CN1125155C - 隔热阻尼胶 - Google Patents
隔热阻尼胶 Download PDFInfo
- Publication number
- CN1125155C CN1125155C CN99114375A CN99114375A CN1125155C CN 1125155 C CN1125155 C CN 1125155C CN 99114375 A CN99114375 A CN 99114375A CN 99114375 A CN99114375 A CN 99114375A CN 1125155 C CN1125155 C CN 1125155C
- Authority
- CN
- China
- Prior art keywords
- damping glue
- heat isolating
- reinforcing filler
- water
- isolating damping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了隔热阻尼胶，主要由以下重量比组成：水溶性粘合剂15-35%，碳酸镁5-15%，补强填充剂5-20%，发泡剂1-10%配以余量的水。水溶性粘合剂优选为聚醋酸乙烯-乙烯共聚物，补强填充剂优选为石棉粉、滑石粉、碳酸钙系列。解决了阻燃、隔热和减振以及毒性等问题，降低了成本。应用于制造汽车、列车、轮船等领域须阻燃、隔热、减振的板材、管道。
Description
本发明涉及一种隔热阻尼胶。
目前国内市场使用的隔热阻尼胶材料主要有PVC、EVA或聚氨酯配以其它填充剂、发泡剂而制成，使用时存在着隔热效果差、减振性能差、毒性大、成本高、易燃等问题。
本发明的目的是提供一种阻燃、隔热、减振效果好、无毒、低成本的阻燃隔热阻尼胶。
为达到上述目的，本发明主要由以下重量比组份：水熔性粘合剂15-35％，碳酸镁5-15％，珍珠岩10-20％，补强填充剂5-20％，发泡剂1-10％，余量为水。
水溶性粘合剂优选为聚醋酸乙烯-乙烯共聚物。
补强填充剂为石棉粉、滑石粉，、碳酸钙系列、陶土、硅藻土、橡胶粉、白油膏、高岭土。
填充剂优选为石棉粉、滑石粉、碳酸钙系列。
发泡剂优选为小苏打、苯磺酰肼、三氯乙烷。
以上配方除水溶性粘合剂、发泡剂以外的所有配合料均为无机物，加之水溶性粘合剂不需要有机溶剂，在生产、使用过程中无毒，而且成本低，仅占使用PVC、聚氨酯成本的35-60％。
由于发泡剂的作用和水的助发泡作用，该产品喷涂后烘烤成型时形成了细密的气孔，并且有较好的弹性，提高了其隔热性能和减振效果。经测试导热系数为0.078，内耗因子为0.035。导热系数测试标准为GB/T3399-82，内耗因子测试标准美国ASTME756-83。
补强填充剂的优选和最佳组合，具有很好的阻燃性，其附着力和耐冲击性均大为增强。经测试：附着力2Mpa，耐冲击性为15cm，附着力测试标准为GB/T5210-85，耐冲击性测标准为GB/T1732-930。
实施例一：以15g聚醋酸乙烯-乙烯共聚物、51g水、5g碳酸镁、10g珍珠岩均匀混合为基料，然后分别加入5g石棉粉、5g滑石粉、5g碳酸钙作为填充剂，搅拌均匀后，加入4g发泡剂小苏打，搅拌使其溶解。在使用时，将其喷涂在汽车顶板和测板内壁，升温烘烤使其成型。在成型过程中，小苏打合全物分解出二氧化碳，二氧化碳主发泡，水蒸汽助发泡，形了细密的气孔。
实施例二：发泡剂改为4g用量的苯磺酰肼，其它组份的用量和生产步骤与实施例一相同。
实施例三：以5g三氯乙烷作为发泡剂，其它组份的用量和生产步骤与实施例一相同。
Claims (4)
1、一种隔热阻尼胶，主要由以下重量比组份组成：水熔怀粘合剂15-35％，碳酸镁5-15％，珍珠岩10-20％，补强填充剂5-20％，发泡剂1-10％，余量为水。
2、根据权利要求1所述的一种隔热阻尼胶，其特征在于水溶性粘合剂为聚醋酸乙烯-乙烯共聚物。
3、根据权利要求1所述的一种隔热阻尼胶，其特征在于补强填充剂为石棉粉、滑石粉、碳酸钙系列、陶土、硅藻土、橡胶粉、白油膏、高岭土单独或者部分组成使用。
4、根据权利要求1所述的一种隔热阻尼胶，其特征在于其发泡剂为小苏打、苯磺酰肼、三氯乙烷。