CN113305972A - Preparation process of environment-friendly soft-seat toilet lid - Google Patents
Preparation process of environment-friendly soft-seat toilet lid Download PDFInfo
- Publication number
- CN113305972A CN113305972A CN202110664933.0A CN202110664933A CN113305972A CN 113305972 A CN113305972 A CN 113305972A CN 202110664933 A CN202110664933 A CN 202110664933A CN 113305972 A CN113305972 A CN 113305972A
- Authority
- CN
- China
- Prior art keywords
- coating material
- toilet
- core
- seat
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of environment-friendly soft-seat toilet covers, in particular to a preparation process of an environment-friendly soft-seat toilet cover, which comprises the following steps: s1, selecting plate cores for the toilet seat and the toilet cover plate, and pressing the plate cores into the shapes of the toilet seat and the toilet cover plate by a wood powder molding press, or selecting PP plate cores; s2, polishing and grinding the pressed wood board core; s3, selecting a toilet seat and a coating material in the shape of a toilet cover plate, horizontally cutting the coating material, and arranging a plate core between the upper and lower layers of coating materials; s4, wrapping and pressing the wrapping material on the outer side of the wrapping material through a high-frequency machine, wherein the plate core is used as the base plate, the plate core is wrapped by the soft wrapping material which is only sponge or sponge and pearl cotton, and is very comfortable, and the TPU is wrapped on the outer layer, so that the toilet cover plate and the toilet ring are very environment-friendly and safe, do not have pungent taste, and are convenient for users to select at home healthily.
Description
Technical Field
The invention relates to the technical field of environment-friendly soft-seat toilet covers, in particular to a preparation process of an environment-friendly soft-seat toilet cover.
Background
The toilet lid is a device which is installed above an indoor toilet and used for isolating peculiar smell gas in the toilet when the toilet is idle so as to prevent people from flowing for the gas in a large range when people go to the toilet, thereby improving the overall quality of an indoor air environment, and being convenient for people to sit more comfortably when people go to the toilet, and the toilet lid is widely used in the field of daily living.
Soft seat closestool apron and closestool circle of doing such as PVC, leather on the existing market, its material is not environmental protection, and material itself will have the taste to produce moreover, environmental protection inadequately, and when like the lavatory take a seat, the comfort level of closestool circle is not good enough.
Therefore, we propose a process for preparing an environment-friendly soft-seated toilet lid to solve the above problems.
Disclosure of Invention
The invention aims to solve the defects in the prior art and provides a preparation process of an environment-friendly soft-seat toilet lid.
The utility model provides a soft seat toilet lid of environmental protection, includes toilet lid and closestool circle, the middle part of toilet lid and closestool circle is provided with the board core, and the outside cladding of board core has the cladding material, and the outside of cladding material is wrapped up in and is equipped with the wrapping material.
Preferably, the coating material is sponge or sponge and pearl cotton, and the plate core and the coating material are pressed together through a high-frequency machine.
Preferably, the wrapping material is TPU, and the wrapping material is wrapped and pressed on the outer side of the wrapping material at the outer side of the wrapping material through a high-frequency machine.
A preparation process of an environment-friendly soft-seat toilet lid comprises the following steps:
s1, selecting toilet seat and toilet cover plate core materials: the toilet seat and the toilet cover plate are made of plate cores, and the shapes of the toilet seat and the toilet cover plate are formed by pressing a wood powder molding press;
s2, polishing and grinding the pressed wood board core, and spraying environment-friendly protective paint on the board core;
s3, selecting a toilet seat and a toilet cover plate-shaped coating material, horizontally cutting the coating material, placing the plate core in the S2 between the upper layer of coating material and the lower layer of coating material, and pressing the plate core, the upper layer of coating material and the lower layer of coating material together through a high-frequency machine;
s4, adding an antibacterial agent on the coating material, wherein micropores are formed in the upper coating material, and perfume micro-beads are placed in the micropores;
s5, wrapping the wrapping material on the outer side of the wrapping material through a high-frequency machine, and pressing the wrapping material on the outer side of the wrapping material, wherein the wrapping material is TPU, and the thickness of the TPU is 0.1-1 mm.
Preferably, the board core in S1 is a wood board core or a PP material core, and the thickness of the board core is 5-30 mm.
Preferably, the coating material in the S3 is sponge or sponge and pearl wool.
Preferably, the thickness of the coating material is 10-60mm, after the coating material is horizontally cut, the thickness of the upper-layer coating material is 5-40mm, and the thickness of the lower-layer coating material is 5-50 mm.
Preferably, the antibacterial agent sprayed on the outer side of the coating is nano silver ion powder, the nano silver ion powder is adhered to the outer side of the coating, and the perfume micro-beads in the upper coating are jasmine micro-beads or sweet osmanthus micro-beads.
The invention has the beneficial effects that:
1. according to the invention, the plate core is used as the base plate, the plate core is wrapped by the soft wrapping material which is only sponge or sponge and pearl cotton, so that the toilet cover plate and the toilet ring are very comfortable, and the outer layer is wrapped by the TPU, so that the toilet cover plate and the toilet ring are very environment-friendly and safe, do not have pungent taste, are more comfortable when sitting in a toilet, and are convenient for healthy home selection of a user.
2. According to the invention, the environment-friendly antibacterial agent and the perfume micro-beads are arranged at the coating material, so that the antibacterial performance of the toilet seat and the toilet cover is improved, the toilet cover and the toilet seat have light natural fragrance, and the healthy home selection of a user is facilitated.
Drawings
Fig. 1 is a schematic structural view of an environment-friendly soft-seat toilet lid.
In the figure, 1 toilet lid, 2 toilet ring, 3 plate core, 4 coating material and 5 coating material.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example one
An environment-friendly toilet lid with a soft seat comprises a toilet lid plate 1 and a toilet ring 2, wherein a plate core 3 is arranged in the middle of the toilet lid plate 1 and the toilet ring 2, a coating material 4 is coated outside the plate core 3, and a coating material 5 is coated outside the coating material 4, as shown in figure 1.
The coating material 4 is made of sponge or sponge and pearl cotton, and the plate core 3 and the coating material 5 are pressed together through a high-frequency machine.
The wrapping material 5 is TPU, and is wrapped and pressed on the outer side of the wrapping material 4 at the outer side of the wrapping material through a high-frequency machine.
A preparation process of an environment-friendly soft-seat toilet lid comprises the following steps:
s1, selecting toilet seat and toilet cover plate core materials: the toilet seat and the toilet cover plate are both made of wood or PP material, the thickness of the wood core is 5mm, and the wood powder is pressed into the shapes of the toilet seat and the toilet cover plate by a mould press;
s2, polishing and grinding the pressed wood board core, and spraying environment-friendly protective paint on the board core;
s3, selecting a toilet seat and a coating material in the shape of a toilet cover plate, wherein the coating material is made of sponge or sponge and pearl cotton, horizontally cutting the coating material, placing the plate core in the step S2 between an upper layer of coating material and a lower layer of coating material, and pressing the plate core with the upper layer of coating material and the lower layer of coating material together through a high-frequency machine, wherein the thickness of the coating material is 10mm, after the coating material is horizontally cut, the thickness of the upper layer of coating material is 5mm, and the thickness of the lower layer of coating material is 5 mm;
s4, uniformly spraying an antibacterial agent on the coating material, wherein micropores are formed in the upper coating material, perfume micro-beads are placed in the micropores, the antibacterial agent sprayed on the outer side of the coating material is nano silver ion powder, the nano silver ion powder is adhered to the outer side of the coating material, and the perfume micro-beads in the upper coating material are jasmine micro-beads or sweet-scented osmanthus micro-beads;
s5, wrapping the wrapping material on the outer side of the wrapping material through a high-frequency machine, and pressing the wrapping material into the wrapping material, wherein the wrapping material is TPU, and the thickness of the TPU is 0.1 mm.
Example two
An environment-friendly toilet lid with a soft seat comprises a toilet lid plate 1 and a toilet ring 2, wherein a plate core 3 is arranged in the middle of the toilet lid plate 1 and the toilet ring 2, a coating material 4 is coated outside the plate core 3, and a coating material 5 is coated outside the coating material 4, as shown in figure 1.
The coating material 4 is made of sponge or sponge and pearl cotton, and the plate core 3 and the coating material 5 are pressed together through a high-frequency machine.
The wrapping material 5 is TPU, and is wrapped and pressed on the outer side of the wrapping material 4 at the outer side of the wrapping material through a high-frequency machine.
A preparation process of an environment-friendly soft-seat toilet lid comprises the following steps:
s1, selecting toilet seat and toilet cover plate core materials: the toilet seat and the toilet cover plate are both made of wood or PP material, the thickness of the wood core is 18mm, and the wood powder is pressed into the shapes of the toilet seat and the toilet cover plate by a mould press;
s2, polishing and grinding the pressed wood board core, and spraying environment-friendly protective paint on the board core;
s3, selecting a toilet seat and a coating material in the shape of a toilet cover plate, wherein the coating material is made of sponge or sponge and pearl cotton, horizontally cutting the coating material, placing the plate core in the step S2 between an upper layer of coating material and a lower layer of coating material, and pressing the plate core and the upper layer of coating material and the lower layer of coating material together through a high-frequency machine, wherein the thickness of the coating material is 30mm, after the coating material is horizontally cut, the thickness of the upper layer of coating material is 15mm, and the thickness of the lower layer of coating material is 15 mm;
s4, uniformly spraying an antibacterial agent on the coating material, wherein micropores are formed in the upper coating material, perfume micro-beads are placed in the micropores, the antibacterial agent sprayed on the outer side of the coating material is nano silver ion powder, the nano silver ion powder is adhered to the outer side of the coating material, and the perfume micro-beads in the upper coating material are jasmine micro-beads or sweet-scented osmanthus micro-beads;
s5, wrapping the wrapping material on the outer side of the wrapping material through a high-frequency machine, and pressing the wrapping material into the wrapping material, wherein the wrapping material is TPU, and the thickness of the TPU is 0.7 mm.
EXAMPLE III
An environment-friendly toilet lid with a soft seat comprises a toilet lid plate 1 and a toilet ring 2, wherein a plate core 3 is arranged in the middle of the toilet lid plate 1 and the toilet ring 2, a coating material 4 is coated outside the plate core 3, and a coating material 5 is coated outside the coating material 4, as shown in figure 1.
The coating material 4 is made of sponge or sponge and pearl cotton, and the plate core 3 and the coating material 5 are pressed together through a high-frequency machine.
The wrapping material 5 is TPU, and is wrapped and pressed on the outer side of the wrapping material 4 at the outer side of the wrapping material through a high-frequency machine.
A preparation process of an environment-friendly soft-seat toilet lid comprises the following steps:
s1, selecting toilet seat and toilet cover plate core materials: the toilet seat and the toilet cover plate are both made of wood or PP material, the thickness of the wood core is 30mm, and the wood powder is pressed into the shapes of the toilet seat and the toilet cover plate by a mould press;
s2, polishing and grinding the pressed wood board core, and spraying environment-friendly protective paint on the board core;
s3, selecting a toilet seat and a coating material in the shape of a toilet cover plate, wherein the coating material is made of sponge or sponge and pearl cotton, horizontally cutting the coating material, placing the plate core in the step S2 between an upper layer of coating material and a lower layer of coating material, and pressing the plate core with the upper layer of coating material and the lower layer of coating material together through a high-frequency machine, wherein the thickness of the coating material is 60mm, after the coating material is horizontally cut, the thickness of the upper layer of coating material is 30mm, and the thickness of the lower layer of coating material is 30 mm;
s4, uniformly spraying an antibacterial agent on the coating material, wherein micropores are formed in the upper coating material, perfume micro-beads are placed in the micropores, the antibacterial agent sprayed on the outer side of the coating material is nano silver ion powder, the nano silver ion powder is adhered to the outer side of the coating material, and the perfume micro-beads in the upper coating material are jasmine micro-beads or sweet-scented osmanthus micro-beads;
s5, wrapping the wrapping material outside the wrapping material, wrapping the wrapping material by a high-frequency machine, and pressing the wrapping material outside the wrapping material, wherein the wrapping material is TPU, and the thickness of the TPU is 1 mm.
In examples 1 to 3, the core sheet is used as the substrate, the core sheet is an environmentally friendly wood sheet, and then the core sheet is pressed together with the upper and lower cladding materials by the high frequency machine, the core sheet is wrapped by the soft cladding material alone with sponge or sponge and pearl wool, which is very comfortable, and the cladding material is wrapped and pressed on the outer side of the cladding material by the high frequency machine at the outer side of the cladding material, which is a TPU with very good environmental protection and safety performance, wherein the TPU is a thermoplastic polyurethane elastomer rubber, and the TPU is a high molecular material polymerized by co-reacting diisocyanate molecules such as diphenylmethane diisocyanate (MDI) or Toluene Diisocyanate (TDI), macromolecular polyol and low molecular polyol (chain extender), and does not contain prohibited materials such as plasticizer and phthalate, and the TPU has wear resistance, source resistance, low temperature resistance, oil resistance, chemical resistance, and the like, The rebound resilience is superior to that of other materials such as PVC and the like, no smell is smelled, and the toilet cover is environment-friendly and degradable and meets the use requirements, so that the toilet cover has no smell and is very comfortable to sit.
Through setting up the antibiotic agent of environment-friendly and spices microballon in cladding material department for the antibacterial property of closestool circle and closestool lid promotes, and makes closestool lid and closestool circle have light natural fragrance, and the healthy selection at home of the user of being convenient for.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (5)
1. The utility model provides a preparation technology of soft seat toilet lid of environmental protection, its characterized in that, soft seat toilet lid of environmental protection includes toilet lid and closestool circle, the middle part of toilet lid and closestool circle is provided with the board core, and the outside cladding of board core has the cladding material, and the outside of cladding material wraps up in and is equipped with the cladding material, preparation technology includes following step:
s1, selecting toilet seat and toilet cover plate core materials: the toilet seat and the toilet cover plate are made of plate cores, and the shapes of the toilet seat and the toilet cover plate are formed by pressing a wood powder molding press;
s2, polishing and grinding the pressed wood board core, and spraying environment-friendly protective paint on the board core;
s3, selecting a toilet seat and a toilet cover plate-shaped coating material, horizontally cutting the coating material, placing the plate core in the S2 between the upper layer of coating material and the lower layer of coating material, and pressing the plate core, the upper layer of coating material and the lower layer of coating material together through a high-frequency machine;
s4, adding an antibacterial agent on the coating material, wherein micropores are formed in the upper coating material, and perfume micro-beads are placed in the micropores;
s5, wrapping the wrapping material on the outer side of the wrapping material through a high-frequency machine, and pressing the wrapping material on the outer side of the wrapping material, wherein the wrapping material is TPU, and the thickness of the TPU is 0.1-1 mm.
2. The process for preparing an environment-friendly soft-seated toilet lid according to claim 1, wherein the core in S1 is a wood core or a PP core, and the thickness of the core is 5-30 mm.
3. The process for preparing an environment-friendly soft-seated toilet lid according to claim 1, wherein the coating material in S3 is sponge alone or sponge and pearl wool.
4. The process for preparing an environment-friendly soft-seated toilet lid according to claim 1, wherein the thickness of the coating material is 10-60mm, after the coating material is horizontally cut, the thickness of the upper coating material is 5-40mm, and the thickness of the lower coating material is 5-50 mm.
5. The process for preparing an environment-friendly toilet soft seat cover according to claim 4, wherein the antibacterial agent sprayed on the outer side of the coating material is nano silver ion powder, the nano silver ion powder is adhered to the outer side of the coating material, and the perfume micro-beads in the upper coating material are jasmine micro-beads or osmanthus micro-beads.