CN112852428A - Electric appliance panel touch glass water-based frosting powder for improving skin touch and application thereof - Google Patents
Electric appliance panel touch glass water-based frosting powder for improving skin touch and application thereof Download PDFInfo
- Publication number
- CN112852428A CN112852428A CN202110125155.8A CN202110125155A CN112852428A CN 112852428 A CN112852428 A CN 112852428A CN 202110125155 A CN202110125155 A CN 202110125155A CN 112852428 A CN112852428 A CN 112852428A
- Authority
- CN
- China
- Prior art keywords
- frosting
- glass
- parts
- electric appliance
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of glass processing, and particularly relates to electric appliance panel touch glass water-based frosting powder for improving skin touch and application thereof. The invention prepares the electric appliance panel touch glass water-based frosting powder for improving skin feel by adjusting the formula of the frosting powder, and is used for processing the frosting of the electric appliance panel touch glass, the obtained electric appliance panel touch glass anti-dazzle parameter can be adjusted, the range is wider, and the roughness range is 0.3-0.7. The surface tension changes in the processing process of the touch glass of the electric appliance panel, so that the surface of the glass can resist corrosion, oil stain and scratch. The anti-dazzle effect of the touch glass of the electric appliance panel can change the light reflecting surface of the original glass into a matte diffuse reflection surface, the light reflecting degree of the touch glass of the electric appliance panel can be reduced, light shadow is reduced, the surface of the touch glass of the electric appliance panel is fine and smooth in hand feeling, and the touch glass is more comfortable.
Description
Technical Field
The invention belongs to the technical field of glass processing, and particularly relates to electric appliance panel touch glass water-based frosting powder for improving skin feel and application of the electric appliance panel touch glass water-based frosting powder in electric appliance panel touch glass frosting processing.
Background
With the development of technology, various glass panels are applied to different furniture and electric appliances, some are applied to the table top of the furniture to obtain decorative and aesthetic effects, and some are applied to the housing of household appliances, such as the glass panel of a refrigerator door. The main problem that the manufactured electric appliance glass panel is easy to reflect light is that the electric appliance glass panel not only causes poor touch feeling, but also easily makes eyes of people dizzy in the using process.
The Chinese patent with the publication number of CN105152541B discloses a frosting powder for processing anti-dazzle glass and a preparation method thereof, wherein the raw materials of the frosting powder and the proportion of the raw materials are selected, and a moisture-proof agent is added under the condition of not influencing the etching property of the frosting powder, so that the problem that the frosting powder is deteriorated due to excessive water absorption is solved, however, the frosting powder in the patent does not have the effect of improving the touch feeling of the glass.
Based on the current situation, the invention aims to develop the glass frosting powder for the touch glass of the panel of the electric appliance and apply the glass frosting powder to the household electric appliance so as to improve the anti-dizziness effect of the existing glass panel and improve the touch of the glass panel.
Disclosure of Invention
In view of the problems in the prior art, the first object of the present invention is to provide an aqueous frosting powder for touch glass of an electrical panel, which can improve the skin feel, and the modification of the structure of the glass surface of the electrical panel can be realized by improving the formula of the frosting powder.
The second purpose of the invention is to provide a preparation method of the electric appliance panel touch glass water-based frosting powder for improving skin feel.
The third purpose of the invention is to provide the application of the electric appliance panel touch glass water-based frosting powder for improving skin feel in electric appliance panel touch glass frosting processing.
Based on the purpose, the invention adopts the following technical scheme:
the electric appliance panel touch glass water-based frosting powder for improving skin feel is prepared by mixing the following raw materials in parts by weight:
40-60 parts of ammonium bifluoride,
5-10 parts of ammonium sulfate, namely ammonium sulfate,
5-10 parts of ammonium chloride, namely,
5-15 parts of potassium chloride, namely,
2-15 parts of potassium sulfate, namely,
5-10 parts of potassium fluoride,
3-5 parts of sodium hexametaphosphate,
5-10 parts of barium sulfate, namely barium sulfate,
0.5-2 parts of Arabic resin adhesive.
Furthermore, the electric appliance panel touch glass water-based frosting powder for improving the skin feel is prepared by mixing the following raw materials in parts by weight:
45-55 parts of ammonium bifluoride,
8-10 parts of ammonium sulfate, namely ammonium sulfate,
8-10 parts of ammonium chloride, namely,
8-12 parts of potassium chloride, namely,
2-10 parts of potassium sulfate, namely,
8-10 parts of potassium fluoride,
4-5 parts of sodium hexametaphosphate,
8-10 parts of barium sulfate, namely barium sulfate,
0.5-1 part of Arabic resin adhesive.
A preparation method of the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
the frosting powder raw material is mixed and stirred according to the proportion of the components, the materials are crushed after stirring, and the crushed materials are filtered through a 100-mesh and 200-mesh screen and packaged, thus obtaining the finished product of the touch glass water-based frosting powder for the electrical appliance panel for improving skin touch.
Specifically, the stirring time is 10-20min, and the stirring temperature is 16-26 ℃.
The electric appliance panel touch glass water-based frosting powder for improving skin feel is applied to electric appliance panel touch glass frosting processing.
A method for processing electric appliance panel touch glass frosting by using the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
(1) before the electric appliance panel touch glass water-based frosting powder for improving skin feel is used, the water-based frosting powder and hydrochloric acid are prepared into a frosting solution, and then the frosting solution and water are prepared into a water-based frosting powder aqueous solution for curing;
(2) before frosting the touch glass of the electric appliance panel, firstly, pickling the touch glass of the electric appliance panel to remove stains on the surface of the glass; washing the mixture to be neutral by using clear water after acid washing;
(3) the glass frosting processing of the touch glass of the electric appliance panel is carried out by adopting a cured water-based frosting powder aqueous solution in a soaking or sand spraying mode;
(4) and cleaning, polishing and drying the glass after the frosting processing to obtain a finished product.
Further, when the preparation in the step (1) is carried out, the weight ratio of the water-based frosting powder to the hydrochloric acid is 4.5-7:1, and the hydrochloric acid is industrial hydrochloric acid with the mass concentration of 30-40%.
Preferably, the weight ratio of the water-based frosting powder to the hydrochloric acid in the preparation in the step (1) is 4.5-5.5: 1.
Further, when curing in the step (1), 5-10 kg of water is added into 25 kg of the frosting solution, and the mixture is mixed uniformly to prepare an aqueous solution, and the aqueous solution is placed until the temperature of the aqueous solution is restored to the room temperature.
Further, the acid washing in the step (2) is mainly carried out by using dilute sulfuric acid with the mass fraction of 15% -18%.
Further, the soaking method in the step (3) comprises the following steps: soaking the cleaned glass into the cured water-based frosting powder aqueous solution at normal temperature (16-26 ℃), shaking for 75-150 seconds, and taking out for cleaning; the sand spraying method comprises the following steps: the glass is sprayed for 75-150 seconds at normal temperature (16-26 ℃) by adopting conventional sand spraying equipment and then cleaned.
Compared with the prior art, the invention has the beneficial effects that:
1. the frosting powder raw material is convenient to transport, and the preparation method is simple.
2. The method for processing the glass frosting with the touch of the electrical panel by the water-based frosting powder is flexible, and the glass frosting can be soaked or sprayed.
3. The obtained touch glass of the electrical appliance panel has adjustable anti-dazzle parameters, a wide range and an adjustable roughness range of 0.3-0.7.
4. The surface tension changes in the processing process of the touch glass of the electric appliance panel, so that the surface of the glass can resist corrosion, oil stain and scratch.
5. The anti-dazzle effect of the touch glass of the electric appliance panel can change the light reflecting surface of the original glass into a matte diffuse reflection surface, the light reflecting degree of the touch glass of the electric appliance panel can be reduced, light shadow is reduced, the surface of the touch glass of the electric appliance panel is fine and smooth in hand feeling, and the touch glass is more comfortable.
Detailed Description
In order to make the technical purpose, technical solutions and advantages of the present invention clearer, the technical solutions of the present invention are further described with reference to specific examples, which are intended to explain the present invention and are not to be construed as limiting the present invention, and those who do not specify a specific technique or condition in the examples follow the techniques or conditions described in the literature in the art or follow the product specification.
Example 1
The electric appliance panel touch glass water-based frosting powder for improving skin feel is prepared by mixing the following raw materials in parts by weight:
50 parts of ammonium bifluoride,
5 parts of ammonium sulfate, namely ammonium sulfate,
5 parts of ammonium chloride, namely 5 parts of ammonium chloride,
5 parts of potassium chloride, namely adding 5 parts of potassium chloride,
2 parts of potassium sulfate, namely potassium sulfate,
5 parts of potassium fluoride, namely potassium fluoride,
7.5 parts of barium sulfate, namely barium sulfate,
5 parts of sodium hexametaphosphate,
0.5 part of Arabic resin glue powder.
The preparation method of the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
the frosting powder raw materials are mixed according to the mixture ratio of the components, placed in a stirring kettle, stirred and fed, stirred for 10min at the temperature of 25 ℃ after the raw materials are added, the stirred materials enter a crusher through a conveying device to be crushed, and the crushed materials pass through a 100-mesh screen and are packaged, so that the finished product of the electric appliance panel touch glass water-based frosting powder for improving the skin feel is obtained.
A method for processing electric appliance panel touch glass frosting by using the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
(1) before the electric appliance panel touch glass water-based frosting powder for improving skin feel is used, firstly, preparing the water-based frosting powder and hydrochloric acid into a frosting solution, then preparing a water-based frosting powder aqueous solution from the frosting solution and water for curing, adding 15 kg of hydrochloric acid into 70.5 kg of water-based frosting powder, uniformly mixing to prepare a frosting solution, adding 10 kg of water into every 25 kg of frosting solution, uniformly mixing to prepare an aqueous solution, and standing until the temperature of the aqueous solution is restored to room temperature, namely the cured product is good; the hydrochloric acid is industrial hydrochloric acid with the mass concentration of 30%;
(2) before frosting the touch glass of the electric appliance panel, firstly, pickling the touch glass of the electric appliance panel to remove stains on the surface of the glass, and during pickling, treating the touch glass by using dilute sulfuric acid with the mass fraction of 15%, and then washing the touch glass to be neutral by using clean water;
(3) the method comprises the following steps of (1) carrying out glass frosting processing on touch glass of an electric appliance panel in a soaking mode by adopting a cured water-based frosting powder aqueous solution, specifically, vertically soaking cleaned glass into the cured water-based frosting powder aqueous solution at normal temperature (20 ℃), shaking the glass for 75-150 seconds at a small amplitude after the glass is completely soaked into the water-based frosting powder aqueous solution, and taking out and cleaning the glass;
(4) and cleaning, polishing and drying the glass after the frosting processing at 25 ℃ to obtain the finished product of the touch glass of the electric appliance panel.
The electric appliance panel touch glass processed by the frosting of the embodiment has smooth touch and good anti-glare effect.
The processed touch glass of the electric appliance panel is checked by a roughness meter, a gloss meter and a photoelectric haze meter, and the detection results are as follows:
roughness (micrometer) index Ra: 0.65-0.75, gloss (60 degree angle) index: 10-15 GU; haze: 80-95 percent.
Example 2
The electric appliance panel touch glass water-based frosting powder for improving skin feel is prepared by mixing the following raw materials in parts by weight:
50 parts of ammonium bifluoride,
7 parts of ammonium sulfate, namely ammonium sulfate,
7 parts of ammonium chloride, namely 7 parts of ammonium chloride,
7 parts of potassium chloride, namely potassium chloride,
2 parts of potassium sulfate, namely potassium sulfate,
7 parts of potassium fluoride, namely 7 parts of potassium fluoride,
7.5 parts of barium sulfate, namely barium sulfate,
5 parts of sodium hexametaphosphate,
1 part of Arabic resin glue powder.
The preparation method of the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
the frosting powder raw materials are mixed according to the mixture ratio of the components, placed in a stirring kettle, stirred and fed, stirred for 20min at the temperature of 16 ℃ after the raw materials are added, the stirred materials enter a crusher through a conveying device to be crushed, and the crushed materials pass through a 100-mesh screen and are packaged, so that the finished product of the electric appliance panel touch glass water-based frosting powder for improving the skin feel is obtained.
A method for processing electric appliance panel touch glass frosting by using the electric appliance panel touch glass water-based frosting powder for improving skin feel comprises the following steps:
(1) before the electric appliance panel touch glass water-based frosting powder for improving skin feel is used, firstly, preparing the water-based frosting powder and hydrochloric acid into a frosting solution, then preparing a water-based frosting powder aqueous solution from the frosting solution and water for curing, adding 25 kg of hydrochloric acid into 137 kg of water-based frosting powder, uniformly mixing to prepare a frosting solution, adding 5 kg of water into each 25 kg of frosting solution, uniformly mixing to prepare an aqueous solution, and standing until the temperature of the aqueous solution is recovered to room temperature, thus obtaining cured glass; the hydrochloric acid is industrial hydrochloric acid with the mass concentration of 40%;
(2) before frosting the touch glass of the electric appliance panel, firstly, pickling the touch glass of the electric appliance panel to remove stains on the surface of the glass, and during pickling, treating the touch glass by using dilute sulfuric acid with the mass fraction of 18%, and then washing the touch glass to be neutral by using clean water;
(3) the method comprises the following steps of (1) carrying out glass frosting processing on touch glass of an electric appliance panel in a soaking mode by adopting a cured water-based frosting powder aqueous solution, specifically, vertically soaking cleaned glass into the cured water-based frosting powder aqueous solution at normal temperature (16 ℃), shaking the glass for 75-150 seconds at a small amplitude after the glass is completely soaked into the water-based frosting powder aqueous solution, and taking out and cleaning the glass;
(4) and cleaning, polishing and drying the glass after the frosting processing at 16 ℃ to obtain the finished product of the touch glass of the electric appliance panel.
The electric appliance panel touch glass processed by the frosting of the embodiment has smooth touch and good anti-glare effect.
The processed touch glass of the electric appliance panel is checked by a roughness meter, a gloss meter and a photoelectric haze meter, and the detection results are as follows:
roughness (micrometer) index Ra: 0.45-0.55, gloss (60 degree angle) index: 10-15 GU; haze: 50 to 70 percent.
Finally, it should be noted that: the above embodiments are merely illustrative and not restrictive of the technical solutions of the present invention, and any equivalent substitutions and modifications or partial substitutions made without departing from the spirit and scope of the present invention should be included in the scope of the claims of the present invention.
Claims (10)
1. The electric appliance panel touch glass water-based frosting powder for improving skin feel is characterized by being prepared by mixing the following raw materials in parts by weight:
40-60 parts of ammonium bifluoride,
5-10 parts of ammonium sulfate, namely ammonium sulfate,
5-10 parts of ammonium chloride, namely,
5-15 parts of potassium chloride, namely,
2-15 parts of potassium sulfate, namely,
5-10 parts of potassium fluoride,
3-5 parts of sodium hexametaphosphate,
5-10 parts of barium sulfate, namely barium sulfate,
0.5-2 parts of Arabic resin adhesive.
2. The skin-feel-improved electric appliance panel touch glass water-based frosting powder as set forth in claim 1, which is prepared by mixing the following raw materials in parts by weight:
45-55 parts of ammonium bifluoride,
8-10 parts of ammonium sulfate, namely ammonium sulfate,
8-10 parts of ammonium chloride, namely,
8-12 parts of potassium chloride, namely,
2-10 parts of potassium sulfate, namely,
8-10 parts of potassium fluoride,
4-5 parts of sodium hexametaphosphate,
8-10 parts of barium sulfate, namely barium sulfate,
0.5-1 part of Arabic resin adhesive.
3. A process for preparing a skin feel improving electrical panel touch glass aqueous frosting powder of claim 1 or 2, comprising the steps of:
the frosting powder raw material is mixed and stirred according to the proportion of the components, the materials are crushed after stirring, and the crushed materials are filtered through a 100-mesh and 200-mesh screen and packaged, thus obtaining the finished product of the touch glass water-based frosting powder for the electrical appliance panel for improving skin touch.
4. The method of claim 3, wherein the stirring time is 10-20min and the stirring temperature is 16-26 ℃.
5. Use of the improved skin feel electrical panel touch glass aqueous frosting powder of claim 1 or 2 in electrical panel touch glass frosting processing.
6. A method of processing an electrical panel touch glass frosting with the skin feel improving electrical panel touch glass aqueous frosting powder of claim 1 or 2, comprising the steps of:
(1) before the electric appliance panel touch glass water-based frosting powder for improving skin feel is used, the water-based frosting powder and hydrochloric acid are prepared into a frosting solution, and then the frosting solution and water are prepared into a water-based frosting powder aqueous solution for curing;
(2) before frosting the touch glass of the electric appliance panel, firstly, pickling the touch glass of the electric appliance panel to remove stains on the surface of the glass; washing the mixture to be neutral by using clear water after acid washing;
(3) the glass frosting processing of the touch glass of the electric appliance panel is carried out by adopting a cured water-based frosting powder aqueous solution in a soaking or sand spraying mode;
(4) and cleaning, polishing and drying the glass after the frosting processing to obtain a finished product.
7. The method for frosting process according to claim 6, wherein the weight ratio of the aqueous frosting powder to the hydrochloric acid is 4.5-7:1 when the step (1) is configured, and the hydrochloric acid is industrial hydrochloric acid with a mass concentration of 30-40%.
8. The method of frosting process according to claim 6, wherein in the aging in step (1), 5-10 kg of water is added to 25 kg of frosting solution, and after mixing, the mixture is made into an aqueous solution, and the aqueous solution is left until the temperature of the aqueous solution is restored to room temperature.
9. The method of frosting process according to claim 6, wherein the acid washing in step (2) is performed by using dilute sulfuric acid with a mass fraction of 15% -18%.
10. The frosting process of claim 6, wherein the soaking in step (3) is performed by: soaking the cleaned glass into the cured water-based frosting powder water solution at the temperature of 16-26 ℃, shaking for 75-150 seconds, and taking out for cleaning; the sand spraying method comprises the following steps: spraying the glass for 75-150 seconds at 16-26 ℃ by adopting sand spraying equipment, and cleaning.