CN112870219A - 一种石膏丸、其制备方法及石膏丸药枕 - Google Patents
一种石膏丸、其制备方法及石膏丸药枕 Download PDFInfo
- Publication number
- CN112870219A CN112870219A CN202110075390.9A CN202110075390A CN112870219A CN 112870219 A CN112870219 A CN 112870219A CN 202110075390 A CN202110075390 A CN 202110075390A CN 112870219 A CN112870219 A CN 112870219A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- shell layer
- pill
- powder
- shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种石膏丸、其制备方法及石膏丸药枕。该石膏丸的制备方法,包括如下步骤:将硅溶胶、转晶剂、抗菌防霉剂和水混合均匀,得到壳层的辅助材料;提供核层材料和壳层的主材料,将壳层材料通过水化凝结的方式包覆在核层材料表面,得到石膏丸;壳层材料由壳层的主材料和壳层的辅助材料组成,壳层的主材料包括石膏粉。本发明中,通过采用石膏粉为壳层的主材料包覆在轻质核层材料表面并直接水化凝结,避免了因石膏粉水化凝固快,不易搓丸的问题,石膏丸成型效果好。本发明所得石膏丸药枕具有按摩功能,同时具有可塑性好,通气,清热,降火,保护颈椎,镇静助眠的优势。
Description
技术领域
本发明涉及石膏制品技术领域,尤其涉及一种石膏丸、其制备方法及石膏丸药枕。
背景技术
枕头是一种睡眠工具,枕头是人类生活必需品,人的一生几乎有三分之一的时间是睡在枕头上,枕头的保健作用不容忽视。
石膏自古被认为是上等的中药药石,其具有降血压预防中风、止头痛镇静安神、消炎退热、调节植物神经等辅助疗效。石膏制成的药枕主要对失眠、头昏、高血压、颈椎病、风火牙痛、面部皮肤炎症等有明显辅助疗效,还可疏通经络、消除疲劳、清热泻火、凉血降压、吸湿除汗、养颜益寿。
目前,石膏枕一般有两种,一是采用天然石膏原石为原料,经雕刻、磨制而成的一种具体降压护脊、除烦镇痛、助眠安神等多重保健药用之功效的一种养生枕头,然而,该枕头质地较硬,重而易碎,塑型性差,长期使用易对颈椎造成损害;二是将石膏粉装在一个布包上,将布包放入枕芯中,虽有一定的塑型性,但枕头通气性较差,效果不好。
将石膏制成丸放入枕头中软硬适中,且塑型性、通气性好。然而,由于石膏具有水化凝结速度快的特点,在用制丸机制丸的过程中,因凝固时间短,不易挤出滚压导致无法获得石膏丸。
发明内容
有鉴于此,有必要提供一种石膏丸、其制备方法及石膏丸药枕,用以解决现有技术中因石膏快速凝固、不易制丸以及现有的石膏枕硬度大、不透气、可塑性差的技术问题。
本发明的第一方面提供一种石膏丸的制备方法,包括如下步骤:
将硅溶胶、转晶剂、抗菌防霉剂和水混合均匀,得到壳层的辅助材料;
提供核层材料和壳层的主材料,将壳层材料通过水化凝结的方式包覆在核层材料表面,得到石膏丸;壳层材料由壳层的主材料和壳层的辅助材料组成,壳层的主材料包括石膏粉。
本发明的第二方面提供一种石膏丸,该石膏丸通过本发明第一方面提到的石膏丸的制备方法得到。
本发明的第三方面提供一种石膏丸药枕,该石膏丸药枕包含本发明第一方面提供的石膏丸的制备方法得到的石膏丸。
与现有技术相比,本发明的有益效果为:
本发明中,通过采用石膏粉为壳层的主材料包覆在轻质核层材料表面并直接水化凝结,避免了因石膏粉水化凝固快,不易搓丸的问题,石膏丸成型效果好。
本发明所得石膏丸药枕具有按摩功能,同时具有可塑性好,通气,清热,降火,保护颈椎,镇静助眠的优势。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明的第一方面提供了一种石膏丸的制备方法,包括如下步骤:
S1将硅溶胶、转晶剂、抗菌防霉剂和水混合均匀,得到壳层的辅助材料;
S2提供核层材料和壳层的主材料,将壳层材料通过水化凝结的方式包覆在核层材料表面,得到石膏丸。其中,壳层材料由壳层的主材料和壳层的辅助材料组成,壳层的主材料包括石膏粉。
本发明中,通过采用石膏粉作为壳层的主材料包覆在轻质核层材料表面并直接水化凝结,避免了因石膏粉水化凝固快,不易搓丸的问题,石膏丸成型效果好,同时所得石膏丸具有质轻的优势。
本发明中,通过加入硅溶胶能够与石膏粉配合,起到无机粘结剂的作用,将石膏粉粘合在核层材料表面,同时显著提高石膏丸的力学性能,避免其表面破裂;通过加入转晶剂能够促进晶体转化,提高所得石膏丸的强度;通过加入抗菌防霉剂能够提高石膏丸的抑菌、防霉性能。
本实施方式中,壳层的辅助材料,按重量份计,包括:硅溶胶80~100份、转晶剂2~8份、抗菌防霉剂2~8份和水900~1200份。
本发明对硅溶胶、转晶剂和抗菌防霉剂的具体种类和型号不作限定,本领域技术人员可以根据实际情况进行选择。例如,硅溶胶可以为ZS-30,转晶剂可以为HQ-G100,抗菌防霉剂可以为HQ-FM。
本实施方式中,石膏粉为α石膏粉、β石膏粉中的一种或两种。
本实施方式中,壳层的主材料还包括中药粉或花草粉中的一种或两种。本发明中,对中药粉和花草粉的具体组成不做限制,其可为保健枕领域常见的中药粉和花草粉。例如,中药粉可以为何首乌、白芷、葛根、干姜、紫苏、杏仁、酸枣仁、益智仁、藿香、荷叶、决明子、丁香中的一种或多种,花草粉可以为玫瑰花粉、薰衣草粉等。本发明中,通过将石膏粉与中药粉和/或花草粉混合,制成石膏丸,能够发挥中药粉和花草粉的功效,提高保健枕的性能。
进一步地,石膏粉与中药粉和/或花草粉的质量比为1:(0.25~0.4)。在该范围内,所得石膏丸具有更好的强度,同时能更好的发挥中药粉和花草粉的功效。
本实施方式中,核层材料的容重为50~300kg/m3,粒径范围为0.01mm~5mm,进一步为0.02~2.5mm。本发明通过选用轻质材料作为核层材料,有利于降低所得石膏丸的重量;本发明对具体选用的轻质材料的种类不作限定,能满足上述要求即可。例如,选用的核层可以为玻化微珠、膨胀珍珠岩、EPS(聚苯乙烯泡沫)或EPP(聚丙烯塑料发泡材料)中的一种或多种。
本实施方式中,壳层的主材料与壳层的辅助材料的质量比为1:(0.05~0.1),进一步为1:(0.065~0.1)。
本实施方式中,核层材料与壳层材料的质量比为1:(45~100),进一步为1:(60~100)。
本发明中,所得石膏丸的粒径范围为1mm~8mm。
本实施方式中,上述将壳层材料通过水化凝结的方式包覆在核层材料表面具体为:采用喷雾的方式使壳层的辅助材料润湿核层材料,随后加入壳层的主材料,使壳层材料在核层材料表面水化凝结,然后进行成化干燥,得到石膏丸。
进一步地,壳层材料包覆在核层材料表面的过程可通过圆盘造球机进行,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动后形成母球,细粒度物料在潮湿的母球表面滚动,使得母球长大并具有一定的强度,不同的球粒在圆盘中沿不同轨道运行,最终得到成品。更进一步地,该过程持续5~30min,优选为10~15min。
进一步地,壳层的主材料材料也采用喷雾的方式加入;干燥可为烘干或风干,且烘干的温度不超过100℃。更进一步地,烘干后还可进行筛选分级。
本发明的第二方面提供了一种石膏丸,该石膏丸通过本发明第一方面提到的石膏丸的制备方法得到。
本发明的第三方面提供了一种石膏丸药枕,该石膏丸药枕包含本发明第一方面提供的石膏丸的制备方法得到的石膏丸。
进一步地,石膏丸药枕包括枕芯,枕芯内填充有本发明第一方面提付的石膏丸的制备方法得到的石膏丸。
本发明通过将石膏丸取代现有的石膏枕中的石膏粉和石膏块,药效时间长、效果好、透气性好、塑型性佳。
本发明以下实施例和对比例中,所用部分组分技术指标如下:
α石膏粉,购自湖北沃欲新材料有限公司,粒度500目,初凝时间6min;
β石膏粉,购自湖北沃欲新材料有限公司,粒度300目,初凝时间4min;
玫瑰花粉和何首乌粉,粒度500目;
硅溶胶,购自浙江宇达化工有限公司,型号为ZS-30;
转晶剂,购自浙江恒起新材料科技有限公司,型号为HQ-G100;
抗菌防霉剂,购自浙江恒起新材料科技有限公司,型号为HQ-FM;
玻化微珠,购自信阳市中森珍珠岩应用有限公司,具体指标如表1:
表1
闭孔珍珠岩,购自信阳市中森珍珠岩应用有限公司,具体指标如表2:
表2
物理性能 | 参数 |
粒径(mm) | 0.02-2.50 |
容重(Kg/m<sup>3</sup>) | 100-265 |
导热系数(w/m.k) | 0.036-0.054 |
压缩比(1Mp) | <0.50 |
吸水率(%) | 50-86 |
灼失率(%) | <0.5 |
耐火度(℃) | 1280-1360℃ |
实施例1
本实施例提供了一种石膏丸药枕,包括枕芯,枕芯内填充有石膏丸。
石膏丸具体通过如下步骤制备:
(1)将0.9g硅溶胶、0.04g转晶剂、0.06g抗菌防霉剂和10g水混合均匀,得到壳层的辅助材料;
(2)提供3g玻化微珠、90gα石膏粉和80gβ石膏粉,将玻化微珠加入圆盘造球机中,并采用喷雾的方式使壳层的辅助材料润湿玻化微珠,随后加入预先混合好的α石膏粉和β石膏粉,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动,持续10~15min,直至壳层材料在玻化微珠表面水化凝结,经成化干燥,得到石膏丸。
实施例2
本实施例提供了一种石膏丸药枕,包括枕芯,枕芯内填充有石膏丸。
石膏丸具体通过如下步骤制备:
(1)将0.8g硅溶胶、0.08g转晶剂、0.02g抗菌防霉剂和9g水混合均匀,得到壳层的辅助材料;
(2)提供3g闭孔珍珠岩、100gβ石膏粉和25g玫瑰花粉,将闭孔珍珠岩加入圆盘造球机中,并采用喷雾的方式使壳层的辅助材料润湿闭孔珍珠岩,随后加入预先混合好的β石膏粉和玫瑰花粉,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动,持续10~15min,直至壳层材料在闭孔珍珠岩表面水化凝结,经成化干燥,得到石膏丸。
实施例3
本实施例提供了一种石膏丸药枕,包括枕芯,枕芯内填充有石膏丸。
石膏丸具体通过如下步骤制备:
(1)将1g硅溶胶、0.02g转晶剂、0.08g抗菌防霉剂和12g水混合均匀,得到壳层的辅助材料;
(2)提供1.35g玻化微珠和90gα石膏粉、35g何首乌粉,将玻化微珠加入圆盘造球机中,并采用喷雾的方式使壳层的辅助材料润湿玻化微珠,随后加入预先混合好的α石膏粉和何首乌粉,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动,持续10~15min,直至壳层材料在玻化微珠表面水化凝结,经成化干燥,得到石膏丸。
实施例4
本实施例提供了一种石膏丸药枕,包括枕芯,枕芯内填充有石膏丸。
石膏丸具体通过如下步骤制备:
(1)将0.8g硅溶胶、0.08g转晶剂、0.02g抗菌防霉剂和9g水混合均匀,得到壳层的辅助材料;
(2)提供3g闭孔珍珠岩和80gβ石膏粉和45g玫瑰花粉,将闭孔珍珠岩加入圆盘造球机中,并采用喷雾的方式使壳层的辅助材料润湿闭孔珍珠岩,随后加入预先混合好的石膏粉和玫瑰花粉,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动,持续10~15min,直至壳层材料在闭孔珍珠岩表面水化凝结,经成化干燥,得到石膏丸。
对比例1
对比例1中,未加入硅溶胶,其余与实施例1一致。具体原料为:
0.04g转晶剂、0.06g抗菌防霉剂、10g水、3g玻化微珠、90gα石膏粉和80gβ石膏粉。
对比例2
对比例2中,采用何首乌粉替代石膏粉,其余与实施例1一致。具体原料为:
0.9g硅溶胶、0.04g转晶剂、0.06g抗菌防霉剂、10g水、3g玻化微珠、170g何首乌粉。
试验组
对上述实施例1~4和对比例1~2所得石膏丸进行性能测试,结果见表1。
表3
由表3可以看出,本发明实施例1~4所得石膏丸成型效果好,具有较高的筒压强度,能够满足枕头的需求;同时解决了现有的石膏枕硬度大,不透气,可塑性差的难题。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到的变化或替换,都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种石膏丸的制备方法,其特征在于,包括如下步骤:
将硅溶胶、转晶剂、抗菌防霉剂和水混合均匀,得到壳层的辅助材料;
提供核层材料和壳层的主材料,将壳层材料通过水化凝结的方式包覆在所述核层材料表面,得到石膏丸;所述壳层材料由所述壳层的主材料和所述壳层的辅助材料组成,所述壳层的主材料包括石膏粉。
2.根据权利要求1所述石膏丸的制备方法,其特征在于,所述壳层的辅助材料,按重量份计,包括:硅溶胶80~100份、转晶剂2~8份、抗菌防霉剂2~8份和水900~1200份。
3.根据权利要求1所述石膏丸的制备方法,其特征在于,所述壳层的主材料还包括中药粉或花草粉。
4.根据权利要求3所述石膏丸的制备方法,其特征在于,所述石膏粉与所述中药粉和/或花草粉的质量比为1:(0.25~0.4)。
5.根据权利要求1所述石膏丸的制备方法,其特征在于,所述核层材料的容重为50~300kg/m3,粒径范围为0.01mm~5mm。
6.根据权利要求1所述石膏丸的制备方法,其特征在于,所述壳层的主材料与所述壳层的辅助材料的质量比为1:(0.05~0.1),所述核层材料与所述壳层材料的质量比为1:(45~100)。
7.根据权利要求1所述石膏丸的制备方法,其特征在于,所述将壳层材料通过水化凝结的方式包覆在核层材料表面具体为:采用喷雾的方式使所述壳层的辅助材料润湿所述核层材料,随后加入所述壳层的主材料,使所述壳层材料在所述核层材料表面水化凝结,然后进行成化干燥,得到石膏丸。
8.根据权利要求7所述石膏丸的制备方法,其特征在于,所述壳层材料包覆在所述核层材料表面的过程通过圆盘造球机进行,混合料在倾斜且旋转的圆盘中受重力、离心力和摩擦力的共同作用产生滚动和搓动后形成母球,细粒度物料在潮湿的母球表面滚动,使得母球长大并具有一定的强度,不同的球粒在圆盘中沿不同轨道运行,最终得到成品。
9.一种石膏丸,其特征在于,所述石膏丸通过权利要求1~8中任一项所述石膏丸的制备方法得到。
10.一种石膏丸药枕,其特征在于,所述石膏丸药枕包含权利要求1~8中任一项所述石膏丸的制备方法得到的石膏丸。