CN113351156A - 去除空气中酸性气体的活性氧化铝改性方法 - Google Patents
去除空气中酸性气体的活性氧化铝改性方法 Download PDFInfo
- Publication number
- CN113351156A CN113351156A CN202110740364.3A CN202110740364A CN113351156A CN 113351156 A CN113351156 A CN 113351156A CN 202110740364 A CN202110740364 A CN 202110740364A CN 113351156 A CN113351156 A CN 113351156A
- Authority
- CN
- China
- Prior art keywords
- activated alumina
- alumina
- drying
- humidity
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种去除空气中酸性气体的活性氧化铝改性方法，包括以下步骤：1）选用蜂窝状的活性氧化铝；2）用过量的稀硝酸对氧化铝进行清洗至少半小时，然后，用过量的清水进行清洗；3）配制改性液：水中加入碳酸钾和高锰酸钾，溶解后，使碳酸钾的浓度为5~30%质量分数，高锰酸钾浓度为5~30%质量分数；4）将活性氧化铝浸渍在改性液中，且浸渍比为1:1；浸渍时间至少为半小时；5）将浸渍后的活性氧化铝取出，对其进行烘干；6）对烘干后的活性氧化铝进行静置干燥；7）对活性氧化铝进行筛分，去除粉尘。本发明可有效提高活性氧化铝对酸性气体的吸附效率，并可增加其使用范围和应用场景，充分满足市场的需求。
Description
技术领域
本发明涉及一种过滤材料制备方法，尤其是一种活性氧化铝制备方法，具体的说是一种去除空气中酸性气体的活性氧化铝改性方法。
背景技术
活性氧化铝是一种多孔、具有高分散度的固体物质，有很高的比表面积，它独特的微孔结构使其具有吸附性能、表面酸性及热稳定性等特性。同时，其除了具有很高的比表面积、合适的孔容与孔径，其烧结体还具有很高的机械强度与耐热性，因此被广泛的用作催化剂的载体。活性氧化铝的改性主要是通过一些化学或者物理的方法使其孔隙结构发生变化，同时负载吸附剂以实现对特定物质吸附的效果。
目前使用的改性活性氧化铝，大都存在以下问题：
1）大都使用氧化铝小球作为吸附剂载体，在吸附时容易被穿透，且效率较低。
2、大都使用氧化铝粉末在氧化铝小球造粒过程中加入改性溶剂，使加工后的改性氧化铝中存有大量粉末，在后续处理过程中容易脱落，污染客户现场。
3、主要使用高锰酸钾对活性氧化铝进行改性，仅对硫化氢具有较强的吸附效果，吸附对象单一。
因此，需要加以改进，以便提高其吸附效率和使用范围。
发明内容
本发明的目的是针对现有技术的不足，提供一种去除空气中酸性气体的活性氧化铝改性方法，可有效提高活性氧化铝对酸性气体的吸附效率，并可增加其使用范围和应用场景。
本发明的技术方案是：
一种去除空气中酸性气体的活性氧化铝改性方法，包括以下步骤：
1）选用蜂窝状的活性氧化铝；
2）用过量的稀硝酸对氧化铝进行清洗至少半小时，然后，用过量的清水进行清洗；
3）配制改性液：水中加入碳酸钾和高锰酸钾，溶解后，使碳酸钾的浓度为5~30%质量分数，高锰酸钾浓度为5~30%质量分数；
4）将活性氧化铝浸渍在改性液中，且浸渍比为1:1；浸渍时间至少为半小时；
5）将浸渍后的活性氧化铝取出，对其进行烘干；
6）对烘干后的活性氧化铝进行静置干燥；
7）对活性氧化铝进行筛分，去除粉尘。
进一步的，所述步骤2）中，所述稀硝酸的浓度为5%。
进一步的，所述步骤2）中，所述稀硝酸完全浸没活性氧化铝；所述清水完全浸没活性氧化铝。
进一步的，所述步骤5）中，放置在恒温恒湿干燥箱中进行烘干，该恒温恒湿干燥箱的温度为40~70℃，湿度为75%；烘干时间为至少4小时。
进一步的，所述步骤6）中，放置在恒温恒湿干燥箱中进行静置干燥，该恒温恒湿干燥箱中的温度为22℃，湿度为40%，静置干燥时间至少24小时。
进一步的，所述步骤7）中，使用振筛机进行筛分。
本发明的有益效果：
本发明设计合理，操作方便，效果突出，可有效提高活性氧化铝对酸性气体的吸附效率，并可增加其使用范围和应用场景，充分满足市场的需求。
具体实施方式
下面结合实施例对本发明作进一步的说明。
一种去除空气中酸性气体的活性氧化铝改性方法，包括以下步骤：
1）选用蜂窝状的活性氧化铝，其尺寸为50*150*300mm，孔数60*60，壁厚0.5mm；并将其切割成50*50*50mm的小块，方便后期置入过滤器中；也可根据其他过滤器的大小而切割成其他规格；
2）在酸缸中放置5%稀硝酸，将上述活性氧化铝浸渍在该稀硝酸中，并使活性氧化铝完全被浸没；30分钟后将活性氧化铝取出，用大量的清水进行清洗，直至清洗的水的pH为7；
3）配制与活性氧化铝等质量的改性液，例如，可在180mL水中，加入14.4g高锰酸钾和18g碳酸钾配制成8% 高锰酸钾和10% 碳酸钾的混合水溶液；
4）将活性氧化铝浸渍在改性液中，浸渍比为1:1；浸渍时间半小时或以上；所述浸渍比是指活性氧化铝与改性液的质量比；
5）将浸渍后的活性氧化铝取出，放置在恒温恒湿干燥箱内部进行烘干，并设置箱内的温度为60℃，湿度为75%，烘干4小时，使活性氧化铝上多余的水分快速蒸发；
6）将恒温恒湿干燥箱内的温度调为22℃，湿度为40%，再放置24小时或以上，进行静置干燥，使吸附质完全附载在活性氧化铝表面；
7）使用振筛机对活性氧化铝进行筛分，去除粉尘；该振筛机为30目，摇动次数约221次/min，振击次数147次/min，运转10min。
将制备好的活性氧化铝装入HCC化学过滤器中，使用滤料测试台将其与现有产品进行比较性试验，测试包括对硫化氢和二氧化硫的吸附效率。表1为本发明方法制备的产品与现有产品的测试数据。
表1
由此可以看出，本发明制备的产品相较于现有产品，对硫化氢具有更高的吸附效率，而且，还实现了同时对硫化氢和二氧化硫进行吸附的效果，充分满足不同场景的使用需求。
本发明未涉及部分均与现有技术相同或可采用现有技术加以实现。
Claims (6)
1.一种去除空气中酸性气体的活性氧化铝改性方法，其特征是，包括以下步骤：
1）选用蜂窝状的活性氧化铝；
2）用过量的稀硝酸对氧化铝进行清洗至少半小时，然后，用过量的清水进行清洗；
3）配制改性液：水中加入碳酸钾和高锰酸钾，溶解后，使碳酸钾的浓度为5~30%质量分数，高锰酸钾浓度为5~30%质量分数；
4）将活性氧化铝浸渍在改性液中，且浸渍比为1:1；浸渍时间至少为半小时；
5）将浸渍后的活性氧化铝取出，对其进行烘干；
6）对烘干后的活性氧化铝进行静置干燥；
7）对活性氧化铝进行筛分，去除粉尘。
2.根据权利要求1所述的去除空气中酸性气体的活性氧化铝改性方法，其特征是，所述步骤2）中，所述稀硝酸的浓度为5%。
3.根据权利要求1所述的去除空气中酸性气体的活性氧化铝改性方法，其特征是，所述步骤2）中，所述稀硝酸完全浸没活性氧化铝；所述清水完全浸没活性氧化铝。
4.根据权利要求1所述的去除空气中酸性气体的活性氧化铝改性方法，其特征是，所述步骤5）中，放置在恒温恒湿干燥箱中进行烘干，该恒温恒湿干燥箱的温度为40~70℃，湿度为75%；烘干时间为至少4小时。
5.根据权利要求1所述的去除空气中酸性气体的活性氧化铝改性方法，其特征是，所述步骤6）中，放置在恒温恒湿干燥箱中进行静置干燥，该恒温恒湿干燥箱中的温度为22℃，湿度为40%，静置干燥时间至少24小时。
6.根据权利要求1所述的去除空气中酸性气体的活性氧化铝改性方法，其特征是，所述步骤7）中，使用振筛机进行筛分。