CN1130509C - 具有阻燃塑料层的铝塑复合管 - Google Patents
具有阻燃塑料层的铝塑复合管 Download PDFInfo
- Publication number
- CN1130509C CN1130509C CN 00110515 CN00110515A CN1130509C CN 1130509 C CN1130509 C CN 1130509C CN 00110515 CN00110515 CN 00110515 CN 00110515 A CN00110515 A CN 00110515A CN 1130509 C CN1130509 C CN 1130509C
- Authority
- CN
- China
- Prior art keywords
- aluminium
- plastic
- composite pipe
- layer
- layers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种铝塑复合管材。其管材为五层结构，中间为铝质层，内外层为塑料层，内外塑料层与铝质层之间为热熔胶，在内外层聚乙烯内填加阻燃剂，有十溴联苯醚、三氧化二锑及红磷，按比例加入塑料内，经加工制成铝塑复合管材。优点：制造工艺简单，生产容易，无需增加特殊设备，塑料中填加阻燃剂，生产的管材具有很强的阻燃性能，可广泛应用在各个领域，代替金属管材具有很大的社会效益和经济效益。
Description
技术领域
本发明涉及一种铝塑材质的复合管材。
背景技术
目前，在很多领域中采用铝塑复合管代替金属管材，铝塑复合管是由一种内外层聚烯烃塑料、铝层，铝层与内外塑料层之间通过热熔胶粘接而成的具有五层结构的管型材料，其优点是它具有塑料管材的防腐性能和金属管材的强度，小管径管材可以弯曲，金属层可以屏蔽电信号，适用作电线、电缆穿线管，但其不足是由于复合管材用的内外层塑料主要是聚烯烃类材料聚乙烯、聚丙烯为主，这类塑料是易燃品，不符合电线、电缆、化工流体和燃气管的阻燃使用性能，给工业上应用安全生产带来不便。
发明内容
为解决铝塑复合管材阻燃性能差的不足，本发明的目的提供一种具有阻燃塑料层的铝塑复合管，利用填加阻燃剂的制备方法，制造出铝塑复合管，以达到具有阻燃的性能。
本发明具有阻燃塑料层的铝塑复合管由五层组成(如附图所示)，内外层为聚烯烃，中间层为铝材质，内外层分别与中间层之间填加热熔胶。此复合管所用材质及重量百分比为：
内外层聚烯烃 60～80％
中间铝材质层 10～29.33％
铝塑间热熔胶 0.5～15％
其中聚烯烃材料为高密度聚乙烯、中密度聚乙烯、低密度聚乙烯、线性低密度聚乙烯、醋酸乙烯脂共聚物、聚丙烯材料；铝材质层铝带牌号为8011A、1145、1235、1100、1200、1050、1060，状态0或H22的高等级软铝；热熔胶为丙烯酸或马来酸酐改性聚乙烯。
另外在内外层聚烯烃中加有阻燃剂，占有聚烯烃重量的3～30％，阻燃剂由一种至三种材料组成：
其中三种材料为：十溴联苯醚、三氧化二锑、红磷
重量比为：十溴联苯醚 40～50％
三氧化二锑 40～50％
红 磷 5～20％
二种材料为：十溴联苯醚与三氧化二锑
重量比为：十溴联苯醚 50～60％
三氧化二锑 40～50％
一种材料为：单独使用改性红磷，自身重量比为100％。
三种配方中，其中任何一种配方都能使铝塑复合管的塑料层达到V0级阻燃效果。
本复合管材的制备方法：
制造设备采用搭接焊式铝塑复合管挤出机组成生产塑料层阻燃的铝塑复合管，制备过程：生产线上，铝带开卷成型后，内塑料层挤出机挤出内塑料层，内粘接层挤出机将热熔胶挤出在内塑料层管外壁，铝带包在涂有热熔胶的内塑管上，用超声波焊接机连续在搭接处焊接后，再通过外层胶挤出机涂上热熔胶，加工温度为190～240℃之间，同时通过外塑料层挤出机挤出含有阻燃剂的外层塑料层，这时将含有内外阻燃塑料层的铝塑复合管通过水槽冷却、切割、包装后成成品。
本发明的优点：制造工艺简单，生产容易，无需增加特殊设备，塑料中填加阻燃剂，生产的管材具有很强的阻燃性能，可广泛应用在各种领域，代替金属管材具有很大的社会效益和经济效益。
本发明具有阻燃塑料层的铝塑复合管其结构如附图给出。
附图说明
图1为具有阻燃塑料层的铝塑复合管结构图。
其中：1、5为内外层聚乙烯，2、4为专用热熔胶，3为铝管，6为铝管焊缝。
具体实施方式
本发明之实施例：
例1
1)内外塑料层材料总重量为100kg，阻燃剂为两种材料：
高密度聚乙烯 80kg
十溴联苯醚 10kg
三氧化二锑 10kg
将上述三种原料按上述比例在高速搅拌机内搅均后，把混合物71.7kg和28.3kg分别加入铝塑管生产线内外层挤出机料斗内，加工温度为190～240℃之间进行。
2)内外粘接层用丙烯酸改性聚乙烯热熔胶作粘接剂，重量12.5kg，把6.1kg和6.4kg热熔胶分别加入内外层粘接剂挤出机，加工温度190～240℃。
3)铝带用型号为8011、状态0的高等级软铝，规格为0.2×49mm，重量为46.7kg。
加工过程：铝带开卷成型后，内塑料层挤出机挤出内塑料层，内粘接层挤出机将热熔胶挤出在内塑料层管外壁，铝带包在涂有热熔胶的内塑管上，用超声波焊接机连续在搭接处焊接后，再通过外层胶挤出机涂上热熔胶，加工温度为190～240℃之间，同时通过外塑料层挤出机挤出含有阻燃剂的塑料层，这时将含有内外阻燃塑料层的铝塑复合管通过水模冷却、切割、包装后成成品。
例2：阻燃剂为三种材料：
取高密度聚乙烯 80kg
十溴联苯醚 8kg
三氧化二锑 8kg
红磷 4kg
其它原料与例1相同。
例3：阻燃剂为一种材料：
取高密度聚乙烯 85kg
红磷 15kg
其它原料与例1相同。
制备方法同上。
Claims (4)
1.一种具有阻燃塑料层的铝塑复合管，它是由五层组成，内外层为聚烯烃，中间层为铝材质，内外层分别与中间层之间填加热熔胶，其特征是此复合管所用材质及重量百分比为：
内外层聚烯烃 60～80％
中间铝材质层 10～29.33％
铝塑间热熔胶 0.5～15％
其中在内外层聚烯烃中加有阻燃剂，占有聚烯烃重量的3～30％，阻燃剂由一种至三种材料组成：
其中三种材料为：十溴联苯醚、三氧化二锑、红磷
重量比为：十溴联苯醚 40～50％
三氧化二锑 40～50％
红 磷 5～20％
二种材料为：十溴联苯醚与三氧化二锑
重量比为：十溴联苯醚 50～60％
三氧化二锑 40～50％
一种材料为：单独使用改性红磷，自身重量比为100％。
2.按权利要求1所述之铝塑复合管，其特征是所用聚烯烃材料为高密度聚乙烯、中密度聚乙烯、低密度聚乙烯、线性低密度聚乙烯、醋酸乙烯酯共聚物、聚丙烯材料。
3.按权利要求1所述之铝塑复合管，其特征是所用铝材质层铝带牌号为8011A、1145、1235、1100、1200、1050、1060，状态0或H22的高等级软铝。
4.按权利要求1所述之铝塑复合管，其特征是所用热熔胶为丙烯酸或马来酸酐改性聚乙烯。