished brick, the matt brick has a non-bright surface, can avoid light pollution, and is easy to maintain. The matt rock plate is developed on the basis of matt bricks.
The traditional matte brick production process is to spray protective glaze after spraying surface glaze and printing patterns, thereby improving surface texture, improving surface antifouling strength and wear resistance, but the existing problems are that: by adopting the glaze spraying process, the glaze surface is uneven and the light sensation is inconsistent.
The matt rock plate is improved by means of the process of matt bricks, 2 channels of an ink-jet printer are adopted, a large-scale spray head of hydrogen fluoride HF is used for spraying digital ink (namely digital protection ink), so that the process is simplified, the glaze surface is uniform and fine, and the inks with different melting temperatures of different types of work are adoptedThe process is widely applied all the time, but the cost cannot be reduced all the time. The ink-jet printing equipment adopted by the process is expensive, the price of the digital protection ink is high, and the cost of each square product is increased by 3-5 yuan/m compared with that of the common rock plate3And moreover, the glaze layer of the digital protective ink is thin and has poor wear resistance, and the matt rock plate produced by the process is not suitable for the ground or other scenes with high wear degree.
Disclosure of Invention
The embodiment of the invention provides a dry particle glaze material for replacing digital ink by a matt rock plate, which can realize lower price, thicker glaze layer and stronger wear resistance than the digital ink, and can be applied to scenes with high wear degree such as ground and the like besides common use.
In order to solve the problems, the dry-particle glaze for replacing digital ink by the matt rock plate provided by the invention comprises the following components in parts by weight:
20-50 parts of glaze powder, 50-80 parts of dry particles, 80-100 parts of suspension dispersion liquid and 20-50 parts of water.
Preferably, the dry particles are ultrafine dry particles with a particle size of 200-300 meshes.
Preferably, the composition is: 40 parts of glaze powder, 50-80 parts of dry particles, 92 parts of suspension dispersion liquid and 39 parts of water.
Preferably, the glaze powder comprises: 100 parts of porcelain glaze, 6-10 parts of clay, 0.5-0.7 part of potassium carbonate and 65 parts of silicon.
Preferably, the glaze powder comprises: 100 parts of porcelain glaze, 8 parts of clay, 0.6 part of potassium carbonate and 65 parts of silicon.
According to the technical scheme, the implementation mode of the invention has the following advantages:
the invention discloses a dry particle glaze material for replacing digital ink by a matt rock plate, which is a matt rock plate capable of being used as a floor tile and a dry particle glaze material capable of replacing digital inkThe board has the same matte characteristic, the dry particle glaze has strong dispersion performance, can completely replace the defect of uneven spraying glaze, the glaze layer can reach 100-300 mu m, the durability and the wear resistance are greatly improved compared with the conventional digital ink, the applicability is not limited, the board can be used in the scene with high damage degree, the cost is low, and the board can be controlled at 1-1.5 yuan/m3。
Detailed Description
The embodiment of the invention provides a dry particle glaze material for replacing digital ink by a matt rock plate, which can realize lower price, thicker glaze layer and stronger wear resistance than the digital ink, and can be applied to scenes with high wear degree such as ground and the like besides common use.
The matt rock plate is one of the rock plates and has a color similar to that of the matt brick.
The invention discloses a dry particle glaze material for replacing digital ink with a matt rock plate, which comprises the following components in parts by weight:
20-50 parts of glaze powder, 50-80 parts of dry particles, 80-100 parts of suspension dispersion liquid and 20-50 parts of water.
Preferably, the dry particles are ultrafine dry particles with a particle size of 200-300 meshes.
Preferably, the composition is: 40 parts of glaze powder, 50-80 parts of dry particles, 92 parts of suspension dispersion liquid and 39 parts of water.
Preferably, the glaze powder comprises: 100 parts of porcelain glaze, 6-10 parts of clay, 0.5-0.7 part of potassium carbonate and 65 parts of silicon.
Preferably, the glaze powder comprises: 100 parts of porcelain glaze, 8 parts of clay, 0.6 part of potassium carbonate and 65 parts of silicon.
The use method of the invention adopts the conventional traditional process, the dry particle glaze is used as the protective glaze in the traditional process, the improvement of the protective glaze does not influence the property of matt, the thickness of the produced matt rock plate glaze layer can reach 100-300 mu m, the durability and the wear resistance are strong, the application range is wide, the dry particle glaze can be used as a floor tile, and the cost is 1-1.5 yuan/m3。
The invention is described in detail below by means of a number of examples:
example 1
The dry particle glaze material for replacing digital ink by the matt rock plate comprises the following components in parts by weight:
50 parts by weight of glaze powder, 80 parts by weight of ultrafine dry particles with the particle size of 300 meshes, 100 parts by weight of suspension dispersion liquid and 50 parts by weight of water.
According to the preparation method of the traditional process, raw materials are pressed into green bricks, the green bricks are dried, glaze is coated on the green bricks, patterns are printed, the dry-particle glaze is sprayed on the green bricks, and the green bricks are fired to obtain the matt rock board.
Wherein, glaze powder includes: 100 parts of porcelain glaze, 10 parts of clay, 0.7 part of potassium carbonate and 65 parts of silicon.
Example 2
Essentially the same as in example 1, except that:
the components are as follows:
40 parts of glaze powder, 70 parts of superfine dry particles with the particle size of 300 meshes, 92 parts of suspension dispersion liquid and 39 parts of water.
Example 3
Essentially the same as in example 1, except that:
the components are as follows:
20 parts by weight of glaze powder, 50 parts by weight of dry particles, 80 parts by weight of suspension dispersion liquid and 25 parts by weight of water.
Comparing all the thicknesses of the matt rock plates (hereinafter referred to as digital ink matt rock plates) which are produced by the production of the matt rock plates produced in the examples 1 to 3 and purchased from the market and prepared by a digital ink process, and comparing:
visual identification: the visual identification effects are basically similar, and the distinction is difficult to distinguish.
Hardness test (test as impact resistance): the impact resistance of the matt rock plate in the embodiments 1 to 3 is far greater than that of the matt rock plate made of digital ink.
As described above, the above embodiments and examples are only for illustrating the technical solution of the present invention, and not for limiting the same; although the present invention has been described in detail with reference to the foregoing embodiments and examples, it will be understood by those of ordinary skill in the art that: the technical solutions described in the foregoing embodiments may still be modified, or some technical features may be equivalently replaced; and such modifications or substitutions do not depart from the spirit and scope of the corresponding technical solutions of the embodiments and examples of the present invention.
Claims (5)
1. A dry particle glaze material for replacing digital ink with a matt rock plate is characterized by comprising the following components in parts by weight:
20-50 parts of glaze powder, 50-80 parts of dry particles, 80-100 parts of suspension dispersion liquid and 20-50 parts of water.
2. The matt rock panel as claimed in claim 1 instead of digital ink dry particle glaze, wherein the dry particles are ultrafine dry particles with a particle size of 200-300 meshes.
3. The dry-particle glaze material for replacing digital ink by matt rock plates as claimed in claim 1, which is characterized by comprising the following components: 40 parts of glaze powder, 50-80 parts of dry particles, 92 parts of suspension dispersion liquid and 39 parts of water.
4. The matt rock plate dry bead glaze replacing digital ink as claimed in claim 1, wherein the glaze powder comprises: 100 parts of porcelain glaze, 6-10 parts of clay, 0.5-0.7 part of potassium carbonate and 65 parts of silicon.
5. The matt rock plate dry bead glaze replacing digital ink as claimed in claim 4, wherein the glaze powder comprises: 100 parts of porcelain glaze, 8 parts of clay, 0.6 part of potassium carbonate and 65 parts of silicon.