CN112981394A - 一种茶桌表面耐高温涂层制备方法 - Google Patents
一种茶桌表面耐高温涂层制备方法 Download PDFInfo
- Publication number
- CN112981394A CN112981394A CN202110160079.4A CN202110160079A CN112981394A CN 112981394 A CN112981394 A CN 112981394A CN 202110160079 A CN202110160079 A CN 202110160079A CN 112981394 A CN112981394 A CN 112981394A
- Authority
- CN
- China
- Prior art keywords
- temperature
- preparation
- tea table
- resistant coating
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种茶桌表面耐高温涂层制备方法，属于涂层技术领域；包括：茶桌基表面清洗、激光熔覆、多弧离子镀、耐高温油漆涂覆；本发明的特点在于采用激光熔覆、多弧离子镀两种技术共建耐高温抗氧化涂层；激光熔覆所用粉末为钴基中耐温耐磨耐蚀合金粉末，氧化锆为陶瓷粉末具有高强度、硬度、耐高温、耐酸碱腐蚀及散热性能优良等优点；同时多弧离子镀AlCrN涂层，AlCrN涂层具有耐高温抗氧化性能；两者结合共建的涂层能够为茶桌提供耐高温抗氧化性能，能够有效保护桌面不因高温导致桌面老化降低寿命；同时采用耐高温油漆对桌面进行最后处理，一来进一步提高桌面耐高温性能，二来可使茶桌表面更为美观。
Description
技术领域
本发明属于涂层技术领域，特别涉及一种茶桌表面耐高温涂层制备方法。
背景技术
茶桌是放置茶具等用的家具，一般分方形、矩形两种，比桌子小，高度与扶手椅的扶手相当。通常情况下是两把椅子中间夹一茶桌，用以放杯盘茶具，故名茶桌。但目前的茶桌多为木质，不耐高温容易老化；而采用金属材料的茶桌易高温氧化，久而久之极易生锈老化；所以亟待开发一种茶桌表面耐高温涂层制备方法。
发明内容
(一)要解决的技术问题
本发明提供了一种茶桌表面耐高温涂层制备方法；包括：茶桌基表面清洗、激光熔覆、多弧离子镀、耐高温油漆涂覆；本发明的特点在于采用激光熔覆、多弧离子镀两种技术共建耐高温抗氧化涂层；激光熔覆所用粉末为钴基中耐温耐磨耐蚀合金粉末，氧化锆为陶瓷粉末具有高强度、硬度、耐高温、耐酸碱腐蚀及散热性能优良等优点；同时多弧离子镀AlCrN涂层，AlCrN涂层具有耐高温抗氧化性能；两者结合共建的涂层能够为茶桌提供耐高温抗氧化性能，能够有效保护桌面不因高温导致桌面老化降低寿命；同时采用耐高温油漆对桌面进行最后处理，一来进一步提高桌面耐高温性能，二来可使茶桌表面更为美观。
(二)技术方案
本发明通过如下技术方案实现：
一种茶桌表面耐高温涂层制备方法，包括如下步骤：
步骤100：茶桌基表面清洗；无水乙醇清洗、高温杀菌消毒；
步骤200：激光熔覆；在茶桌基表面熔覆耐高温涂层；
步骤300：多弧离子镀；在耐高温涂层表面镀上一层耐高温抗氧化涂层；
步骤400：耐高温油漆涂覆。
进一步的，所述步骤200还包括如下步骤：
步骤210：配置粉末；
步骤220：粉末充分混合；
步骤230：激光熔覆；
步骤240：激光重熔；
步骤250：纳米远红外加热器保温30min；
步骤260：纳米远红外加热器控制温度直至耐高温涂层降至室温。
进一步的，所述粉末包括以下重量百分数的各组分：71.8％Co40粉末+28.2％ZrO2粉末；所述Co40粉末粒度为200μm；所述ZrO2粉末粒度为50μm。
进一步的，所述步骤220采用行星式球磨机进行混合。
进一步的，所述步骤230激光熔覆工艺如下：功率2100W，氩气流量1800ml/min，扫描速度5mm/s，离焦量20mm，送粉量110g/min。
进一步的，所述步骤250保温温度为600℃；所述步骤260采取20℃/min的梯度降至室温。
进一步的，所述步骤300还包括如下步骤：
步骤310：熔覆涂层磨削加工；
步骤320：研磨机打磨抛光至镜面，表面粗糙度；
步骤330：无水乙醇清洗表面；
步骤340：Ar离子辉光清洗表面；
步骤350：多弧离子镀。
进一步的，所述步骤310采用纳米磨削机床进行磨削。
进一步的，所述步骤320粗糙度Ra≤0.025μm。
进一步的，所述步骤350采用99.99％的Al75Cr25合金靶材；所述多弧离子镀工艺参数如下：弧电流95A，偏压-170V，沉积时间25min，靶基距25cm，工作压力2.7×10-3Pa，温度290℃，旋转速度4r/min，保护气体N2。
(三)有益效果
本发明相对于现有技术，具有以下有益效果：
本发明的特点在于采用激光熔覆、多弧离子镀两种技术共建耐高温抗氧化涂层；激光熔覆所用粉末为钴基中耐温耐磨耐蚀合金粉末，氧化锆为陶瓷粉末具有高强度、硬度、耐高温、耐酸碱腐蚀及散热性能优良等优点；同时多弧离子镀AlCrN涂层，AlCrN涂层具有耐高温抗氧化性能；两者结合共建的涂层能够为茶桌提供耐高温抗氧化性能，能够有效保护桌面不因高温导致桌面老化降低寿命；同时采用耐高温油漆对桌面进行最后处理，一来进一步提高桌面耐高温性能，二来可使茶桌表面更为美观。
具体实施方式
一种茶桌表面耐高温涂层制备方法，包括如下步骤：
步骤100：茶桌基表面清洗；无水乙醇清洗、高温杀菌消毒；
步骤200：激光熔覆；在茶桌基表面熔覆耐高温涂层；
步骤300：多弧离子镀；在耐高温涂层表面镀上一层耐高温抗氧化涂层；
步骤400：耐高温油漆涂覆。
其中，所述步骤200还包括如下步骤：
步骤210：配置粉末；
步骤220：粉末充分混合；
步骤230：激光熔覆；
步骤240：激光重熔；
步骤250：纳米远红外加热器保温30min；
步骤260：纳米远红外加热器控制温度直至耐高温涂层降至室温。
其中，所述粉末包括以下重量百分数的各组分：71.8％Co40粉末+28.2％ZrO2粉末；所述Co40粉末粒度为200μm；所述ZrO2粉末粒度为50μm。
其中，所述步骤220采用行星式球磨机进行混合。
其中，所述步骤230激光熔覆工艺如下：功率2100W，氩气流量1800ml/min，扫描速度5mm/s，离焦量20mm，送粉量110g/min。
其中，所述步骤250保温温度为600℃；所述步骤260采取20℃/min的梯度降至室温。
其中，所述步骤300还包括如下步骤：
步骤310：熔覆涂层磨削加工；
步骤320：研磨机打磨抛光至镜面，表面粗糙度；
步骤330：无水乙醇清洗表面；
步骤340：Ar离子辉光清洗表面；
步骤350：多弧离子镀。
其中，所述步骤310采用纳米磨削机床进行磨削。
其中，所述步骤320粗糙度Ra≤0.025μm。
其中，所述步骤350采用99.99％的Al75Cr25合金靶材；所述多弧离子镀工艺参数如下：弧电流95A，偏压-170V，沉积时间25min，靶基距25cm，工作压力2.7×10-3Pa，温度290℃，旋转速度4r/min，保护气体N2。
工作原理：
本发明的特点在于采用激光熔覆、多弧离子镀两种技术共建耐高温抗氧化涂层；激光熔覆所用粉末为钴基中耐温耐磨耐蚀合金粉末，氧化锆为陶瓷粉末具有高强度、硬度、耐高温、耐酸碱腐蚀及散热性能优良等优点；同时多弧离子镀AlCrN涂层，AlCrN涂层具有耐高温抗氧化性能；两者结合共建的涂层能够为茶桌提供耐高温抗氧化性能，能够有效保护桌面不因高温导致桌面老化降低寿命；同时采用耐高温油漆对桌面进行最后处理，一来进一步提高桌面耐高温性能，二来可使茶桌表面更为美观。
本发明的控制方式是通过人工启动和关闭开关来控制，动力元件的接线图与电源的提供属于本领域的公知常识，并且本发明主要用来保护机械装置，所以本发明不再详细解释控制方式和接线布置。
本发明的控制方式是通过控制器来自动控制，控制器的控制电路通过本领域的技术人员简单编程即可实现，电源的提供也属于本领域的公知常识，并且本发明主要用来保护机械装置，所以本发明不再详细解释控制方式和电路连接。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种茶桌表面耐高温涂层制备方法，其特征在于：包括如下步骤：
步骤100：茶桌基表面清洗；无水乙醇清洗、高温杀菌消毒；
步骤200：激光熔覆；在茶桌基表面熔覆耐高温涂层；
步骤300：多弧离子镀；在耐高温涂层表面镀上一层耐高温抗氧化涂层；
步骤400：耐高温油漆涂覆。
2.根据权利要求1所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤200还包括如下步骤：
步骤210：配置粉末；
步骤220：粉末充分混合；
步骤230：激光熔覆；
步骤240：激光重熔；
步骤250：纳米远红外加热器保温30min；
步骤260：纳米远红外加热器控制温度直至耐高温涂层降至室温。
3.根据权利要求2所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述粉末包括以下重量百分数的各组分：71.8％Co40粉末+28.2％ZrO2粉末；所述Co40粉末粒度为200μm；所述ZrO2粉末粒度为50μm。
4.根据权利要求2所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤220采用行星式球磨机进行混合。
5.根据权利要求2所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤230激光熔覆工艺如下：功率2100W，氩气流量1800ml/min，扫描速度5mm/s，离焦量20mm，送粉量110g/min。
6.根据权利要求2所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤250保温温度为600℃；所述步骤260采取20℃/min的梯度降至室温。
7.根据权利要求1所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤300还包括如下步骤：
步骤310：熔覆涂层磨削加工；
步骤320：研磨机打磨抛光至镜面，表面粗糙度；
步骤330：无水乙醇清洗表面；
步骤340：Ar离子辉光清洗表面；
步骤350：多弧离子镀。
8.根据权利要求7所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤310采用纳米磨削机床进行磨削。
9.根据权利要求7所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤320粗糙度Ra≤0.025μm。
10.根据权利要求7所述的一种茶桌表面耐高温涂层制备方法，其特征在于：所述步骤350采用99.99％的Al75Cr25合金靶材；所述多弧离子镀工艺参数如下：弧电流95A，偏压-170V，沉积时间25min，靶基距25cm，工作压力2.7×10-3Pa，温度290℃，旋转速度4r/min，保护气体N2。