CN112981989A - Printing and dyeing additive and method for dyeing real silk/viscose composite fabric - Google Patents
Printing and dyeing additive and method for dyeing real silk/viscose composite fabric Download PDFInfo
- Publication number
- CN112981989A CN112981989A CN202110220269.0A CN202110220269A CN112981989A CN 112981989 A CN112981989 A CN 112981989A CN 202110220269 A CN202110220269 A CN 202110220269A CN 112981989 A CN112981989 A CN 112981989A
- Authority
- CN
- China
- Prior art keywords
- parts
- composition
- dyeing
- real silk
- composite fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of printing and dyeing industry, in particular to a printing and dyeing additive, which comprises a composition A and a composition B, wherein the composition A and the composition B respectively comprise the following components in parts by weight: composition A: 20-45 parts of urea, 10-15 parts of sodium acetate, 5-10 parts of sodium metaborate, 1-5 parts of potassium citrate, 1-3 parts of xanthan gum and 1000 parts of water; composition B: 10-30 parts of aminosilane coupling agent, 20-30 parts of deacetylated chitin, 100-200 parts of methanol and 600-800 parts of water. The method overcomes the defect that the dyeing effect is poor due to the fact that the method for dyeing the real silk/viscose composite fabric in the prior art cannot simultaneously take the characteristics of the two fabrics into consideration, firstly opens the hydrogen bonds in the fabric through the composition A in the actual dyeing process, so that modification of the fabric by modified molecules is facilitated, and meanwhile, the dyeing performance of the real silk and viscose two fabrics is estimated, so that the combination of the reactive dye and the fabric is facilitated, and the dyeing effect is effectively improved.
Description
Technical Field
The invention relates to the field of printing and dyeing industry, in particular to a printing and dyeing additive and a method for dyeing real silk/viscose composite fabric.
Background
The real silk fabric is named as 'fabric queen', the characteristics of smooth and soft texture, high elasticity, bright and soft luster are favored by consumers, and the real silk fabric has excellent dye performance and can be dyed by acid, neutral, direct, active, cationic, reductive, soluble reductive, insoluble azo dyes and the like. However, it is easily damaged in alkaline media, so that acid dyes are generally used as the main materials, and neutral, direct and reactive dyes are used as auxiliary materials.
The common viscose fiber has good hygroscopicity, easy dyeing, difficult static generation and better spinnability. The short fiber can be spun purely or blended with other textile fibers, and the fabric is soft, smooth, good in air permeability, comfortable to wear, bright in color after being dyed and good in color fastness. It is suitable for making underwear, outerwear and various decorative articles. However, viscose is less alkali and acid resistant due to its chemical composition similar to cotton, and is therefore generally not suitable for acid dyes.
Therefore, the real silk/viscose composite fabric needs to consider the different properties of the real silk fabric and the viscose fabric at the same time in the dyeing process, but the characteristics of the real silk fabric and the viscose fabric cannot be considered in the prior art, so that the dyeing effect of the real silk/viscose composite fabric is poor.
Disclosure of Invention
The invention provides a dyeing additive and a dyeing method of a real silk/viscose composite fabric, aiming at overcoming the defect of poor dyeing effect caused by the fact that the dyeing method of the real silk/viscose composite fabric in the prior art cannot simultaneously take the characteristics of two fabrics into consideration.
In order to achieve the purpose, the invention is realized by the following technical scheme:
the printing and dyeing additive comprises a composition A and a composition B, wherein the composition A and the composition B respectively comprise the following components in parts by weight:
composition A: 20-45 parts of urea, 10-15 parts of sodium acetate, 5-10 parts of sodium metaborate, 1-5 parts of potassium citrate, 1-3 parts of xanthan gum and 1000 parts of water;
composition B: 10-30 parts of aminosilane coupling agent, 20-30 parts of deacetylated chitin, 100-200 parts of methanol and 600-800 parts of water.
Further preferably, the composition A and the composition B respectively comprise the following components in parts by weight:
composition A: 30-40 parts of urea, 10-15 parts of sodium acetate, 6-9 parts of sodium metaborate, 3-5 parts of potassium citrate, 1-2 parts of xanthan gum and 1000 parts of water;
composition B: 15-25 parts of aminosilane coupling agent, 25-30 parts of deacetylated chitin, 150-200 parts of methanol and 650-750 parts of water.
Still further preferably, the composition a and the composition B respectively comprise, in parts by weight:
composition A: 35 parts of urea, 12 parts of sodium acetate, 8 parts of sodium metaborate, 4 parts of potassium citrate, 1.5 parts of xanthan gum and 1000 parts of water;
composition B: 20 parts of aminosilane coupling agent, 28 parts of deacetylated chitin, 180 parts of methanol and 700 parts of water.
Preferably, the silane coupling agent is one of gamma-aminopropyltriethoxysilane, gamma-aminopropyltrimethoxysilane, phenylaminomethyltriethoxysilane or N-beta (aminoethyl) -gamma-aminopropylmethyldimethoxysilane.
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in the solution containing the composition A, and heating for a certain time;
(S.2) modifying the surface of the fabric: adding a certain amount of the composition B into the solution, continuously soaking for a certain time under the stirring condition, taking out the real silk/viscose composite fabric, and drying;
(S.3) dyeing: and (3) placing the real silk/viscose composite fabric subjected to surface modification into reactive dye liquor for dyeing, soaping after dyeing is finished, and drying to finish dyeing.
Preferably, the amount of composition A added in step (S.1) is 1-3% by volume fraction.
Preferably, the treatment temperature in the step (S.1) is 50-65 ℃, and the treatment time is 20-60 min.
Preferably, the amount of the composition B added in the step (S.2) is 1 to 5% by volume fraction, and the impregnation method is two-dipping and two-rolling.
Preferably, the single stirring and dipping time is 10-45 min, the rolling residual rate is 90%, and the drying temperature is 75-85 ℃.
Preferably, the dyeing temperature is 40-50 ℃, and the dyeing time is 30-40 min.
The invention has the following beneficial effects:
the printing additive of the present invention includes the composition a and the composition B, and the functions of both are different. The composition A has a certain alkalescence effect, can destroy hydrogen bonds in viscose fibers and silk fabrics at a certain temperature, effectively improves the permeability, and can be combined with hydrogen bond fracture positions in cellulose by matching with the addition of xanthan gum, so that hydrogen bonds can not be formed again in cellulose molecules. In addition, the addition of the sodium metaborate can also play a certain role in improving the toughness of the fabric, so that the mechanical strength of the fabric during the printing and dyeing pretreatment can be protected.
The composition B is used for modifying the broken part of the hydrogen bond after the hydrogen bond of the fabric is opened, so that the groups which have binding force to dye molecules in the fabric are increased, and the real silk/viscose composite fabric can be better dyed.
The chitosan contains more hydroxyl and amino which are active groups, and the chitosan has good reaction activity with the active dye, so that the chitosan is added and then is combined with the silane coupling agent containing the amino, so that the dyeing effect of the fabric can be effectively improved.
Therefore, in the actual dyeing process, the hydrogen bonds in the fabric are firstly opened through the composition A, so that the fabric is modified by modified molecules conveniently, and meanwhile, the dyeing properties of the real silk fabric and the viscose fabric are estimated, so that the combination of the reactive dye and the fabric is facilitated, and the dyeing effect is effectively improved.
Detailed Description
The invention is further described with reference to specific examples. Those skilled in the art will be able to implement the invention based on these teachings. Moreover, the embodiments of the present invention described in the following description are generally only some embodiments of the present invention, and not all embodiments. Therefore, all other embodiments obtained by a person of ordinary skill in the art based on the embodiments of the present invention without any creative effort shall fall within the protection scope of the present invention.
Example 1
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in an aqueous solution containing 1% of the composition A by volume fraction, heating to 50 ℃, and soaking for 20 min.
Wherein the composition A comprises the following components in parts by weight: 20 parts of urea, 10 parts of sodium acetate, 5 parts of sodium metaborate, 1 part of potassium citrate, 1 part of xanthan gum and 1000 parts of water.
(S.2) modifying the surface of the fabric: adding the composition B with the volume fraction of 1% into the solution, soaking and rolling for two times under stirring, wherein the soaking time is 10min under single stirring, the rolling residual rate is 90%, taking out the real silk/viscose composite fabric, and drying at 75 ℃.
Wherein the composition B comprises the following components in parts by weight: 10 parts of gamma-aminopropyltriethoxysilane, 20 parts of deacetylated chitin, 100 parts of methanol and 600 parts of water.
(S.3) dyeing: and (2) dyeing the surface-modified real silk/viscose composite fabric in 1 wt% of red reactive dye BFS dye liquor, soaping after dyeing is finished, adjusting the dyeing pH to 6 by acetic acid, and drying to finish dyeing, wherein the bath ratio is 1:10, the dyeing temperature is 80 ℃, the dyeing time is 30 min.
Example 2
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in an aqueous solution containing 3 volume percent of the composition A, heating to 65 ℃, and soaking for 60 min.
Wherein the composition A comprises the following components in parts by weight: 45 parts of urea, 15 parts of sodium acetate, 10 parts of sodium metaborate, 5 parts of potassium citrate, 3 parts of xanthan gum and 1000 parts of water.
(S.2) modifying the surface of the fabric: adding the composition B with the volume fraction of 5% into the solution, soaking and rolling for two times under stirring, wherein the soaking time is 45min under single stirring, the rolling residual rate is 90%, and then taking out the real silk/viscose composite fabric and drying at 85 ℃.
Wherein the composition B comprises the following components in parts by weight: 30 parts of gamma-aminopropyl trimethoxy silane, 30 parts of deacetylated chitin, 200 parts of methanol and 800 parts of water.
(S.3) dyeing: and (2) dyeing the surface-modified real silk/viscose composite fabric in 1 wt% of red reactive dye BFS dye liquor, soaping after dyeing is finished, adjusting the dyeing pH to 6 by acetic acid at a bath ratio of 1:15 and at a dyeing temperature of 50 ℃ for 40min, and drying to finish dyeing.
Example 3
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in an aqueous solution containing 2% of the composition A by volume fraction, heating to 55 ℃, and soaking for 40 min.
Wherein the composition A comprises the following components in parts by weight: 30 parts of urea, 10 parts of sodium acetate, 6 parts of sodium metaborate, 3 parts of potassium citrate, 1 part of xanthan gum and 1000 parts of water.
(S.2) modifying the surface of the fabric: adding the composition B with the volume fraction of 2.5% into the solution, soaking and rolling for two times under stirring, wherein the soaking time is 30min under single stirring, the rolling residual rate is 90%, taking out the real silk/viscose composite fabric, and drying at 80 ℃.
Wherein the composition B comprises the following components in parts by weight: 15 parts of phenylaminomethyl triethoxysilane, 25 parts of deacetylated chitin, 150 parts of methanol and 650 parts of water.
(S.3) dyeing: and (2) dyeing the surface-modified real silk/viscose composite fabric in 1 wt% of red reactive dye BFS dye liquor, soaping after dyeing is finished, regulating the dyeing pH to 6 by using acetic acid, and drying to finish dyeing, wherein the bath ratio is 1:12, the dyeing temperature is 55 ℃, the dyeing time is 35 min.
Example 4
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in an aqueous solution containing 1.5 percent of the composition A by volume fraction, heating to 55 ℃, and soaking for 30 min.
Wherein the composition A comprises the following components in parts by weight: 40 parts of urea, 15 parts of sodium acetate, 9 parts of sodium metaborate, 5 parts of potassium citrate, 2 parts of xanthan gum and 1000 parts of water (S.2) for surface modification of the fabric: adding the composition B with the volume fraction of 1.5% into the solution, soaking and rolling for two times under stirring, wherein the soaking time is 35min under single stirring, the rolling residual rate is 90%, taking out the real silk/viscose composite fabric, and drying at 80 ℃.
Wherein the composition B comprises the following components in parts by weight: 25 parts of N-beta (aminoethyl) -gamma-aminopropylmethyldimethoxysilane, 30 parts of deacetylated chitin, 200 parts of methanol and 750 parts of water.
(S.3) dyeing: and (2) dyeing the surface-modified real silk/viscose composite fabric in 1 wt% of red reactive dye BFS dye liquor, soaping after dyeing is finished, regulating the dyeing pH to 6 by using acetic acid, and drying to finish dyeing, wherein the bath ratio is 1:11, the dyeing temperature is 72 ℃, the dyeing time is 35 min.
Example 5
A dyeing method of real silk/viscose composite fabric comprises the following steps:
(S.1) preprocessing the fabric: soaking the real silk/viscose composite fabric in an aqueous solution containing 1-3% of the composition A by volume fraction, heating to 60 ℃, and soaking for 50 min.
Wherein the composition A comprises the following components in parts by weight: 35 parts of urea, 12 parts of sodium acetate, 8 parts of sodium metaborate, 4 parts of potassium citrate, 1.5 parts of xanthan gum and 1000 parts of water.
(S.2) modifying the surface of the fabric: adding the composition B with the volume fraction of 4.5% into the solution, soaking and rolling for two times under stirring, wherein the soaking time is 40min under single stirring, the rolling residual rate is 90%, taking out the real silk/viscose composite fabric, and drying at 78 ℃.
Wherein the composition B comprises the following components in parts by weight: 20 parts of gamma-aminopropyl trimethoxy silane, 28 parts of deacetylated chitin, 180 parts of methanol and 700 parts of water.
(S.3) dyeing: and (2) dyeing the surface-modified real silk/viscose composite fabric in 1 wt% of red reactive dye BFS dye liquor, soaping after dyeing is finished, regulating the dyeing pH to 6 by using acetic acid, and drying to finish dyeing, wherein the bath ratio is 1:13, the dyeing temperature is 68 ℃, the dyeing time is 35 min.
The dyeing performance tests of the examples 1-5 and the untreated real silk/viscose composite fabric (comparative example 1) were carried out:
test of percentage of dye uptake: the absorbance of the dye bath before and after dyeing was measured at the maximum absorption wavelength using a model 721 spectrophotometer, respectively.
Dye uptake (%) - (1-I)1/I0)*100％；
In the formula I1Absorbance of the residue after dyeing, I0Initial absorbance of the residue.
Fastness of dyeing of the dyed fabric: the grading is carried out according to the GB/T3920-1997 assay with a color-changing gray sample card (GB 251-1984).
The wash fastness was rated according to GB/T3920-1997.
The results are shown in the following table:
TABLE 1
From the data in the above table, it can be seen that the dye uptake of the dyed real silk/viscose composite fabric is greatly improved, and the rubbing color fastness and the washing color fastness are both improved to a certain extent.
Claims (10)
1. The printing and dyeing additive is characterized by comprising a composition A and a composition B, wherein the composition A and the composition B respectively comprise the following components in parts by weight:
composition A: 20-45 parts of urea, 10-15 parts of sodium acetate, 5-10 parts of sodium metaborate, 1-5 parts of potassium citrate, 1-3 parts of xanthan gum and 1000 parts of water;
composition B: 10-30 parts of aminosilane coupling agent, 20-30 parts of deacetylated chitin, 100-200 parts of methanol and 600-800 parts of water.
2. The printing additive of claim 1, wherein the composition a and the composition B comprise, in parts by weight:
composition A: 30-40 parts of urea, 10-15 parts of sodium acetate, 6-9 parts of sodium metaborate, 3-5 parts of potassium citrate, 1-2 parts of xanthan gum and 1000 parts of water;
composition B: 15-25 parts of aminosilane coupling agent, 25-30 parts of deacetylated chitin, 150-200 parts of methanol and 650-750 parts of water.
3. The printing additive of claim 1, wherein the composition a and the composition B comprise, in parts by weight:
composition A: 35 parts of urea, 12 parts of sodium acetate, 8 parts of sodium metaborate, 4 parts of potassium citrate, 1.5 parts of xanthan gum and 1000 parts of water;
composition B: 20 parts of aminosilane coupling agent, 28 parts of deacetylated chitin, 180 parts of methanol and 700 parts of water.
4. The printing additive of claim 1, 2 or 3, wherein the silane coupling agent is one of gamma-aminopropyltriethoxysilane, gamma-aminopropyltrimethoxysilane, phenylaminomethyltriethoxysilane, or N-beta (aminoethyl) -gamma-aminopropylmethyldimethoxysilane.
5. A dyeing method of real silk/viscose composite fabric is characterized by comprising the following steps:
(S.1) preprocessing the fabric: soaking a real silk/viscose composite fabric in a solution containing the composition A as claimed in claims 1-3, and heating for a certain time;
(S.2) modifying the surface of the fabric: adding a certain amount of the composition B into the solution, continuously soaking for a certain time under the stirring condition, taking out the real silk/viscose composite fabric, and drying;
(S.3) dyeing: and (3) placing the real silk/viscose composite fabric subjected to surface modification into reactive dye liquor for dyeing, soaping after dyeing is finished, and drying to finish dyeing.
6. The method for dyeing the real silk/viscose composite fabric according to claim 5, wherein the addition amount of the composition A in the step (S.1) is 1-3% by volume fraction.
7. The dyeing method of the real silk/viscose glue composite fabric according to claim 5 or 6, wherein the treatment temperature in the step (S.1) is 50-65 ℃, and the treatment time is 20-60 min.
8. The dyeing method of the real silk/viscose glue composite fabric according to claim 5, characterized in that the addition amount of the composition B in the step (S.2) is 1-5% according to volume fraction, and the dipping mode is two dipping and two rolling.
9. The method for dyeing the real silk/viscose composite fabric according to claim 8, wherein the single stirring dipping time is 10-45 min, the rolling residual rate is 90%, and the drying temperature is 75-85 ℃.
10. The dyeing method of the real silk/viscose glue composite fabric according to claim 5, wherein the dyeing temperature is 50-80 ℃, and the dyeing time is 30-40 min.