CN112500662A - 一种制造耐腐蚀防老化吧椅椅座的材料及其制作方法 - Google Patents
一种制造耐腐蚀防老化吧椅椅座的材料及其制作方法 Download PDFInfo
- Publication number
- CN112500662A CN112500662A CN202011465029.9A CN202011465029A CN112500662A CN 112500662 A CN112500662 A CN 112500662A CN 202011465029 A CN202011465029 A CN 202011465029A CN 112500662 A CN112500662 A CN 112500662A
- Authority
- CN
- China
- Prior art keywords
- chair seat
- aging
- bar chair
- corrosion
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种制造耐腐蚀防老化吧椅椅座的材料，防腐蚀耐老化吧椅座的制作材料由按以下重量份比例的原材料组成：偏氟乙烯、聚乙烯、玻璃纤维、甲基丙烯酸缩水甘油酯、硬脂酸、聚氯乙烯树脂、受阻胺光稳定剂、抗氧化剂、防老化剂、固化剂、相容剂、润滑剂分散剂、增韧剂。本发明具有如下有益效果：通过防腐蚀耐老化吧椅座的制作配方中各组分之间相互配合相互促进，提高制得的吧椅座的抗氧化抗紫外线性能，使得吧椅座具有良好的防腐蚀耐老化功能。
Description
技术领域
本发明涉及家具技术领域，尤其涉及一种制造耐腐蚀防老化吧椅椅座的材料及其制作方法。
背景技术
吧椅最初主要使用是在酒吧，吧椅的使用已经越来越多，被广泛使用在涮吧、快餐厅、茶餐厅、咖啡厅、珠宝卖场、化妆品卖场等场地，吧椅在椅业产品中是近几年来开发和生产出的衍生产品，吧椅主要由办公椅的通用配件如吧椅座、气弹簧、托盘、脚轮等及其特有的喇叭盘、座板等配件组成。由于部分吧椅座经常在暴露于户外的条件下使用，因此很容易会出现吧椅座快速老化的情况，吧椅座老化后容易脆化，易碎裂，容易对人造成伤害，此外现有的吧椅座不耐腐蚀，长期在户外使用后会被雨水等腐蚀而留下痕迹，影响吧椅的整体美观。
发明内容
针对现有技术中所存在的不足，本发明提供了一种制造耐腐蚀防老化吧椅椅座的材料，其解决了现有技术中吧椅座不耐腐蚀不耐老化的技术问题。
本发明通过以下技术方案解决上述技术问题，一种制造耐腐蚀防老化吧椅椅座的材料，防腐蚀耐老化吧椅座的制作材料由按以下重量份比例的原材料组成：
通过采用上述技术方案，本发明的吧椅座原材料配方中，以偏氟乙烯为母材，偏氟乙烯具有良好的化学稳定性，聚乙烯是一种常见的热塑性树脂，具有无味无毒的特点，能耐大部分的酸碱腐蚀且能在高温和低温环境中保持稳定，玻璃纤维能提高吧椅座的整体强度，甲基丙烯酸缩水甘油酯能够改善本配方中的原材料在注塑时的挤出性能，硬脂酸能提高吧椅座的热稳定性，聚氯乙烯树脂能提高制得的吧椅座的韧性和延展性，受阻胺光稳定剂能提高吧椅座在长时间阳光照射下的抗老化性能，使得吧椅座的材料不会受紫外线影响而快速脆化，抗氧化剂能提高吧椅座的抗氧化性能，延缓吧椅座被氧化而塑化的过程，固化剂能提高吧椅座的固化程度，使吧椅座更加牢固，相容剂能使各原材料在混炼塑化过程中混合更加均匀，润滑剂能使各原材料在在造粒过程中流动更快，分散剂能偏氟乙烯和聚乙烯的门尼粘度，使各原料得以充分融合，最终所得的塑料成型件分散均匀，性质稳定，增韧剂能提高吧椅座的柔韧性。
优选的，所述偏氟乙烯采用粒径为20-30nm，松密度为0.5-1.8g/cm3的颗粒规格。
通过采用上述技术方案，选用粒径更小，松密度也更小的偏氟乙烯有助于使吧椅座更加坚固且更加轻盈。
优选的，所述抗氧化剂分为主抗氧化剂和辅助抗氧化剂，所述主抗氧化剂选用对苯二酚抗氧化剂和对苯二胺抗氧化剂中的一种或两种的组合物，所述辅助抗氧化剂选用有机硫化物或者亚磷酸盐，所述主抗氧化剂和辅助抗氧化剂的重量比在5:1-6:1。
通过采用上述技术方案，主抗氧剂为氢给予型的链终止型抗氧剂，能终止氧化过程中自由基链的传递与增长，减缓聚合物的氧化老化-自由基链反应，防止游离基的产生，防止游离基链的传递，辅助抗氧剂为防止游离基链的传递，两者共同作用，能起到很好的抗氧化作用。
优选的，所述防老化剂选用防老化剂IPPD和防老剂AW按照1：1的重量比配比形成的混合防老化剂。
通过采用上述技术方案，两者混合使用，对吧椅座的臭氧龟裂和自然老化防护效能更高。
优选的，所述固化剂选用乙烯基三胺固化剂。
通过采用上述技术方案，乙烯基三胺固化剂是一种十分适合偏氟乙烯、聚乙烯和聚氯乙烯树脂的固化剂，固化速度快，固化效果不会受温度影响而产生较大波动。
优选的，所述相容剂选用恶唑啉型相容剂。
通过采用上述技术方案，恶唑啉型相容剂可直接用于塑料的改性和相容。
优选的，所述润滑剂为聚乙烯蜡或低分子量聚丙烯。
通过采用上述技术方案，聚乙烯蜡和低分子量聚丙烯具有良好的耐热性，即使在高温下仍能保持润滑性能，且还能提高乙烯类的脱模性。
优选的，所述分散剂为十二烷基硫酸钠、甲基戊醇中的一种或多种配合使用。
通过采用上述技术方案，十二烷基硫酸钠具有良好的乳化性，起泡性，并且在在较宽pH值的溶液中保持稳定性，因此是一种稳定性好，分散能力强的分散剂，甲基戊醇是一种能改善液体物料分散性能的分散剂，可以很好的跟有较低亲水亲油平衡值的分散物形成稳定的分散体系。
优选的，所述增韧剂为聚烯烃类增韧剂。
通过采用上述技术方案，聚烯烃类增韧剂能有效防止吧椅座因脆化而产生细小裂纹。
一种防腐蚀耐老化吧椅座的制作方法，包括以下步骤：
S1，备料，按照上述各原材料的重量比准备原材料偏氟乙烯、聚乙烯、玻璃纤维、甲基丙烯酸缩水甘油酯、硬脂酸和聚氯乙烯树脂。
S2，烘干，将上述原材料混合均匀后进行烘干，烘干至含水量小于等于1％；
S3，融合，在原料中加入相容剂、润滑剂、抗氧化剂、分散剂、增韧剂、受阻胺光稳定剂、防老化剂和固化剂；
S4，调色，加入调色剂调出需求的颜色；
S5，混炼造粒，在双螺杆造粒机中混炼塑化后挤出，得到塑料颗粒；
S6，注塑成型，将塑料颗粒在注塑机中注塑成型得到吧椅座。
通过采用上述技术方案，脚踏能为乘坐者提供一个搁脚的支撑处，使吧椅的乘坐者坐姿更加舒适。
相比于现有技术，本发明具有如下有益效果：通过防腐蚀耐老化吧椅座的制作配方中各组分之间相互配合相互促进，提高制得的吧椅座的抗氧化抗紫外线性能，使得吧椅座具有良好的防腐蚀耐老化功能。
具体实施方式
下面结合实施例对本发明中的技术方案进一步说明。
实施例1
一种防腐蚀耐老化吧椅座的制作方法，包括以下步骤：
S1，备料，按照上述各原材料的重量比准备原材料偏氟乙烯、聚乙烯、玻璃纤维、甲基丙烯酸缩水甘油酯、硬脂酸和聚氯乙烯树脂；
S2，烘干，将上述原材料混合均匀后进行烘干，烘干至含水量小于等于1％；
S3，融合，在原料中加入相容剂、润滑剂、抗氧化剂、分散剂、增韧剂、受阻胺光稳定剂、防老化剂和固化剂；
S4，调色，加入调色剂调出需求的颜色；
S5，混炼造粒，在双螺杆造粒机中混炼塑化后挤出，得到塑料颗粒；
S6，注塑成型，将塑料颗粒在注塑机中注塑成型得到吧椅座。
其中，其中各原料组分的规格如表1所示，按重量份计每100重量份的原料中各组分的重量如表二所示。
表1原料组分的规格型号及生产厂家
实施例2，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
实施例3，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
实施例4，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
实施例5，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
对比例1，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
对比例2，一种制造耐腐蚀防老化吧椅椅座的材料，与实施例1不同之处在于原料中各组分及重量如图表二所示。
表二原料中各组分及数量
性能检测试验
1、强度测试
本实验将用实施例1-5中对比例1-2的各吧椅座的制作配方制作的吧椅座进行拉伸测试，测试温度25摄氏度，直接检测吧椅座被撕裂所需的撕扯力。检测结果件表3所示。
2、耐候性测试
本实验将用实施例1-5对比例1-2中的各吧椅座的制作配方制作的吧椅座进行耐候性测试，测试温度从0摄氏度到40摄氏度，每2小时温度提高或降低5摄氏度，且在测试过程中每隔6小时进行喷水一次，每隔10小时吹风一次，总测试市场240小时，测试完成后检测吧椅座被撕裂所需的撕扯力。检测结果件表3所示。
3、高温测试实验
本实验将用实施例1-5及对比例1-2中的各吧椅座的制作配方制作的吧椅座进行高温测试，测试温度从0摄氏度到80摄氏度，每24小时温度提高10摄氏度，且在测试过程中每隔10小时检测吧椅座被撕裂所需的撕扯力。检测结果件表3所示。
4、耐腐蚀测试实验
本实验将用实施例1-5及对比例1-2中的各吧椅座的制作配方制作的吧椅座进行耐腐蚀测试，测试温度25摄氏度，在吧椅座表面滴加酸性和碱性腐蚀液，观察腐蚀程度。检测结果件表3所示。
表3性能检测实验结果
根据表3中的数据可以看出，相对传统的吧椅座的原材料配方，本发明的实施例均具有拉伸强度和耐腐蚀性，且具有良好的耐高温性能和抗老化性能。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (10)
1.一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于，防腐蚀耐老化吧椅座的制作材料由按以下重量份比例的原材料组成：
2.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述偏氟乙烯采用粒径为20-30nm，松密度为0.5-1.8g/cm3的颗粒规格。
3.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述抗氧化剂分为主抗氧化剂和辅助抗氧化剂，所述主抗氧化剂选用对苯二酚抗氧化剂和对苯二胺抗氧化剂中的一种或两种的组合物，所述辅助抗氧化剂选用有机硫化物或者亚磷酸盐，所述主抗氧化剂和辅助抗氧化剂的重量比在5:1-6:1。
4.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述防老化剂选用防老化剂IPPD和防老剂AW按照1：1的重量比配比形成的混合防老化剂。
5.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述固化剂选用乙烯基三胺固化剂。
6.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述相容剂选用恶唑啉型相容剂。
7.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述润滑剂为聚乙烯蜡或低分子量聚丙烯。
8.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述分散剂为十二烷基硫酸钠、甲基戊醇中的一种或多种配合使用。
9.如权利要求1所述的一种制造耐腐蚀防老化吧椅椅座的材料，其特征在于：所述增韧剂为聚烯烃类增韧剂。
10.一种防腐蚀耐老化吧椅座的制作方法，其特征在于，包括以下步骤：
S1，备料，按照权利要求1中各原材料的重量比准备原材料偏氟乙烯、聚乙烯、玻璃纤维、甲基丙烯酸缩水甘油酯、硬脂酸和聚氯乙烯树脂；
S2，烘干，将上述原材料混合均匀后进行烘干，烘干至含水量小于等于1％；
S3，融合，在原料中加入相容剂、润滑剂、抗氧化剂、分散剂、增韧剂、受阻胺光稳定剂、防老化剂和固化剂；
S4，调色，加入调色剂调出需求的颜色；
S5，混炼造粒，在双螺杆造粒机中混炼塑化后挤出，得到塑料颗粒；
S6，注塑成型，将塑料颗粒在注塑机中注塑成型得到吧椅座。