CN112501535B - 一种增强新能源汽车塑料配件镀层结合力的方法及装置 - Google Patents

一种增强新能源汽车塑料配件镀层结合力的方法及装置 Download PDF

Info

Publication number
CN112501535B
CN112501535B CN202011476768.8A CN202011476768A CN112501535B CN 112501535 B CN112501535 B CN 112501535B CN 202011476768 A CN202011476768 A CN 202011476768A CN 112501535 B CN112501535 B CN 112501535B
Authority
CN
China
Prior art keywords
new energy
energy automobile
spray head
low
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202011476768.8A
Other languages
English (en)
Other versions
CN112501535A (zh
Inventor
方继刚
熊志明
程根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Hengmao Yigao Electroplating Technology Co ltd
Original Assignee
Anhui Hengmao Yigao Electroplating Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Hengmao Yigao Electroplating Technology Co ltd filed Critical Anhui Hengmao Yigao Electroplating Technology Co ltd
Priority to CN202011476768.8A priority Critical patent/CN112501535B/zh
Publication of CN112501535A publication Critical patent/CN112501535A/zh
Application granted granted Critical
Publication of CN112501535B publication Critical patent/CN112501535B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种增强新能源汽车塑料配件镀层结合力的方法及装置，使用该装置处理的方法为：首先对塑料配件进行预处理，在预处理后的塑料配件表面喷涂增强剂，然后立即进行等离子体处理，本发明克服了现有技术的不足，有效的解决了增强剂与塑料配件结合不牢固，造成塑料配件表面形成的镀层容易脱落的问题。

Description

一种增强新能源汽车塑料配件镀层结合力的方法及装置
技术领域
本发明涉及塑料镀层加工技术领域，具体属于一种增强新能源汽车塑料配件镀层结合力的方法及装置。
背景技术
金属材料有着让人喜爱的质感，尤其是现在的金属手机外壳大潮令金属表面处理大受关注，然而金属材料质量大成本高，限制了一些日常产品的应用。塑料质轻且机械性能能够满足部分产品应用，然而缺乏金属的光泽，不够美观，不导电及由此带来的静电作用等等。到目前为止，研究人员已经能够设法在塑料的表面镀敷一层金属来改善塑料的性能，产生了一些展现金属质感外观的塑料制品，这都归功于塑料表面金属化工艺。化学镀是目前使用最广泛的一种塑料金属化加工方法，依据氧化还原反应原理，利用强还原剂在含有金属离子的溶液中，将金属离子还原成金属而沉积在各种材料表面形成致密镀层的方法。但是现有的电镀处理方法需要进行镀铜，且厚度较大，在进行镀层加工的过程中由于环境的细微变化容易导致一些区域的镀层结合力较差，造成镀层在恶劣环境下容易脱落或鼓包的问题。
发明内容
本发明的目的是提供一种增强新能源汽车塑料配件镀层结合力的方法及装置，克服了现有技术的塑料配件表面镀层在恶劣环境下容易脱落或鼓包的问题。
为解决上述问题，本发明所采取的技术方案如下：
一种增强新能源汽车塑料配件镀层结合力的方法，首先对塑料配件进行预处理，在预处理后的塑料配件表面喷涂增强剂，然后立即进行等离子体处理。
优选地，所述的预处理的工艺为：化学除油→粗化→中和→催化→解胶。
优选地，还包括对等离子处理后的塑料配件进行喷涂抗氧化层涂料、半光镍电镀和复合耐腐蚀层的步骤。
优选地，所述的增强剂由以下重量份的原料制成：偶氮二异丁腈0.1-0.5份、乙酸乙酯3-5份、硅丙乳液15-20份。
优选地，所述的等离子体处理的温度为40-60℃。
优选地，所述的抗氧化层涂料包括炭粉、维生素C和水性丙烯酸树脂乳液。
应用于增强新能源汽车塑料配件镀层结合力的方法的装置，包括工作平台，所述的工作平台上设有支腿和控制面板，所述的工作平台的顶部设有传送装置，所述的传送装置两侧的工作平台上依次安装有第一支架和第二支架，所述的第一支架上安装有增强剂喷头，所述的第二支架上安装有低温等离子体喷头，所述的增强剂喷头和低温等离子体喷头位于传送装置的正上方，且增强剂喷头和低温等离子体喷头分别与第一进样泵和低温等离子体发生器连接，所述的传送装置、第一进样泵和低温等离子体发生器分别与控制面板电连接。
优选地，所述的第二支架后方的传送装置两侧的工作平台上还安装有第三支架，所述的第三支架上安装有抗氧化层涂料喷头，所述的抗氧化层涂料喷头位于传送装置的正上方，且连接有第三进样泵，所述的第三进样泵与控制面板电连接。
优选地，所述的增强剂喷头、低温等离子体喷头和抗氧化层涂料喷头的前侧边沿上还分别安装有一个光电传感器，所述的光电传感器与控制面板电连接。
优选地，所述的传送装置为皮带输送机。
本发明与现有技术相比较，本发明的实施效果如下：
1、本发明的方法通过使用偶氮二异丁腈、乙酸乙酯和硅丙乳液组成的增强剂，在配合低温等离子体处理后，增强剂中的偶氮二异丁腈在低温等离子体产生的电子的引发作用下，分解产生大量的自由基，对塑料制品的表面进行深度活化，使塑料制品的表面与硅丙乳液之间实现了紧密结合，同时，在硅丙乳液固化的过程中，由于其表面裸露在外，经低温等离子体处理后，经抗氧化层的喷涂，使其与抗氧化层涂料实现了固化结合，有效的增强了抗氧化层与塑料配件之间的结合强度。
2、本发明使用低温等离子体配合增强剂，有效的解决了增强剂与塑料配件结合不牢固，造成塑料配件表面形成的镀层容易脱落的问题。
3、本发明的装置能够自动感应塑料配件的位置，自动开启和关闭增强剂喷头、低温等离子体喷头和抗氧化层涂料喷头，对塑料配件进行自动化的喷涂和低温等离子体处理，同时该装置能够及时的对喷涂增强剂后的塑料配件进行低温等离子体处理和喷涂抗氧化层涂料，有效的保证了该方法的工艺的进行，使塑料配件镀层结合力得到了提高。
附图说明
图1为本发明的装置的主视图。
附图标记说明：1、工作平台；10、塑料配件；11、第一支架；12、第二支架；13、第三支架；14、控制面板；2、皮带输送机；3、增强剂喷头；4、低温等离子体喷头；5、抗氧化层涂料喷头；6、第一进样泵；60、第一储料箱；7、低温等离子体发生器、8、第二进样泵；80、第二储料箱；9、光电传感器。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
如图1所示，在本发明中用于增强新能源汽车塑料配件镀层结合力的方法的装置包括工作平台1，工作平台1上设有支腿和控制面板14(内置PLC控制器)，控制面板14由外接电源供电，工作平台1的顶部设有皮带输送机2，皮带输送机2两侧的工作平台1上依次安装有第一支架11、第二支架12和第三支架13，第一支架11上安装有增强剂喷头3，第二支架12上安装有低温等离子体喷头4，第三支架13上安装有抗氧化层涂料喷头5，增强剂喷头3、低温等离子体喷头4和抗氧化层涂料喷头5均位于皮带输送机2的正上方，且增强剂喷头3与第一进样泵6连接，而第一进样泵6与第一储料箱60连接；低温等离子体喷头4与低温等离子体发生器7连接，低温等离子体发生器7为温州市亿鸿科技有限公司CRF-APO-RP1020-A型设备；抗氧化层涂料喷头5与第二进样泵8连接，而第二进样泵8与第二储料箱80连接；增强剂喷头3、低温等离子体喷头4和抗氧化层涂料喷头5的前侧边沿上还分别安装有一个光电传感器9，皮带输送机2、第一进样泵6、第二进样泵8、低温等离子体发生器7和光电传感器9分别与控制面板14电连接，光电传感器9为反射式红外感应开关。
使用时将控制面板14与外接电源连接，开启皮带输送机2，将然后将第一进样泵6、第二进样泵8、低温等离子体发生器7和光电传感器9的电路接通，然后将预处理后的新能源汽车塑料配件10置于皮带输送机2上，在塑料配件10向前移动的过程中，位于增强剂喷头3上的光电传感器9首先接收到信号，此时控制面板14控制第一进样泵6开始工作，当塑料配件10从位于增强剂喷头3上的光电传感器9下方移开后，此时控制面板14控制第一进样泵6停止工作，按照同样的方式，低温等离子体喷头4和抗氧化层涂料喷头5的前侧边沿上的光电传感器9控制低温等离子体发生器7和第二进样泵8工作，实现喷涂增强剂，并进行低温等离子体处理和喷涂抗氧化层涂料的操作。
实施例1
将0.3kg偶氮二异丁腈溶于3kg的乙酸乙酯中，然后与18kg硅丙乳液混合均匀，得到增强剂。将炭粉1.4kg和维生素C 0.6kg、水性丙烯酸树脂乳液40kg搅拌混合均匀，在密闭的反应釜内加热至35℃，然后冷却至室温，得到抗氧化层涂料，水性丙烯酸树脂乳液来源于上海凯茵化工有限公司。
新能源汽车塑料配件材质为ABS，对新能源汽车塑料配件表面进行预处理：化学除油→粗化→中和→催化→解胶，该工艺流程按照行业内常规处理工艺进行；接着将预处理后的新能源汽车塑料配件送入增强新能源汽车塑料配件镀层结合力的方法的装置喷涂增强剂，并进行低温等离子体处理和喷涂抗氧化层涂料，等离子体处理的温度为45℃，然后置于洁净的环境中自然干燥，得到8um厚的抗氧化层；然后进行半光镍电镀，得到11um厚的半光镍层；然后在半光镍的表层喷涂氰基丙烯酸酯胶粘剂，然后迅速喷涂聚四氟乙烯层12um，干燥后，得到具有表面金属层的新能源汽车塑料配件。
实施例2
将0.4kg偶氮二异丁腈溶于5kg的乙酸乙酯中，然后与20kg硅丙乳液混合均匀，得到增强剂。将炭粉1.4kg和维生素C 0.6kg、水性丙烯酸树脂乳液40kg搅拌混合均匀，在密闭的反应釜内加热至35℃，然后冷却至室温，得到抗氧化层涂料。
新能源汽车塑料配件材质为ABS，对新能源汽车塑料配件表面进行预处理：化学除油→粗化→中和→催化→解胶，该工艺流程按照行业内常规处理工艺进行；接着将预处理后的新能源汽车塑料配件送入增强新能源汽车塑料配件镀层结合力的方法的装置喷涂增强剂，并进行低温等离子体处理和喷涂抗氧化层涂料，等离子体处理的温度为60℃，然后置于洁净的环境中自然干燥，得到8um厚的抗氧化层；然后通过现有的技术进行半光镍电镀，半光镍电镀液使用本领域常用的配方，得到11um厚的半光镍层；然后在半光镍的表层喷涂氰基丙烯酸酯胶粘剂，然后迅速喷涂聚四氟乙烯层12um，干燥后，得到具有表面金属层的新能源汽车塑料配件。
对照例1
与实施例1的区别在于，偶氮二异丁腈的加入量为0。
对照例2
与实施例1的区别在于，不进行低温等离子体处理。
对照例3
与实施例1的区别在于，炭粉的加入量为0。
将实施例1-2和对照例1-3中的具有表面金属层的新能源汽车塑料配件按照ASTMB368-09进行防腐蚀测试；按照ASTMG85-9进行盐雾测试；按照ASMEA112.18.1-2005/CSAB125.1-05在-40℃至75℃的环境中进行冷热循环测试，测试结果如下表：
Figure BDA0002837493780000061
由上表可知，本发明的装置通过使用增强剂配合低温等离子体对新能源汽车塑料配件进行处理，有效的增强了抗氧化层与塑料配件的结合强度，同时通过在抗氧化层内添加导电的炭粉，使抗氧化层起到了电子转移的作用，使表面金属层吸收的氧化电子被转移给具有还原能力的维生素C，有效的提高了新能源汽车塑料配件表面镀层的抗腐蚀能力。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (5)

1.一种增强新能源汽车塑料配件镀层结合力的方法，首先对塑料配件进行预处理，其特征在于，在预处理后的塑料配件表面喷涂增强剂，然后立即进行等离子体处理；
所述的预处理的工艺为：化学除油→粗化→中和→催化→解胶；
还包括对等离子处理后的塑料配件进行喷涂抗氧化层涂料、半光镍电镀和复合耐腐蚀层的步骤；
所述的增强剂由以下重量份的原料制成：偶氮二异丁腈0.1-0.5份、乙酸乙酯3-5份、硅丙乳液15-20份；
所述的等离子体处理的温度为40-60℃。
2.应用于权利要求1所述的增强新能源汽车塑料配件镀层结合力的方法的装置，其特征在于，包括工作平台，所述的工作平台上设有支腿和控制面板，所述的工作平台的顶部设有传送装置，所述的传送装置两侧的工作平台上依次安装有第一支架和第二支架，所述的第一支架上安装有增强剂喷头，所述的第二支架上安装有低温等离子体喷头，所述的增强剂喷头和低温等离子体喷头位于传送装置的正上方，且增强剂喷头和低温等离子体喷头分别与第一进样泵和低温等离子体发生器连接，所述的传送装置、第一进样泵和低温等离子体发生器分别与控制面板电连接。
3.根据权利要求2所述的应用于增强新能源汽车塑料配件镀层结合力的方法的装置，其特征在于，所述的第二支架后方的传送装置两侧的工作平台上还安装有第三支架，所述的第三支架上安装有抗氧化层涂料喷头，所述的抗氧化层涂料喷头位于传送装置的正上方。
4.根据权利要求3所述的应用于增强新能源汽车塑料配件镀层结合力的方法的装置，其特征在于，所述的增强剂喷头、低温等离子体喷头和抗氧化层涂料喷头的前侧边沿上还分别安装有一个光电传感器，所述的光电传感器与控制面板电连接。
5.根据权利要求4所述的应用于增强新能源汽车塑料配件镀层结合力的方法的装置，其特征在于，所述的传送装置为皮带输送机。
CN202011476768.8A 2020-12-15 2020-12-15 一种增强新能源汽车塑料配件镀层结合力的方法及装置 Active CN112501535B (zh)