CN112735706A - 一种导热云母带的制备方法 - Google Patents
一种导热云母带的制备方法 Download PDFInfo
- Publication number
- CN112735706A CN112735706A CN202011539695.2A CN202011539695A CN112735706A CN 112735706 A CN112735706 A CN 112735706A CN 202011539695 A CN202011539695 A CN 202011539695A CN 112735706 A CN112735706 A CN 112735706A
- Authority
- CN
- China
- Prior art keywords
- graphene
- organic silicon
- heat
- mica tape
- conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种导热云母带的制备方法，包括以下步骤，步骤1：将玻纤布与云母纸进行复合，得到云母带；步骤2：将石墨烯胶涂于云母带上；步骤3：将第二步得到的云母带进行烘干和收卷。由此，石墨烯具有优良的导热性能，石墨烯的加入显著提升了云母带的导热性能；石墨烯仅喷涂在玻纤布表面，不会对玻纤布和云母纸的粘结性产生影响；工艺简单，通过喷淋即可使石墨烯在玻纤布表面均匀分散，提高了云母带的导热性能。
Description
技术领域
本发明涉及云母带领域，尤其涉及一种导热云母带的制备方法。
背景技术
如今，电机的电压等级和单机容量不断增大，设备工作时产生的热量也越来越大，使得电机的温升不断增加，温度的升高不仅影响电机的使用寿命，还影响电机的安全性。
云母带是直接缠绕在铜线外面的耐火绝缘材料，云母带的制备过程通常包括玻纤布上胶、云母纸复合、第二次上胶、高温固化、收卷等步骤。发明专利CN105632660B公开了一种高导热云母带的制作方法，通过将导热填料涂布在玻纤布表面、烘干，再通过胶黏剂与云母纸复合，得到高导热云母纸。该方法步骤繁琐，玻纤布和云母纸之间的粘结力不够稳定。
发明内容
本发明的目的是在于提供一种导热云母带的制备方法，解决上述现有技术问题中的一个或者多个。
根据本发明的一个方面，提供一种导热云母带的制备方法，包括以下步骤，步骤1：将玻纤布与云母纸进行复合，得到机硅云母纸复合带；步骤2：将石墨烯胶涂于机硅云母纸复合带上；步骤3：将第二步得到的机硅云母纸复合带进行烘干和收卷。
在一些实施方式中：所述第二步中，将石墨烯胶通过喷淋的方式涂布于所述机硅云母纸复合带上。
在一些实施方式中：石墨烯胶的喷射压力为2～5MPa。
在一些实施方式中：所述第一步中，将玻纤布通过有机硅胶槽上胶后，与云母纸进行复合。
在一些实施方式中：所述石墨烯胶为石墨烯有机硅甲苯溶液，其制备方法为：将苝-3,4,9,10-四羧酸二酐与三乙烯四胺在甲苯中回流反应，甲酸酸化处理后，加入石墨烯粉末，进行超声处理，得到石墨烯甲苯溶液；继续加入有机硅甲苯溶液，超声处理，既得石墨烯有机硅甲苯溶液。
在一些实施方式中：所述石墨烯有机硅甲苯溶液中石墨烯的浓度为2～5％。
在一些实施方式中：所述石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:1～3。
与现有技术相比，本发明具有如下优点：
1、石墨烯具有优良的导热性能，石墨烯的加入显著提升了云母带的导热性能；
2、石墨烯仅在玻纤布表面，不会对玻纤布和云母纸的粘结性产生影响；
3、工艺简单，通过喷淋即可使石墨烯在玻纤布表面均匀分散，提高了云母带的导热性能。
具体实施方式
下面对本发明作进一步详细说明。
实施例1：
步骤1、复合：将玻纤布通过有机硅胶槽上胶后，与云母纸进行复合，得到有机硅云母纸复合带；
步骤2、喷淋：将浓度为2％的石墨烯有机硅甲苯溶液喷淋到机硅云母纸复合带上的玻纤布一侧，喷射压力为2Mpa，石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:1。
步骤3、最后经过烘道烘干，收卷，得到云母带。
实施例2：
步骤1、复合：将玻纤布通过有机硅胶槽上胶后，与云母纸进行复合，得到有机硅云母纸复合带；
步骤2、喷淋：将浓度为3％的石墨烯有机硅甲苯溶液喷淋到机硅云母纸复合带上的玻纤布一侧，喷射压力为3Mpa，石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:2。
步骤3、最后经过烘道烘干，收卷，得到云母带。
实施例3：
步骤1、复合：将玻纤布通过有机硅胶槽上胶后，与云母纸进行复合，得到有机硅云母纸复合带；
步骤2、喷淋：将浓度为5％的石墨烯有机硅甲苯溶液喷淋到机硅云母纸复合带上的玻纤布一侧，喷射压力为5Mpa，石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:3。
步骤3、最后经过烘道烘干，收卷，得到云母带。
对比例1：
对比例1和实施例1的区别为不含石墨烯。
对比例2：
对比例2和实施例1的区别为石墨烯的引入通过浸胶槽。
性能测试结果如表1所示
表1
| 导热系数 | |
| 实施例1 | 0.41 |
| 实施例2 | 0.44 |
| 实施例3 | 0.43 |
| 对比例1 | 0.21 |
| 对比例2 | 0.33 |
由此可以看出，石墨烯具有优良的导热性能，石墨烯的加入显著提升了云母带的导热性能；石墨烯仅喷涂在玻纤布表面，不会对玻纤布和云母纸的粘结性产生影响；工艺简单，通过喷淋即可使石墨烯在玻纤布表面均匀分散，提高了云母带的导热性能。
其中，石墨烯有机硅甲苯溶液的制备方法为：将苝-3,4,9,10-四羧酸二酐与三乙烯四胺在甲苯中回流反应1h，甲酸酸化处理后，加入石墨烯粉末，超声处理30min，超声功率800W，得到均匀分散的石墨烯甲苯溶液；继续加入有机硅甲苯溶液，超声处理10min，既得石墨烯有机硅甲苯溶液。石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:1～3。石墨烯有机硅甲苯溶液中石墨烯的浓度为2～5％。
以上所述仅是本发明的一种实施方式，应当指出，对于本领域普通技术人员来说，在不脱离本发明创造构思的前提下，还可以做出若干相似的变形和改进，这些也应视为本发明的保护范围之内。
Claims (7)
1.一种导热云母带的制备方法，其特征在于：包括以下步骤，
步骤1：将玻纤布与云母纸进行复合，得到机硅云母纸复合带；
步骤2：将石墨烯胶涂于所述机硅云母纸复合带上；
步骤3：将第二步得到的所述机硅云母纸复合带进行烘干和收卷。
2.根据权利要求1所述的一种导热云母带的制备方法，其特征在于：所述第二步中，将石墨烯胶通过喷淋的方式涂布于所述机硅云母纸复合带上。
3.根据权利要求1所述的一种导热云母带的制备方法，其特征在于：所述石墨烯胶的喷射压力为2～5MPa。
4.根据权利要求1所述的一种导热云母带的制备方法，其特征在于：所述第一步中，将玻纤布通过有机硅胶槽上胶后，与云母纸进行复合。
5.根据权利要求1所述的一种导热云母带的制备方法，其特征在于：所述石墨烯胶为石墨烯有机硅甲苯溶液，其制备方法为：将苝-3,4,9,10-四羧酸二酐与三乙烯四胺在甲苯中回流反应，甲酸酸化处理后，加入石墨烯粉末，进行超声处理，得到石墨烯甲苯溶液；继续加入有机硅甲苯溶液，超声处理，既得石墨烯有机硅甲苯溶液。
6.根据权利要求5所述的一种导热云母带的制备方法，其特征在于：所述石墨烯有机硅甲苯溶液中石墨烯的浓度为2～5％。
7.根据权利要求5所述的一种导热云母带的制备方法，其特征在于：所述石墨烯有机硅甲苯溶液中石墨烯与有机硅的质量比为1:1～3。