CN113100087A - 一种膨润土破碎猫砂的生产工艺 - Google Patents
一种膨润土破碎猫砂的生产工艺 Download PDFInfo
- Publication number
- CN113100087A CN113100087A CN202110441435.XA CN202110441435A CN113100087A CN 113100087 A CN113100087 A CN 113100087A CN 202110441435 A CN202110441435 A CN 202110441435A CN 113100087 A CN113100087 A CN 113100087A
- Authority
- CN
- China
- Prior art keywords
- bentonite
- composite material
- modified
- cat litter
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种膨润土破碎猫砂的生产工艺，包括以下制备工艺：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；改性膨润土载复合材料的制备工艺包括以下步骤：将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到氯化钙溶液，搅拌，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料；本发明的猫砂具有很好的抗菌性能、净化猫舍、以及避免食用的优点。
Description
技术领域
本发明属于猫砂技术领域，具体为一种膨润土破碎猫砂的生产工艺。
背景技术
猫砂是饲主为其饲养的猫用来掩埋粪便和尿液的物体，有较好的吸水性，一般会与猫砂盆(或称猫厕所)一并使用，将适量的猫砂倒于猫砂盆内，受过训练的猫当需要排泄时便会走进猫砂盆内猫屎于其上面。
对比CN109169311A公开了一种抗菌猫砂，选用纳米氢氧化铜作为抗菌剂，并选用复合微纳米材料作为载体，负载所述纳米氢氧化铜制备微纳米复合抗菌材料，之后将所述复合抗菌材料喷淋在猫砂表面，制备出所述抗菌猫砂，并对其抗菌性能、抗致病菌和长效抗菌性进行了抗菌效果验证。本发明的抗菌猫砂，通过采用上述技术方案，解决了抑制病菌的生长和抑制病菌滋长产生臭味的问题，降低了病菌的传播几率，为猫咪饲养者提供了更安全健康的生活环境。还公开了所述抗菌猫砂制备方法，在现有猫砂制备工艺的基础上，只需在喷淋造粒阶段进行改进即可实施，工艺简单，具备放大生产的条件。
现有技术中，猫砂具有着在抗菌性能方面表现不够好、不能有效去除猫舍中的臭味，以及还存在着猫等动物容易将猫砂误食到体内的问题。
发明内容
本发明的目的就在于为了解决现有技术中，猫砂具有着在抗菌性能方面表现不够好、不能有效去除猫舍中的臭味，以及还存在着猫等动物容易将猫砂误食到体内的问题，而提出一种膨润土破碎猫砂的生产工艺。
本发明的目的可以通过以下技术方案实现：
一种膨润土破碎猫砂的生产工艺，包括以下制备工艺：
第一步：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；
第二步：将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；改性膨润土载复合材料的制备工艺包括以下步骤：
将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到氯化钙溶液，搅拌30min后，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料。
优选的，控制改性膨润土载复合材料、硅藻土、凹凸棒石、沸石、除臭剂和误食剂的质量比为30-50:10-20:10-20:10-20:12-18:5-9；控制复合材料、改性膨润土、去离子、摩尔浓度为0.25mol/L的氯化钙溶液的质量比为5-10：2-5:50-80:200-400。
优选的，改性膨润土的制备工艺包括以下步骤：
将膨润土与去离子水混合，并超声分散，得到膨润土混合液；向质量分数为10％的膨润土混合液加入双十二烷基二甲基溴化铵溶液，进行混合30min，真空冷却干燥，研磨，过筛，得到改性膨润土；控制膨润土、去离子水的质量比为1-1.5:100-150；控制质量分数为10％的膨润土混合液、双十二烷基二甲基溴化铵溶液质量比为10-20:25-50。
优选的，复合材料的制备工艺包括以下步骤：
将改性壳聚糖与质量分数为2％的醋酸水溶液混合，配制质量浓度为5％的改性壳聚糖的醋酸水溶液，将质量浓度为5％的改性壳聚糖的醋酸水溶液与质量分数为5％的硝酸银水溶液中混合，并加入柠檬酸钠还原剂，置于微波反应器中，在功率600W下，反应30min后，得到改性壳聚糖和纳米银复合溶胶，再对改性壳聚糖和纳米银复合溶胶辐照70min后，冷却至室温，即得到改性壳聚糖和纳米银复合溶胶，用无水乙醇与改性壳聚糖和纳米银复合溶胶进行混合，进行过滤洗涤，再干燥，即得到复合材料；
控制壳聚糖、硝酸银和柠檬酸钠的摩尔比为3-6:1:3-6；控制壳聚糖与质量分数为2％的醋酸水溶液的质量比5-10:100-200；
改性壳聚糖的制备工艺包括以下步骤：将壳聚糖、石蜡的水溶液、乳化剂在温度30℃的条件下搅拌30min后，升温至50℃，加入硝酸铈铵，反应30min后，滴加二甲基二烯丙基氯化铵，在温度50℃的条件下反应4h后，冷却室温，加入乙醇，破乳沉淀，过滤，再依次用相同重量的石油醚、乙醇、水进行洗涤，得到改性壳聚糖；控制壳聚糖、石蜡的水溶液、乳化剂、硝酸铈铵、二甲基二烯丙基氯化铵的质量比为1:10-20:6-12：0.2-0.5:3-5；乳化剂为司盘80。
优选的，除臭剂的制备工艺包括以下步骤：
第一步：将竹炭洗净、干燥、粉碎，得到竹炭粉；将竹炭粉浸泡在质量分数为60％的氯化锌溶液中，浸泡时间8h，在温度100℃的条件下保温8h，再在温度500℃的条件下保温60min后，自然冷却至室温，再加入质量分数为10％的盐酸溶液，在温度90℃的条件下搅拌20min，过滤，去离子水洗涤至滤液为中性，滤饼干燥，得到除臭剂；控制竹炭粉、质量分数为60％的氯化锌溶液和质量分数为10％的盐酸溶液的质量比10-20:30-60:40-80。
优选的，误食剂的制备工艺包括以下步骤：
将柠檬皮粉碎，再加入到去离子水中进行煎煮30min，趁热过滤，得到滤液；
将滤液与改性吸附剂在温度65℃的条件下搅拌50min后，过滤、干燥，即得到误食剂；控制滤液与改性吸附剂的质量比为100-200：5-15。
优选的，改性吸附剂的制备工艺包括以下步骤：
第一步：将甘蔗渣清洗、烘干、粉碎，得到甘蔗渣粉末；
第二步：将摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵与去离子水混合，再加入摩尔体积分数为1mol/L的氯化铁的溶液，在室温条件下混合30min，得到A液；将甘蔗渣粉末加入到A液中，在温度60℃的条件下搅拌8h，待反应结束后，通过质量分数为20％的氨水溶液调节pH为8，得到B液；
第三步：将B液进行过滤，得到滤饼，滤饼在温度为500℃的炭化炉中进行炭化后研磨，即得到改性吸附剂。
控制甘蔗渣粉末、摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵和摩尔体积分数为1mol/L的氯化铁的溶液的用量比为80-100g：1200-1500mL：150-250mL。
与现有技术相比，本发明的有益效果是：
膨润土是以蒙脱石为主要矿物成分的非金属矿产，蒙脱石结构是由两个硅氧四面体夹一层铝氧八面体组成的2:1型晶体结构，蒙脱石具有很高的刚性，且层间不易滑移，使得蒙脱石吸附能力较弱；双十二烷基二甲基溴化铵为一种双链烷基的阳离子表面活性剂，通过双十二烷基二甲基溴化铵对蒙脱石进行插层改性，使得阳离子部分附着在蒙脱石的片层上，有机部分留在层间，使得蒙脱石的层间距增大，改善了层间的微环境，降低其表面能，使得蒙脱石对复合材料吸附性能；
壳聚糖与二甲基二烯丙基氯化铵在硝酸铈铵的引发下发生接枝反应：Ce4+先与壳聚糖残基的C2-NH2和C3-OH反应，形成一种复合物，再歧化形成-CH＝NH和-CH(OH)自由基，当温度在50℃时，-CH(OH)被铈离子氧化成碳基自由基而引发接枝反应，生产壳聚糖季铵盐，该壳聚糖季铵盐即为改性壳聚糖，该改性壳聚糖不仅兼具壳聚糖杀菌优点，还具有着季铵盐杀菌的优点；
复合材料是由改性壳聚糖的乙酸溶液为介质，通过银离子与改性壳聚糖的螯合，用柠檬酸钠还原硝酸银，微波辅助加热法制备得到的，微波激发壳聚糖分子产生大量的氨基和其他基团，改性壳聚糖通过氨基和羟基中的N原子和O原子提供孤电子对，与未配位的银离子形成共价键，同时柠檬酸钠还原作用形成纳米银粒子，由于改性壳聚糖分子链的空间位阻作用，阻碍纳米银颗粒的聚集长大，起到稳定纳米银的作用；复合材料是将改性壳聚糖与纳米银复合制成的，同时兼具着壳聚糖、季铵盐和纳米银的抗菌范围，所以本发明制备的改性膨润土载复合材料可以吸附动物中粪便，其中，蒙脱石对粪便具有吸附功能，然后复合材料对吸附的粪便中的细菌再起到杀菌的作用；
本发明以竹炭为原料，具有原料便宜易购，且含有大量的木质素和纤维素，然后，通过竹炭粉和氯化锌之间发生活化反应制备得到除臭剂，本发明制备得到的除臭剂具有比表面积大，总孔容积高的优点，所以对异味具有很好的吸附作用，所以将除臭剂添加到猫砂中，可以把尿液或粪便中的臭味紧紧吸住不散发，保持环境的空气清新无异味；
本发明的改性吸附剂是氯化铁溶液浸渍甘蔗渣的过程中，氯化铁溶液中的铁离子进入纤维孔隙，在炭化、活化过程中使纤维发生润胀水解、氧化降解反应，有利于甘蔗渣生物炭孔隙结构的形成，从而形成具有孔隙均匀、吸附性好和容量大的改性吸附剂，然后，再将改性吸附剂与柠檬皮的提取液进行混合，制备得到含有柠檬酸的误食剂，因为猫等动物对柠檬酸的气味刺激性很大，可以很好避免猫等动物将猫砂误食到体内，解决了现有技术中，很多猫咪对猫砂感兴趣，常会弄出来玩，有的猫咪还会把水晶砂吃掉，比较危险的问题；
本发明的猫砂具有很好的抗菌性能、净化猫舍、以及避免食用的优点。
具体实施方式
下面将结合实施例对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1
一种膨润土破碎猫砂的生产工艺，包括以下制备工艺：
第一步：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；
第二步：将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；改性膨润土载复合材料的制备工艺包括以下步骤：
将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到摩尔浓度为0.25mol/L的氯化钙溶液，搅拌30min后，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料。
控制改性膨润土载复合材料、硅藻土、凹凸棒石、沸石、除臭剂和误食剂的质量比为30:10:10:10:12:5；控制复合材料、改性膨润土、去离子、摩尔浓度为0.25mol/L的氯化钙溶液的质量比为5：2:50:200。
改性膨润土的制备工艺包括以下步骤：
将膨润土与去离子水混合，并超声分散，得到质量分数为10％的膨润土混合液；向质量分数为10％的膨润土混合液加入双十二烷基二甲基溴化铵溶液，进行混合30min，真空冷却干燥，研磨，过筛，得到改性膨润土；控制膨润土、去离子水的质量比为1:100；控制质量分数为10％的膨润土混合液、双十二烷基二甲基溴化铵溶液质量比为10:25。
复合材料的制备工艺包括以下步骤：
将改性壳聚糖与质量分数为2％的醋酸水溶液混合，配制质量浓度为5％的改性壳聚糖的醋酸水溶液，将质量浓度为5％的改性壳聚糖的醋酸水溶液与质量分数为5％的硝酸银水溶液中混合，并加入柠檬酸钠还原剂，置于微波反应器中，在功率600W下，反应30min后，得到改性壳聚糖和纳米银复合溶胶，再对改性壳聚糖和纳米银复合溶胶辐照70min后，冷却至室温，即得到改性壳聚糖和纳米银复合溶胶，用无水乙醇与改性壳聚糖和纳米银复合溶胶进行混合，进行过滤洗涤，再干燥，即得到复合材料；
控制改性壳聚糖、硝酸银和柠檬酸钠的摩尔比为3:1:3；控制改性壳聚糖与质量分数为2％的醋酸水溶液的质量比5:100；
改性壳聚糖的制备工艺包括以下步骤：将壳聚糖、石蜡的水溶液、乳化剂在温度30℃的条件下搅拌30min后，升温至50℃，加入硝酸铈铵，反应30min后，滴加二甲基二烯丙基氯化铵，在温度50℃的条件下反应4h后，冷却室温，加入乙醇，破乳沉淀，过滤，再依次用相同重量的石油醚、乙醇、水进行洗涤，得到改性壳聚糖；控制壳聚糖、石蜡的水溶液、乳化剂、硝酸铈铵、二甲基二烯丙基氯化铵的质量比为1:10:6：0.2:3；乳化剂为司盘80。
实施例2
一种膨润土破碎猫砂的生产工艺，包括以下制备工艺：
第一步：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；
第二步：将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；改性膨润土载复合材料的制备工艺包括以下步骤：
将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到摩尔浓度为0.25mol/L的氯化钙溶液，搅拌30min后，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料。
控制改性膨润土载复合材料、硅藻土、凹凸棒石、沸石、除臭剂和误食剂的质量比为40:15:15:15:15:7；控制复合材料、改性膨润土、去离子、摩尔浓度为0.25mol/L的氯化钙溶液的质量比为8：3:65:300。
改性膨润土的制备工艺包括以下步骤：
将膨润土与去离子水混合，并超声分散，得到质量分数为10％的膨润土混合液；向质量分数为10％的膨润土混合液加入双十二烷基二甲基溴化铵溶液，进行混合30min，真空冷却干燥，研磨，过筛，得到改性膨润土；控制膨润土、去离子水的质量比为1.3:120；控制质量分数为10％的膨润土混合液、双十二烷基二甲基溴化铵溶液质量比为15:35。
复合材料的制备工艺包括以下步骤：
将改性壳聚糖与质量分数为2％的醋酸水溶液混合，配制质量浓度为5％的改性壳聚糖的醋酸水溶液，将质量浓度为5％的改性壳聚糖的醋酸水溶液与质量分数为5％的硝酸银水溶液中混合，并加入柠檬酸钠还原剂，置于微波反应器中，在功率600W下，反应30min后，得到改性壳聚糖和纳米银复合溶胶，再对改性壳聚糖和纳米银复合溶胶辐照70min后，冷却至室温，即得到改性壳聚糖和纳米银复合溶胶，用无水乙醇与改性壳聚糖和纳米银复合溶胶进行混合，进行过滤洗涤，再干燥，即得到复合材料；
控制改性壳聚糖、硝酸银和柠檬酸钠的摩尔比为4:1:4；控制改性壳聚糖与质量分数为2％的醋酸水溶液的质量比8:150；
改性壳聚糖的制备工艺包括以下步骤：将壳聚糖、石蜡的水溶液、乳化剂在温度30℃的条件下搅拌30min后，升温至50℃，加入硝酸铈铵，反应30min后，滴加二甲基二烯丙基氯化铵，在温度50℃的条件下反应4h后，冷却室温，加入乙醇，破乳沉淀，过滤，再依次用相同重量的石油醚、乙醇、水进行洗涤，得到改性壳聚糖；控制壳聚糖、石蜡的水溶液、乳化剂、硝酸铈铵、二甲基二烯丙基氯化铵的质量比为1:15:9：0.3:4；乳化剂为司盘80。
实施例3
一种膨润土破碎猫砂的生产工艺，包括以下制备工艺：
第一步：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；
第二步：将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；改性膨润土载复合材料的制备工艺包括以下步骤：
将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到摩尔浓度为0.25mol/L的氯化钙溶液，搅拌30min后，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料。
控制改性膨润土载复合材料、硅藻土、凹凸棒石、沸石、除臭剂和误食剂的质量比为50:20:20:20:18:9；控制复合材料、改性膨润土、去离子、摩尔浓度为0.25mol/L的氯化钙溶液的质量比为10：5:80:400。
改性膨润土的制备工艺包括以下步骤：
将膨润土与去离子水混合，并超声分散，得到质量分数为10％的膨润土混合液；向质量分数为10％的膨润土混合液加入双十二烷基二甲基溴化铵溶液，进行混合30min，真空冷却干燥，研磨，过筛，得到改性膨润土；控制膨润土、去离子水的质量比为1.5:150；控制质量分数为10％的膨润土混合液、双十二烷基二甲基溴化铵溶液质量比为20:50。
复合材料的制备工艺包括以下步骤：
将壳聚糖与质量分数为2％的醋酸水溶液混合，配制质量浓度为5％的壳聚糖的醋酸水溶液，将质量浓度为5％的壳聚糖的醋酸水溶液与质量分数为5％的硝酸银水溶液中混合，并加入柠檬酸钠还原剂，置于微波反应器中，在功率600W下，反应30min后，得到壳聚糖和纳米银复合溶胶，再对壳聚糖和纳米银复合溶胶辐照70min后，冷却至室温，即得到壳聚糖和纳米银复合溶胶，用无水乙醇与壳聚糖和纳米银复合溶胶进行混合，进行过滤洗涤，再干燥，即得到复合材料；
控制壳聚糖、硝酸银和柠檬酸钠的摩尔比为6:1:6；控制壳聚糖与质量分数为2％的醋酸水溶液的质量比10:200；
改性壳聚糖的制备工艺包括以下步骤：将壳聚糖、石蜡的水溶液、乳化剂在温度30℃的条件下搅拌30min后，升温至50℃，加入硝酸铈铵，反应30min后，滴加二甲基二烯丙基氯化铵，在温度50℃的条件下反应4h后，冷却室温，加入乙醇，破乳沉淀，过滤，再依次用相同重量的石油醚、乙醇、水进行洗涤，得到改性壳聚糖；控制壳聚糖、石蜡的水溶液、乳化剂、硝酸铈铵、二甲基二烯丙基氯化铵的质量比为1:20:12：0.5:5；乳化剂为司盘80。
实施例4
除臭剂的制备工艺包括以下步骤：
第一步：将竹炭洗净、干燥、粉碎，得到竹炭粉；将竹炭粉浸泡在质量分数为60％的氯化锌溶液中，浸泡时间8h，在温度100℃的条件下保温8h，再在温度500℃的条件下保温60min后，自然冷却至室温，再加入质量分数为10％的盐酸溶液，在温度90℃的条件下搅拌20min，过滤，去离子水洗涤至滤液为中性，滤饼干燥，得到除臭剂；控制竹炭粉、质量分数为60％的氯化锌溶液和质量分数为10％的盐酸溶液的质量比10:30:40。
误食剂的制备工艺包括以下步骤：
将柠檬皮粉碎，再加入到去离子水中进行煎煮30min，趁热过滤，得到滤液；
将滤液与改性吸附剂在温度65℃的条件下搅拌50min后，过滤、干燥，即得到误食剂；控制滤液与改性吸附剂的质量比为100：5。
改性吸附剂的制备工艺包括以下步骤：
第一步：将甘蔗渣清洗、烘干、粉碎，得到甘蔗渣粉末；
第二步：将摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵与去离子水混合，再加入摩尔体积分数为1mol/L的氯化铁的溶液，在室温条件下混合30min，得到A液；将甘蔗渣粉末加入到A液中，在温度60℃的条件下搅拌8h，待反应结束后，通过质量分数为20％的氨水溶液调节pH为8，得到B液；
第三步：将B液进行过滤，得到滤饼，滤饼在温度为500℃的炭化炉中进行炭化后研磨，即得到改性吸附剂。
控制甘蔗渣粉末、摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵和摩尔体积分数为1mol/L的氯化铁的溶液的用量比为80g：1200mL：150mL。
实施例5
除臭剂的制备工艺包括以下步骤：
第一步：将竹炭洗净、干燥、粉碎，得到竹炭粉；将竹炭粉浸泡在质量分数为60％的氯化锌溶液中，浸泡时间8h，在温度100℃的条件下保温8h，再在温度500℃的条件下保温60min后，自然冷却至室温，再加入质量分数为10％的盐酸溶液，在温度90℃的条件下搅拌20min，过滤，去离子水洗涤至滤液为中性，滤饼干燥，得到除臭剂；控制竹炭粉、质量分数为60％的氯化锌溶液和质量分数为10％的盐酸溶液的质量比15:45:60。
误食剂的制备工艺包括以下步骤：
将柠檬皮粉碎，再加入到去离子水中进行煎煮30min，趁热过滤，得到滤液；
将滤液与改性吸附剂在温度65℃的条件下搅拌50min后，过滤、干燥，即得到误食剂；控制滤液与改性吸附剂的质量比为150：10。
改性吸附剂的制备工艺包括以下步骤：
第一步：将甘蔗渣清洗、烘干、粉碎，得到甘蔗渣粉末；
第二步：将摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵与去离子水混合，再加入摩尔体积分数为1mol/L的氯化铁的溶液，在室温条件下混合30min，得到A液；将甘蔗渣粉末加入到A液中，在温度60℃的条件下搅拌8h，待反应结束后，通过质量分数为20％的氨水溶液调节pH为8，得到B液；
第三步：将B液进行过滤，得到滤饼，滤饼在温度为500℃的炭化炉中进行炭化后研磨，即得到改性吸附剂。
控制甘蔗渣粉末、摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵和摩尔体积分数为1mol/L的氯化铁的溶液的用量比为90g：1400mL：200mL。
实施例6
除臭剂的制备工艺包括以下步骤：
第一步：将竹炭洗净、干燥、粉碎，得到竹炭粉；将竹炭粉浸泡在质量分数为60％的氯化锌溶液中，浸泡时间8h，在温度100℃的条件下保温8h，再在温度500℃的条件下保温60min后，自然冷却至室温，再加入质量分数为10％的盐酸溶液，在温度90℃的条件下搅拌20min，过滤，去离子水洗涤至滤液为中性，滤饼干燥，得到除臭剂；控制竹炭粉、质量分数为60％的氯化锌溶液和质量分数为10％的盐酸溶液的质量比20:60:80。
误食剂的制备工艺包括以下步骤：
将柠檬皮粉碎，再加入到去离子水中进行煎煮30min，趁热过滤，得到滤液；
将滤液与改性吸附剂在温度65℃的条件下搅拌50min后，过滤、干燥，即得到误食剂；控制滤液与改性吸附剂的质量比为200：15。
改性吸附剂的制备工艺包括以下步骤：
第一步：将甘蔗渣清洗、烘干、粉碎，得到甘蔗渣粉末；
第二步：将摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵与去离子水混合，再加入摩尔体积分数为1mol/L的氯化铁的溶液，在室温条件下混合30min，得到A液；将甘蔗渣粉末加入到A液中，在温度60℃的条件下搅拌8h，待反应结束后，通过质量分数为20％的氨水溶液调节pH为8，得到B液；
第三步：将B液进行过滤，得到滤饼，滤饼在温度为500℃的炭化炉中进行炭化后研磨，即得到改性吸附剂。
控制甘蔗渣粉末、摩尔体积分数为0.05mol/L的溴化十六烷基三甲基氯化铵和摩尔体积分数为1mol/L的氯化铁的溶液的用量比为100g：1500mL：250mL。
对比例1
对比例1为市售的猫砂：
对实施例1-3和对比例1的性能进行检测，结果如下表所示：
| 杀菌率(％) | 吸附值(cm<sup>3</sup>/g) | |
| 实施例1 | 94.63 | 2981 |
| 实施例2 | 95.11 | 3035 |
| 实施例3 | 95.76 | 3594 |
| 对比例1 | 56.89 | 568 |
本发明以纸对大肠杆菌和金黄色葡萄球菌为菌种检测制备得到的膨润土破碎猫砂的杀菌率，其实施例1-3的杀菌率在94.63-95.76％，相对于对比例的猫砂具有很好的抗菌性能；对猫砂环境中的空气进行吸附，其中实施例1-3的吸附值在2981-3594cm3/g远大于对比例的猫砂，所以，本发明的猫砂具有很好的抗菌性能、净化猫舍的优点。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节，也不限制该发明仅为的具体实施方式。显然，根据本说明书的内容，可作很多的修改和变化。本说明书选取并具体描述这些实施例，是为了更好地解释本发明的原理和实际应用，从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (4)
1.一种膨润土破碎猫砂的生产工艺，包括以下步骤：
第一步：将改性膨润土载复合材料、硅藻土、凹凸棒石、沸石为原料，输送至挤压机内，挤压成柱状块料；
第二步：将柱状块料烘干、粉碎、造粒、再烘干、筛分，即得到膨润土破碎猫砂，造粒的同时加入除臭剂和误食剂；其特征在于：改性膨润土载复合材料的制备工艺包括以下步骤：
将复合材料、改性膨润土加入到去离子水中，并超声分散，得到复合材料的水溶液，将复合材料的水溶液滴加到氯化钙溶液，搅拌30min后，过滤，用去离子水洗涤，干燥，得到改性膨润土载复合材料；
其中，复合材料的制备工艺包括以下步骤：
将改性壳聚糖的醋酸水溶液与硝酸银水溶液中混合，并加入柠檬酸钠还原剂，置于微波反应器中反应，得到改性壳聚糖和纳米银复合溶胶，再对改性壳聚糖和纳米银复合溶胶辐照70min后，冷却至室温，即得到改性壳聚糖和纳米银复合溶胶，用无水乙醇与改性壳聚糖和纳米银复合溶胶进行混合，过滤洗涤，再干燥，即得到复合材料。
2.根据权利要求1所述的一种膨润土破碎猫砂的生产工艺，其特征在于，控制改性膨润土载复合材料、硅藻土、凹凸棒石、沸石、除臭剂和误食剂的质量比为30-50:10-20:10-20:10-20:12-18:5-9；控制复合材料、改性膨润土、去离子、氯化钙溶液的质量比为5-10：2-5:50-80:200-400。
3.根据权利要求1所述的一种膨润土破碎猫砂的生产工艺，其特征在于，改性膨润土的制备工艺包括以下步骤：
将膨润土与去离子水混合，并超声分散，得到质量分数为10％的膨润土混合液；向质量分数为10％的膨润土混合液加入双十二烷基二甲基溴化铵溶液，进行混合30min，真空冷却干燥，研磨，过筛，得到改性膨润土。
4.根据权利要求1所述的一种膨润土破碎猫砂的生产工艺，其特征在于，改性壳聚糖的制备工艺包括以下步骤：
将壳聚糖、石蜡的水溶液、乳化剂在温度30℃的条件下搅拌30min后，升温至50℃，加入硝酸铈铵，反应30min后，滴加二甲基二烯丙基氯化铵，在温度50℃的条件下反应4h后，冷却室温，加入乙醇，破乳沉淀，过滤，再依次用相同重量的石油醚、乙醇、水进行洗涤，得到改性壳聚糖。