CN112891619B - 具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及其制备方法 - Google Patents

具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及其制备方法 Download PDF

Info

Publication number
CN112891619B
CN112891619B CN202110114443.3A CN202110114443A CN112891619B CN 112891619 B CN112891619 B CN 112891619B CN 202110114443 A CN202110114443 A CN 202110114443A CN 112891619 B CN112891619 B CN 112891619B
Authority
CN
China
Prior art keywords
target material
gene
smooth muscle
coating material
vector
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110114443.3A
Other languages
English (en)
Other versions
CN112891619A (zh
Inventor
余泓池
向茂龙
刘肖珩
马佳
罗日方
曹成建
沈阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan University
Original Assignee
Sichuan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan University filed Critical Sichuan University
Priority to CN202110114443.3A priority Critical patent/CN112891619B/zh
Publication of CN112891619A publication Critical patent/CN112891619A/zh
Application granted granted Critical
Publication of CN112891619B publication Critical patent/CN112891619B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及其制备方法，属于生物医学工程功能材料技术。其制备方法包括：对经清洗后的金属基底材料进行表面氨基官能化处理。将上述材料置于pH为3～5的富含强氧化剂的溶液中，加入浓度为0.1～5mg/mL的亲水性化合物溶液，获得目标材料A。制备可抑制Yes‑associated protein(YAP)表达的慢病毒基因载体目标材料B，其中，载体为慢病毒载体。将目标材料B固定在目标材料A表面，即获得具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料。该涂层具有微纳拓扑结构，可为基因载体提供保护性的温床，为基因递送创造有利条件。

Description

具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及 其制备方法
技术领域
本发明属于生物医学工程功能材料技术领域，具体涉及一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及其制备方法。
背景技术
血管支架植入术已成为治疗冠状动脉硬化性心脏病(冠心病)的主要手段，然而早期的金属裸支架(Bare Metal Stent,BMS)植入后易引发新生内膜过度增生，从而导致支架内再狭窄(In-stent Restenosis,ISR)发生概率较高(20％～30％)；而药物洗脱支架(Drug-eluting Stent,DES)虽可以通过抗增生药物(如雷帕霉素、依维莫司等)的原位释放，有效抑制ISR的发生概率，但是随后的临床报道发现，DES在抑制血管平滑肌细胞(Smooth Muscle Cells,SMCs)过度增生的同时，也抑制了血管内皮细胞层(EndothelialCells,ECs)的愈合延迟，导致了晚期血栓的发生(Late Stent Thrombosis,LST)(发生率约1.5％～2％)，成为DES使用中的严重隐患。SMCs的表型转化在动脉粥样硬化的发展中起重要作用。当SMCs发生表型转化后，收缩型(contractile phenotype)标志蛋白下调表达，合成型(synthetic phenotype)标志蛋白上调表达，SMCs获得更强的迁移增殖能力，由血管中层迁入血管内层并增生从而促进支架内再狭窄的发展。因此，寻找可选择性抑制SMCs表型转化且不影响ECs迁移/粘附的支架功能性涂层可望解决现有药物支架所造成的晚期血栓的发生。
由于基因治疗在靶向性和持久性上的特殊性，基因洗脱支架(Gene-elutingStent,GES)也应运而生，其核心是选择合适的基因，进行靶向递送、转染及表达，发挥调节血管组织修复进程的功能。此外，基因载体可根据实际需要进行设计，因此可特异性的针对不同种类的细胞构建靶向基因载体。共转录因子Yes-associated protein(YAP)在调控平滑肌细胞各类生物学行为过程中起到关键作用。研究表明，YAP蛋白在动脉粥样硬化中SMCs中呈现高表达，抑制YAP蛋白可显著抑制SMCs的增殖行为。但是，在心血管支架领域，还没有尝试利用YAP蛋白的重要作用来治疗支架植入后带来的各类临床问题。
发明内容
本发明提供了一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料、其制备方法及心血管支架，可利用具有微纳拓扑结构的材料涂层将治疗基因导入受体细胞中，可降低支架植入后的平滑肌细胞异常增殖，并不影响血管内皮细胞的正常功能，有望解决晚期血栓问题。
第一方面，本发明提供一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)对经清洗后的金属基底材料进行表面氨基官能化处理。
(2)将步骤(1)所得材料置于pH为3～5的富含强氧化剂的溶液中，加入浓度为0.1～5mg/mL的亲水性化合物溶液，控制反应温度为55～65℃，进一步反应5～120min后，清洗1～3次后氮气干燥，获得具有微纳拓扑结构，同时富含反应性醌基和氨基的目标材料A；其中，亲水性化合物为单宁酸和聚乙烯亚胺的混合物。
(3)制备可在平滑肌细胞中特异性抑制Yes-associated protein(YAP)表达的慢病毒基因载体目标材料B，其中，载体为慢病毒载体。
(4)将目标材料B固定在目标材料A表面，即获得目标选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料。
进一步地，金属基底材料选自铁合金、镁合金、锌合金、钛合金及钴铬合金中的一种。
进一步地，表面氨基官能化处理的方式选自氨基等离子体处理、多巴胺溶液浸泡处理及多巴胺与多聚赖氨酸的混合溶液浸泡处理中的其中一种。
进一步地，强氧化剂选自过硫酸盐、硫酸铜、高碘酸盐以及芬顿试剂中的其中一种。
进一步地，所述可在平滑肌细胞中特异性抑制Yes-associated protein(YAP)表达的质粒DNA基因载体为：构建了平滑肌细胞特异性的启动子(Promoter)序列,同时构建了可抑制Yes-associated protein(YAP)表达的shRNA序列的质粒DNA。质粒DNA基因载体中平滑肌细胞特异性的启动子序列为：CTGGTGCCAGGCTTTCGGTGCTAAGGCCTGCAAGGGGCCTAGGTACGACCCTCCTCCCTGACCTGTGCTTGGAGCTGGCTCTTCAGCAGTGAGGGCCAGCCCAAGTTGAGTCTTCTGATCGGGGACTGAATTCAGAGGCCACCTCATCCCACCAGCCACTAGAATGATGCCAGCACTAGGGTTGGTGGGAAGTGGCAACTCACTGTCCCCTTCCACACCCTCAGTCCTGCCAAGCCCCAGATGGGGGCCTCTCAGTGCCATTGACACTGCCCAAGAATGTCTAGAGGCCACGGAACGGTGCCAAGCACACAGTCCCTTTTGCCTCTTTCACGGGAGCAGGAGTCCCAGTGCCTGTCGTGGAAAGGGAGGAACATGCCAGGTCCCTGTGTGTCCTTGGCCCTGTCTCACCAAAGGACTCAGGGCTGGTTTCTGAGTTTCCGTCCAGTATTTAGCCAAGTTCTGTGTTAGTCACGTAGGCCTAAGAGCCTTGGCGTTTACAGAGTCACCCAGCTCTGGCCCCTGGCCATTCTGGTCCTTGGCGTTTACAGAGTCACCCAGCTCCAGGCCCCTGGCCACTTTGGTACTTGGTTGCCCTTCACTCCACCAGGTCCATTCCAGATGCCAAGAGTGGGCCCCAGGAATGTGTTTCCTTCTCTCCACCATGTTTTTATAGCTCTTGGGCTGGGAGAAGAGGCGGGTCTGGGTCTTTGTTTCTGAGCTTTGTTCTATGTTCCTCCATGCTACGGTTGCAATTGTTTTCTATGAACGAGTACATTCAATAAAGACAACCAGACCTGGGATTTGGGGTCTTACTGATGTGTTGGGAGGTGCAGGAGCCTCCGTGTCCCATTTATTTTGGCCTTCCCGTCTCGTTTCTGTGCGTGGCTACATTGGGAATGACCTTCCTTGATCCCACCAAGCCACCCATTGATTCTGTAAACATGTGACCCTTGCTCCAAGCATTGCTTACAGGAGCAGGATACTGAAAGTGTGTCTGTGCCCTCTCCTGATAACCCCTCCCTTCAGCAGGCACACAGCACCTGACTACCCACCACGTATGTAAACGTCAGTATCCTTTCCAGCCAGCTCTGCAGATGGGTGTCCAGGCTGTGCCATGATGCACCTCAAGTGGGCAGAGCCCTTGCAGGCCAAGGTTTTAAAGGCTGTTCAGGAATGGATGGCAAGCAGGATCTAAGAGGAGGGGGGGTTGTTGTTGTTTGGGGGGGGGGTGGTTTTGGTTTGTTTTTTTTGAGACAGGGTTTCTCTGTGTGGCCCTGGCCCTCCTGGAACCCACTCTGTAGACCAGGCTGGCCTTGAACTCAGAAATCTGCCTGCCTCTGCCTCCCGAGTGCTGGGATTAAAGGCGTGTGCCCATCGAGGAGGGAGATTTTATTTAGATTATAAAAAGGACGGGATTTGGGGAATCCTGTCTAGTGAATTCAGGACGTAATCAGTGGCTGGAAAGCAAGAGCTCTAGAGGAGCTCCAGCTTATTATGACCCTTCCTTCAGATGCCACAAGGAGGTGCTGGAGTTCTATGCACCAATAGCTTAAACCAGCCAGGCTGGCTGTAGTGGATTGAGCGTCTGAGGCTGCACCTCTCTGGCCTGCAGCCAGTTCTGGGTGAGACTGACCCTGCCTGAGGGTTCTCTCCTTCCCTCTCTCTACTCCTTTCTCCCTCTCCCTCTCCCTCTCTCTGTTTCCTGAGGTTTCCAGAATTGGGGATGGGACTCAGAGACACCACTAAAGCCTTACCTTTTAAGAAGTTGCATTCAGTGAGTGTGTGAGACATAGCACAGATAGGGGCAGAGGAGAGCTGGTTCTGTCTCCACTGTGTTTGGTCTTGGGTACTGAACTCAGACCATCAGGTGTGATAGCAGTTGTCTTTAACCCTAACCCTGAGCCTGTCTCACCTGTCCCTTCCCAAGACCACTGAAGCTAGGTGCAAGATAAGTGGGGACCCTTTCTGAGGTGGTAGGATCTTTCACGATAAGGACTATTTTGAAGGGAGGGAGGGTGACACTGTCCTAGTCCTCTTACCCTAGTGTCTCCAGCCTTGCCAGGCCTTAAACATCCGCCCATTGTCACCGCTCTAGAAGGGGCCAGGGTTGACTTGCTGCTAAACAAGGCACTCCCTAGAGAAGCACCCGCTAGAAGCATACCATACCTGTGGGCAGGATGACCCATGTTCTGCCATGCACTTGGTAGCCTTGGAAAGGCCACTTTGAACCTCAATTTTCTCAACTGTTAAATGGAGTGGTAACTGCTATCTCATAATAAAGGGGAACGTGAAAGGAAGGCGTTTGCATAGTGCCTGGTTGTGCAGCCAGGCTGCAGTCAAGACTAGTTCCCACCAACTCGATTTTAAAGCCTTGCAAGAAGGTGGCTTGTTTGTCCCTTGCAGGTTCCTTTGTCGGGCCAAACTCTAGAATGCCTCCCCCTTTCTTTCTCATTGAAGAGCAGACCCAAGTCCGGGTAACAAGGAAGGGTTTCAGGGTCCTGCCCATAAAAGGTTTTTCCCGGCCGCCCTCAGCACCGCCCCGCCCCGACCCCCGCAGCATCTCCAAAGCATGCAGAGAATGTCTCCGGCTGCCCCCGACAGACTGCTCCAACTTGGTGTCTTTCCCCAAATATGGAGCCTGTGTGGAGTGAGTGGGGCGGCCCGGGGTGGTGAGCCAAGCAGACTTCCATGGGCAGGGAGGGGCGCCAGCGGGCGGCAGAGGGGTGACATCACTGCCTAGGCGGCCTTTAAACCCCTCACCCAGCCGGCGCCCCGGCCCGTCTGCCCCAGCCCAGACACCGAAGCTACTCTCCT。抑制YAP表达的shRNA序列为：GCTCAGCATCTTCGACAGTCT。
进一步地，将目标材料B固定在目标材料A上的方法为共价结合法。
进一步地，共价结合法为目标材料B上的氨基(慢病毒载体上的氨基)和目标材料A上的醌基之间形成的迈克尔加成反应。
进一步地，迈克尔加成反应是在pH为7.5～9的溶液体系中进行。
进一步地，所用共价结合法为目标材料B上的羧基(慢病毒载体上的羧基)和目标材料A上的氨基之间通过脱水缩合形成的酰胺键。
进一步地，脱水缩合形成的酰胺键是在反应体系为pH为5～7的溶液体系中进行。
第二方面，本发明提供一种选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料，由上述制备方法制备得到。
本发明提供的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料、其制备方法及心血管支架的有益效果包括：
亲水性目标材料A具有微纳拓扑结构，并且表面富含反应性醌基和氨基，与表面富含羧基和氨基的目标材料B固定在一起，目标材料A可以为目标材料B提供固定的基础，从而通过目标材料A将目标材料B治疗基因导入受体细胞中，可降低支架植入后的平滑肌细胞异常增殖且不影响血管内皮细胞的正常功能，有望解决晚期血栓问题。
附图说明
为了更清楚地说明本申请实施例的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本申请的某些实施例，因此不应被看作是对范围的限定，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他相关的附图也属于本申请的保护范围。
图1为目标材料A的XPS分析图；
图2为实施例5提供的涂层的亲疏水性评判图；
图3为实施例5提供的涂层的微纳拓扑结构图；
图4为实施例5提供的涂层的血管平滑肌细胞及血管内皮细胞转染效率；
图5为实施例5提供的涂层的血管平滑肌细胞YAP表达情况图；
图6为试验列1中转入基因载体后的平滑肌细胞表型转化标记物的表达情况图；
图7为对比例1提供的涂层的亲疏水性评判图；
图8为对比例2提供的涂层的亲疏水性评判图；
图9为对比例3提供的涂层的亲疏水性评判图。
具体实施方式
为了对本发明的技术特征、目的和有益效果有更加清楚的理解，现对本发明的技术方案进行以下详细说明，但不能理解为对本发明的可实施范围的限定。
实施例1
一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)将1mg/mL多巴胺溶液和15mg/mL的聚乙烯亚胺溶液混合得到混合液，将经清洗后的铁合金基底材料浸泡在混合液中，在pH为9的溶液条件下共聚合2h得到氨基官能化表面；
(2)将步骤(1)所得材料置于pH为3的过硫酸盐溶液中，加入浓度为0.5mg/mL的单宁酸及聚乙烯亚胺的混合物(单宁酸的浓度为0.2mg/mL，聚乙烯亚胺的浓度为0.3mg/mL)，控制反应温度为60℃，进一步反应50min后，清洗3次后氮气干燥，获得目标材料A；
(3)制备可在平滑肌细胞中特异性抑制YAP蛋白表达的质粒DNA，载体为慢病毒载体，所得基因载体为目标材料B；所用核心质粒为pLenti-SM22-shYAP-Flag-6His-CMV-GFP-P2A-Puro，包装质粒为pAXPS,pMD2.G，上述质粒以4:3:1的比例转染HEK293T细胞，48h/72h后分别收集细胞上清，过0.45μm滤器，以分子量8000的聚乙二醇(PEG8000)溶液过夜沉淀病毒，4000g离心，获得浓缩病毒。
(4)将目标材料A浸泡在pH为8.5的水溶液中，缓慢加入适量目标材料B(2μg/cm2)，使目标材料B固定在目标材料A表面。
实施例2
一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)将经清洗后的镁合金基底材料置于低温等离子体发生仪中，在0.5Pa真空度下，通入烯丙胺单体，辉光放电10min后得到氨基正电荷表面；
(2)将步骤(1)所得材料置于pH为3的硫酸铜溶液中，加入浓度为0.5mg/mL的单宁酸及聚乙烯亚胺的混合物(单宁酸的浓度为0.2mg/mL，聚乙烯亚胺的浓度为0.3mg/mL)，控制反应温度为60℃，进一步反应50min后，清洗3次后氮气干燥，获得目标材料A；
(3)制备可在平滑肌细胞中特异性抑制YAP蛋白表达的质粒DNA，载体为慢病毒载体，所得基因载体为目标材料B；所用核心质粒为pLenti-SM22-shYAP-Flag-6His-CMV-GFP-P2A-Puro，包装质粒为pAXPS,pMD2.G，上述质粒以4:3:1的比例转染HEK293T细胞，48h/72h后分别收集细胞上清，过0.45μm滤器，以分子量8000的聚乙二醇(PEG8000)溶液过夜沉淀病毒，4000g离心，获得浓缩病毒。
(4)将目标材料A浸泡在pH为8.5的水溶液中，缓慢加入适量目标材料B(2μg/cm2)，使目标材料B固定在目标材料A表面。
实施例3
一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)将经清洗后的锌合金基底材料置于低温等离子体发生仪中，在0.5Pa真空度下，通入烯丙胺单体，辉光放电10min后得到氨基正电荷表面；
(2)将步骤(1)所得材料置于pH为3的高碘酸盐溶液中，加入浓度为2mg/mL的单宁酸及聚乙烯亚胺的混合物(单宁酸的浓度为0.5mg/mL，聚乙烯亚胺的浓度为1.5mg/mL)，控制反应温度为60℃，进一步反应90min后，清洗3次后氮气干燥，获得目标材料A；
(3)制备可在平滑肌细胞中特异性抑制YAP蛋白表达的质粒DNA，载体为慢病毒载体，所得基因载体为目标材料B；所用核心质粒为pLenti-SM22-shYAP-Flag-6His-CMV-GFP-P2A-Puro，包装质粒为pAXPS,pMD2.G，上述质粒以4:3:1的比例转染HEK293T细胞，48h/72h后分别收集细胞上清，过0.45μm滤器，以分子量8000的聚乙二醇(PEG8000)溶液过夜沉淀病毒，4000g离心，获得浓缩病毒。
(4)将目标材料A浸泡在pH为8.5的水溶液中，缓慢加入适量目标材料B(2μg/cm2)，使目标材料B固定在目标材料A表面。
实施例4
一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)将1mg/mL多巴胺溶液和15mg/mL的聚乙烯亚胺溶液混合得到混合液，将经清洗后的钛合金基底材料浸泡在混合液中，在pH为8的溶液条件下共聚合2h得到氨基官能化表面；
(2)将步骤(1)所得材料置于pH为3的高碘酸盐溶液中，加入浓度为3mg/mL的单宁酸及聚乙烯亚胺的混合物(单宁酸的浓度为1mg/mL，聚乙烯亚胺的浓度为2mg/mL)，控制反应温度为60℃，进一步反应120min后，清洗3次后氮气干燥，获得目标材料A；
(3)制备可在平滑肌细胞中特异性抑制YAP蛋白表达的质粒DNA，载体为慢病毒载体，所得基因载体为目标材料B；所用核心质粒为pLenti-SM22-shYAP-Flag-6His-CMV-GFP-P2A-Puro，包装质粒为pAXPS,pMD2.G，上述质粒以4:3:1的比例转染HEK293T细胞，48h/72h后分别收集细胞上清，过0.45μm滤器，以分子量8000的聚乙二醇(PEG8000)溶液过夜沉淀病毒，4000g离心，获得浓缩病毒。
(4)将目标材料A浸泡在pH为8.5的水溶液中，缓慢加入适量目标材料B(2μg/cm2)，使目标材料B固定在目标材料A表面。
实施例5
一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，包括以下步骤：
(1)使经清洗后的钴铬合金基底材料进行表面氨基官能化处理；通过0.5mg/mL单宁酸和2mg/mL赖氨酸，于pH为9的溶液条件下共聚合3h，得到富含氨基的表面；
(2)将步骤(1)所得材料置于pH为3的芬顿试剂溶液中，加入浓度为5mg/mL的单宁酸及聚乙烯亚胺的混合物(单宁酸的浓度为1mg/mL，聚乙烯亚胺的浓度为4mg/mL)，控制反应温度为60℃，进一步反应120min后，清洗3次后氮气干燥，获得目标材料A；
(3)制备可在平滑肌细胞中特异性抑制YAP蛋白表达的质粒DNA，载体为慢病毒载体，所得基因载体为目标材料B；所用核心质粒为pLenti-SM22-shYAP-Flag-6His-CMV-GFP-P2A-Puro，包装质粒为pAXPS,pMD2.G，上述质粒以4:3:1的比例转染HEK293T细胞，48h/72h后分别收集细胞上清，过0.45μm滤器，以分子量8000的聚乙二醇(PEG8000)溶液过夜沉淀病毒，4000g离心，获得浓缩病毒。
(4)将目标材料A浸泡在pH为8.5的水溶液中，缓慢加入适量目标材料B(2μg/cm2)，使目标材料B固定在目标材料A表面。
对比例1
一种金属基底的表面氨基化处理方法，包括：
(1)使经清洗后的钴铬合金基底材料进行表面氨基官能化处理；通过0.5mg/mL单宁酸和2mg/mL赖氨酸，于pH为9的溶液条件下共聚合3h，得到富含氨基的表面。
对比例2
一种目标材料A的制备方法，包括如下步骤：
(1)使经清洗后的钴铬合金基底材料进行表面氨基官能化处理；通过0.5mg/mL单宁酸和2mg/mL赖氨酸，于pH为9的溶液条件下共聚合3h，得到富含氨基的表面。
(2)将步骤(1)所得材料置于pH为3的芬顿试剂溶液中，加入浓度为5mg/mL的单宁酸，控制反应温度为60℃，进一步反应120min后，清洗3次后氮气干燥，获得目标材料A。
对比例3
一种目标材料A的制备方法，包括如下步骤：
(1)使经清洗后的钴铬合金基底材料进行表面氨基官能化处理；通过0.5mg/mL单宁酸和2mg/mL赖氨酸，于pH为9的溶液条件下共聚合3h，得到富含氨基的表面。
(2)将步骤(1)所得材料置于pH为3的芬顿试剂溶液中，加入浓度为5mg/mL的聚乙烯亚胺的混合物，控制反应温度为60℃，进一步反应120min后，清洗3次后氮气干燥，获得目标材料A。
试验例1
以镁合金为基底材料，以实施列1，实施例5中的方法构建目标材料A，分别对两种目标材料A进行XPS分析，从图1可以看出(C、N、O的高分辨解谱图)，目标材料A表面含有氨基、酚羟基、醌基等多种基团，可与目标材料B按不同反应方式结合)。如图2所示，该涂层具有很好的亲水性能，且涂层表面具有显著的维纳拓扑结构，如图3所示。
分别将血管平滑肌细胞(SMCs)和血管内皮内皮细胞(1×107个)种植于实施例5中所得涂层，48h后荧光显微镜观察质粒DNA转染效率，如图4所示，该涂层对SMCs有极高的转染效率，另一方面，质粒DNA无法在ECs中被特异性启动表达。此外，收集种植于涂层上的SMCs,采用western-blot分析质粒DNA对YAP蛋白表达的抑制效果，图5显示，该涂层所转染的质粒DNA可显著降低YAP蛋白的表达。如图6所示，该涂层抑制SMCs中YAP蛋白的表达后可显著降低SMCs合成型(synthetic phenotype)标志蛋白的表达。
从图7可以看出，如果合金基底仅经过氨基化处理，不添加单宁酸和聚乙烯亚胺进行亲水性处理，则得到的目标材料的亲水性效果不佳，不利于后续涂层的制备。
从图8和图9中可以看出，如果合金基底材料经过了氨基化处理以后，单独使用单宁酸或单独使用聚乙烯亚胺进行亲水性处理，其亲水效果均差于实施例5的亲水性处理方式，可以说明单宁酸和聚乙烯亚胺具有一定的协同效果，二者的结合可以使目标材料A亲水性效果最佳，以便后续涂层的制备，可以使涂层效果更佳。

Claims (9)

1.一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，包括以下步骤：
（1）对经清洗后的金属基底材料进行表面氨基官能化处理；所述表面氨基官能化处理的方式选自氨基等离子体处理、多巴胺溶液浸泡处理及多巴胺与多聚赖氨酸的混合溶液浸泡处理中的一种；
（2）将步骤（1）所得材料置于pH为3~5的富含强氧化剂的溶液中，加入浓度为0.1~5 mg/mL的亲水性化合物溶液，控制反应温度为55~65℃，进一步反应5~120 min后，清洗1~3次后氮气干燥，获得具有微纳拓扑结构，同时富含反应性醌基和氨基的目标材料A；其中，所述亲水性化合物为单宁酸和聚乙烯亚胺的混合物；
（3）制备可特异性抑制平滑肌细胞中Yes-associated protein表达的慢病毒基因载体目标材料B，其中，载体为慢病毒载体；
（4）将目标材料B固定在目标材料A表面，即获得具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料。
2.根据权利要求1所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述金属基底材料选自铁合金、镁合金、锌合金、钛合金及钴铬合金中的一种。
3.根据权利要求1所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述强氧化剂选自过硫酸盐、硫酸铜、高碘酸盐以及芬顿试剂中的一种。
4.根据权利要求1所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，将所述目标材料B固定在所述目标材料A上的方法为共价结合法。
5.根据权利要求4所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述共价结合法为所述目标材料B上的氨基和所述目标材料A上的醌基之间形成的迈克尔加成反应。
6.根据权利要求5所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述迈克尔加成反应是在pH为7.5~9的溶液体系中进行。
7.根据权利要求4所述的一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述共价结合法为所述目标材料B上的羧基和所述目标材料A上的氨基之间通过脱水缩合形成的酰胺键。
8.根据权利要求7所述一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料的制备方法，其特征在于，所述脱水缩合形成的酰胺键是在反应体系为pH为5~7的溶液体系中进行。
9.一种具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料，其特征在于，由权利要求1~8任一项所述的制备方法制备得到。
CN202110114443.3A 2021-01-28 2021-01-28 具有选择性抑制平滑肌细胞表型转化的基因洗脱涂层材料及其制备方法 Active CN112891619B (zh)