CN112299385B - Nano aluminum nitride powder synthesis production line - Google Patents
Nano aluminum nitride powder synthesis production line Download PDFInfo
- Publication number
- CN112299385B CN112299385B CN202011081582.2A CN202011081582A CN112299385B CN 112299385 B CN112299385 B CN 112299385B CN 202011081582 A CN202011081582 A CN 202011081582A CN 112299385 B CN112299385 B CN 112299385B
- Authority
- CN
- China
- Prior art keywords
- unit
- nitrogen
- aluminum
- gas
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of aluminum nitride synthesis, and discloses a nano aluminum nitride powder synthesis production line which comprises a nano aluminum nitride powder synthesis device, a material collection system, a nitrogen supply system, a refrigeration system and an argon supply system. The nano aluminum nitride powder synthesis device comprises: the device comprises a shell, a spraying unit, a gasification unit, a reaction unit and a cooling unit. The material collecting system is connected with an outlet of the cooling unit and is used for gas-powder separation, recovery and packaging of materials. The nitrogen supply system is used for supplying nitrogen for the spraying unit, the reaction unit and the cooling unit. The refrigerating system is used for the cold medium circulation supply of the spraying unit, the gasification unit and the cooling unit. The argon supply system is communicated with the spraying unit and the shell and is used for supplying argon. The aluminum nitride is synthesized by the production line of the invention, the raw materials react completely, the synthesized aluminum nitride powder has high purity, the particle size of the powder is uniform and nano-scale, the powder is not easy to agglomerate, the continuous production can be realized, the yield is high, the output is fast, the required supporting equipment is few, and the cost is low.
Description
Technical Field
The invention relates to the field of aluminum nitride synthesis, in particular to a nano aluminum nitride powder synthesis production line.
Background
In the 21 st century, people are praised as three scientific pillars for materials, information and energy, and the materials are the material basis of human production and life and are the signs of human progress and human civilization. With the emergence and development of new technologies such as space technology, infrared technology, sensing technology, energy technology and the like, materials are required to have superior performances such as high temperature resistance, corrosion resistance, high insulation and the like so as to be used in harsh environments. Aluminum nitride materials stand out from new materials due to their unique and excellent characteristics, and are increasingly highly valued by scientists in various countries. The aluminum nitride does not exist in the natural world, is artificially synthesized, belongs to an industrial special ceramic material, has excellent thermal, electrical and mechanical properties, is high-temperature resistant, good in heat conduction (second to aluminum), high in insulation, high in hardness, wear-resistant, low in expansion and corrosion-resistant, and is an ideal material for a large-scale integrated circuit radiating substrate, a smelting crucible, a casting mold, heat conduction and the like. The quality of the aluminum nitride powder prepared at present in China is a low-end product, the purity is within 95 percent, the particle size is more than 0.5 micrometer, the technology of high-purity and nano-grade powder is mastered in Japan, Germany and America, and China lags behind the industry for more than 15 years because of technical blockade, monopoly of products, forbidden sale of products and international market price of more than 100 ten thousand yuan/ton. At present, the domestic preparation method mainly comprises the following major categories:
(1) direct nitridation method: the direct nitriding method of aluminum powder is to continuously flow N2(or NH)3) Aluminum powder and N under atmosphere (or in a closed nitrogen atmosphere container)2(or NH)3) The method for preparing the AlN powder by directly carrying out chemical reaction at higher temperature has the following reaction equation:
2Al+N2→2AlN
the disadvantages of this method are: the melting point of aluminum is 660 ℃, the nitriding temperature is 1000-1600 ℃, and an aluminum nitride layer is generated on the surface of aluminum water (liquid) during nitriding, so that N is prevented2Further penetration into the aluminum water (liquid) results in the product being in a massive form and having a low purity due to the heat released during nitriding.
(2) A thermal reduction method: mixing Al2O3Flow N of the powder and excess C (activated carbon) powder at a certain temperature (1200 ℃ C. and 1800 ℃ C.)2Carrying out nitrogen reduction reaction under the atmosphere condition to prepare AlN powder, wherein the reaction equation is as follows:
Al2O3+3C+N2→AlN+3CO↑
the disadvantages of this method are: the synthesis time is long, the temperature is high, and the excessive C and CO after synthesis are separated and treated, so that the cost is low and high.
(3) Arc plasma torch gasification method: melting aluminum in a crucible in a closed container to form molten aluminum, burning the molten aluminum by flame of a plasma torch against the molten aluminum to make the aluminum sublimate and flow into a reaction chamber, and introducing nitrogen to cool and react.
The disadvantages of this method are: the heat conversion rate of the plasma torch is lower than 20 percent, the energy consumption is high, and the equipment investment is large; the electrodes for generating the electric arc are red copper and tungsten alloy, the electrodes are quickly ablated and gasified at the temperature of over 5 kilo DEG C, and the gasified tungsten copper and the aluminum gas are mixed together to influence the purity; the tungsten copper electrode is replaced for about 100 hours, so that the material cost is high; the torch electrode is cooled by water, and once the copper electrode ablates and perforates at ultrahigh temperature, the cooling water is sprayed into the crucible to cause instant water vapor expansion and explosion; because the production cost is too high, the industrial production is not formed in China at present.
(4) An arc atomization method: two aluminum wires which can move uniformly and in the same direction are used as electrodes, electric arcs (high temperature) are generated when two ends of the aluminum wires are close to each other, the end parts of the aluminum wires are atomized instantly, nitrogen is sprayed to the middle of the electric arcs to spray aluminum mist, and the aluminum mist and the nitrogen react and synthesize in a reaction kettle.
The disadvantages of this method are: because the sizes and the temperatures of the aluminum fog particles are different, the surfaces of some particles are nitrided, the middle is not nitrided, and the purity is not high.
In summary, the technical difficulties of several methods in the prior art mainly lie in:
(1) the raw materials can not be completely reacted, or the impurities are contained, and the purity is low.
(2) The direct nitriding method and the thermal reduction method are adopted in China, the products are agglomerated and are grinded, the problems of high cost, uneven thickness, high grinding loss and difficulty in reaching the fineness of the grinded particles are solved, and the deep processing quality is greatly influenced.
(3) At present, the domestic production process can not reach high-purity nano powder.
(4) Intermittent production: feeding → preheating → heating → reaction → heat preservation → cooling → discharging → crushing → separation → grinding → separation → drying → classification → packaging, one furnace for one furnace, the equipment utilization rate is low.
(5) The production management is difficult: the method has the advantages of multiple devices, large factory building, multiple links, multiple processes, large investment and multiple personnel.
(6) The supporting facilities are many: auxiliary facilities for removing dust, preventing static electricity, isolating vibration, clearing noise and the like.
Therefore, it is necessary to develop a new technique for producing aluminum nitride powder to solve the above technical problems.
Disclosure of Invention
In order to solve the technical problems, the invention provides a nano aluminum nitride powder synthesis production line, the aluminum nitride powder synthesis is carried out through the production line, the raw material reaction is complete, the purity of the synthesized aluminum nitride powder is high (up to more than 99.99 percent), the particle size of the powder is uniform and nano-scale, the powder is not easy to agglomerate, the continuous production can be realized, the yield is high, the output is fast, the required matched equipment is few, and the cost is low.
The specific technical scheme of the invention is as follows:
a nanometer aluminium nitride powder synthesis production line includes: the device comprises a nano aluminum nitride powder synthesis device, a material collecting system, a nitrogen supply system, a refrigerating system and an argon supply system.
The nano aluminum nitride powder synthesis device comprises: the device comprises a shell, a spraying unit arranged in the shell, a gasification unit arranged in the shell and connected below the spraying unit, a reaction unit arranged in the shell and connected below the gasification unit, and a cooling unit connected below the gasification unit.
The invention relates to synthesis for preparing aluminum nitride based on aluminum gasification reaction, which has the following reaction equation: 2Al + N2→ 2AlN + heat. The synthesis process flow can be summarized as follows:
in the spraying unit, solid aluminum particles (preferably deoxidized, high-purity and same-size aluminum round particles) are heated and melted (above 1500 ℃), and nitrogen gas is used for conveying aluminum liquid to the gasification unit in the form of aluminum mist.
In the gasification unit, the aluminum mist and the nitrogen gas are heated (about 2500 ℃) in the gasification chamber to form aluminum gas (single atoms), and the aluminum gas and the nitrogen gas are continuously led to the reaction unit.
In the reaction unit, nitrogen is introduced for cooling to 1300-1500 ℃, and aluminum gas (monatomic) and nitrogen react to synthesize aluminum nitride.
The aluminum nitride obtained by the synthesis was further cooled in a cooling unit and discharged.
The device of the invention is used for synthesizing the aluminum nitride powder, the raw materials react completely, the purity of the synthesized aluminum nitride powder is high (reaching more than 99.99 percent), the particle diameter of the powder is uniform and nano-scale, the powder is not easy to agglomerate, the continuous production can be realized, the yield is high, the output is fast, the required supporting equipment is few, and the cost is low.
And the material collecting system is connected with an outlet of the cooling unit and is used for gas-powder separation, recovery and packaging of materials.
The nitrogen supply system is used for supplying nitrogen for the spraying unit, the reaction unit and the cooling unit.
The refrigerating system is used for cold medium circulation supply of the spraying unit, the gasification unit and the cooling unit.
The argon supply system is communicated with the spraying unit (the top of the aluminum liquid bin) and the shell and is used for supplying argon.
Preferably, the material collecting system comprises a gas-powder separating device, a packaging device and a recovered gas storage tank; the gas-powder separation device is connected with an outlet of the cooling unit, and the packaging device and the recovered gas storage tank are respectively connected with a powder outlet and a gas outlet of the gas-powder separation device; the recovered gas storage tank also provides power gas for the packaging device and the spraying unit (aluminum conveying mechanism) respectively.
Preferably, the nitrogen making system comprises a nitrogen making device, a nitrogen tank, a nitrogen refrigerator and a liquid ammonia tank; the nitrogen making device is connected with a nitrogen tank, the nitrogen tank is respectively connected with the spraying unit, the reaction unit and the cooling unit, and a nitrogen refrigerator is arranged on a pipeline for connecting the nitrogen tank with the reaction unit and the cooling unit; the liquid ammonia tank is connected with the reaction unit.
The invention adopts nitrogen and liquid ammonia to transport nitrogen source for the reaction unit, and has the advantages that: adding a trace amount of liquid ammonia outside the device into nitrogen, inputting the added liquid ammonia into a reaction unit, and decomposing the liquid ammonia into hydrogen atoms and nitrogen atoms after the temperature of the reaction unit is raised; secondly, inputting nitrogen into the reaction unit, mixing the nitrogen with the gas descending from the gasification unit, cooling to 1300-1500 ℃, and reacting the nitrogen with the aluminum gas to synthesize aluminum nitride, wherein the nitrogen is used as a reaction raw material; thirdly, the nitrogen gas and the aluminum gas react in the reaction unit to synthesize the aluminum nitride powder, the aluminum nitride powder becomes solid by gas, the temperature is reduced by 800 degrees and is increased by 1000 degrees, the pressure is rapidly reduced, and the input nitrogen keeps the air pressure.
Argon of an argon supply system is introduced into an aluminum liquid bin of a spraying unit, and is synchronously pressurized with a nitrogen conveying pipe in the aluminum liquid bin, so that the aluminum liquid is sprayed out through a nozzle; argon is introduced into the shell to play a pressure maintaining role.
The distribution trend of the refrigerant medium in the refrigerating system of the invention is as follows: one path is introduced into a top cover of a spraying unit; introducing two paths of connecting pipes into pressure measuring ports of the gasification unit and the reaction unit for cooling; introducing one path into an induction coil for cooling; and the two paths are introduced into the upper section part and the lower section part of the cooling unit.
The nitrogen in the nitrogen tank is distributed in five ways: firstly, introducing an aluminum conveying mechanism as protective gas; introducing a nitrogen spray pipe of the spraying unit, and carrying out air-borne spraying; thirdly, introducing the reaction unit to perform cooling, reaction and pressurization effects; fourthly, introducing the mixture into a cooling unit to play roles of cooling and pressurizing; introducing a nitrogen refrigerator, and leading the refrigerated nitrogen to the reaction unit and the cooling unit in two paths. The liquid ammonia in the invention is introduced into the reaction unit.
In the invention, after gas-powder separation is carried out on gas-powder at the outlet of the cooling unit, the gas is recovered by a booster pump, and the gas-powder is 25-30 ℃.
The recycling gas in the invention has the following use and distribution trend: firstly, packaging equipment power gas; secondly, air is used for power of the aluminum conveying mechanism; thirdly, the blanking valve of the aluminum feeding mechanism uses air for power.
Preferably, the spraying unit includes: send aluminium mechanism, heat preservation casing, heating mantle, aluminium liquid storehouse, nitrogen gas spray tube and insulating cover seat. The heating cover is arranged in the heat-insulating shell, and the inner wall of the heating cover is provided with heating wires; the middle lower section of the aluminum liquid bin is arranged in the heating cover, a gap is formed between the middle lower section of the aluminum liquid bin and the inner wall of the heating cover, and the bottom of the aluminum liquid bin extends out of the bottom of the heating cover and is provided with a downward atomizing nozzle; the nitrogen spray pipe is introduced into the center of the aluminum liquid bin, and the air outlet of the nitrogen spray pipe faces the atomizing nozzle; the aluminum conveying mechanism is arranged at the top of the aluminum liquid bin; the insulating cover seat is arranged below the heat preservation shell and the heating cover, and a gap is formed between the inner ring of the insulating cover seat and the outer wall of the bottom of the aluminum liquid bin.
The working principle of the spraying unit of the invention is as follows: introducing argon into the aluminum liquid bin to pressurize to 0.5-0.55MPa (5-5.5 kg), heating the heating cover in a subsection manner, controlling the temperature in a subsection manner, heating the solid aluminum particles to 800 ℃ at the upper part of the aluminum liquid bin, and heating the aluminum liquid to 1700 ℃ at the middle and lower parts with different electric powers; nitrogen is introduced into the nitrogen spray pipe to pressurize to 0.55-0.6MPa (5.5-6 kg) to be used as spray conveying gas, and aluminum mist is sprayed out through an atomizing nozzle to enter a gasification unit.
Preferably, the spray unit is fixed in the housing by a bracket. Specifically, the bracket may be formed by connecting four metal strips perpendicular to each other and a middle ring (made of ceramic material), and the metal strips of the bracket are placed on a stopper on the inner wall of the housing to suspend the bracket. The heating cover is hung on the bracket, and the bottom of the heating cover is embedded into the insulating cover seat. The aluminum liquid bin is inserted into the heating cover from a flange opening at the top of the shell, a gap is formed between the aluminum liquid bin and a heating wire of the heating cover, and a flange at the upper part of the spraying unit is fixed on a flange at the top of the shell.
Preferably, the clearance between the inner ring of the insulation cover seat and the outer wall of the bottom of the aluminum liquid bin is 1-2 mm.
The bottom of the spraying unit is separated from the inner ring of an insulating cover seat embedded in the gasification unit, and the insulating cover seat is arranged above the gasification unit. It is particularly noted that a 1-2mm gap is reserved between the inner ring of the annular insulating cover seat and the outer wall of the bottom of the aluminum liquid bin, and the gap can ensure that the aluminum liquid bin has enough expansion reserved space after heating expansion. And the insulating cover seat has the following functions: the gasification unit adopts medium-frequency induction heating, a heating body inner layer is arranged in the heating body inner layer and can generate induced electricity, the aluminum liquid bin is made of tungsten alloy, and the insulating cover seat can isolate the heating body inner layer and the aluminum liquid bin from contacting and conducting after thermal expansion.
Preferably, the housing is provided with an argon inlet.
The invention has the following effects on introducing argon into the shell: first, since graphite or graphite felt is preferable as the heat generating filler, the heat insulating layer, and the heat insulating plate in the apparatus of the present invention, carbon particles are easily emitted at high temperatures. Therefore, the invention can purposefully lead argon into the shell to play a role of protection, so that carbon particles are not diffused and are kept durable; prevent carbon particles from permeating into the gasification unit and the reaction unit to reduce the purity of the aluminum nitride. Secondly, because a gap exists between the insulating cover seat and the aluminum liquid bin, air pressure generated by expansion after aluminum in the gasification unit is gasified can overflow to the gap, and the pressure of the introduced argon is controlled to be more than or equal to the pressure of the gasification chamber, so that the indoor and outdoor air pressure can be kept stable.
Preferably, the top of the aluminum liquid bin is provided with an argon inlet. The invention has the following effects of introducing argon to the top of the aluminum liquid bin: firstly, as the caliber of the spray nozzle is less than 0.5mm, the fluidity of the aluminum liquid is poor, the resistance is large, and when the nitrogen nozzle jets air towards the spray nozzle, nitrogen gas flows out of the aluminum liquid to the upper space of the aluminum liquid bin, firstly, the jetted aluminum liquid cannot be atomized, the upper temperature is overhigh, and secondly, the upper aluminum liquid level and the nitrogen gas are nitrified to synthesize an aluminum nitride film, so that the aluminum liquefaction and atomization are stopped. Introducing argon gas into the upper part of the aluminum melt, pressurizing the aluminum melt and the nitrogen gas simultaneously, wherein the nitrogen gas drives the aluminum melt to be sprayed out from the nozzle to form a mist shape, and the argon gas is inert gas and does not react with the aluminum melt.
Preferably, two valves which are connected in series and are switched in a staggered mode are arranged on a pipeline between the aluminum conveying mechanism and the aluminum liquid bin.
In the prior art, only one valve is usually arranged in a pipeline between an aluminum feeding mechanism and a heating and melting mechanism, or even a plurality of valves are arranged, the valves are only used for standby, and targeted linkage matching is not carried out. Two valves which are connected in series and are switched in a staggered manner are arranged on a pipeline between the aluminum conveying mechanism and the aluminum liquid bin. The two valves are mutually partitioned to contain aluminum round particles, and when the lower valve is opened, the aluminum round particles automatically fall into the spraying unit; when the upper valve is opened, the aluminum round particles fall into the pipe from the storage bin, and the valve can be opened and closed once every 2 to 3 seconds, for example, and feeding is carried out once. Pressure pulse fluctuation in the spraying unit can be effectively reduced through the small-amount frequent special feeding mode, and spraying is uniform.
Preferably, the aluminum conveying mechanism is provided with a nitrogen inlet.
The production line is carried out in a fully closed device, and the inventor finds in practice that the solid aluminum feeding device in the prior art is easy to generate static electricity and aluminum oxidation due to the fact that air brings people during feeding, and materials rub with each other. Therefore, nitrogen is introduced into the bin and the conveying pipeline of the aluminum conveying mechanism to discharge air, and the aluminum conveying mechanism works under the protection of the nitrogen, so that static electricity generated by friction and aluminum oxidation can be avoided.
Preferably, the material sprayed by the atomizing nozzle is conical, the inner angle is 90-120 degrees, the side length is 30-40mm, and the particle size of the mist is 3-5 microns. The sprayed aluminum fog has a weight of 1.5-2 g/s, and the nitrogen is sprayed and conveyed in a volume of 0.8-1 cubic decimeter/s.
The reason why the present invention specifically limits the conditions for the aluminum mist ejection to the above conditions is that: when the spraying angle is less than 90 degrees, the volume of a spray cone is reduced, the distribution density of spray particles is increased, the particles are increased, and the particles are not easy to gasify; secondly, when the spraying angle is smaller than 90 degrees, the volume of the fog cone body is reduced, the height of the fog cone body is increased, the aluminum fog approaches a waist-reducing structure, the temperature of the waist-reducing part is relatively low, and along with the thermal expansion of the nitrogen of the aluminum fog and the pressure difference between the gasification plug (chamber) and the reaction plug (chamber), the aluminum fog which is not atomized and gasified directly flows into the reaction plug (chamber), so that the reaction is incomplete.
Preferably, the calibers of the upper sections of the heating cover and the aluminum liquid bin are larger than the calibers of the lower sections.
Preferably, an upper refrigerant jacket is arranged on the top wall of the aluminum liquid bin.
The aluminum liquid bin, the atomizing nozzle and the nitrogen gas spray pipe are made of tungsten alloy materials; the heating cover and the insulating cover seat are made of ceramic materials.
Preferably, the gasification unit comprises: the gasification chamber and the induction coil are sequentially formed by an upper heat-preservation insulating outer layer, a heat-preservation middle layer and a heating body inner layer. An opening for arranging an insulating cover seat is formed in the center of the top of the gasification chamber; the center of the bottom of the gasification chamber is provided with an opening communicated with the reaction unit; the induction coil is wrapped on the outer side of the upper heat-insulation outer layer; the bottom of the inner layer of the heating body is in a cone shape with the caliber decreasing progressively, and a gap between the cone shape and the heat insulation middle layer is filled with a heating filling body and a heat insulation plate; the heat insulation plate is positioned at the bottom of the gasification chamber.
The working principle of the gasification unit is as follows: the inner layer of the heating body is inductively heated to about 2500 ℃ by adopting a medium-frequency induction coil, so that the space temperature in the gasification chamber exceeds 2327 ℃ (the aluminum gasification temperature is 2327 ℃), the aluminum gas and the nitrogen gas in the gasification chamber expand after being heated, the aluminum mist is continuously sprayed, certain air pressure is generated in the gasification chamber, and the air flow is downwards introduced into the reaction unit.
An hourglass-shaped waisted structure is designed between the bottom of the gasification unit and the reaction unit. The structure has the following functions: firstly, the heat preservation effect is achieved, the flow velocity of the gas up and down is reduced after the waist is contracted, so that the retention time of the aluminum fog in the gasification chamber is prolonged, and the aluminum fog is completely gasified; the temperature of the gasification chamber is required to be 2500 ℃, the temperature of the reaction chamber is required to be 1300-.
The induction heating effect is poor because the inner layer of the heating body at the waist shrinking structure is far away from the induction coil. Therefore, the heating filler is filled in the structure and transfers heat to the waist-contracting part, and the heating filler is heated firstly during induction heating and then transfers heat to the inner layer of the heating body, so that the temperature of the bottom of the gasification chamber is ensured.
The temperature difference between the gasification chamber and the reaction chamber reaches 900-.
Preferably, the reaction unit comprises: a reaction chamber consisting of a lower heat-insulating outer layer and a heat-resistant inner layer, and a vortex nozzle. The bottom of heat-resisting inlayer is the degressive toper of bore, and toper bottom central authorities are connected with the discharging pipe, the vortex spray tube passes through the discharging pipe and stretches into in the reaction chamber by the reaction chamber outward, and the end of giving vent to anger of vortex spray tube is equipped with the vortex nozzle, the vortex nozzle is located under the gasification chamber bottom opening and jet-propelled direction upwards.
The working principle of the reaction unit of the invention is as follows: when the aluminum gas and the nitrogen gas flow into the reaction chamber, the temperature is more than 2327 ℃, the aluminum gas and the nitrogen gas (part of dissociated single atoms) are very active, the optimal reaction temperature is 1300-1500 ℃, in order to realize rapid cooling, the invention adopts a nitrogen gas introduction mode to cool to the reaction temperature, and the reaction raw materials react rapidly to synthesize the aluminum nitride.
However, the inventors discovered a new technical problem during the test: the synthesis reaction is a process of changing gas into solid, the volume of the gas is rapidly shrunk, the pressure is rapidly reduced, so that the pressure difference is generated between the gasification chamber and the reaction chamber, and the upper and lower flow rates are too high. Therefore, the invention blows the external nitrogen to the downward air flow in a spiral way through the vortex nozzle, and the blown air flow is spirally diffused to the periphery, so that the gas distribution is uniform, the temperature is uniform, the reaction is uniform, and the reaction is complete. The nitrogen is introduced into the powder to be excessive, and the excessive nitrogen drives the powder to flow. After external nitrogen is input in this way, the pressure in the gasification chamber and the reaction chamber can be kept balanced, and the material flow rate is reduced.
Preferably, the air flow sprayed by the vortex nozzle is in a fan shape with an internal angle spiral of 50-70 degrees.
The reason why the present invention specifically limits the air flow to the above-described angle is that: when the internal angle is less than 50 degrees, the fan-shaped arc is short, the jet force of the air flow is large, the descending aluminum gas is easy to jet to the top of the reaction chamber, the temperature at the top is too high, and the rebounding air flow quickly flows into the cooling unit, so that the temperature is not uniformly reduced, and the reaction is incomplete; and when the internal angle is larger than 70 degrees, the arc length of the fan is long, the gas density is low, the jet force is low, the descending aluminum gas is not easy to blow away, the aluminum gas wraps around the vortex nozzle, the temperature is not uniformly reduced, and the reaction is not complete.
Preferably, the upper heat-insulating outer layer and the lower heat-insulating outer layer are integrally formed; the heating element inner layer and the heat-resistant inner layer are formed separately and are connected in an inserting mode.
Preferably, the upper and lower heat-insulating outer layers are made of heat-insulating cotton; the heat insulation middle layer and the heat insulation plate are made of hard graphite felt; the heating filler is made of graphite. The inner layer of the heating body and the heat-resistant inner layer are made of tungsten alloy materials.
Preferably, the reaction unit is arranged at the bottom of the shell through a bottom support seat frame; the bottom bracket is made of metal, preferably, the spraying unit, the gasification unit and the reaction unit are arranged in the same stainless steel shell and are arranged in an organized manner in a stacking manner, a heat-resistant inner layer and a heat-resistant inner layer are arranged on the ceramic bottom bracket during installation, a heating plate is arranged on the heat-resistant inner layer, a heating filler is arranged on the heating plate, a heating body inner layer of the gasification unit is arranged on the heating filler, a heat-insulating plate is arranged on the heating body inner layer, an insulating cover seat is simultaneously arranged on the heat-insulating plate, heat-insulating and heat-insulating materials are arranged on the gasification unit and the reaction unit, induction coils are arranged around the outer wall of the gasification unit, a bracket is arranged on the upper part of the shell, a heating cover is inserted into the ring from the inner ring of the bracket ring and is arranged on the ring, the upper cover of the shell is covered, the aluminum liquid bin is inserted into the inner ring of, the parts need to be replaced, repaired and cleaned in the using process, so that great convenience is brought.
Preferably, the cooling unit includes: a cooling chamber shell, a spiral nozzle and a lower refrigerant jacket; an opening is formed in the center of the top of the cooling chamber shell, the spiral nozzle is arranged at the opening and is connected with a discharge pipe of the reaction unit through a connecting flange, and the spiral nozzle is downward; a nitrogen inlet is arranged on the cooling chamber shell, the bottom of the cooling chamber shell is in a conical shape with the caliber decreasing progressively, and the center of the conical bottom is provided with a gas powder outlet; the lower refrigerant jacket is arranged on the outer side of the cooling chamber shell.
The cooling unit of the invention adopts two modes of cooling by a refrigerant jacket (preferably water cooling) and nitrogen cooling, and the combined cooling has the advantages that: firstly, the temperature of gas powder flowing into a cooling unit from a reaction chamber is reduced from about 1450 ℃ to about 50 ℃, the temperature difference reaches 1400 ℃, rapid cooling cannot be carried out in a short time, the water cooling cost is low compared with nitrogen cooling, but the time is long, the cooling is not uniform, the cooling rate is slow, and particles are easy to agglomerate and bond; and the cooling time can be reduced by matching with nitrogen for cooling, and the agglomerated particles can be effectively dispersed. Secondly, after the gas powder is rapidly cooled in the cooling unit, the pressure is rapidly reduced, so that the pressure difference between the reaction chamber and the cooling chamber is increased, the gas powder flows too fast, nitrogen is introduced into the cooling chamber for cooling, the pressure of the cooling chamber can be increased, the flow speed of the gas powder flowing to the cooling chamber in the reaction chamber is reduced, and more time is won for cooling the gas powder while the gas powder is reduced in speed.
Preferably, the cooling unit adopts upper and lower two-section split flange connection, and has the advantages that: when the lower segment is detached, the spiral spray pipe and the spiral nozzle are installed and replaced from the opening, and the repair and the cleaning are very convenient.
The cooling unit of the invention is provided with a spiral nozzle which is opened towards the bottom of the reaction chamber and has the functions of: firstly, the gas powder is blocked by the spiral strip in the spiral nozzle, so that the direct spraying sinking speed of the gas powder is reduced, and the impact of the powder on the inner wall is effectively reduced. Secondly, when the synthetic powder in the reaction chamber passes through the discharge port, the particles are extruded, the density is increased, agglomeration is easy to generate, and the synthetic powder can be scattered after being impacted by the spiral strip of the spiral nozzle. And thirdly, the spiral gas powder sprayed out by the spiral nozzle is uniformly distributed in the cooling chamber, and the cooling is rapid and uniform.
The spiral nozzle of the cooling unit is tightly connected with the discharge pipe at the bottom of the reaction chamber through the connecting flange, and can play a role in controlling gas powder flow (different inner diameters of the connecting pipes are selected).
Preferably, the gas powder is sprayed from the spiral strip gap of the spiral nozzle to form a fan-shaped spiral rotating airflow with an inner angle of 90-120 degrees.
The reason why the present invention specifically limits the spiral rotating airflow to the above-described angle is: firstly, particles are easy to agglomerate when passing through a nozzle pipeline, and when the internal angle is more than 120 degrees, the jet force of gas powder on a nozzle spiral strip is reduced, and the agglomerated particles are not easy to break up; when the internal angle is less than 90 degrees, the jet force is large, the flow velocity is too fast, the temperature reduction is not uniform, and the particles can be agglomerated.
Preferably, the discharge pipe and the connecting flange are made of tungsten alloy materials; the spiral nozzle is made of ceramic material.
Preferably, the shell, the spraying unit, the gasification unit, the reaction unit and the cooling unit are provided with temperature measuring ports and pressure measuring ports at different positions.
In conclusion, the following points need to be made in the implementation process of the device of the invention: firstly, the pressure and the temperature of the aluminum water in the spraying unit, the air pressure and the air flow in the nitrogen spray pipe are controlled, and the particle size of the aluminum mist is ensured to be between 3 and 5 micrometers. The temperature of the gasification chamber is more than 2327 ℃, and the temperature of the reaction chamber is 1300-1500 ℃. Thirdly, in order to promote the reaction, the flow velocity of gas and gas powder is stable, and partial pressure is adopted to have pressure difference. Fourthly, for an ideal reaction, the temperature needs to be reduced to 1300 ℃ and 1500 ℃; the reaction synthesis is an exothermic reaction, and agglomerated large particles are easily generated when the materials fall; in addition, the aluminum gas reacts with the nitrogen to synthesize the aluminum nitride powder, the aluminum nitride powder reacts after being cooled, the aluminum nitride powder is changed into solid from gas, and the pressure in the reaction chamber is reduced. Therefore, the way and the process of introducing nitrogen into the reaction chamber are required to be controlled well to realize cooling, air supplement, temperature equalization, pressurization and prevention of particle agglomeration.
The invention introduces a vortex spray pipe with a vortex nozzle at the outlet into a discharge pipe of a reaction chamber, the nozzle is arranged in the middle and upwards blows with the descending gas of a gasification chamber, the airflow sprayed by the vortex nozzle forms a fan-shaped spiral and is uniformly mixed with the descending gas, the temperature is reduced to 1300 ℃ and 1500 ℃, reaction is generated, after the temperature is reduced, the air pressure is reduced, the aluminum gas and the nitrogen react to synthesize aluminum nitride particles, the specific gravity of the excessive nitrogen and the particles is increased, the nitrogen and the particles sink slowly, and the particles fall into a cooling unit while reacting. The reaction chamber is funnel-shaped, the temperature of the gas powder entering the cooling unit when the gas powder passes through the reducing pipeline is 1300 ℃ and 1500 ℃, and the density of the gas powder is increased to generate collision agglomeration. Therefore, the discharge pipe at the lower end of the reaction chamber extends to the cooling unit, gas powder is scattered after being impacted by the spiral strips of the spiral nozzle and is sprayed out through gaps among the spiral strips to form fan-shaped rotating airflow, and the fan-shaped rotating airflow is cooled through rapid cooling of water and cold nitrogen without generating agglomerated large particles. The subsequent crushing and grinding are not needed, the direct formation of high-purity, high-fineness and nano-grade powder is ensured, the powder is easy to deeply process, and the sintering activity is good.
Compared with the prior art, the invention has the beneficial effects that:
(1) the production line is used for synthesizing aluminum nitride through the cooperative matching and the optimized design among all the units in all the systems and the synthesizing device, not only the raw materials are completely reacted, but also the synthesized aluminum nitride has high purity (up to more than 99.99 percent), and the powder has uniform particle size of nanometer level and is not easy to agglomerate.
(2) The nano aluminum nitride powder synthesis device continuously feeds materials from the aluminum conveying mechanism of the spraying unit and continuously discharges materials from the bottom of the cooling unit to form continuous flow production, continuous production can be realized, and the yield is high and fast.
(3) The production line of the invention needs less supporting equipment and has low cost.
Drawings
FIG. 1 is a schematic view of a connection of the production line of the present invention;
FIG. 2 is a cross-sectional view of the internal structure of the apparatus for synthesizing nano-sized aluminum nitride powder according to the present invention;
FIG. 3 is a top view of a bracket for hanging a spraying unit in the nano aluminum nitride powder synthesizing apparatus according to the present invention;
FIG. 4 is a schematic structural diagram of an aluminum liquid bin and a nitrogen gas nozzle in a spraying unit of the nano aluminum nitride powder synthesizing device;
FIG. 5 is a schematic structural diagram of a heating cover in a spraying unit of the nano aluminum nitride powder synthesizing apparatus according to the present invention;
FIG. 6 is a schematic structural diagram of a gap between an aluminum liquid bin and an insulating cover seat in a spraying unit of the nano aluminum nitride powder synthesizing device according to the present invention;
FIG. 7 is a schematic structural diagram of a gasification unit of the apparatus for synthesizing nano aluminum nitride powder according to the present invention;
FIG. 8 is a schematic structural diagram of a reaction unit of the nano aluminum nitride powder synthesizing apparatus according to the present invention;
FIG. 9 is a schematic structural diagram of a cooling unit of the nano aluminum nitride powder synthesizing apparatus according to the present invention;
FIG. 10 is a schematic diagram of the disassembly of a reaction unit discharge pipe, a connecting flange and a cooling unit spiral nozzle in the nano aluminum nitride powder synthesizing apparatus according to the present invention.
The reference signs are:
the device comprises a nano aluminum nitride powder synthesis device 1, a refrigeration system 2, an argon supply system 3, a gas-powder separation device 4, a packaging device 5, a recovered gas storage tank 6, a nitrogen making device 7, a nitrogen tank 8, a nitrogen refrigerator 9 and a liquid ammonia tank 10;
the device comprises a shell 100, an argon inlet 101, a bracket 102, a bottom base 103, a temperature measuring port 104 and a pressure measuring port 105;
the aluminum feeding mechanism 201, the heat preservation shell 202, the heating cover 203, the aluminum liquid bin 204, the nitrogen gas spray pipe 205, the insulating cover seat 206, the heating wire 207, the argon gas inlet 208, the atomizing nozzle 209, the valve 210, the nitrogen gas inlet 211 and the upper refrigerant jacket 212;
an upper heat-preservation insulating outer layer 301, a heat-preservation middle layer 302, a heating body inner layer 303, an induction coil 304, a heating filler 305 and a heat-insulation plate 306;
a lower heat-insulating outer layer 401, a heat-resistant inner layer 402, a vortex nozzle 403, a discharge pipe 404 and a vortex nozzle 405;
a cooling chamber shell 501, a spiral nozzle 502, a lower refrigerant jacket 503, a connecting flange 504, a nitrogen inlet 505 and a gas powder outlet 506.
Detailed Description
The present invention will be further described with reference to the following examples.
Example 1
As shown in fig. 1, a nano aluminum nitride powder synthesis production line includes: the device comprises a nano aluminum nitride powder synthesis device 1, a material collection system, a nitrogen supply system, a refrigeration system 2 and an argon supply system 3.
Specifically, the method comprises the following steps:
as shown in fig. 2, the nano aluminum nitride powder synthesis apparatus includes: the gasification device comprises a shell 100, a spraying unit arranged in the shell, a gasification unit arranged in the shell and connected below the spraying unit, a reaction unit arranged in the shell and connected below the gasification unit, and a cooling unit connected below the gasification unit.
As shown in fig. 1, the material collection system is connected with the outlet of the cooling unit for gas-powder separation, recovery and packaging of the material. The material collecting system comprises a gas-powder separating device 4, a packaging device 5 and a recovered gas storage tank 6. The gas-powder separation device is connected with an outlet of the cooling unit, and the packaging device and the recovered gas storage tank are respectively connected with a powder outlet and a gas outlet of the gas-powder separation device (a booster pump is arranged on a pipeline between the recovered gas storage tank and the gas-powder separation device); the recovered gas tank is also connected to the packaging device and the atomizing unit (aluminum feeding mechanism) respectively to supply nitrogen gas for power. As shown in fig. 1, the nitrogen supply system includes a nitrogen generator 7, a nitrogen gas tank 8, a nitrogen gas refrigerator 9, and a liquid ammonia tank 10. The nitrogen making device is connected with a nitrogen tank, the nitrogen tank is respectively connected with the spraying unit, the reaction unit and the cooling unit, and a nitrogen refrigerator is arranged on a pipeline connecting the nitrogen tank with the reaction unit and the cooling unit; the liquid ammonia tank is connected with the reaction unit.
As shown in figure 1, the refrigerating system is used for the circulation supply of cold medium of the spraying unit, the gasification unit and the cooling unit, and a conveying pump is arranged in a pipeline.
As shown in fig. 1, the argon supply system is in communication with the spray unit (top of the aluminum liquid bin), the housing for argon supply.
More specifically, in the nano aluminum nitride powder synthesis device:
as shown in fig. 2, an argon gas inlet 101 is formed at an upper portion of a sidewall of the housing.
As shown in fig. 2 and 4 to 5, the spray unit includes: the aluminum conveying mechanism 201, the heat preservation shell 202, the heating cover 203, the aluminum liquid bin 204, the nitrogen gas spray pipe 205 and the insulation cover seat 206. The aluminum conveying mechanism is arranged at the top of the aluminum liquid bin, and two valves 210 which are connected in series and are switched in a staggered mode are arranged on a pipeline between the aluminum conveying mechanism and the aluminum liquid bin. The aluminum feeding mechanism is provided with a nitrogen inlet 211. The heating cover is arranged in the heat-insulating shell, and the inner wall of the heating cover is provided with an electric heating wire 207; the middle-lower section of the aluminum liquid bin is arranged in the heating cover, a gap is formed between the middle-lower section of the aluminum liquid bin and the inner wall of the heating cover, and the calibers of the heating cover and the upper section of the aluminum liquid bin are larger than the calibers of the lower section. The top of the aluminum liquid bin is provided with an argon inlet 208, the top wall of the aluminum liquid bin is provided with an upper refrigerant jacket 212, and the bottom of the aluminum liquid bin extends out of the bottom of the heating cover and is provided with a downward atomizing nozzle 209; the nitrogen spray pipe is introduced into the center of the aluminum liquid bin, and the air outlet of the nitrogen spray pipe faces the atomizing nozzle; the insulating cover seat is arranged below the heat preservation shell and the heating cover, and as shown in figure 5, a gap (preferably 1-2mm) is arranged between the inner ring of the insulating cover seat and the outer wall of the bottom of the aluminum liquid bin. Wherein, the material sprayed by the atomizing nozzle is conical, the inner angle is 90-120 degrees, the side length is 30-40mm, and the particle size of the mist is 3-5 microns.
The spray unit is fixed in the housing by a bracket 102 made of metal. As shown in fig. 3, the bracket is formed by connecting four metal strips which are mutually vertical and a middle ring made of ceramic materials, the metal strips of the bracket are placed on a stop block on the inner wall of the shell to suspend the bracket, the upper part of the heating cover is hung on the ring, the ring is padded with heat insulation materials, and the bottom of the heating cover is embedded into an insulating cover seat which is placed on the gasification unit and plays a role in positioning. In the spraying unit, an aluminum liquid bin, an atomizing nozzle, a nitrogen spray pipe and a heating wire are made of tungsten alloy materials; the heating cover and the insulating cover seat are made of ceramic materials.
As shown in fig. 2 and 7, the gasification unit includes: a gasification chamber and an induction coil 304 which are sequentially composed of an upper heat-preservation insulating outer layer 301, a heat-insulation middle layer 302 and a heating body inner layer 303. The center of the top of the gasification chamber is provided with an opening for arranging an insulating cover seat; the center of the bottom of the gasification chamber is provided with an opening communicated with the reaction unit; the induction coil is wrapped on the outer side of the upper heat-insulation outer layer; the bottom of the inner layer of the heating body is in a cone shape with the caliber decreasing progressively, and a heating filling body 305 and a heat insulation plate 306 are filled in a gap between the cone shape and the heat insulation middle layer; the heat insulation plate is positioned at the bottom of the gasification chamber.
As shown in fig. 2 and 8, the reaction unit is mounted on the bottom of the housing by a bottom base 103 made of ceramic. The reaction unit includes: a reaction chamber consisting of a lower heat-insulating outer layer 401 and a heat-resistant inner layer 402, and a vortex nozzle 403. The bottom of heat-resisting inlayer is the degressive toper of bore, and toper bottom central authorities are connected with discharging pipe 404, the vortex spray tube passes through the discharging pipe and stretches into in the reaction chamber by the reaction chamber outward, and the end of giving vent to anger of vortex spray tube is equipped with vortex nozzle 405, vortex nozzle is located under the gasification chamber bottom opening and jet-propelled direction upwards. The air flow sprayed by the vortex nozzle is in a fan shape and is spiral at an inner angle of 50-70 degrees.
The upper heat-insulating outer layer and the lower heat-insulating outer layer are integrally formed; the heating element inner layer and the heat-resistant inner layer are connected in a split type insertion mode. The upper and lower insulating outer layers are made of insulating cotton; the heat insulation middle layer and the heat insulation plate are made of graphite hard felt; the heating filler is made of graphite. The inner layer of the heating body and the heat-resistant inner layer are made of tungsten alloy materials.
As shown in fig. 2 and 9, the cooling unit includes: a cooling chamber housing 501, a spiral nozzle 502, and a lower coolant jacket 503. The center of the top of the cooling chamber shell is provided with an opening. As shown in fig. 10, the spiral nozzle is disposed at the opening and connected to the discharge pipe of the reaction unit through a connecting flange 504, the spiral nozzle is directed downward, and the gas powder is ejected from the spiral strip gap of the spiral nozzle to form a fan-shaped (preferably 60-90 °) spiral rotating gas flow. A nitrogen inlet 505 is arranged on the cooling chamber shell, the bottom of the cooling chamber shell is in a conical shape with the caliber decreasing progressively, and the center of the conical bottom is provided with a gas powder outlet 506; the lower refrigerant jacket is arranged on the outer side of the cooling chamber shell. Wherein the discharge pipe and the connecting flange are made of tungsten alloy materials; the spiral nozzle is made of ceramic material.
In addition, a temperature measuring port 104 and a pressure measuring port 105 are arranged at different positions of the shell, the spraying unit, the gasification unit, the reaction unit and the cooling unit.
In the production line of the invention, the air pressure in the nano aluminum nitride powder synthesis device is controlled to be 1.2-1.5 kg, the air pressure in the gasification chamber is controlled to be 1-1.3 kg, the air pressure in the reaction chamber is controlled to be 0.9-1.2 kg, and the air pressure in the cooling unit is controlled to be 0.7-1 kg. The temperature of the aluminum liquid bin of the spraying unit is controlled to be 700-800 ℃, the temperature of the nitrogen gas spray pipe is controlled to be 1600-1700 ℃, the temperature of the gasification chamber is controlled to be 2400-2500 ℃, the temperature of the reaction chamber is controlled to be 1300-1500 ℃ and the temperature of the cooling unit is controlled to be 40-60 ℃.
Compared with the domestic peer (equal equipment investment), the production line of the invention has the following data:
the raw materials and equipment used in the invention are common raw materials and equipment in the field if not specified; the methods used in the present invention are conventional in the art unless otherwise specified.
The above description is only a preferred embodiment of the present invention, and is not intended to limit the present invention, and all simple modifications, alterations and equivalents of the above embodiments according to the technical spirit of the present invention are still within the protection scope of the technical solution of the present invention.
Claims (9)
1. A nanometer aluminium nitride powder body synthesis production line is characterized by comprising: the device comprises a nano aluminum nitride powder synthesis device (1), a material collection system, a nitrogen supply system, a refrigeration system (2) and an argon supply system (3);
the nano aluminum nitride powder synthesis device comprises: the device comprises a shell (100), a spraying unit arranged in the shell, a gasification unit arranged in the shell and connected below the spraying unit, a reaction unit arranged in the shell and connected below the gasification unit, and a cooling unit connected below the gasification unit;
the spray unit includes: the aluminum conveying mechanism (201), the heat preservation shell (202), the heating cover (203), the aluminum liquid bin (204), the nitrogen gas spray pipe (205) and the insulating cover seat (206); the heating cover is arranged in the heat-insulating shell, and the inner wall of the heating cover is provided with heating wires (207); the middle lower section of the aluminum liquid bin is arranged in the heating cover, a gap is formed between the middle lower section of the aluminum liquid bin and the inner wall of the heating cover, the top of the aluminum liquid bin is provided with an argon inlet (208), and the bottom of the aluminum liquid bin extends out of the bottom of the heating cover and is provided with a downward atomizing nozzle (209); the nitrogen spray pipe is introduced into the center of the aluminum liquid bin, and the air outlet of the nitrogen spray pipe faces the atomizing nozzle; the aluminum conveying mechanism is arranged at the top of the aluminum liquid bin; the insulating cover seat is arranged below the heat-insulating shell and the heating cover, and a gap is formed between the inner ring of the insulating cover seat and the outer wall of the bottom of the aluminum liquid bin;
the gasification unit comprises: a gasification chamber and an induction coil (304) which are sequentially composed of an upper heat-preservation insulating outer layer (301), a heat-insulation middle layer (302) and a heating body inner layer (303); an opening for arranging an insulating cover seat is formed in the center of the top of the gasification chamber; the center of the bottom of the gasification chamber is provided with an opening communicated with the reaction unit; the induction coil is wrapped on the outer side of the upper heat-insulation outer layer; the bottom of the inner layer of the heating body is in a cone shape with the caliber decreasing progressively, and a heating filling body (305) and a heat insulation plate (306) are filled in a gap between the cone shape and the heat insulation middle layer; the heat insulation plate is positioned at the bottom of the gasification chamber;
the reaction unit includes: a reaction chamber and a vortex nozzle (403) which are formed by a lower heat-insulating outer layer (401) and a heat-resistant inner layer (402); the bottom of the heat-resistant inner layer is in a tapered shape with the caliber decreasing progressively, the center of the tapered bottom is connected with a discharge pipe (404), the vortex nozzle extends into the reaction chamber from the outside of the reaction chamber through the discharge pipe, the gas outlet end of the vortex nozzle is provided with a vortex nozzle (405), and the vortex nozzle is positioned right below the opening at the bottom of the gasification chamber and has an upward gas injection direction;
the material collecting system is connected with an outlet of the cooling unit and is used for gas-powder separation, recovery and packaging of materials;
the nitrogen supply system is used for supplying nitrogen for the spraying unit, the reaction unit and the cooling unit;
the refrigerating system is used for circularly supplying cold media of the reaction unit and the cooling unit;
the argon supply system is communicated with the spraying unit and the shell and used for supplying argon.
2. The production line of claim 1, wherein: the material collecting system comprises a gas-powder separating device (4), a packaging device (5) and a recovered gas storage tank (6); the gas-powder separation device is connected with an outlet of the cooling unit, and the packaging device and the recovered gas storage tank are respectively connected with a powder outlet and a gas outlet of the gas-powder separation device; the recovered gas storage tank is also respectively connected with the packaging device and the spraying unit to supply power and gas.
3. The production line of claim 1, wherein: the nitrogen supply system comprises a nitrogen making device (7), a nitrogen tank (8), a nitrogen refrigerator (9) and a liquid ammonia tank (10); the nitrogen making device is connected with a nitrogen tank, the nitrogen tank is respectively connected with the spraying unit, the reaction unit and the cooling unit, and a nitrogen refrigerator is arranged on a pipeline for connecting the nitrogen tank with the reaction unit and the cooling unit; the liquid ammonia tank is connected with the reaction unit.
4. The production line of claim 1, wherein: the shell is provided with an argon inlet (101), and the top of the aluminum liquid bin is provided with an argon inlet (208).
5. The production line of claim 1, wherein:
the clearance between the inner ring of the insulating cover seat and the outer wall of the bottom of the aluminum liquid bin is 1-2 mm; and/or
Two valves (210) which are connected in series and are switched in a staggered manner are arranged on a pipeline between the aluminum conveying mechanism and the aluminum liquid bin; and/or
The material sprayed by the atomizing nozzle is conical, the inner angle is 90-120 degrees, the side length is 30-40mm, and the particle size of the mist is 3-5 microns; and/or
The aluminum conveying mechanism is provided with a nitrogen inlet (211); and/or
The calibers of the upper sections of the heating cover and the aluminum liquid bin are larger than the calibers of the lower sections; and/or
An upper refrigerant jacket (212) is arranged on the top wall of the aluminum liquid bin; and/or
The electric heating wire, the aluminum liquid bin, the atomizing nozzle and the nitrogen spray pipe are made of tungsten alloy materials; the heating cover and the insulating cover seat are made of ceramic materials.
6. The production line of claim 1, wherein:
the airflow sprayed by the vortex nozzle is in a fan-shaped spiral with an inner angle of 50-70 degrees; and/or
The upper heat-insulating outer layer and the lower heat-insulating outer layer are integrally formed; the inner layer of the heating body and the heat-resistant inner layer are connected in a split manner; and/or
The upper heat-insulating outer layer and the lower heat-insulating outer layer are made of heat-insulating cotton; the heat insulation middle layer and the heat insulation plate are made of hard graphite felt; the heating filler is made of graphite; the inner layer of the heating body and the heat-resistant inner layer are made of tungsten alloy materials; and/or
The spraying unit is fixed at the upper part in the shell through a bracket (102); the reaction unit is erected at the bottom of the shell through a bottom bracket (103); the bracket and the bottom bracket are made of ceramic materials.
7. The production line of claim 1, wherein: the cooling unit includes: a cooling chamber shell (501), a spiral nozzle (502) and a lower refrigerant jacket (503);
an opening is formed in the center of the top of the cooling chamber shell, the spiral nozzle is arranged at the opening and is connected with a discharge pipe of the reaction unit through a connecting flange (504), and the direction of the spiral nozzle is downward; a nitrogen inlet (505) is arranged on the cooling chamber shell, the bottom of the cooling chamber shell is in a conical shape with the caliber decreasing progressively, and the center of the conical bottom is provided with a gas powder outlet (506); the lower refrigerant jacket is arranged on the outer side of the cooling chamber shell.
8. The production line of claim 7, wherein:
the gas powder is sprayed out from the spiral strip gap of the spiral nozzle to form a fan-shaped spiral rotating air flow of 60-90 degrees; and/or
The discharge pipe and the connecting flange are made of tungsten alloy materials; the spiral nozzle is made of ceramic material.
9. The production line of claim 1, wherein: and a temperature measuring port (104) and a pressure measuring port (105) are arranged at different positions of the shell, the spraying unit, the gasification unit, the reaction unit and the cooling unit.