CN105970629A - After-finishing process for textile fabric with antistatic function - Google Patents
After-finishing process for textile fabric with antistatic function Download PDFInfo
- Publication number
- CN105970629A CN105970629A CN201610447460.8A CN201610447460A CN105970629A CN 105970629 A CN105970629 A CN 105970629A CN 201610447460 A CN201610447460 A CN 201610447460A CN 105970629 A CN105970629 A CN 105970629A
- Authority
- CN
- China
- Prior art keywords
- dry
- dressing liquid
- water
- finishing process
- postfinishing process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an after-finishing process for a textile fabric with an antistatic function. The after-finishing process is characterized in that the after-finishing process is finished by scouring, singeing, washing, steeping, rolling, stirring, secondary rolling and drying. The after-finishing process has the following advantages: the fabric produced by the antistatic after-finishing process is good in stability, a nano-scale metal oxide is uniformly distributed on the fabric and has low probability of falling off, and excellent antistatic and antibacterial functions are achieved.
Description
Technical field
The invention belongs to textile technology field, be specifically related to the rear finishing duplex of a kind of weaving face fabric with anti-static function
Skill.
Background technology
Along with raising, the enhancing of the awareness of environment protection and health of people's living standard, the requirement to fabric is more and more higher,
Ask fabric not only to have certain softness, a characteristic such as crease-resistant, and simultaneously need to fabric has antistatic, the function such as antibacterial.Logical
Normal method is to add antistatic fibre to carry out blending in woollen, metal system antistatic fibre good conductivity, and resistivity is low, but
It is that feel is poor;White carbon black system antistatic fibre color is single, limits the color of wool spinning fabric itself;Conductive polymer subbundle is steady
Qualitative difference, the prolongation over time of its antistatic behaviour is slowly failed.Therefore, it is necessary to antistatic wool spinning fabric in prior art
Production technology improves.
Summer, aerial temperature and humidity was big, and antibacterial easily grows, and the therefore exploitation one contact existing cool feeling of skin has again antibacterial guarantor
The bed necessaries fabric of health-care function is particularly important.Flax fiber is described as " fiber queen ", have moisture absorption breathe freely good, clearly perspire, anti-
Natural anti-ultraviolet that bacterium is antibacterial, stronger and the antistatic behaviour performance of excellence, but the degree of crystallinity of fiber is high, the degree of orientation big, fiber
Rigidity is big, poor flexibility, therefore coherent is poor, is unfavorable for yarn strength and production high-count yarn.Chitin fiber have antibacterial,
Biodegradable and excellent moisture retentive heat insulation function, but chitin fiber fineness slightly, the least, coefficient of friction is little, fiber obvolvent
Power is little, and spinnability is poor.
Summary of the invention
Present invention aims to the deficiencies in the prior art, propose a kind of fabric good stability, nano level metal oxygen
Compound is evenly distributed and difficult drop-off on cloth, have excellence antistatic and antibacterial functions there is spinning of anti-static function
Knitted fabric postfinishing process.
For achieving the above object, the technical scheme is that the rear whole of a kind of weaving face fabric with anti-static function
Science and engineering skill, its innovative point is: through kiering, singe, rinse, impregnate, dry, stir, secondary dries and completes with baking step
Postfinishing process;Specifically comprise the following steps that
(1) kiering: described working solution uses solute to be NaOH, Na2SiO3, refining agent ZTO, penetrating agent section woods and chelating agen, institute
State NaOH, Na2SiO3, refining agent ZTO, the concentration of penetrating agent section woods and chelating agen be followed successively by 10-20g/L, 4-5g/L, 9-13g/
L, 80-100g/L, 1-2g/L, the solvent of described working solution is water;
(2) singe: described in speed of singing be 70-90m/min, flame temperature is 1200-1300 DEG C;
(3) rinse: select clear water to be rinsed;
(4) dipping: be positioned in the first dressing liquid immersion treatment 30-45min under room temperature, the component of described first dressing liquid and each
Weight percentages of components is respectively as follows: polyurethane resin 4-8%, softening agent 1-2%, fatty alcohol-polyoxyethylene ether 0.2-0.3%, Fructus Citri Limoniae
Acid 1-4%, residue is all water;
(5) dry: dry in roll;
(6) stirring: be positioned in the second dressing liquid and soak and stir process 20-30min under room temperature, the group of described second dressing liquid
Divide and each weight percentages of components is respectively as follows: nanometer SnO2 powder body 0.1-0.2%, nano ZnO powder 0.2-0.3%, poly alkyl alcohol
Oxygen vinyl Ether 0.2-0.3%, Polyethylene Glycol 10-16%;Acid-base modifier 0.1-0.2%, remaining is water, described second dressing liquid
PH value is 7;
(7) secondary dries: dry in roll;
(8) dry: the temperature of described baking oven is 90-120 DEG C.
Further, dry described in and pick-up that secondary dries is 70-90%.
Further, in described baking step, described drying time is 15-20min.
Beneficial effects of the present invention is as follows: the fabric good stability that the antistatic postfinishing process of the present invention produces, nanometer
Level metal-oxide is evenly distributed and difficult drop-off on cloth, has antistatic and the antibacterial functions of excellence.
Detailed description of the invention
By particular specific embodiment, embodiments of the present invention being described below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
The postfinishing process of a kind of weaving face fabric with anti-static function, through kiering, singes, rinses, impregnates, dries, stirs
Mix, secondary dries and completes postfinishing process with baking step;Specifically comprise the following steps that
(1) kiering: working solution uses solute to be NaOH, Na2SiO3, refining agent ZTO, penetrating agent section woods and chelating agen, NaOH,
Na2SiO3, refining agent ZTO, the concentration of penetrating agent section woods and chelating agen be followed successively by 10g/L, 4g/L, 9g/L, 80g/L, 1 g/L, work
The solvent making liquid is water;
(2) singing: speed of singing is 70m/min, flame temperature is 1200 DEG C;
(3) rinse: select clear water to be rinsed;
(4) dipping: be positioned in the first dressing liquid immersion treatment 30min, the component of the first dressing liquid and each component weight under room temperature
Amount percentage ratio is respectively as follows: polyurethane resin 4%, softening agent 1%, fatty alcohol-polyoxyethylene ether 0.2%, citric acid 1%, and residue is all
Water;
(5) drying: dry in roll, pick-up is 70%;
(6) stirring: be positioned in the second dressing liquid under room temperature and soak and stir process 20min, the component of the second dressing liquid and each
Weight percentages of components is respectively as follows: nanometer SnO2 powder body 0.1%, nano ZnO powder 0.2%, fatty alcohol-polyoxyethylene ether 0.2%, gathers
Ethylene glycol 10%;Acid-base modifier 0.1%, remaining is water, and the pH value of the second dressing liquid is 7;
(7) secondary dries: dry in roll, and pick-up is 70%;
(8) dry: the temperature of baking oven is 90 DEG C;Drying time is 15min.
Embodiment 2
The postfinishing process of a kind of weaving face fabric with anti-static function, through kiering, singes, rinses, impregnates, dries, stirs
Mix, secondary dries and completes postfinishing process with baking step;Specifically comprise the following steps that
(1) kiering: working solution uses solute to be NaOH, Na2SiO3, refining agent ZTO, penetrating agent section woods and chelating agen, NaOH,
Na2SiO3, refining agent ZTO, the concentration of penetrating agent section woods and chelating agen be followed successively by 20g/L, 5g/L, 13g/L, 100g/L, 2g/L,
The solvent of working solution is water;
(2) singing: speed of singing is 90m/min, flame temperature is 1300 DEG C;
(3) rinse: select clear water to be rinsed;
(4) dipping: be positioned in the first dressing liquid immersion treatment 45min, the component of the first dressing liquid and each component weight under room temperature
Amount percentage ratio is respectively as follows: polyurethane resin 8%, softening agent 2%, fatty alcohol-polyoxyethylene ether 0.3%, citric acid 4%, and residue is all
Water;
(5) drying: dry in roll, pick-up is 90%;
(6) stirring: be positioned in the second dressing liquid under room temperature and soak and stir process 30min, the component of the second dressing liquid and each
Weight percentages of components is respectively as follows: nanometer SnO2 powder body 0.2%, nano ZnO powder 0.3%, fatty alcohol-polyoxyethylene ether 0.3%, gathers
Ethylene glycol 16%;Acid-base modifier 0.2%, remaining is water, and the pH value of the second dressing liquid is 7;
(7) secondary dries: dry in roll, and pick-up is 90%;
(8) dry: the temperature of baking oven is 120 DEG C;Drying time is 20min.
Embodiment 3
The postfinishing process of a kind of weaving face fabric with anti-static function, through kiering, singes, rinses, impregnates, dries, stirs
Mix, secondary dries and completes postfinishing process with baking step;Specifically comprise the following steps that
(1) kiering: working solution uses solute to be NaOH, Na2SiO3, refining agent ZTO, penetrating agent section woods and chelating agen, NaOH,
Na2SiO3, refining agent ZTO, the concentration of penetrating agent section woods and chelating agen be followed successively by 15g/L, 4.5g/L, 10g/L, 90g/L, 1.5g
/ L, the solvent of working solution is water;
(2) singing: speed of singing is 80m/min, flame temperature is 1250 DEG C;
(3) rinse: select clear water to be rinsed;
(4) dipping: be positioned in the first dressing liquid immersion treatment 38min, the component of the first dressing liquid and each component weight under room temperature
Amount percentage ratio is respectively as follows: polyurethane resin 6%, softening agent 1.5%, fatty alcohol-polyoxyethylene ether 0.25%, citric acid 2%, and residue is complete
For water;
(5) drying: dry in roll, pick-up is 80%;
(6) stirring: be positioned in the second dressing liquid under room temperature and soak and stir process 25min, the component of the second dressing liquid and each
Weight percentages of components is respectively as follows: nanometer SnO2 powder body 0.15%, nano ZnO powder 0.25%, fatty alcohol-polyoxyethylene ether
0.25%, Polyethylene Glycol 13%;Acid-base modifier 0.15%, remaining is water, and the pH value of the second dressing liquid is 7;
(7) secondary dries: dry in roll, and pick-up is 80%;
(8) dry: the temperature of baking oven is 105 DEG C;Drying time is 17min.
The fabric good stability that the antistatic postfinishing process of the present invention produces, nanosize metal oxide divides on cloth
Cloth uniformly and difficult drop-off, has antistatic and the antibacterial functions of excellence.
Above-described embodiment is presently preferred embodiments of the present invention, is not the restriction to technical solution of the present invention, as long as
The technical scheme that can realize on the basis of above-described embodiment without creative work, is regarded as falling into patent of the present invention
Rights protection in the range of.
Claims (3)
1. the postfinishing process of a weaving face fabric with anti-static function, it is characterised in that: through kiering, singe, rinse,
Impregnate, dry, stir, secondary dries and completes postfinishing process with baking step;Specifically comprise the following steps that
(1) kiering: described working solution uses solute to be NaOH, Na2SiO3, refining agent ZTO, penetrating agent section woods and chelating agen, described
NaOH、Na2SiO3, refining agent ZTO, the concentration of penetrating agent section woods and chelating agen be followed successively by 10-20g/L, 4-5g/L, 9-13g/L,
80-100g/L, 1-2g/L, the solvent of described working solution is water;
(2) singe: described in speed of singing be 70-90m/min, flame temperature is 1200-1300 DEG C;
(3) rinse: select clear water to be rinsed;
(4) dipping: be positioned in the first dressing liquid immersion treatment 30-45min under room temperature, the component of described first dressing liquid and each
Weight percentages of components is respectively as follows: polyurethane resin 4-8%, softening agent 1-2%, fatty alcohol-polyoxyethylene ether 0.2-0.3%, Fructus Citri Limoniae
Acid 1-4%, residue is all water;
(5) dry: dry in roll;
(6) stirring: be positioned in the second dressing liquid and soak and stir process 20-30min under room temperature, the group of described second dressing liquid
Divide and each weight percentages of components is respectively as follows: nanometer SnO2 powder body 0.1-0.2%, nano ZnO powder 0.2-0.3%, poly alkyl alcohol
Oxygen vinyl Ether 0.2-0.3%, Polyethylene Glycol 10-16%;Acid-base modifier 0.1-0.2%, remaining is water, described second dressing liquid
PH value is 7;
(7) secondary dries: dry in roll;
(8) dry: the temperature of described baking oven is 90-120 DEG C.
The postfinishing process of a kind of weaving face fabric with anti-static function the most according to claim 1, it is characterised in that:
Dry and pick-up that secondary dries is 70-90%.
The postfinishing process of a kind of weaving face fabric with anti-static function the most according to claim 1, it is characterised in that:
In described baking step, described drying time is 15-20min.