CN113072892A - 一种双面抗静电pet保护膜 - Google Patents
一种双面抗静电pet保护膜 Download PDFInfo
- Publication number
- CN113072892A CN113072892A CN202110409818.9A CN202110409818A CN113072892A CN 113072892 A CN113072892 A CN 113072892A CN 202110409818 A CN202110409818 A CN 202110409818A CN 113072892 A CN113072892 A CN 113072892A
- Authority
- CN
- China
- Prior art keywords
- pet
- antistatic
- film layer
- film
- pps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种双面抗静电PET保护膜，涉及PET保护膜技术领域，为解决现有抗静电PET保护膜的耐高温性能一般，在高温环境下，边缘处易回缩卷曲的问题。所述双面抗静电保护膜主体绕卷在卷筒的外壁上，所述双面抗静电保护膜主体的内部设置有基膜层，所述基膜层包括PET高透明原膜层、第一PPS透明薄膜层和第二PPS透明薄膜层，所述第一PPS透明薄膜层和第二PPS透明薄膜层分别设置在PET高透明原膜层的上表面和下表面，所述基膜层的上表面设置有PET硬化膜，所述PET硬化膜的上表面设置有第一PET离型膜，所述基膜层的下表面设置有抗静电硅胶粘合剂，所述抗静电硅胶粘合剂的下表面设置有第二PET离型膜，所述第二PET离型膜的下表面设置有除尘基层。
Description
技术领域
本发明涉及PET保护膜技术领域，具体为一种双面抗静电PET保护膜。
背景技术
因为PET材质具有重量轻，强度高，透明性和阻气性好，无毒，无味等优点，获得迅速的发展。进入90年代以来塑料包装材料的生产和应用如同雨后春笋般的发展起来，而后随着触控技术的成熟，PET材料也就顺理成章的用到了各种液晶显示屏上，也就是今天的PET保护膜。PET保护膜材料为透明无色的，表面经过了硬化处理，一般PET保护膜材料根据产地的不同，表面的硬化值在3H-4H之间，表面硬化越好，其耐磨性越强。透光率也是PET保护膜材料的主要性质，一般透光率在90％以上。而PET抗静电保护膜是以防静电处理的聚酯薄膜作为基材，涂布丙烯酸胶粘剂与防静电处理层并贴合离型膜而成，具有防止灰尘和杂质吸附以及防止静电损伤功能的表面保护材料。
但是，现有抗静电PET保护膜的耐高温性能一般，在高温环境下，边缘处易回缩卷曲；因此，不满足现有的需求，对此我们提出了一种双面抗静电PET保护膜。
发明内容
本发明的目的在于提供一种双面抗静电PET保护膜，以解决上述背景技术中提出的现有抗静电PET保护膜的耐高温性能一般，在高温环境下，边缘处易回缩卷曲的问题。
为实现上述目的，本发明提供如下技术方案：一种双面抗静电PET保护膜，包括双面抗静电保护膜主体和卷筒，所述双面抗静电保护膜主体绕卷在卷筒的外壁上，所述双面抗静电保护膜主体的内部设置有基膜层，所述基膜层包括PET高透明原膜层、第一PPS透明薄膜层和第二PPS透明薄膜层，所述第一PPS透明薄膜层和第二PPS透明薄膜层分别设置在PET高透明原膜层的上表面和下表面，所述基膜层的上表面设置有PET硬化膜，所述PET硬化膜的上表面设置有第一PET离型膜，所述基膜层的下表面设置有抗静电硅胶粘合剂，所述抗静电硅胶粘合剂的下表面设置有第二PET离型膜，所述第二PET离型膜的下表面设置有除尘基层。
优选的，所述PET高透明原膜层与第一PPS透明薄膜层和第二PPS透明薄膜层之间通过挤出复合法连接，所述PET高透明原膜层的厚度为40±2μm，所述第一PPS透明薄膜层和第二PPS透明薄膜层的厚度为15±2μm。
优选的，所述抗静电硅胶粘合剂由粘性为500g/in至5000g/in的硅胶与3％-5％的抗静电剂混合而成，所述抗静电硅胶粘合剂的厚度为5-10μm。
优选的，所述PET硬化膜的厚度为25±2μm，所述PET硬化膜通过粘黏剂与基膜层固定连接。
优选的，所述PET硬化膜的外壁上设置有抗静电抗菌涂层，所述抗静电抗菌涂层的厚度为2-4μm。
优选的，所述抗静电抗菌涂层由抗静电涂料与0.5-2％的锌离子抗菌剂混合制备而成。
优选的，所述除尘基层包括超细涤棉纤维层和胶涂层，且胶涂层设置在超细涤棉纤维层的上表面。
优选的，所述卷筒的两端均设置有连接头，所述连接头的一端安装有十字支撑杆，所述十字支撑杆上安装有加固杆，且加固杆与十字支撑杆焊接连接，所述十字支撑杆下方的两端均安装有橡胶减震球，所述橡胶减震球的外壁上设置有防滑纹，且防滑纹与橡胶减震球为一体结构。
优选的，所述十字支撑杆上方的两端安装有塑料对接头，所述塑料对接头的内部设置有半球形槽。
与现有技术相比，本发明的有益效果是：
1、本发明通过在PET高透明原膜层的上表面和下表面分别设置第一PPS透明薄膜层和第二PPS透明薄膜层，且三者间采用挤出复合法连接，挤出复合法是将PPS透明薄膜原料经热熔挤出后，淋在PET高透明原膜层上，再经由压合冷却的复合加工工艺，复合后的基膜层既具有PET材料的良好耐弯折、耐水气性能，又依靠PPS材料弥补了耐高温性的不足，使得保护膜具有较好的阻燃性能，同时两者均具有良好的耐化学腐蚀性能，使用寿命长，避免了现有抗静电PET保护膜的耐高温性能一般，在高温环境下，边缘处易回缩卷曲的情况发生。
2、通过在PET硬化膜外层的抗静电涂层内添加0.5-2％的锌离子抗菌剂，锌离子抗菌剂是以亚微米玻璃和磷酸锆为载体，搭载安全、高能效抗菌锌离子的一种助剂，本色透明，不会影响到薄膜的透明度，采用锌离子作为抗菌剂，对人体安全无害，其能通过对细菌蛋白质进行干扰破坏，实现广谱的抗菌效果，对含有蛋白质衣壳的各类真菌具有较好的抑制作用，尤其针对疫情严重地区，具有较好的泛用性。
3、通过在第二PET离型膜的表面设置除尘基层，在准备贴膜前，可先将除尘基层揭下，利用基层内壁的胶涂层将其贴附于需要粘附保护膜的产品表面，贴附平整后，将其撕下，以去除产品表面的粉尘，除尘基层背面为超细涤棉纤维层，除尘完毕后可利用超细涤棉纤维层擦拭产品表面，保证贴附面的整洁度，以确保后续贴膜质量。
4、通过在保护膜卷筒的两端设置十字支撑杆，十字支撑杆下端为橡胶减震球，其表面设有防滑纹，具有较好的减震防滑性能，避免薄膜触地，且保证了放置时的稳定性，当需要运输时，可将卷筒堆叠组合，利用十字支撑杆下端的橡胶减震球与上端的塑料对接头卡合固定，实现连接，既保证了运输平稳，又能避免薄膜间相互接触，导致外层磨损的情况发生。
附图说明
图1为本发明的整体结构示意图；
图2为本发明的双面抗静电保护膜主体分层结构示意图；
图3为本发明的基膜层结构示意图；
图4为本发明的除尘基层结构示意图；
图5为本发明的双面抗静电保护膜主体复合结构示意图；
图中：1、双面抗静电保护膜主体；2、卷筒；3、连接头；4、十字支撑杆；5、加固杆；6、橡胶减震球；7、防滑纹；8、塑料对接头；9、半球形槽；10、基膜层；101、PET高透明原膜层；102、第一PPS透明薄膜层；103、第二PPS透明薄膜层；11、PET硬化膜；12、第一PET离型膜；13、抗静电硅胶粘合剂；14、第二PET离型膜；15、除尘基层；151、超细涤棉纤维层；152、胶涂层；16、粘黏剂；17、抗静电抗菌涂层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
请参阅图1-5，本发明提供的一种实施例：一种双面抗静电PET保护膜，包括双面抗静电保护膜主体1和卷筒2，双面抗静电保护膜主体1绕卷在卷筒2的外壁上，双面抗静电保护膜主体1的内部设置有基膜层10，基膜层10包括PET高透明原膜层101、第一PPS透明薄膜层102和第二PPS透明薄膜层103，第一PPS透明薄膜层102和第二PPS透明薄膜层103分别设置在PET高透明原膜层101的上表面和下表面，基膜层10的上表面设置有PET硬化膜11，PET硬化膜11的上表面设置有第一PET离型膜12，基膜层10的下表面设置有抗静电硅胶粘合剂13，抗静电硅胶粘合剂13的下表面设置有第二PET离型膜14，第二PET离型膜14的下表面设置有除尘基层15。
进一步，PET高透明原膜层101与第一PPS透明薄膜层102和第二PPS透明薄膜层103之间通过挤出复合法连接，PET高透明原膜层101的厚度为40±2μm，第一PPS透明薄膜层102和第二PPS透明薄膜层103的厚度为15±2μm，挤出复合法是将PPS透明薄膜原料经热熔挤出后，淋在PET高透明原膜层101上，再经由压合冷却的复合加工工艺，复合后的基膜层10既具有PET材料的良好耐弯折、耐水气性能，又依靠PPS材料弥补了耐高温性的不足，使得保护膜具有较好的阻燃性能，同时两者均具有良好的耐化学腐蚀性能，使用寿命长。
进一步，抗静电硅胶粘合剂13由粘性为500g/in至5000g/in的硅胶与3％-5％的抗静电剂混合而成，抗静电硅胶粘合剂13的厚度为5-10μm，底层的抗静电硅胶粘合剂13与外层的抗静电抗菌涂层17均具有较好的抗静电性能，能够防止静电损伤电子产品。
进一步，PET硬化膜11的厚度为25±2μm，PET硬化膜11通过粘黏剂16与基膜层10固定连接，粘黏剂16为粘性为500g/in至5000g/in的压敏胶，PET硬化膜11经由HC硬化处理，具有较好的耐磨防刮性能，能够对贴附的产品起到良好的保护效果。
进一步，PET硬化膜11的外壁上设置有抗静电抗菌涂层17，抗静电抗菌涂层17的厚度为2-4μm，抗静电抗菌涂层17使得PET硬化膜11表面具有防静电以及防菌的性能。
进一步，抗静电抗菌涂层17由抗静电涂料与0.5-2％的锌离子抗菌剂混合制备而成，锌离子抗菌剂以亚微米玻璃和磷酸锆为载体，搭载安全、高能效抗菌锌离子的一种助剂，本色透明，不会影响到薄膜的透明度，采用锌离子作为抗菌剂，对人体安全无害，其能通过对细菌蛋白质进行干扰破坏，实现广谱的抗菌效果，对含有蛋白质衣壳的各类真菌具有较好的抑制作用，尤其针对疫情严重地区，具有较好的泛用性。
进一步，除尘基层15包括超细涤棉纤维层151和胶涂层152，且胶涂层152设置在超细涤棉纤维层151的上表面，在使用时，可将除尘基层15从第二PET离型膜14上揭下，利用内层的胶涂层152贴附于需要粘附保护膜的产品表面，贴附平整后，将其撕下，以去除产品表面的粉尘，完毕后再利用背面的超细涤棉纤维层151擦拭产品表面，即可保证贴附面的整洁度，保证后续贴膜质量。
进一步，卷筒2的两端均设置有连接头3，连接头3的一端安装有十字支撑杆4，十字支撑杆4上安装有加固杆5，且加固杆5与十字支撑杆4焊接连接，十字支撑杆4下方的两端均安装有橡胶减震球6，橡胶减震球6的外壁上设置有防滑纹7，且防滑纹7与橡胶减震球6为一体结构，卷筒2两侧的采用十字支撑杆4结构，其下端的橡胶减震球6能够保证薄膜放置和运输时的稳定性。
进一步，十字支撑杆4上方的两端安装有塑料对接头8，塑料对接头8的内部设置有半球形槽9，在运输时，可将卷筒2堆叠组合，利用十字支撑杆4下端的橡胶减震球6与上端的塑料对接头8卡合固定，实现连接，既保证了运输时的稳定性，又能避免薄膜间相互接触，导致外层磨损的情况发生。
工作原理：使用时，首先拉伸出适当长度的双面抗静电保护膜主体1，进行裁切，之后将第二PET离型膜14表面的除尘基层15揭下，利用基层内壁的胶涂层152将其贴附于需要粘附保护膜的产品表面，贴附平整后，将其撕下，以去除产品表面的粉尘，除尘基层15背面为超细涤棉纤维层151，除尘完毕后可利用超细涤棉纤维层151擦拭产品表面，保证贴附面的整洁度，以确保后续贴膜质量，之后将第二PET离型膜14撕下，外露出抗静电硅胶粘合剂13，利用抗静电硅胶粘合剂13将双面抗静电保护膜主体1贴附于产品表面，完毕后撕取表层的第一PET离型膜12，即可完成保护膜的贴附工作，双面抗静电保护膜主体1的外壁和内壁分别为抗静电硅胶粘合剂13和抗静电抗菌涂层17，两者均含有高分子导电聚合物，电阻率低，性能稳定，且不受环境温湿度的影响，具有较好的抗静电性能，能够防止静电损伤电子产品，其中抗静电抗菌涂层17的内部还混合有0.5-2％的锌离子抗菌剂，锌离子抗菌剂是以亚微米玻璃和磷酸锆为载体，搭载安全、高能效抗菌锌离子的一种助剂，本色透明，不会影响到薄膜的透明度，对人体安全无害，其能通过对细菌蛋白质进行干扰破坏，实现广谱的抗菌效果，对含有蛋白质衣壳的各类真菌具有较好的抑制作用，尤其针对疫情严重地区，具有较好的泛用性，保护膜的基膜层10采用PET高透明原膜层101和PPS透明薄膜层挤出复合而成，既具有PET材料的良好耐弯折、耐水气性能，又依靠PPS材料弥补了耐高温性的不足，使得保护膜具有较好的阻燃性能，同时两者均具有良好的耐化学腐蚀性能，使用寿命长，该保护膜的卷筒2两端设置有十字支撑杆4，十字支撑杆4下端为橡胶减震球6，其表面设有防滑纹7，具有较好的减震防滑性能，避免薄膜触地，且保证了放置时的稳定性，当需要运输时，可将卷筒2堆叠组合，利用十字支撑杆4下端的橡胶减震球6与上端的塑料对接头8卡合固定，实现连接，既保证了运输平稳，又能避免薄膜间相互接触，导致外层磨损的情况发生。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
Claims (9)
1.一种双面抗静电PET保护膜，包括双面抗静电保护膜主体(1)和卷筒(2)，其特征在于：所述双面抗静电保护膜主体(1)绕卷在卷筒(2)的外壁上，所述双面抗静电保护膜主体(1)的内部设置有基膜层(10)，所述基膜层(10)包括PET高透明原膜层(101)、第一PPS透明薄膜层(102)和第二PPS透明薄膜层(103)，所述第一PPS透明薄膜层(102)和第二PPS透明薄膜层(103)分别设置在PET高透明原膜层(101)的上表面和下表面，所述基膜层(10)的上表面设置有PET硬化膜(11)，所述PET硬化膜(11)的上表面设置有第一PET离型膜(12)，所述基膜层(10)的下表面设置有抗静电硅胶粘合剂(13)，所述抗静电硅胶粘合剂(13)的下表面设置有第二PET离型膜(14)，所述第二PET离型膜(14)的下表面设置有除尘基层(15)。
2.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述PET高透明原膜层(101)与第一PPS透明薄膜层(102)和第二PPS透明薄膜层(103)之间通过挤出复合法连接，所述PET高透明原膜层(101)的厚度为40±2μm，所述第一PPS透明薄膜层(102)和第二PPS透明薄膜层(103)的厚度为15±2μm。
3.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述抗静电硅胶粘合剂(13)由粘性为500g/in至5000g/in的硅胶与3％-5％的抗静电剂混合而成，所述抗静电硅胶粘合剂(13)的厚度为5-10μm。
4.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述PET硬化膜(11)的厚度为25±2μm，所述PET硬化膜(11)通过粘黏剂(16)与基膜层(10)固定连接。
5.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述PET硬化膜(11)的外壁上设置有抗静电抗菌涂层(17)，所述抗静电抗菌涂层(17)的厚度为2-4μm。
6.根据权利要求5所述的一种双面抗静电PET保护膜，其特征在于：所述抗静电抗菌涂层(17)由抗静电涂料与0.5-2％的锌离子抗菌剂混合制备而成。
7.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述除尘基层(15)包括超细涤棉纤维层(151)和胶涂层(152)，且胶涂层(152)设置在超细涤棉纤维层(151)的上表面。
8.根据权利要求1所述的一种双面抗静电PET保护膜，其特征在于：所述卷筒(2)的两端均设置有连接头(3)，所述连接头(3)的一端安装有十字支撑杆(4)，所述十字支撑杆(4)上安装有加固杆(5)，且加固杆(5)与十字支撑杆(4)焊接连接，所述十字支撑杆(4)下方的两端均安装有橡胶减震球(6)，所述橡胶减震球(6)的外壁上设置有防滑纹(7)，且防滑纹(7)与橡胶减震球(6)为一体结构。
9.根据权利要求8所述的一种双面抗静电PET保护膜，其特征在于：所述十字支撑杆(4)上方的两端安装有塑料对接头(8)，所述塑料对接头(8)的内部设置有半球形槽(9)。