CN1133328A

CN1133328A - Luminous multi-colour porcelain-imitated paint

Info

Publication number: CN1133328A
Application number: CN 94106400
Authority: CN
Inventors: 章永来
Original assignee: Individual
Current assignee: Individual
Priority date: 1994-06-21
Filing date: 1994-06-21
Publication date: 1996-10-16

Abstract

The luminescent multi-colour imitation porcelain coating is mainly characterized by that it is a two-component solvent-type luminescent multi-colour imitation porcelain coating made up by using epoxy resin as main body material and adding other materials, such as synthetic resin with good physical and chemical properties and photoaccumulation type material and making them pass through a certain preparation process. It is an ideal decorative material for internal and external wall surface instead of traditional porcelain glaze.

Description

Luminous multi-colour porcelain-imitated paint

The invention discloses a kind of luminous multi-colour porcelain-imitated paint and preparation method thereof, belong to the luminescent coating field.

At present, the luminous paint kind is a lot, and the present still blank of luminous multi-colour porcelain-imitated paint, in order to fill up this piece blank, I on the basis that looks through a great amount of information through repeatedly studying and testing, success develop a kind of surface property that can reach wall tile, can reach the luminous multi-colour porcelain-imitated paint of illumination functions of the low end again.

The purpose of this invention is to provide that a kind of to be main body with Resins, epoxy become two ingredient liquids with the synthetic resins and the safe and reliable preparation of raw material such as photic accumulating type material of "dead" essence of other physiological property excellence.Spray film forming, and reach the luminous multi-colour porcelain-imitated paint of porcelain facing effect and noctilucence performance.

For achieving the above object, the present invention by the following technical solutions: luminous multi-colour porcelain-imitated paint is to be that binder resin adds photic energy section bar material and color stuffing is that effective constituent is by the formulated two component solvent-borne type luminous multi-colour porcelain-imitated paints of portion rate with the high molecular synthetic resin.Priming paint selects for use the T3 epoxy curing agent as the bottom solidifying agent.Surface layer is suitable for the Polyurethane tree and refers to 7110T3, the last light that forms such as flow agent 590-3 and photic accumulating type material, the filming of tough and tensile plentiful exquisiteness.Luminous multi-colour porcelain-imitated paint is except that the general character with common solvent type coating.The main A of being group reticulates the type molecular structure with B group crosslinking reaction, to improve its inner quality.Selecting the import titanium dioxide when the face porcelain is made for use is that tinting pigment and physique filler add the photic accumulating type material that does not contain the radioactivity essence, and with the proportioning of strictness, advanced technology is made the obvious results luminous multi-colour porcelain-imitated paint.

Luminous multi-colour porcelain-imitated paint, by Resins, epoxy, alkyd resin, aminoresin, titanium dioxide, photic accumulating type material is formed.Be divided into end porcelain A, end porcelain B, face porcelain A, face porcelain B, form respectively by weight percentage that the effect of porcelain is the full weight that improves sticking power and increase coating at the bottom of the luminous multi-colour porcelain-imitated paint, therefore when making, do not add photic accumulating type material.End porcelain A is zinc sulfide white, talcum powder, process white, homemade titanium dioxide 101, aminoresin 590-3: Resins, epoxy 601 Resins, epoxy 604 dimethylbenzene: the ring ethyl ketone=(14.8-21.8): (9.4-11.4): (4.2-6.2): (6.28-8.28): (2.12-4.12); (4.2-6.2): (11.48-13.48): (23.6-25.6): (13.8-14.8); End porcelain B is the T31 epoxy hardener, butanols: dimethylbenzene=(35-45): (15-25): (35-45); Face porcelain A is: import titanium dioxide rutile-type R902: photic accumulating type material: Resins, epoxy 601: Resins, epoxy 604; Ring ethyl ketone: dimethylbenzene: aminoresin 590-3: alkyd resin 7110J3=(23.7-25.7): (10-20): (5.4-7.4): (12.2-14.2): (15.2-17.2); (17.7-20.7): 91.2-3.2); (7.6-9.6); Face porcelain B is that polyurethane 7110 first are (65-75): biuret H01 (25-35).

During actual the use, end porcelain A and end porcelain B spray after mixing stirring, form the hard porcelain facing of light at last.

For being suitable for service requirements, also prepare stained porcelain, it consists of Resins, epoxy 601 by weight percentage: Resins, epoxy 604: pimelinketone: dimethylbenzene: alkyd resin J3: aminoresin 590-3: talcum powder: toner=(5-7): (11.5-13.5): (5-7): (10.5-12.5): (8-10): (8-10):: (4-6): (20-40); The dyeing powder is bright red, green, when blue, needs to add 2% process white, and look porcelain and face porcelain A stir the back spraying, promptly form required colorful porcelain facing.

The photic accumulating type material body colour that the present invention was suitable for is red, and Huang is green, indigo plant, and light color is selected for use in the time of can requiring system 2 to make face porcelain A according to required color; When system 2 is made face porcelain A, add photic accumulating type material ranges 10%-20% according to required brightness.

Adopt above-mentioned end porcelain A, end porcelain B, face porcelain A, face porcelain B, the prescription of look porcelain; Adopt following system 2 Preparation Methods.Can make 2 one-tenth solvent-borne type luminous multi-colour porcelain-imitated paints, its preparation method: solvent preparation → dissolving matrix resin → powder stir → adds the stirring → grinding of color filler again and adds solvent in proportion and other resin → stirring → test package for doing → add photic accumulating type material.

This luminous multi-colour porcelain-imitated paint is all spendable a kind of flawless finish coating of indoor and outdoor building.It has remarkable decorate properties and workability.Characteristics of the present invention: 1. good decorating effect, decorative cover gloss on daytime is according to the people, and beautiful in colour, present colorful evening, multicoloured scene; 2. the comprehensive physicochemical property excellence of filming; It not only has Resins, epoxy, and the gentle of alkyd resin coating closed and plentiful feature, also has both high gloss and its acid and alkali-resistance of flexible characteristic of amino-resin coating, radioprotective, salt spray resistance, weather resisteant, high-low temperature resistant, scrubbing resistance, anti-wasting property, the comprehensive advantage of aspects such as anti-pollution surmounts other luminescent coating.This coating select for use photic wait can the section bar material different with traditional fluorescent luminescent powder mechanism, it is a kind of high efficiency energy storage section bar material, by absorbing daylight, light, behind the visible lights such as stray light, sustainable luminous more than 12 hours at the dark place, do not contain radioelement, life-span can reach more than 20 years, put the detection of thanking property supervision inspection center by State Bureau of Building Materials Industry's building material product and building materials with industrial residue and put thanking property nucleic specific activity ²²⁶Ra ²³²Th ⁴⁰K is lower than detection limit, is not detected, and be a kind of safe and reliable luminescent coating therefore; 4. model applied widely: be not only applicable to the decoration of building inside and outside wall face, also can be used for ground, furniture, the electronic product surface, plastics system 2 product surface advertisement boards, road sign and railway, boats and ships, military engineering, civil air defense constructions and installations, down-hole, mine, aspects such as technology system 2 product, 5. easy construction is adopted spraying to brush and all can be obtained gratifying effect.

Claims

1. luminous multi-colour porcelain-imitated paint, by Resins, epoxy, alkyd resin aminoresin, photic accumulating type material, titanium dioxide is formed, be divided into end porcelain A, end porcelain B, face porcelain A, it is zinc sulfide white that face porcelain B forms end porcelain A by weight percentage respectively, talcum powder, process white, titanium dioxide B101 aminoresin: dimethylbenzene: ring ethyl ketone: Resins, epoxy 601 Resins, epoxy 604=(19.8-21.8): (9.4-11.4): (4.2-6.2): (6.28-8.28): (2.12-4.12): (23.6-25.6): (13.8-14.8): (4.2-6.2): (11.48-13.48); End porcelain B is the T31 epoxy hardener: butanols: dimethylbenzene=(35-45): (15-25): (35-45); Face porcelain A is import rutile-type R902: photic accumulating type material: Resins, epoxy 601: Resins, epoxy 604: ring ethyl ketone: dimethylbenzene: aminoresin 590-3, alkyd resin 7110J3=(23.7-25.7): (10-20): (5.4-7.4): (12.2-14.2): (15.2-17.2): (17.7-20.7): (1.2-3.2): (7.6-9.6); Face porcelain B is that polyurethane 7110 first are (65-75): biuret HOI (25-35).

2. luminous multi-colour porcelain-imitated paint as claimed in claim 1, it is characterized in that, also comprise the look porcelain, it consists of by weight percentage: Resins, epoxy 601: Resins, epoxy 604: ring ethyl ketone: dimethylbenzene: (ring ethyl ketone: dimethylbenzene): alkyd resin 7110J3 or J4, aminoresin 590-3: talcum powder: toner=(5-7): (11.5-13.5): (5-7): (5-7): (10.5-12.5): (8-10): (8-10): (4-6): (20-40).

3. luminous multi-colour porcelain-imitated paint as claimed in claim 2 is characterized in that, described toner is bright red, green, when blue, needs to add 2% process white.

4. luminous multi-colour porcelain-imitated paint as claimed in claim 1, its feature also comprises: photic accumulating type material body colour is red, yellow, green, blue simplely select for use can require system 2 make face porcelain A according to required luminous color the time, when system 2 is made face porcelain A, add photic accumulating type material ranges 10%-20% according to required brightness.

5. its feature of luminous multi-colour porcelain-imitated paint as claimed in claim 1 also comprises: photic accumulating type material radioactivity essence detects index: radionuclide specific activity 226Ra ²³²Th ⁴⁰K is lower than detection limit and is not detected, and belongs to the luminescent material of "dead" essence.

6. luminous multi-colour porcelain-imitated paint as claimed in claim 1, its preparation method is characterised in that: the solvent preparation → dissolving matrix resin → photic accumulating type material of powder oven dry → adding stirring → adding color stuffing → grinding also adds solvent and other resin → stirring → test package in proportion.