CN112745652A - 一种透明低烟长效阻燃聚碳酸酯复合材料 - Google Patents
一种透明低烟长效阻燃聚碳酸酯复合材料 Download PDFInfo
- Publication number
- CN112745652A CN112745652A CN202011610072.XA CN202011610072A CN112745652A CN 112745652 A CN112745652 A CN 112745652A CN 202011610072 A CN202011610072 A CN 202011610072A CN 112745652 A CN112745652 A CN 112745652A
- Authority
- CN
- China
- Prior art keywords
- flame
- retardant
- parts
- composite material
- smoke
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种透明低烟长效阻燃聚碳酸酯复合材料，其由聚碳酸酯树脂45～68份、难燃高分子树脂1～15份、相容聚合物1～15份、高分子磷酸酯阻燃剂2～50份和助剂0.5～2份组成。本发明提供了一种透明、低烟、长效阻燃，并且能应用于薄壁塑料件的聚碳酸酯复合材料。通过聚碳酸酯与难燃高分子以及高分子量共聚阻燃剂共混/合金方式来实现阻燃，获得透明低烟的阻燃产品。本发明通过高分子量阻燃剂实现与树脂更好的相容性，在特定添加量时，能够使本发明的阻燃等级达到V0级，并保持优异的透明性，透光率≥70％，雾度低于10％。本发明通过聚苯醚树脂以及共聚膦酸酯之间的协同作用,使本发明的烟密度等级Ds4≤150。
Description
技术领域
本发明属于有机复合材料技术领域，具体的说是涉及一种透明低烟长效阻燃聚碳酸酯复合材料。
背景技术
目前现有技术中通过在聚碳酸酯中加入阻燃剂,以提高材料阻燃级别的研究已有很多,如采用溴系阻燃剂、磷酸酯类阻燃剂、磺酸盐阻燃剂、聚硅氧烷阻燃剂等。其中阻燃剂一般都以小分子或者低分子量齐聚物的形式共混加入，阻燃性能好，但现有技术中的阻燃剂在使用过程中容易析出，使阻燃性降低，还会有耐水性不佳等问题出现。如果能够通过聚碳酸酯与难燃高分子以及高分子量共聚阻燃剂共混/合金方式来实现阻燃，则可以克服此类问题，同时获得透明低烟的阻燃产品。
发明内容
本发明为了克服现有技术存在的不足，提供一种透明、低烟、长效阻燃，并且能应用于薄壁塑料件的透明低烟长效阻燃聚碳酸酯复合材料。
本发明是通过以下技术方案实现的：本发明公开了一种透明低烟长效阻燃聚碳酸酯复合材料，其由下述重量份的原料组成：聚碳酸酯树脂45～68份、难燃高分子树脂1～15份、相容聚合物1～15份、高分子磷酸酯阻燃剂2～50份和助剂0.5～2份。
作为本发明的优选实施方式，本发明透明低烟长效阻燃聚碳酸酯复合材料由下述重量份的原料组成：聚碳酸酯树脂50～60份、难燃高分子树脂3～10份、相容聚合物5～12份、高分子磷酸酯阻燃剂15～40份和助剂1～1.5份。
所述聚碳酸酯树脂为光气法或酯交换法制备的聚碳酸酯树脂,聚碳酸酯树脂的相对分子量为10000～80000，优选15000～50000。
所述难燃高分子树脂选择氧指数≥27的难燃塑料，可不影响甚至提高复合材料的阻燃性能和低烟性能。所述难燃高分子树脂为酚醛树脂PF、聚苯醚PPO、聚砜PSF、聚酰亚胺PEI、聚苯硫醚中的一种或多种，优选为聚2,6-二甲基-1,4-苯醚，其相对分子量为10000～50000，优选15000～25000。
所述相容聚合物为促进聚碳酸酯和难燃高分子树脂相容的聚合物，相容聚合物为聚苯乙烯PS、聚甲基丙烯酸甲酯PMMA和丙烯腈-丁二烯-苯乙烯共聚物ABS中的一种或多种。优选为聚苯乙烯均聚物或共聚物，如高抗冲聚苯乙烯，采用本体法生产或悬浮聚合法生产。
所述高分子磷酸酯阻燃剂为共聚聚酯/磷酸酯、共聚膦酸酯/碳酸酯、支化共聚膦酸酯碳酸酯中的一种或两种混合。特殊地，阻燃剂为FRX聚合物公司生产的CO6000、CO3000、HM1100中的一种或几种，磷含量5～20％。
所述助剂由下述重量份的原料组成：0.02～1份抗氧剂、0.02～1份加工流动助剂和0～1份阻燃协效剂。
所述抗氧剂为亚磷酸酯抗氧剂168、受阻酚抗氧剂1010、受阻酚抗氧剂1098和受阻酚抗氧剂1076中的一种或两种。
所述加工流动助剂为聚乙烯蜡、氧化聚乙烯蜡、季戊四醇硬脂酸酯和长链脂肪酸多官能团酯中的一种或几种混合。
所述阻燃协效剂为聚四氟乙烯抗滴落剂。
本发明的有益效果是：本发明提供了一种透明、低烟、长效阻燃，并且能应用于薄壁塑料件的聚碳酸酯复合材料。本发明中的透明低烟长效阻燃聚碳酸酯复合材料通过聚碳酸酯与难燃高分子以及高分子量共聚阻燃剂共混/合金方式来实现阻燃，可以克服现有技术中存在的问题，同时获得透明低烟的阻燃产品。本发明通过高分子量阻燃剂实现与树脂更好的相容性，在特定添加量时，能够使本发明透明低烟长效阻燃聚碳酸酯复合材料的阻燃等级达到V0级，并保持优异的透明性，透光率≥70％，雾度低于10％。本发明通过聚苯醚树脂以及共聚膦酸酯之间的协同作用,使本发明的烟密度等级Ds4≤150；聚苯醚比聚碳酸酯阻燃性好，氧指数高，烟密度低，添加进去可有效降低复合材料的总体烟密度。高分子量磷酸酯的成炭原理，可以增加复合材料的炭层强度和厚度，减少小分子炭的燃烧和扩散，从而减少烟浓度。本发明中的高分子量聚磷酸酯基本不影响PC树脂的耐热性，获得的阻燃PC耐热性好，应用温度范围广。
具体实施方式
以下结合具体实施例对本发明作详细描述。
| 实施例 | 1 | 2 | 3 | 4 |
| 聚碳酸酯 | 75.4 | 70.4 | 65.4 | 86.4 |
| 聚苯醚 | - | 5 | 10 | 5 |
| 聚苯乙烯 | 8 | 8 | 8 | 8 |
| 共聚膦酸酯 | 16 | 16 | 16 | - |
| 抗氧剂1 | 0.2 | 0.2 | 0.2 | 0.2 |
| 抗氧剂2 | 0.2 | 0.2 | 0.2 | 0.2 |
| 加工助剂 | 0.2 | 0.2 | 0.2 | 0.2 |
| 抗滴落剂 | - | - | 0.1 | - |
| 透光率 | 81 | 75 | 71 | 76 |
| 雾度 | 2 | 5 | 8 | 5 |
| 阻燃等级 | V0 | V0 | V0 | V2 |
| 烟密度Ds4 | 240 | 168 | 135 | 420 |
本发明透明低烟长效阻燃聚碳酸酯复合材料的生产方法为：将聚碳酸酯树脂和难燃高分子树脂与阻燃剂在120℃下烘干4h，保证含水量＜0.02％，然后将各个组分混合均匀,然后在250～290℃下经双螺杆挤出机挤出，经水槽冷却、造粒机切粒后得到复合材料。优选挤出机各段温度为220℃、250℃、260℃、280℃、280℃、280℃和280℃；真空度≤-0.02MPa；挤出螺杆转速300～500rpm，造粒机转速40rpm。
最后应当说明的是，以上内容仅用以说明本发明的技术方案，而非对本发明保护范围的限制，本领域的普通技术人员对本发明的技术方案进行的简单修改或者等同替换，均不脱离本发明技术方案的实质和范围。
Claims (10)
1.一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述透明低烟长效阻燃聚碳酸酯复合材料由下述重量份的原料组成：聚碳酸酯树脂45～68份、难燃高分子树脂1～15份、相容聚合物1～15份、高分子磷酸酯阻燃剂2～50份和助剂0.5～2份。
2.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述透明低烟长效阻燃聚碳酸酯复合材料由下述重量份的原料组成：聚碳酸酯树脂50～60份、难燃高分子树脂3～10份、相容聚合物5～12份、高分子磷酸酯阻燃剂15～40份和助剂1～1.5份。
3.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述聚碳酸酯树脂为光气法或酯交换法制备的聚碳酸酯树脂,聚碳酸酯树脂的相对分子量为10000～80000。
4.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述难燃高分子树脂选择氧指数≥27的难燃塑料，所述难燃高分子树脂为酚醛树脂PF、聚苯醚PPO、聚砜PSF、聚酰亚胺PEI和聚苯硫醚中的一种或多种，其相对分子量为10000～50000。
5.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述相容聚合物为促进聚碳酸酯和难燃高分子树脂相容的聚合物，相容聚合物为聚苯乙烯PS、聚甲基丙烯酸甲酯PMMA和丙烯腈-丁二烯-苯乙烯共聚物ABS中的一种或多种。
6.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述高分子磷酸酯阻燃剂为共聚聚酯/磷酸酯、共聚膦酸酯/碳酸酯和支化共聚膦酸酯碳酸酯中的一种或两种混合。
7.根据权利要求1所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述助剂由下述重量份的原料组成：0.02～1份抗氧剂、0.02～1份加工流动助剂和0～1份阻燃协效剂。
8.根据权利要求7所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述抗氧剂为亚磷酸酯抗氧剂168、受阻酚抗氧剂1010、受阻酚抗氧剂1098和受阻酚抗氧剂1076中的一种或两种。
9.根据权利要求7所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述加工流动助剂为聚乙烯蜡、氧化聚乙烯蜡、季戊四醇硬脂酸酯和长链脂肪酸多官能团酯中的一种或几种混合。
10.根据权利要求7所述的一种透明低烟长效阻燃聚碳酸酯复合材料，其特征在于：所述阻燃协效剂为聚四氟乙烯抗滴落剂。