CN112647659A - 一种具有节能效果的博物馆装饰用墙面涂层及其制备方法 - Google Patents
一种具有节能效果的博物馆装饰用墙面涂层及其制备方法 Download PDFInfo
- Publication number
- CN112647659A CN112647659A CN202011384495.4A CN202011384495A CN112647659A CN 112647659 A CN112647659 A CN 112647659A CN 202011384495 A CN202011384495 A CN 202011384495A CN 112647659 A CN112647659 A CN 112647659A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- coating
- energy
- foam layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及涂层的制备方法,尤其涉及一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层;其中:所述基底层中含有活性羟基;所述泡沫层中含有能够与活性羟基反应的基团,且能够在大于10℃条件下发泡膨胀,形成密集的小气孔;所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结。本发明克服了现有技术中的博物馆内的墙壁热传导效率较高,导致能耗较高的缺陷,本发明通过多层结构能够使得涂层具有良好的保温隔热效果,有效降低了能耗,同时具有良好的力学性能,从而具有较长的使用寿命的优点,此外还具有良好的隔音吸音效果,能够吸收博物馆内的噪音。
Description
技术领域
本发明涉及涂层的制备方法,尤其涉及一种具有节能效果的博物馆装饰用墙面涂层及其制备方法。
背景技术
博物馆是征集、典藏、陈列和研究代表自然和人类文化遗产的实物的场所,同时也是对馆藏物品分类管理,为公众提供知识、教育和欣赏的文化教育的机构、建筑物、地点或者社会公共机构。博物馆内部由于需要防止馆内藏品遭到环境的破坏,使得馆内环境需要保持恒温恒湿的条件,为了达到恒温条件,因此需要24h开启空调。但是常规的博物馆墙壁通常是有热传递效率较高的混凝土制成,因此馆内的热量容易散失,因此博物馆内用于调节气温的空调的能耗较大,不具备节能效果。
发明内容
本发明是为了克服现有技术中的博物馆内的墙壁热传导效率较高,导致能耗较高的缺陷,因此提供了一种具有节能效果的博物馆装饰用墙面涂层及其制备方法。
为实现上述发明目的,本发明通过以下技术方案实现:
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层;
其中:所述基底层中含有活性羟基;
所述泡沫层中含有能够与活性羟基反应的基团,且能够在大于10℃条件下发泡膨胀,形成密集的小气孔;
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结。
本发明中的墙面涂层包括三层,其中基底层的作用是与墙面相贴合,从而提升了泡沫层的粘结强度。泡沫层中具有密集的小气孔,其能够起到保温的作用有效防止了热量的散失,因此大大降低了热损耗。同时小气孔还具有良好的吸音隔音效果,从而能够使得在博物馆中保持安静的展览环境。同时,密封层覆盖在泡沫层的外表面,能够保证泡沫层不会被外界机械应力破坏。
作为优选,所述基底层按照重量份数计包括以下组分:双酚A环氧树脂30份、脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚15~30份、聚酯多元醇20~30份、中空玻璃微珠10~30份以及二亚乙基三胺3~10份。
本发明中的基底层的主体由环氧树脂构成,其能够与混凝土表面的羟基发生交联,从而能够稳定的附着在混凝土表面,同时其内部含有中空玻璃微珠其同样具有隔热的效果,能够作为一个层阻隔物阻隔混凝土与博物馆室内的热量交换,从而与泡沫层起到双重隔热的效果。
作为优选,所述双酚A环氧树脂0.23~0.25mol/L,所述脂肪族环氧树脂的环氧值为0.4~0.45mol/L。
作为优选,所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油10~30份、聚酯多元醇20~30份、椰油酰胺丙基甜菜碱3~8份、羟丙基甲基纤维素15~30份、乙二醇二缩水甘油醚10~15份、三(五氟苯基)硼酸酯0.5~1份。
本发明中的泡沫层中含有含有硅氢结构的低聚磷硅氧烷的硅氢键能够在三(五氟苯基)硼酸酯的催化下与其他组分中的羟基反应,从而生成氢气从而起到发泡作用,当氢气散去后即可形成表面开口的气泡。而本发明中的形成的泡沫结构中含有硅磷元素,其能够起到协同阻燃作用,从而有效克服了泡沫材料易燃的缺陷。同时磷硅氧烷还具有良好的阻尼性能,因此其隔音效果相较于传统的聚氨酯泡沫而言更加有效。
作为优选,所述密封层按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯30~50份、乙烯基超支化有机硅树脂20~40份、丙烯酸羟乙酯10~30份、气相法白炭黑10~20份、MQ树脂20~30份、2-羟基-2-甲基-1-苯基-1-丙酮0.5~1份以及2,2-二甲氧基-2-苯基苯乙酮1份。
本发明中的密封层中为光固化树脂,其中三羟甲基丙烷三丙烯酸酯以及丙烯酸羟乙酯能够作为光固化的主要原料,其具有较低的粘度,使得能够封闭泡沫层表面的开口气泡。同时乙烯基超支化有机硅树脂其能够调节整个体系的粘度,使得未固化的组合物具有良好的流平性,同时乙烯基超支化有机硅树脂由于具有较多的乙烯基,其能够具有在固化后形成交联网络,使得固化后得到的漆膜具有良好的力学性能。
作为优选,所述乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在40~60℃下水解2~3h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至80~100℃后反应2~5h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
作为优选,所述含有硅氢结构的聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂溶于酒精后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-10~0℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至25~45℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
作为优选,所述步骤(S.1)中的硅烷偶联剂为KH-550、KH-570、KH-791或KH-602中的一种,所述硅烷偶联剂溶液的浓度为0.5~1%。
因此,本发明具有以下有益效果;
(1)本发明通过多层结构能够使得涂层具有良好的保温隔热效果,有效降低了能耗;
(2)具有良好的力学性能,从而具有较长的使用寿命;
(3)具有良好的隔音吸音效果,能够吸收博物馆内的噪音。
具体实施方式
下面结合具体实施例对本发明做进一步描述。本领域普通技术人员在基于这些说明的情况下将能够实现本发明。此外,下述说明中涉及到的本发明的实施例通常仅是本发明一部分的实施例,而不是全部的实施例。因此,基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例,都应当属于本发明保护的范围。
实施例1
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层。
其中:所述基底层按照重量份数计包括以下组分:环氧值为0.23mol/L的双酚A环氧树脂30份、环氧值为0.4mol/L的脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚15份、聚酯多元醇20份、中空玻璃微珠10份以及二亚乙基三胺3份。
泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油10份、聚酯多元醇20份、椰油酰胺丙基甜菜碱3份、羟丙基甲基纤维素15份、乙二醇二缩水甘油醚10份、三(五氟苯基)硼酸酯0.5份。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结,其按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯30份、乙烯基超支化有机硅树脂20份、丙烯酸羟乙酯10份、气相法白炭黑10份、MQ树脂20份、2-羟基-2-甲基-1-苯基-1-丙酮0.5份以及2,2-二甲氧基-2-苯基苯乙酮1份。
乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在40℃下水解2h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的低聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至80℃后反应2h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂KH-550溶于酒精形成0.5%的溶液,然后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-10℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至25℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
实施例2
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层。
其中:所述基底层按照重量份数计包括以下组分:环氧值为0.25mol/L的双酚A环氧树脂30份、环氧值为0.45mol/L的脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚30份、聚酯多元醇230份、中空玻璃微珠30份以及二亚乙基三胺10份。
所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油30份、聚酯多元醇30份、椰油酰胺丙基甜菜碱8份、羟丙基甲基纤维素30份、乙二醇二缩水甘油醚15份、三(五氟苯基)硼酸酯1份。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结,其按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯50份、乙烯基超支化有机硅树脂40份、丙烯酸羟乙酯30份、气相法白炭黑20份、MQ树脂30份、2-羟基-2-甲基-1-苯基-1-丙酮1份以及2,2-二甲氧基-2-苯基苯乙酮1份。
乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在60℃下水解3h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的低聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至100℃后反应5h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂KH-570溶于酒精形成1%的溶液,然后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在0℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至45℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
实施例3
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层。
其中:所述基底层按照重量份数计包括以下组分:环氧值为0.24mol/L的双酚A环氧树脂30份、环氧值为0.42mol/L的脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚20份、聚酯多元醇25份、中空玻璃微珠20份以及二亚乙基三胺5份。
所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油20份、聚酯多元醇25份、椰油酰胺丙基甜菜碱5份、羟丙基甲基纤维素25份、乙二醇二缩水甘油醚12份、三(五氟苯基)硼酸酯0.8份。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结,其按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯40份、乙烯基超支化有机硅树脂30份、丙烯酸羟乙酯20份、气相法白炭黑15份、MQ树脂25份、2-羟基-2-甲基-1-苯基-1-丙酮0.8份以及2,2-二甲氧基-2-苯基苯乙酮1份。
乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在50℃下水解2.5h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的低聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至90℃后反应3h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂KH-791溶于酒精形成0.8%的溶液,然后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-5℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至35℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
实施例4
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层。
其中:所述基底层按照重量份数计包括以下组分:环氧值为0.23mol/L的双酚A环氧树脂30份、环氧值为0.45mol/L的脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚18份、聚酯多元醇22份、中空玻璃微珠14份以及二亚乙基三胺4份。
所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油16份、聚酯多元醇24份、椰油酰胺丙基甜菜碱4份、羟丙基甲基纤维素16份、乙二醇二缩水甘油醚12份、三(五氟苯基)硼酸酯0.6份。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结,其按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯32份、乙烯基超支化有机硅树脂25份、丙烯酸羟乙酯15份、气相法白炭黑13份、MQ树脂24份、2-羟基-2-甲基-1-苯基-1-丙酮0.6份以及2,2-二甲氧基-2-苯基苯乙酮1份。
乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在45℃下水解2.5h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的低聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至85℃后反应2~5h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂KH-602溶于酒精形成0.8%的溶液,然后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-2℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至26℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
实施例5
一种具有节能效果的博物馆装饰用墙面涂层,所述涂层从内至外依次包括基底层、泡沫层以及密封层。
其中:所述基底层按照重量份数计包括以下组分:环氧值为0.25mol/L的双酚A环氧树脂30份、环氧值为0.4mol/L的脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚28份、聚酯多元醇26份、中空玻璃微珠29份以及二亚乙基三胺9份。
所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油26份、聚酯多元醇28份、椰油酰胺丙基甜菜碱7份、羟丙基甲基纤维素22份、乙二醇二缩水甘油醚14份、三(五氟苯基)硼酸酯0.8份。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结,其按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯45份、乙烯基超支化有机硅树脂35份、丙烯酸羟乙酯25份、气相法白炭黑18份、MQ树脂27份、2-羟基-2-甲基-1-苯基-1-丙酮0.6份以及2,2-二甲氧基-2-苯基苯乙酮1份。
乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在55℃下水解3h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的低聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至95℃后反应2~5h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
一种具有节能效果的博物馆装饰用墙面涂层的制备方法,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂KH-550溶于酒精形成0.8%的溶液,然后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-5℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至40℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
Claims (9)
1.一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述涂层从内至外依次包括基底层、泡沫层以及密封层;
其中:所述基底层中含有活性羟基;
所述泡沫层中含有能够与活性羟基反应的基团,且能够在大于10℃条件下发泡膨胀,形成密集的小气孔;
所述密封层能够覆盖泡沫层表面的小气孔,其能够与泡沫层相互粘结。
2.根据权利要求1所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述基底层按照重量份数计包括以下组分:双酚A环氧树脂30份、脂肪族环氧树脂50份、1,4-丁二醇二缩水甘油醚15~30份、聚酯多元醇20~30份、中空玻璃微珠10~30份以及二亚乙基三胺3~10份。
3.根据权利要求2所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述双酚A环氧树脂的环氧值为0.23~0.25mol/L,所述脂肪族环氧树脂的环氧值为0.4~0.45mol/L。
4.根据权利要求1所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述泡沫层按照重量份数计包括以下组分:含有硅氢结构的低聚磷硅氧烷30份、羟基硅油10~30份、聚酯多元醇20~30份、椰油酰胺丙基甜菜碱3~8份、羟丙基甲基纤维素15~30份、乙二醇二缩水甘油醚10~15份、三(五氟苯基)硼酸酯0.5~1份。
5.根据权利要求1所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述密封层按照重量份数计包括以下组分:三羟甲基丙烷三丙烯酸酯30~50份、乙烯基超支化有机硅树脂20~40份、丙烯酸羟乙酯10~30份、气相法白炭黑10~20份、MQ树脂20~30份、2-羟基-2-甲基-1-苯基-1-丙酮0.5~1份以及2,2-二甲氧基-2-苯基苯乙酮1份。
6.根据权利要求1所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述乙烯基超支化有机硅树脂制备方法如下:
(1)单体制备:按照物质的量1:1.5称取三甲氧基硅烷以及1,3-二乙烯基-1,1,3,3四甲基二硅氧烷混合,然后加入三倍三甲氧基硅烷摩尔量的水,混合均匀后加入催化剂量的12mol/L的浓盐酸,在40~60℃下水解2~3h后,经蒸馏得到三(二甲基乙烯基硅基)硅氧烷;
(2)聚合反应:将得到的三(二甲基乙烯基硅基)硅氧烷与含有硅氢结构的聚磷硅氧烷按照质量比10:1混合后溶于甲苯中,向其中加入催化剂量的卡斯特催化剂,升高温度至80~100℃后反应2~5h,反应结束后蒸除溶剂得到乙烯基超支化有机硅树脂。
7.根据权利要求4或6所述的一种具有节能效果的博物馆装饰用墙面涂层,其特征在于,所述含有硅氢结构的低聚磷硅氧烷结构如下:[H-Si(CH3 )2-O-CH2]3-P=O。
8.一种如权利要求1~7中任意一项所述具有节能效果的博物馆装饰用墙面涂层的制备方法,其特征在于,所述方法包括以下步骤:
(S.1)墙面处理:将硅烷偶联剂溶于酒精后对墙壁进行喷涂,从而对墙面进行表面粘结改性处理;
(S.2)基底层处理:按照配方称取基底层的原料,混合均匀后涂覆于经过表面粘结改性处理的墙面,经过自然干燥固化后得到基底层;
(S.3)发泡处理:在-10~0℃下按照配方称取基底层的原料混合均匀后,涂覆于基底层表面,然后升高温度至25~45℃,物料发泡从而形成具有密集小气孔的泡沫层;
(S.4)密封层:按照配方称取密封层的原料混合均匀后,涂覆于泡沫层表面,然后经过紫外线照射后固化得到,从而得到密封层。
9.根据权利要求8所述的一种具有节能效果的博物馆装饰用墙面涂层的制备方法,其特征在于,所述步骤(S.1)中的硅烷偶联剂为KH-550、KH-570、KH-791或KH-602中的一种,所述硅烷偶联剂溶液的浓度为0.5~1%。