Prior art keywords
layer
type
algan
topological insulator
visible
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202011337520.3A
Other languages
Chinese (zh)
Other versions
CN112490305B (en
Inventor
张云霄
李爱民
张远祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Jinhang Institute of Technical Physics
Original Assignee
Tianjin Jinhang Institute of Technical Physics
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Jinhang Institute of Technical Physics filed Critical Tianjin Jinhang Institute of Technical Physics
Priority to CN202011337520.3A priority Critical patent/CN112490305B/en
Publication of CN112490305A publication Critical patent/CN112490305A/en
Application granted granted Critical
Publication of CN112490305B publication Critical patent/CN112490305B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/08—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors
    • H01L31/10—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors characterised by potential barriers, e.g. phototransistors
    • H01L31/101—Devices sensitive to infrared, visible or ultraviolet radiation
    • H01L31/102—Devices sensitive to infrared, visible or ultraviolet radiation characterised by only one potential barrier
    • H01L31/109—Devices sensitive to infrared, visible or ultraviolet radiation characterised by only one potential barrier the potential barrier being of the PN heterojunction type
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/0256—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by the material
    • H01L31/0264—Inorganic materials
    • H01L31/0304—Inorganic materials including, apart from doping materials or other impurities, only AIIIBV compounds
    • H01L31/03044—Inorganic materials including, apart from doping materials or other impurities, only AIIIBV compounds comprising a nitride compounds, e.g. GaN
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/0256—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by the material
    • H01L31/0264—Inorganic materials
    • H01L31/0304—Inorganic materials including, apart from doping materials or other impurities, only AIIIBV compounds
    • H01L31/03046—Inorganic materials including, apart from doping materials or other impurities, only AIIIBV compounds including ternary or quaternary compounds, e.g. GaAlAs, InGaAs, InGaAsP
    • H01L31/03048—Inorganic materials including, apart from doping materials or other impurities, only AIIIBV compounds including ternary or quaternary compounds, e.g. GaAlAs, InGaAs, InGaAsP comprising a nitride compounds, e.g. InGaN
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/0256—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by the material
    • H01L31/0264—Inorganic materials
    • H01L31/032—Inorganic materials including, apart from doping materials or other impurities, only compounds not provided for in groups H01L31/0272 - H01L31/0312
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/0352—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their shape or by the shapes, relative sizes or disposition of the semiconductor regions
    • H01L31/035272—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their shape or by the shapes, relative sizes or disposition of the semiconductor regions characterised by at least one potential jump barrier or surface barrier
    • H01L31/03529—Shape of the potential jump barrier or surface barrier
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/08—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors
    • H01L31/10—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors characterised by potential barriers, e.g. phototransistors
    • H01L31/101—Devices sensitive to infrared, visible or ultraviolet radiation
    • H01L31/1013—Devices sensitive to infrared, visible or ultraviolet radiation devices sensitive to two or more wavelengths, e.g. multi-spectrum radiation detection devices
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/08—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors
    • H01L31/10—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof in which radiation controls flow of current through the device, e.g. photoresistors characterised by potential barriers, e.g. phototransistors
    • H01L31/101—Devices sensitive to infrared, visible or ultraviolet radiation
    • H01L31/11—Devices sensitive to infrared, visible or ultraviolet radiation characterised by two potential barriers, e.g. bipolar phototransistors

Landscapes

  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • Electromagnetism (AREA)
  • General Physics & Mathematics (AREA)
  • Engineering & Computer Science (AREA)
  • Computer Hardware Design (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Power Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Light Receiving Elements (AREA)

Abstract

The invention belongs to the technical field of semiconductor photoelectric detectors, and particularly relates to a visible-ultraviolet double-color detector which adopts a longitudinal integrated structure and comprises an nGaN substrate, an n-type GaN contact layer, a lower metal electrode, an AlGaN matching layer, an AlGaN ultraviolet absorption layer, a two-dimensional boron nitride film barrier layer, a topological insulator visible light absorption layer, an n-type topological insulator film contact layer, an upper metal electrode and a passivation layer. The detectors with two wave bands in the detector have a bottom-up integrated structure, visible and ultraviolet double-color detection can be realized by controlling bias voltage, the false alarm rate is reduced, the size of a device is reduced, and the complexity of a preparation process and a detection system is reduced.

Description

Visible-ultraviolet double-color detector
Technical Field
The invention belongs to the technical field of semiconductor photoelectric detectors, and particularly relates to a visible-ultraviolet double-color detector.
Background
The photoelectric detector has wide application in various fields such as national economy, military and the like. The photoelectric detector based on different wave band detection has important effect on detection in different fields. In visible and near infrared, the photoelectric detector is mainly applied to the aspects of ray measurement and detection, industrial automatic control, photometric measurement and the like; the ultraviolet band is mainly used in military and civil fields such as ultraviolet guidance, ultraviolet alarm, ultraviolet communication, ultraviolet countermeasure, electric power monitoring and the like. The traditional group III nitride material system represented by a gallium nitride/aluminum gallium nitride system is an optimal material for realizing ultraviolet detection, but the detection of visible light and near infrared is difficult to realize, and the photodetectors based on silicon and GaAs are increasingly mature in the aspects of visible light and near infrared, but are difficult to expand towards ultraviolet detection, so that the detection of ultraviolet and visible multiband is difficult to realize by one material system, and a new way for realizing adjustable ultraviolet-visible two-color integrated detection is urgently needed.
Disclosure of Invention
Technical problem to be solved
The technical problem to be solved by the invention is as follows: in view of the above technical shortcomings and needs for improvement, how to provide a visible-ultraviolet dual-color detector capable of multiband response.
(II) technical scheme
In order to solve the above technical problem, the present invention provides a visible-ultraviolet two-color detector, which adopts a longitudinal integrated structure, comprising: the GaN-based LED chip comprises an n-type GaN substrate, an n-type GaN contact layer, a lower metal electrode layer, an n-type AlGaN matching layer, an AlGaN ultraviolet absorption layer, a two-dimensional boron nitride film barrier layer, an n-type topological insulator visible light absorption layer, an n-type topological insulator film contact layer, an upper metal electrode layer and a passivation layer;
the n-type GaN contact layer is extended on the n-type GaN substrate;
the lower metal electrode layer is arranged on the upper surface of the n-type GaN contact layer, is an annular electrode and is provided with an n-type bonding pad;
the n-type AlGaN matching layer is arranged on the n-type GaN contact layer and is positioned in an area within the annular lower metal electrode layer;
the AlGaN ultraviolet absorption layer is extended on the n-type AlGaN matching layer;
the two-dimensional boron nitride film barrier layer is arranged on the AlGaN ultraviolet absorption layer;
the n-type topological insulator visible light absorption layer is arranged on the two-dimensional boron nitride film barrier layer;
the n-type topological insulator thin film contact layer is arranged on the n-type topological insulator visible light absorption layer;
the upper metal electrode layer is arranged on the n-type topological insulator thin film contact layer, is an annular electrode and is provided with an n-type bonding pad;
the passivation layer is arranged on the side walls of the n-type AlGaN matching layer, the AlGaN ultraviolet absorption layer, the two-dimensional boron nitride film barrier layer, the n-type topological insulator visible light absorption layer and the n-type topological insulator film contact layer, and the area, which is not covered with the electrode, of the upper surfaces of the n-type GaN contact layer and the n-type topological insulator film contact layer.
Wherein the thickness of the n-type GaN substrate is 0.3-0.5 mm;
the doping concentration of the n-type GaN contact layer is more than or equal to 1018cm3The thickness is 400nm +/-20 nm;
the n-type AlGaN matching layer has a doping concentration of 1017cm3～1018cm3Within the range, the thickness is 200nm plus or minus 20 nm;
the doping concentration of the AlGaN ultraviolet absorption layer is 1016cm3The thickness is 150nm plus or minus 10 nm;
the doping concentration of the two-dimensional boron nitride film barrier layer is 1016cm3The thickness is 30-50 nm;
the doping concentration of the n-type topological insulator visible light absorption layer is 1016cm3Within.
The doping concentration of the n-type topological insulator thin film contact layer is 1018cm3Above, 10nm to 30nm thick.
The n-type GaN substrate is formed by epitaxial growth of the n-type GaN contact layer, the n-type AlGaN matching layer and the AlGaN ultraviolet absorption layer on the n-type GaN substrate in sequence through MBE technology.
And the diameters of the annular electrodes of the lower metal electrode layer and the upper metal electrode layer are reduced in sequence.
The n-type topological insulator thin film contact layer is a bismuth selenide or bismuth-oxygen-selenium thin film layer, and the thickness of the n-type topological insulator thin film contact layer is 10nm to 60 nm;
the two-dimensional boron nitride film barrier layer and the n-type topological insulator film contact layer are prepared on the n-type AlGaN absorption layer by adopting a film transfer method.
Wherein the energy gap of the AlGaN ultraviolet absorption layer is within the range of 3.4-6.2 eV;
wherein the forbidden band width of the topological insulator thin film layer is in the range of 1.2-3.4 eV;
wherein, lower metal electrode layer, last metal electrode layer are: ti and Au electrodes, wherein the thickness of the lower layer Ti is 20-40nm, and the thickness of the upper layer Au is 60-120 nm.
Wherein the passivation layer is made of silicon oxide, silicon nitride, polyimide or BCB.
(III) advantageous effects
Aiming at the technical defects and improvement requirements, the invention provides a visible-ultraviolet double-color detector capable of multiband response, which integrates an AlGaN material and a topological insulator thin film material, combines the advantages of the AlGaN material in ultraviolet detection with the advantages of the topological insulator thin film material in visible light detection, solves a series of problems of limited response, limited detection waveband and the like of a single-material photodetector, can ensure that a device has the characteristics of high speed, broadband response, low dark current and the like, and can improve the monolithic integration level of the device by adopting a longitudinal vertical device structure.
Compared with the prior art, the AlGaN material adopted by the invention has good light absorption characteristic in an ultraviolet band and high responsivity, and the topological insulator thin film material has good light absorption characteristic in a visible light band and is easy to integrate with other semiconductor materials;
the invention adopts a vertical n-type AlGaN material/BN/n-type topological insulator thin film material heterojunction structure, realizes dual-band detection by adjusting bias voltage applied by an upper electrode and a lower electrode, and adopts an nBn-type single carrier detection structure to mainly rely on minority hole transport to generate photo-generated current, thereby reducing the generation of composite current and surface leakage current.
The heterojunction structure of the vertical n-type AlGaN material/BN/n-type topological insulator thin film material can improve the responsivity of the device, solves the problems of low optical responsivity, narrow waveband range, difficult integration and the like of the optical detector based on a single material system, and has great potential for realizing a wide-spectrum detector.
Drawings
Fig. 1 is a cross-sectional view of a visible-ultraviolet two-color detector according to an embodiment of the present invention.
Fig. 2 is a top view of a visible-ultraviolet two-color detector according to an embodiment of the present invention.
Detailed Description
In order to make the objects, contents, and advantages of the present invention clearer, the following detailed description of the embodiments of the present invention will be made in conjunction with the accompanying drawings and examples.
In recent years, two-dimensional layered materials attract great attention, and particularly, free-hanging bonds on the surfaces of the two-dimensional materials enable the two-dimensional materials to be combined with other semiconductors, so that the limitation of crystal lattices is overcome, and an ideal design platform is provided for the realization of a multi-band detector. Particularly, the bismuth oxide topological insulator is a brand new two-dimensional semiconductor chip material (bismuth selenide and bismuth selenide) which has the characteristics of ultrahigh electron mobility, proper band gap, stable environment and batch preparation, the energy gap is adjustable in the range of 0.91-2.3eV, and the bismuth oxide topological insulator has excellent performance in the aspect of visible light detection. Therefore, high-performance adjustable ultraviolet-visible double-color integrated detection can be realized by constructing the bismuth topological insulator film and the GaN heterojunction device.
In order to solve the above technical problem, the present invention provides a visible-ultraviolet two-color detector, as shown in fig. 1, the visible-ultraviolet two-color detector adopts a longitudinal integrated structure, including: the GaN-based LED chip comprises an n-type GaN substrate, an n-type GaN contact layer, a lower metal electrode layer, an n-type AlGaN matching layer, an AlGaN ultraviolet absorption layer, a two-dimensional boron nitride film barrier layer, an n-type topological insulator visible light absorption layer, an n-type topological insulator film contact layer, an upper metal electrode layer and a passivation layer;
the n-type GaN contact layer is extended on the n-type GaN substrate;
the lower metal electrode layer is arranged on the upper surface of the n-type GaN contact layer, is an annular electrode and is provided with an n-type bonding pad;
the n-type AlGaN matching layer is arranged on the n-type GaN contact layer and is positioned in an area within the annular lower metal electrode layer;
the AlGaN ultraviolet absorption layer is extended on the n-type AlGaN matching layer;
the two-dimensional boron nitride film barrier layer is arranged on the AlGaN ultraviolet absorption layer;
the n-type topological insulator visible light absorption layer is arranged on the two-dimensional boron nitride film barrier layer;
the n-type topological insulator thin film contact layer is arranged on the n-type topological insulator visible light absorption layer;
the upper metal electrode layer is arranged on the n-type topological insulator thin film contact layer, is an annular electrode and is provided with an n-type bonding pad;
the passivation layer is arranged on the side walls of the n-type AlGaN matching layer, the AlGaN ultraviolet absorption layer, the two-dimensional boron nitride film barrier layer, the n-type topological insulator visible light absorption layer and the n-type topological insulator film contact layer, and the area, which is not covered with the electrode, of the upper surfaces of the n-type GaN contact layer and the n-type topological insulator film contact layer.
Wherein the thickness of the n-type GaN substrate is 0.3-0.5 mm;
the doping concentration of the n-type GaN contact layer is more than or equal to 1018cm3The thickness is 400nm +/-20 nm;
the n-type AlGaN matching layer has a doping concentration of 1017cm3～1018cm3Within the range, the thickness is 200nm plus or minus 20 nm;
the doping concentration of the AlGaN ultraviolet absorption layer is 1016cm3The thickness is 150nm plus or minus 10 nm;
the doping concentration of the two-dimensional boron nitride film barrier layer is 1016cm3The thickness is 30-50 nm;
the doping concentration of the n-type topological insulator visible light absorption layer is 1016cm3Within.
The doping concentration of the n-type topological insulator thin film contact layer is 1018cm3Above, 10nm to 30nm thick.
The n-type GaN substrate is formed by epitaxial growth of the n-type GaN contact layer, the n-type AlGaN matching layer and the AlGaN ultraviolet absorption layer on the n-type GaN substrate in sequence through MBE technology.
And the diameters of the annular electrodes of the lower metal electrode layer and the upper metal electrode layer are reduced in sequence.
The n-type topological insulator thin film contact layer is a bismuth selenide or bismuth-oxygen-selenium thin film layer, and the thickness of the n-type topological insulator thin film contact layer is 10nm to 60 nm;
the two-dimensional boron nitride film barrier layer and the n-type topological insulator film contact layer are prepared on the n-type AlGaN absorption layer by adopting a film transfer method.
Wherein the energy gap of the AlGaN ultraviolet absorption layer is within the range of 3.4-6.2 eV;
wherein the forbidden band width of the topological insulator thin film layer is in the range of 1.2-3.4 eV;
wherein, lower metal electrode layer, last metal electrode layer are: ti and Au electrodes, wherein the thickness of the lower layer Ti is 20-40nm, and the thickness of the upper layer Au is 60-120 nm.
Wherein the passivation layer is made of silicon oxide, silicon nitride, polyimide or BCB.
Example 1
Referring to fig. 1, the present embodiment provides a visible-ultraviolet two-color detector, which sequentially includes, from bottom to top, an n-type GaN substrate 1, an n-type GaN contact layer 2, a lower metal electrode layer 3, an n-type AlGaN matching layer 4, an AlGaN ultraviolet absorption layer 5, a two-dimensional boron nitride thin film barrier layer 6, a topological insulator visible light absorption layer 7, an n-type topological insulator thin film contact layer 8, an upper metal electrode layer 10, and a passivation layer 9.
Heterojunction is formed among the n-type GaN substrate 1, the n-type GaN contact layer 2, the lower metal electrode layer 3, the n-type AlGaN matching layer 4, the AlGaN ultraviolet absorption layer 5, the two-dimensional boron nitride film barrier layer 6, the topological insulator visible light absorption layer 7 and the n-type topological insulator film contact layer 8, and the upper metal electrode layer and the lower metal electrode layer are used as two output stages to form the nBn-type heterojunction bicolor detector structure.
The thickness of the n-type GaN substrate 1 is 0.3-0.5 mm;
the doping concentration of the n-type GaN contact layer 2 is more than or equal to 1018cm3The thickness is 400nm +/-20 nm, and the film is extended on the substrate;
the lower metal electrode layer 3 is arranged on the upper surface of the n-type GaN contact layer, is an annular electrode and is provided with an n-type bonding pad 3-1, and the basic structure is shown in FIG. 2;
the n-type AlGaN matching layer 4 has a doping concentration of 1017cm3～1018cm3Within the range, the thickness is 200nm plus or minus 20nm, the n-type GaN contact layer 2 is arranged on the n-type GaN contact layer, and the n-type GaN contact layer is positioned in the inner area of the annular electrode;
the AlGaN ultraviolet absorption layer 5 has a doping concentration of 1016cm3The thickness is 150nm +/-10 nm, and the AlGaN/GaN film is extended on the n-type AlGaN matching layer 4;
the two-dimensional boron nitride film barrier layer 6 has a doping concentration of 1016cm3The AlGaN ultraviolet absorption layer is arranged on the AlGaN ultraviolet absorption layer 5, and the thickness of the AlGaN ultraviolet absorption layer is 30-50 nm;
the n-type topological insulator visible light absorption layer 7 has a doping concentration of 1016cm3The two-dimensional boron nitride film is arranged on the two-dimensional boron nitride film barrier layer 6;
the n-type topological insulator thin film contact layer 8 has the doping concentration of 1018cm3Above, 10nm to 30nm in thickness, disposed on the n-type topological insulator visible light absorbing layer 7;
the upper metal electrode layer 10 is arranged on the n-type topological insulator thin film contact layer 8, is an annular electrode and is provided with an n-type bonding pad 10-1, and the basic structure is shown in figure 2;
the passivation layer 9 is arranged on the side walls of the AlGaN matching layer 4, the AlGaN ultraviolet absorption layer 5, the two-dimensional boron nitride film barrier layer 6, the topological insulator visible light absorption layer 7, the n-type topological insulator film contact layer 8 and the like, and in the areas, which are not covered with the electrodes (3 and 10), of the upper surfaces of the n-type GaN contact layer 2 and the n-type topological insulator film contact layer 8;
the diameters of the annular electrodes of the lower metal electrode layer 3 and the upper metal electrode layer 10 are reduced in sequence;
the n-type GaN contact layer 2, the n-type AlGaN matching layer 4 and the AlGaN ultraviolet absorption layer 5 are formed by epitaxial growth on the n-type GaN substrate 1 in sequence through MBE technology;
the topological insulator thin film layer 7 is a bismuth selenide or bismuth-oxygen-selenium thin film layer, and the thickness is 10nm to 60 nm;
the two-dimensional boron nitride film 6 and the topological insulator film layer 7 are prepared on the n-type AlGaN absorption layer 5 by adopting a common film transfer method;
the forbidden band width of the AlGaN absorption layer 5 is within the range of 3.4-6.2 eV;
the energy gap of the flapping insulator layer 7 is in the range of 1.2-3.4 eV;
the lower metal electrode layer 3 and the upper metal electrode layer 10 are: ti and Au electrodes, wherein the thickness of the lower layer Ti is 20-40nm, and the thickness of the upper layer Au is 60-120 nm;
the passivation layer material 9 is silicon oxide, silicon nitride, polyimide, BCB, etc.
The above description is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, several modifications and variations can be made without departing from the technical principle of the present invention, and these modifications and variations should also be regarded as the protection scope of the present invention.

Claims (10)

1. A visible-ultraviolet dual-color detector, characterized in that the visible-ultraviolet dual-color detector adopts a longitudinal integrated structure, comprising: the GaN-based LED chip comprises an n-type GaN substrate, an n-type GaN contact layer, a lower metal electrode layer, an n-type AlGaN matching layer, an AlGaN ultraviolet absorption layer, a two-dimensional boron nitride film barrier layer, an n-type topological insulator visible light absorption layer, an n-type topological insulator film contact layer, an upper metal electrode layer and a passivation layer;
the n-type GaN contact layer is extended on the n-type GaN substrate;
the lower metal electrode layer is arranged on the upper surface of the n-type GaN contact layer, is an annular electrode and is provided with an n-type bonding pad;
the n-type AlGaN matching layer is arranged on the n-type GaN contact layer and is positioned in an area within the annular lower metal electrode layer;
the AlGaN ultraviolet absorption layer is extended on the n-type AlGaN matching layer;
the two-dimensional boron nitride film barrier layer is arranged on the AlGaN ultraviolet absorption layer;
the n-type topological insulator visible light absorption layer is arranged on the two-dimensional boron nitride film barrier layer;
the n-type topological insulator thin film contact layer is arranged on the n-type topological insulator visible light absorption layer;
the upper metal electrode layer is arranged on the n-type topological insulator thin film contact layer, is an annular electrode and is provided with an n-type bonding pad;
the passivation layer is arranged on the side walls of the n-type AlGaN matching layer, the AlGaN ultraviolet absorption layer, the two-dimensional boron nitride film barrier layer, the n-type topological insulator visible light absorption layer and the n-type topological insulator film contact layer, and the area, which is not covered with the electrode, of the upper surfaces of the n-type GaN contact layer and the n-type topological insulator film contact layer.
2. The visible-ultraviolet dual-color detector of claim 1, wherein the n-type GaN substrate has a thickness of 0.3-0.5 mm;
the doping concentration of the n-type GaN contact layer is more than or equal to 1018cm3The thickness is 400nm +/-20 nm;
the n-type AlGaN matching layer has a doping concentration of 1017cm3～1018cm3Within the range, the thickness is 200nm plus or minus 20 nm;
the doping concentration of the AlGaN ultraviolet absorption layer is 1016cm3The thickness is 150nm plus or minus 10 nm;
the doping concentration of the two-dimensional boron nitride film barrier layer is 1016cm3The thickness is 30-50 nm;
the doping concentration of the n-type topological insulator visible light absorption layer is 1016cm3Within.
The n-type topological insulator film contactThe doping concentration of the layer is 1018cm3Above, 10nm to 30nm thick.
3. The visible-ultraviolet dual-color detector as claimed in claim 1, wherein the n-type GaN contact layer, the n-type AlGaN matching layer and the AlGaN ultraviolet absorption layer are sequentially epitaxially grown on the n-type GaN substrate by MBE technology.
4. The visible-ultraviolet dual-color detector of claim 1, wherein the diameters of the annular electrodes of the lower metal electrode layer and the upper metal electrode layer are sequentially reduced.
5. The visible-ultraviolet dual-color detector of claim 1, wherein the n-type topological insulator thin film contact layer is a bismuth selenide or bismuth selenide thin film layer having a thickness of 10nm to 60 nm.
6. The visible-ultraviolet dual-color detector as claimed in claim 1, wherein the two-dimensional boron nitride film barrier layer and the n-type topological insulator film contact layer are prepared on the n-type AlGaN absorption layer by a film transfer method.
7. The visible-ultraviolet dual color detector of claim 1, wherein the AlGaN ultraviolet absorption layer has a forbidden band width in a range of 3.4 to 6.2 eV.
8. The visible-ultraviolet dual color detector of claim 1, wherein the topological insulator thin film layer has a forbidden bandwidth in the range of 1.2-3.4 eV.
9. The visible-ultraviolet dual-color detector of claim 1, wherein the lower metal electrode layer and the upper metal electrode layer are: ti and Au electrodes, wherein the thickness of the lower layer Ti is 20-40nm, and the thickness of the upper layer Au is 60-120 nm.
10. The visible-ultraviolet dual-color detector of claim 1, wherein the passivation layer material is silicon oxide, silicon nitride, polyimide, or BCB.
CN202011337520.3A 2020-11-25 2020-11-25 Visible-ultraviolet double-color detector Active CN112490305B (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN202011337520.3A CN112490305B (en) 2020-11-25 2020-11-25 Visible-ultraviolet double-color detector

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
CN202011337520.3A CN112490305B (en) 2020-11-25 2020-11-25 Visible-ultraviolet double-color detector

Publications (2)

Publication Number Publication Date
CN112490305A true CN112490305A (en) 2021-03-12
CN112490305B CN112490305B (en) 2022-04-01

Family

ID=74934584

Family Applications (1)

Application Number Title Priority Date Filing Date
CN202011337520.3A Active CN112490305B (en) 2020-11-25 2020-11-25 Visible-ultraviolet double-color detector

Country Status (1)

Country Link
CN (1) CN112490305B (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114005896A (en) * 2021-10-29 2022-02-01 天津津航技术物理研究所 Ultraviolet-visible double-color detector
WO2023087376A1 (en) * 2021-11-18 2023-05-25 中国科学院长春光学精密机械与物理研究所 Photoelectric detector having light-splitting structure and preparation method therefor

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04313735A (en) * 1991-03-29 1992-11-05 Mitsubishi Electric Corp Optical multistable element
US6469358B1 (en) * 2000-09-21 2002-10-22 Lockheed Martin Corporation Three color quantum well focal plane arrays
CN101710600A (en) * 2009-07-06 2010-05-19 中国科学院长春光学精密机械与物理研究所 Method for realizing photoelectric detector with high spectral selectivity
CN106011783A (en) * 2016-07-07 2016-10-12 北京大学 High-mobility-ratio lamellar Bi2O2Se semiconductor film and preparation method thereof
CN108493274A (en) * 2018-03-29 2018-09-04 中国科学院金属研究所 A kind of controllable vertically bismuth selenide nanometer sheet film and preparation method thereof
CN211508181U (en) * 2020-04-15 2020-09-15 广东鸿芯科技有限公司 Semiconductor laser device with constant temperature control function
CN113257933A (en) * 2021-05-26 2021-08-13 哈尔滨工业大学 Bismuth selenide/gallium nitride ultraviolet-infrared broadband detector and preparation method thereof

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04313735A (en) * 1991-03-29 1992-11-05 Mitsubishi Electric Corp Optical multistable element
US6469358B1 (en) * 2000-09-21 2002-10-22 Lockheed Martin Corporation Three color quantum well focal plane arrays
CN101710600A (en) * 2009-07-06 2010-05-19 中国科学院长春光学精密机械与物理研究所 Method for realizing photoelectric detector with high spectral selectivity
CN106011783A (en) * 2016-07-07 2016-10-12 北京大学 High-mobility-ratio lamellar Bi2O2Se semiconductor film and preparation method thereof
CN108493274A (en) * 2018-03-29 2018-09-04 中国科学院金属研究所 A kind of controllable vertically bismuth selenide nanometer sheet film and preparation method thereof
CN211508181U (en) * 2020-04-15 2020-09-15 广东鸿芯科技有限公司 Semiconductor laser device with constant temperature control function
CN113257933A (en) * 2021-05-26 2021-08-13 哈尔滨工业大学 Bismuth selenide/gallium nitride ultraviolet-infrared broadband detector and preparation method thereof

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114005896A (en) * 2021-10-29 2022-02-01 天津津航技术物理研究所 Ultraviolet-visible double-color detector
WO2023087376A1 (en) * 2021-11-18 2023-05-25 中国科学院长春光学精密机械与物理研究所 Photoelectric detector having light-splitting structure and preparation method therefor

Also Published As

Publication number Publication date
CN112490305B (en) 2022-04-01

Similar Documents

Publication Publication Date Title
CN109285911B (en) Short wave/medium wave/long wave three-band infrared detector and preparation method thereof
CN112490305B (en) Visible-ultraviolet double-color detector
CN111900217B (en) Medium/long wave infrared dual-waveband superlattice infrared detector and preparation method thereof
CN108807588B (en) Single-chip n-i-p-i-n type wide spectrum photoelectric detector
US9755091B2 (en) Dual-band infrared detector and method of detecting multiple bands of infrared radiation
CN102386269B (en) GaN-based ultraviolet detector with p-i-p-i-n structure and preparation method thereof
CN108305911B (en) It absorbs, III group-III nitride semiconductor avalanche photodetector of dynode layer separated structure
CN107452820B (en) A kind of homogeneity interface two dimension δ doping type PIN ultraviolet detector
CN104779316B (en) Novel GaN-based ultraviolet detector adopting PIN structure
CN111739960B (en) Gain type heterojunction ultraviolet photoelectric detector
CN105097964B (en) A kind of active area Gauss doping type p π n ultraviolet detector
CN113471326B (en) III-group nitride heterojunction photoelectric detector
CN105655437A (en) Ultraviolet avalanche photo-detector
CN111710732A (en) Structure for inhibiting diffusion dark current in antimonide superlattice very-long-wave infrared detector
CN213242573U (en) Medium-short wave double-color infrared detector based on Sb compound
CN102201484A (en) AlGaN ultraviolet detector with secondary mesa wrapping electrode and manufacturing method thereof
CN101710600A (en) Method for realizing photoelectric detector with high spectral selectivity
CN117747692B (en) Short medium wave superlattice double-color detector with high quantum efficiency
CN110676272A (en) Semiconductor ultraviolet photoelectric detector
CN202134542U (en) AlGaN ultraviolet detector with secondary table top wrapped electrode
CN108305907B (en) A kind of novel homojunction PIN ultraviolet detector
US20240332443A1 (en) Chip for visible light communication and preparation method and application thereof
US10686091B2 (en) Semiconductor device
CN102074609B (en) Ultraviolet avalanche photodiode detector and manufacturing method thereof
CN114335232A (en) Bicolor heterojunction photoelectric transistor and preparation method thereof

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant