CN112280475A - 一种可厚涂的高聚物改性沥青防水涂料 - Google Patents
一种可厚涂的高聚物改性沥青防水涂料 Download PDFInfo
- Publication number
- CN112280475A CN112280475A CN202011164985.3A CN202011164985A CN112280475A CN 112280475 A CN112280475 A CN 112280475A CN 202011164985 A CN202011164985 A CN 202011164985A CN 112280475 A CN112280475 A CN 112280475A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- asphalt waterproof
- modified asphalt
- high polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及改性沥青防水涂料技术领域，且公开了一种可厚涂的高聚物改性沥青防水涂料，包括以下重量份数配比的原料：石油沥青280‑350份，SBS改性剂80‑120份，热塑性橡胶溶液50‑80份，稳定剂5‑10份，聚丙烯树脂10‑30份。该可厚涂的高聚物改性沥青防水涂料，通过在石油沥青的内部加入SBS改性剂，降低了沥青的温度敏感性，改善后针入度下降，软化点下降，弹塑范围扩大，耐流动变形性能力得到改善，在喷涂沥青防水涂料的时候可以喷涂更多层，增加了沥青防水涂料的防水性，同时向改性沥青防水涂料的内部加入细骨料，细骨料应质地坚硬，清洁，级配良好，能够有效的提高改性沥青防水涂料的浓稠度，而且增加了改性沥青防水涂料的密度，让改性沥青防水涂料可厚涂。
Description
技术领域
本发明涉及改性沥青防水涂料技术领域，具体为一种可厚涂的高聚物改性沥青防水涂料。
背景技术
沥青是一种褐色或黑褐色的有机胶凝材料，是土木工程建设中不可缺少的材料，在建筑，公路和桥梁等工程中有着广泛的应用，沥青防水涂料是以沥青为基料配置的溶剂型或水乳型防水涂料，溶剂型沥青防水涂料是指将未改性的石油沥青直接溶解于汽油等溶剂中而配置成。
根据中国授权发明CN 111607305 A提出的聚合物改性沥青防水涂料，其有益效果为本发明提供的聚合物改性沥青防水涂料具有抗裂性能较好的效果，但是传统的改性沥青防水涂料塑性较差无法进行厚涂，导致沥青防水涂料涂抹效果不佳，容易出现漏水的情况，同时耐磨性一般，在长久使用之后容易磨损缩减，使用寿命较短，故而提出一种可厚涂的高聚物改性沥青防水涂料来解决上述问题。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种可厚涂的高聚物改性沥青防水涂料，具备防水效果好和增加使用寿命等优点，解决了传统的改性沥青防水涂料塑性较差无法进行厚涂，导致沥青防水涂料涂抹效果不佳，容易出现漏水的情况，同时耐磨性一般，在长久使用之后容易磨损缩减，使用寿命较短的问题。
(二)技术方案
为实现上述防水效果好和增加使用寿命目的，本发明提供如下技术方案：一种可厚涂的高聚物改性沥青防水涂料，包括以下重量份数配比的原料：石油沥青280-350份，SBS改性剂80-120份，热塑性橡胶溶液50-80份，稳定剂5-10份，聚丙烯树脂10-30份，高分子聚合物30-40份，分散剂2-3份，杀菌剂1-2份，消泡剂2-5份，增稠剂3-5份，细骨料20-50份。
优选的，所述石油沥青是由原油经过减压蒸馏，溶剂脱沥青和氧化的工艺生产而成，且石油沥青的针入度为25℃。
优选的，所述SBS改性剂有苯乙烯与丁二烯采用溶液聚合的方法制备成的苯乙烯和丁二烯嵌段共聚物，所述热塑性橡胶溶液为热塑性橡胶热熔液。
优选的，所述聚丙烯树脂以丙烯为原料，乙烯为共聚单体通过聚合反应生产制得，所述高分子聚合物为聚丙烯酰胺。
优选的，所述消泡剂的组成主要有活性成分，乳化剂，载体和乳化助剂，所述细骨料为细颗粒砂石清洗之后烘干而成。
优选的，所述分散剂包括聚丙烯酰胺，聚丙烯酸钠和聚氧化乙烯中任意一种，所述稳定剂为淀粉-羧甲基纤维素共聚物，所述羧甲基纤维素由天然纤维素经过化学改性得到的水溶性纤维素醚。
优选的，包括以下重量份数配比的原料：石油沥青280份，SBS改性剂80份，热塑性橡胶溶液50份，稳定剂5份，聚丙烯树脂10份，高分子聚合物30份，分散剂2份，杀菌剂1份，消泡剂2份，增稠剂3份，细骨料20份。
优选的，包括以下重量份数配比的原料：石油沥青350份，SBS改性剂120份，热塑性橡胶溶液80份，稳定剂10份，聚丙烯树脂30份，高分子聚合物40份，分散剂3份，杀菌剂2份，消泡剂5份，增稠剂5份，细骨料50份。
(三)有益效果
与现有技术相比，本发明提供了一种可厚涂的高聚物改性沥青防水涂料，具备以下有益效果：
1，该可厚涂的高聚物改性沥青防水涂料，通过在石油沥青的内部加入SBS改性剂，SBS改性剂兼有橡胶和塑料两种性能，常温下具有橡胶的弹性，高温下能像热塑料般熔融流动成为可塑性材料，改变了沥青流变学性质，粘弹性和延性提高，抗开裂能力和耐磨耗能力都大大增加，在使用的过程中能够减低磨损的程度，减缓涂料的磨损速度，增加沥青防水涂料的使用寿命，同时降低了沥青的温度敏感性，改善后针入度下降，软化点下降，弹塑范围扩大，耐流动变形性能力得到改善，在喷涂沥青防水涂料的时候可以喷涂更多层，增加了沥青防水涂料的防水性。
2，该可厚涂的高聚物改性沥青防水涂料，通过增加热塑性橡胶溶液，聚丙烯树脂和细骨料，在沥青防水涂料加工的过程中增加了热塑性橡胶溶液和聚丙烯树脂，使得改性沥青防水涂料的性能得以改善，热塑性橡胶热液能够增加改性沥青防水涂料的热塑性，让改性沥青防水涂料的稠度得到调整，聚丙烯树脂可以有效的提高改性沥青防水涂料的韧性和耐磨性，有效的提高了改性沥青防水涂料的综合性能，同时向改性沥青防水涂料的内部加入细骨料，细骨料应质地坚硬，清洁，级配良好，能够有效的提高改性沥青防水涂料的浓稠度，而且增加了改性沥青防水涂料的密度，让改性沥青防水涂料可厚涂。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚，完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：一种可厚涂的高聚物改性沥青防水涂料，包括以下重量份数配比的原料：石油沥青280份，石油沥青是由原油经过减压蒸馏，溶剂脱沥青和氧化的工艺生产而成，且石油沥青的针入度为25℃，SBS改性剂80份，热塑性橡胶溶液50份，SBS改性剂有苯乙烯与丁二烯采用溶液聚合的方法制备成的苯乙烯和丁二烯嵌段共聚物，热塑性橡胶溶液为热塑性橡胶热熔液，稳定剂5份，聚丙烯树脂10份，高分子聚合物30份，分散剂2份，分散剂包括聚丙烯酰胺，聚丙烯酸钠和聚氧化乙烯中任意一种，稳定剂为淀粉-羧甲基纤维素共聚物，羧甲基纤维素由天然纤维素经过化学改性得到的水溶性纤维素醚，杀菌剂1份，消泡剂2份，消泡剂的组成主要有活性成分，乳化剂，载体和乳化助剂，细骨料为细颗粒砂石清洗之后烘干而成，增稠剂3份，细骨料20份。
实施例二：一种可厚涂的高聚物改性沥青防水涂料，包括以下重量份数配比的原料：石油沥青350份，石油沥青是由原油经过减压蒸馏，溶剂脱沥青和氧化的工艺生产而成，且石油沥青的针入度为25℃，SBS改性剂120份，热塑性橡胶溶液80份，SBS改性剂有苯乙烯与丁二烯采用溶液聚合的方法制备成的苯乙烯和丁二烯嵌段共聚物，热塑性橡胶溶液为热塑性橡胶热熔液，稳定剂10份，聚丙烯树脂30份，高分子聚合物40份，分散剂3份，分散剂包括聚丙烯酰胺，聚丙烯酸钠和聚氧化乙烯中任意一种，稳定剂为淀粉-羧甲基纤维素共聚物，羧甲基纤维素由天然纤维素经过化学改性得到的水溶性纤维素醚，杀菌剂2份，消泡剂5份，消泡剂的组成主要有活性成分，乳化剂，载体和乳化助剂，细骨料为细颗粒砂石清洗之后烘干而成，增稠剂5份，细骨料50份。
试验后证明，经过改性之后的沥青防水涂料，可以有效的增加涂料的抗病害能力，可大大增加防水涂料的使用寿命，延长养护，减少二次涂漆，同时增加了沥青防水涂料的粘稠度和分子质量，从而让沥青防水涂料可厚涂来增加沥青防水涂料的防水效果。
本发明的有益效果是：该可厚涂的高聚物改性沥青防水涂料，通过在石油沥青的内部加入SBS改性剂，SBS改性剂兼有橡胶和塑料两种性能，常温下具有橡胶的弹性，高温下能像热塑料般熔融流动成为可塑性材料，改变了沥青流变学性质，粘弹性和延性提高，抗开裂能力和耐磨耗能力都大大增加，在使用的过程中能够减低磨损的程度，减缓涂料的磨损速度，增加沥青防水涂料的使用寿命，同时降低了沥青的温度敏感性，改善后针入度下降，软化点下降，弹塑范围扩大，耐流动变形性能力得到改善，在喷涂沥青防水涂料的时候可以喷涂更多层，增加了沥青防水涂料的防水性，
并且，通过增加热塑性橡胶溶液，聚丙烯树脂和细骨料，在沥青防水涂料加工的过程中增加了热塑性橡胶溶液和聚丙烯树脂，使得改性沥青防水涂料的性能得以改善，热塑性橡胶热液能够增加改性沥青防水涂料的热塑性，让改性沥青防水涂料的稠度得到调整，聚丙烯树脂可以有效的提高改性沥青防水涂料的韧性和耐磨性，有效的提高了改性沥青防水涂料的综合性能，同时向改性沥青防水涂料的内部加入细骨料，细骨料应质地坚硬，清洁，级配良好，能够有效的提高改性沥青防水涂料的浓稠度，而且增加了改性沥青防水涂料的密度，让改性沥青防水涂料可厚涂，解决了传统的改性沥青防水涂料塑性较差无法进行厚涂，导致沥青防水涂料涂抹效果不佳，容易出现漏水的情况，同时耐磨性一般，在长久使用之后容易磨损缩减，使用寿命较短的问题。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化，修改，替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种可厚涂的高聚物改性沥青防水涂料，其特征在于，包括以下重量份数配比的原料：石油沥青280-350份，SBS改性剂80-120份，热塑性橡胶溶液50-80份，稳定剂5-10份，聚丙烯树脂10-30份，高分子聚合物30-40份，分散剂2-3份，杀菌剂1-2份，消泡剂2-5份，增稠剂3-5份，细骨料20-50份。
2.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，所述石油沥青是由原油经过减压蒸馏，溶剂脱沥青和氧化的工艺生产而成，且石油沥青的针入度为25℃。
3.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，所述SBS改性剂有苯乙烯与丁二烯采用溶液聚合的方法制备成的苯乙烯和丁二烯嵌段共聚物，所述热塑性橡胶溶液为热塑性橡胶热熔液。
4.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，所述聚丙烯树脂以丙烯为原料，乙烯为共聚单体通过聚合反应生产制得，所述高分子聚合物为聚丙烯酰胺。
5.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，所述消泡剂的组成主要有活性成分，乳化剂，载体和乳化助剂，所述细骨料为细颗粒砂石清洗之后烘干而成。
6.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，所述分散剂包括聚丙烯酰胺，聚丙烯酸钠和聚氧化乙烯中任意一种，所述稳定剂为淀粉-羧甲基纤维素共聚物，所述羧甲基纤维素由天然纤维素经过化学改性得到的水溶性纤维素醚。
7.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，包括以下重量份数配比的原料：石油沥青280份，SBS改性剂80份，热塑性橡胶溶液50份，稳定剂5份，聚丙烯树脂10份，高分子聚合物30份，分散剂2份，杀菌剂1份，消泡剂2份，增稠剂3份，细骨料20份。
8.根据权利要求1所述的一种可厚涂的高聚物改性沥青防水涂料，其特征在于，包括以下重量份数配比的原料：石油沥青350份，SBS改性剂120份，热塑性橡胶溶液80份，稳定剂10份，聚丙烯树脂30份，高分子聚合物40份，分散剂3份，杀菌剂2份，消泡剂5份，增稠剂5份，细骨料50份。