CN112680098A - 一种防冻水性无机涂料及其制备方法 - Google Patents
一种防冻水性无机涂料及其制备方法 Download PDFInfo
- Publication number
- CN112680098A CN112680098A CN202011533893.8A CN202011533893A CN112680098A CN 112680098 A CN112680098 A CN 112680098A CN 202011533893 A CN202011533893 A CN 202011533893A CN 112680098 A CN112680098 A CN 112680098A
- Authority
- CN
- China
- Prior art keywords
- inorganic
- parts
- coating
- water
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种防冻水性无机涂料及其制备方法，由以下质量份数的原料制成：水200‑250份、无机增稠剂3‑8份、无机改性纳米硅聚物180‑250份、金红石型钛白粉75‑125份、重钙350‑400份、丙二醇8‑10份、无机净味乳液10‑50份、聚氨酯流平剂1‑2份、无机消泡剂1‑2份。本发明的工艺简单，反应过程中不产生废水，也不使用有机溶剂，减少了对环境的污染。本发明的体系相容性好，具有更好的耐老化性；本发明采用无机净味乳液做分散介质与金红石型钛白粉和超细重钙粉通过合理配比和加压处理工艺，降低了涂料干燥后的收缩率，提高了涂料的遮盖力和防冻性。
Description
技术领域
本发明涉及无机涂料技术领域，具体涉及一种防冻水性无机涂料及其制备方法。
背景技术
无机涂料是一种以无机材料为主要成膜物质的涂料，是全无机矿物涂料的简称，因性能优质，广泛用于建筑、绘画等日常生活领域。无机涂料是由无机聚合物和经过分散活化的金属、金属氧化物纳米材料、稀土超微粉体组成的无机聚合物涂料，能与钢结构表面铁原子快速反应，生成具有物理、化学双重保护作用。现有的无机涂料不具备良好的遮盖力、且防冻性较差。
发明内容
本发明提供一种防冻水性无机涂料及其制备方法，以解决现有的无机涂料不具备良好的遮盖力、且防冻性较差的问题。
为解决上述技术问题，本发明采用如下技术方案：一种防冻水性无机涂料，由以下质量份数的原料制成：水200-250份、无机增稠剂3-8份、无机改性纳米硅聚物180-250份、金红石型钛白粉75-125份、重钙350-400份、丙二醇8-10份、无机净味乳液10-50份、聚氨酯流平剂1-2份、无机消泡剂1-2 份。
一种防冻水性无机涂料的制备方法，包括以下步骤：
1)取相应比例的水和无机增稠剂加入到高速分散机内，设置高速分散机转速700-800转/分，分散一段时间，使无机增稠剂彻底溶解；
2)向步骤1)中的高速分散机中继续依次加入相应比例的无机改性纳米硅聚物、金红石型钛白粉、重钙和丙二醇，经高速分散机，加入去离子水并开蒸汽升温，在88℃时中速分散45分钟；
3)再依次加入相应比例的无机净味乳液、聚氨酯流平剂，经高速分散机，控制转速为600-800转/分，边分散边升温至65-95℃，保温2h。
4)将步骤3)反应后得到的混合液一起倒入器皿中并置于加压处理设备中，加压处理3小时，然后置于无阳光照射的地方放置，静置冷却，备用；
5)取相应比例的无机消泡剂滴加到步骤4)冷却后得到的混合液内，搅拌均匀后，对混合液进行过滤，即得涂料，然后置于干燥通风的地方保存，即可。
进一步的，无机增稠剂为有机膨润土、硅藻土、气相法白炭黑、钠基膨润土、硅凝胶的一种。
进一步的，所述金红石型钛白粉的粒径范围为10～100纳米，所述重钙通过研磨机研磨至1200-1300目。
进一步的，所述无机消泡剂为SN-209无机消泡剂。
进一步的，所述聚氨酯流平剂为SN-2020聚氨酯流平剂。
进一步的，所述无机增稠剂为SN-251无机增稠剂。
进一步的，所述无机改性纳米硅聚物为SN-190无机改性纳米硅聚物。
进一步的，所述无机净味乳液为SN-990无机净味乳液。
本发明与现有技术相比，具有以下优点：
(1)、本发明制备防冻水性无机涂料的工艺简单，反应过程中不产生废水，也不使用有机溶剂，减少了对环境的污染。
(2)、本发明制备防冻水性无机涂料的体系相容性好，具有更好的耐老化性；
(3)、本发明制备防冻水性无机涂料采用无机净味乳液做分散介质与金红石型钛白粉和超细重钙粉通过合理配比和加压处理工艺，降低了涂料干燥后的收缩率，提高了涂料的遮盖力和防冻性。
具体实施方式
以下以具体实施例来说明本发明的技术方案，但本发明的保护范围不限于此：
实施例一
称取水200克、SN-251无机增稠剂3克、SN-190无机改性纳米硅聚物180 克、金红石型钛白粉75克、1200目重钙350克、丙二醇8克、SN-990无机净味乳液10克、SN-2020聚氨酯流平剂1克、SN-209无机消泡剂1克。
1)取相应比例的水和无机增稠剂加入到高速分散机内，设置高速分散机转速700转/分，分散一段时间，使无机增稠剂彻底溶解；2)向步骤1)中的高速分散机中继续依次加入相应比例的无机改性纳米硅聚物、金红石型钛白粉、重钙和丙二醇，经高速分散机，加入去离子水并开蒸汽升温，在88℃时中速分散45分钟；3)再依次加入相应比例的无机净味乳液、聚氨酯流平剂，经高速分散机，控制转速为600转/分，边分散边升温至65℃，保温2h。4)将步骤3)反应后得到的混合液一起倒入器皿中并置于加压处理设备中，加压处理3小时，然后置于无阳光照射的地方放置，静置冷却，备用；5)取相应比例的无机消泡剂滴加到步骤4)冷却后得到的混合液内，搅拌均匀后，对混合液进行过滤，即得涂料，然后置于干燥通风的地方保存，即可。
实施例二
称取水250克、SN-251无机增稠剂8克、SN-190无机改性纳米硅聚物250 克、金红石型钛白粉125克、1300目重钙400克、丙二醇10克、SN-990无机净味乳液10克50克、SN-2020聚氨酯流平剂2克、SN-209无机消泡剂2克。
1)取相应比例的水和无机增稠剂加入到高速分散机内，设置高速分散机转速800转/分，分散一段时间，使无机增稠剂彻底溶解；2)向步骤1)中的高速分散机中继续依次加入相应比例的无机改性纳米硅聚物、金红石型钛白粉、重钙和丙二醇，经高速分散机，加入去离子水并开蒸汽升温，在88℃时中速分散45分钟；3)再依次加入相应比例的无机净味乳液、聚氨酯流平剂，经高速分散机，控制转速为800转/分，边分散边升温至95℃，保温2h。4)将步骤3)反应后得到的混合液一起倒入器皿中并置于加压处理设备中，加压处理3小时，然后置于无阳光照射的地方放置，静置冷却，备用；5)取相应比例的无机消泡剂滴加到步骤4)冷却后得到的混合液内，搅拌均匀后，对混合液进行过滤，即得涂料，然后置于干燥通风的地方保存，即可。
实施例三
称取水230克、SN-251无机增稠剂6克、SN-190无机改性纳米硅聚物200 克、金红石型钛白粉100克、1300目重钙360克、丙二醇9克、SN-990无机净味乳液40克、SN-2020聚氨酯流平剂2克、SN-209无机消泡剂1克。
1)取相应比例的水和无机增稠剂加入到高速分散机内，设置高速分散机转速750转/分，分散一段时间，使无机增稠剂彻底溶解；2)向步骤1)中的高速分散机中继续依次加入相应比例的无机改性纳米硅聚物、金红石型钛白粉、重钙和丙二醇，经高速分散机，加入去离子水并开蒸汽升温，在88℃时中速分散45分钟；3)再依次加入相应比例的无机净味乳液、聚氨酯流平剂，经高速分散机，控制转速为700转/分，边分散边升温至85℃，保温2h。4)将步骤3)反应后得到的混合液一起倒入器皿中并置于加压处理设备中，加压处理3小时，然后置于无阳光照射的地方放置，静置冷却，备用；5)取相应比例的无机消泡剂滴加到步骤4)冷却后得到的混合液内，搅拌均匀后，对混合液进行过滤，即得涂料，然后置于干燥通风的地方保存，即可。
实施例四
称取包括水230克、SN-251无机增稠剂6克、SN-190无机改性纳米硅聚物200克、金红石型钛白粉100克、1300目重钙360克、丙二醇9克、SN-990 无机净味乳液40克、SN-2020聚氨酯流平剂2克、SN-209无机消泡剂1克。
1)将水230和SN-251无机增稠剂加入高速分散机，750转/分钟分散一段时间，2)然后依次加入金红石型钛白粉100和1300目重钙，分散30分钟。 3)最后加入剩余原料，在分散机中，750转分散110分钟，混合均匀即可。
实施例五
称取水230克、SN-251无机增稠剂6克、SN-190无机改性纳米硅聚物200 克、金红石型钛白粉100克、1300目重钙360克、丙二醇9克、SN-990无机净味乳液40克、SN-2020聚氨酯流平剂2克、SN-209无机消泡剂1克。1)将水230和SN-251无机增稠剂加入高速分散机，750转/分钟分散一段时间，2) 然后依次加入金红石型钛白粉100和1300目重钙，分散30分钟。3)最后加入剩余原料，在分散机中，750转分散110分钟，混合均匀即可。
实验例1：
本实施例的防冻水性无机涂料通过与其他涂料的进行实验，对比本发明的情况。
实验方法：将实施例1-5的涂料进行实验，分析出三组中的耐老化性、遮盖力和防冻性，并进行对比。
三组进行效果比较，结果见表1.
经过实验对比，五组情况有明显差异，实施例1-3的耐老化性、遮盖力和防冻性较好。
实验例2：
按照本领域常规的检测方法，检测本发明的实施例1-3的各项指标。检测结果如下表所示，可见本发明的防冻水性无机涂料符合国家标准，具有非常优越的性能。
当然，以上只是本申请的典型实例，除此之外，本申请还可以有其它多种具体实施方式，凡采用等同替换或等效变换形成的技术方案，均落在本申请要求保护的范围之内。
Claims (9)
1.一种防冻水性无机涂料，其特征在于，由以下质量份数的原料制成：水200-250份、无机增稠剂3-8份、无机改性纳米硅聚物180-250份、金红石型钛白粉75-125份、重钙350-400份、丙二醇8-10份、无机净味乳液10-50份、聚氨酯流平剂1-2份、无机消泡剂1-2份。
2.一种防冻水性无机涂料的制备方法，其特征在于，包括以下步骤：
1)取相应比例的水和无机增稠剂加入到高速分散机内，设置高速分散机转速700-800转/分，分散一段时间，使无机增稠剂彻底溶解；
2)向步骤1)中的高速分散机中继续依次加入相应比例的无机改性纳米硅聚物、金红石型钛白粉、重钙和丙二醇，经高速分散机，加入去离子水并开蒸汽升温，在88℃时中速分散45分钟；
3)再依次加入相应比例的无机净味乳液、聚氨酯流平剂，经高速分散机，控制转速为600-800转/分，边分散边升温至65-95℃，保温2h。
4)将步骤3)反应后得到的混合液一起倒入器皿中并置于加压处理设备中，加压处理3小时，然后置于无阳光照射的地方放置，静置冷却，备用；
5)取相应比例的无机消泡剂滴加到步骤4)冷却后得到的混合液内，搅拌均匀后，对混合液进行过滤，即得涂料，然后置于干燥通风的地方保存，即可。
3.如权利要求1所述的一种防冻水性无机涂料，其特征在于，无机增稠剂为有机膨润土、硅藻土、气相法白炭黑、钠基膨润土、硅凝胶的一种。
4.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述金红石型钛白粉的粒径范围为10～100纳米，所述重钙通过研磨机研磨至1200-1300目。
5.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述无机消泡剂为SN-209无机消泡剂。
6.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述聚氨酯流平剂为SN-2020聚氨酯流平剂。
7.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述无机增稠剂为SN-251无机增稠剂。
8.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述无机改性纳米硅聚物为SN-190无机改性纳米硅聚物。
9.如权利要求1所述的一种防冻水性无机涂料，其特征在于，所述无机净味乳液为SN-990无机净味乳液。