CN112159562A - 一种pe手套膜及制备方法 - Google Patents

一种pe手套膜及制备方法 Download PDF

Info

Publication number
CN112159562A
CN112159562A CN202010946129.7A CN202010946129A CN112159562A CN 112159562 A CN112159562 A CN 112159562A CN 202010946129 A CN202010946129 A CN 202010946129A CN 112159562 A CN112159562 A CN 112159562A
Authority
CN
China
Prior art keywords
parts
film
agent
glove
glove film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010946129.7A
Other languages
English (en)
Inventor
苏宗球
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Shengda Medical Health Stock Co ltd
Original Assignee
Shanghai Shengda Medical Health Stock Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Shengda Medical Health Stock Co ltd filed Critical Shanghai Shengda Medical Health Stock Co ltd
Priority to CN202010946129.7A priority Critical patent/CN112159562A/zh
Publication of CN112159562A publication Critical patent/CN112159562A/zh
Pending legal-status Critical Current

Abstract

本发明为一种PE手套膜及制备方法。所述PE手套膜包括以下重量组分：LLDPE 50‑60份、HDPE 30‑35份、LDPE 5‑8份、成核剂1‑3份、抗静电剂1‑3份、抗菌剂0.1‑0.5份。本发明PE手套膜有效减少和降低吹膜过程和手套制成中静电的产生，有效防止细菌滋生发霉，提高韧性和强度，具有降低维卡软化温度，提高手套膜热合强度的优点，大大提高了PE手套在进行折叠和包装时的成品率，及PE手套在存放和使用中的抗菌性。

Description

一种PE手套膜及制备方法
技术领域
本发明涉及一种手套，特别是公开一种PE手套膜及制备方法。
背景技术
PE手套的主要制备方法为，将原料混合后，通过吹膜机，经加热融化再吹成塑料膜，然后通过折叠和包装制成PE手套。
在整个生产制成塑料膜过程中会产生大量的静电，加上塑料膜在手套制成过程当中，由于塑料膜与设备接触面的摩擦也会产生大量的静电。手套静电会造成手套手指过度的上翘，从而在手套自动折叠和包装时，容易造成产品折叠不良，影响产量。
同时，手套膜、手套制品在温湿度较高时，容易滋生细菌而发霉，影响手套膜的热合牢度。
发明内容
本发明的目的在于克服现有技术中存在的问题，提供一种减少和降低吹膜过程、手套制成中静电的产生，提高手套膜热合强度、提高韧性和强度的PE手套膜及制备方法。
本发明是这样实现的：一种PE手套膜，包括以下重量组分：LLDPE 50-60份、HDPE30-35份、LDPE 5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份。
所述成核剂在二苄叉山梨醇、松香酸、硬脂酸钙或月桂醇磷酸酯钾中任选一种或一种以上的组合。
所述抗静电剂在三羟甲基丙烷三端氨基聚环氧丙烷醚、乙氧基化烷基硫酸铵、乙氧基月桂酸胺、硬脂酸甘油酯或乙氧基椰油烷基胺中任选一种或一种以上的组合。
所述抗菌剂在绿原酸、咖啡酸、对甲基苄基三甲基氯化铵、二癸基二甲基氯化铵、三丁基十四烷基氯化鏻或聚b-氨基酸中任选一种或一种以上的组合。
一种如上所述的PE手套膜的制备方法，包括如下步骤：
（1）按重量份将LLDPE 50-60份、HDPE 30-35份、LDPE 5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至170℃~190℃，吹成薄膜。本发明的有益效果是：本发明所述抗静电剂一是需与部分与PE相容，二是能迁移至PE膜表面起消除静电作用；减少和降低吹膜过程和手套制成中静电的产生，有效防止细菌滋生发霉，提高韧性和强度，具有降低维卡软化温度，提高手套膜热合强度的优点，大大提高了PE手套在进行折叠和包装时的成品率。
与现有技术相比，本发明PE手套膜的静电：从4000-5000 KV，降至≤0.2KV；维卡软化温度：从150℃，降至≤125℃；热合强度：从3-4N/15mm，提高至5-6N/15mm。
具体实施方式
本发明一种PE手套膜，包括以下重量组分：LLDPE 50-60份、HDPE 30-35份、LDPE5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份。
其中，所述成核剂二苄叉山梨醇、松香酸、硬脂酸钙或月桂醇磷酸酯钾中任选一种或一种以上的组合。所述抗静电剂在三羟甲基丙烷三端氨基聚环氧丙烷醚、乙氧基化烷基硫酸铵、乙氧基月桂酸胺、硬脂酸甘油酯或乙氧基椰油烷基胺中任选一种或一种以上的组合。所述抗菌剂在绿原酸、咖啡酸、对甲基苄基三甲基氯化铵、二癸基二甲基氯化铵、三丁基十四烷基氯化鏻或聚b-氨基酸中任选一种或一种以上的组合。
本发明一种PE手套膜的制备方法，包括如下步骤：
（1）按重量份将LLDPE 50-60份、HDPE 30-35份、LDPE 5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份混合均匀形成PE物料。
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至170℃~190℃，吹成薄膜。
下面就具体实施例对本发明作进一步阐述。
实施例一：
本实施例包括以下重量组分：LLDPE 50份、HDPE 35份、LDPE 8份、成核剂1份、抗静电剂2份、抗菌剂0.01份。所述成核剂为二苄叉山梨醇，所述抗静电剂为三羟甲基丙烷三端氨基聚环氧丙烷醚，所述抗菌剂为对甲基苄基三甲基氯化铵。
所述三羟甲基丙烷三端氨基聚环氧丙烷醚可采用商品牌号为JEFFAMINE T403抗静电剂。
本实施例制备方法包括如下步骤：
（1）按重量份将LLDPE 50份、HDPE 35份、LDPE 8份、成核剂1份、抗静电剂2份、抗菌剂0.01份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料 ，送至吹膜机，加热至190℃，吹成薄膜。
本实施例的优点是：PE膜抗静电，透光性好，拉伸率提高了，对大肠杆菌、金黄色葡萄球菌和肠道沙门氏菌有抗菌效果（杀菌率98%以上）。
实施例二：
本实施例包括以下重量组分：LLDPE 50份、HDPE 35份、LDPE 6份、成核剂1份、抗静电剂2份、抗菌剂0.005份。所述成核剂为月桂醇磷酸酯钾，所述抗静电剂乙氧基椰油烷基胺，所述抗菌剂为三丁基十四烷基氯化鏻。
本实施例制备方法包括如下步骤：
（1）按重量份将：LLDPE 50份、HDPE 35份、LDPE 6份、成核剂1份、抗静电剂2份、抗菌剂0.005份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至180℃，吹成薄膜。
本实施例的优点是：PE膜抗静电，透光性好，拉伸率提高了，对大肠杆菌、金黄色葡萄球菌和肠道沙门氏菌有抗菌效果（杀菌率97%以上）。
实施例三：
本实施例包括以下重量组分：LLDPE 55份、HDPE 33份、LDPE 7份、成核剂1份、抗静电剂2份、抗菌剂0.008份。所述成核剂为松香酸和硬脂酸钙（1:1混合），所述抗静电剂为硬脂酸甘油酯，所述抗菌剂为三丁基十四烷基氯化鏻。
本实施例制备方法包括如下步骤：
（1）按重量份将：LLDPE 55份、HDPE 33份、LDPE 7份、成核剂1份、抗静电剂2份、抗菌剂0.008份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至175℃，吹成薄膜。
本实施例的优点是：PE膜抗静电，透光性好，拉伸率提高了，对大肠杆菌、金黄色葡萄球菌和肠道沙门氏菌有抗菌效果（杀菌率97%以上）。
实施例四：
本实施例包括以下重量组分：LLDPE 60份；HDPE 30份；LDPE 5份；成核剂3份、抗静电剂2份、抗菌剂0.001份。所述成核剂为二苄叉山梨醇，所述抗静电剂为乙氧基椰油烷基胺，所述抗菌剂为聚b-氨基酸。
所述聚b-氨基酸可采用文献（Macromolecules, 1998,31(1):174-178；功能高分子学报，2018, 31(5):493-500.）合成的抗菌剂，数均分子量3000~4000，对革兰氏阳性菌和金黄色葡萄球菌具有高效的抗菌活性。
本实施例制备方法包括如下步骤：
（1）按重量份将：LLDPE 60份；HDPE 30份；LDPE 5份；成核剂3份、抗静电剂2份、抗菌剂0.001份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至170℃，吹成薄膜。
本实施例的优点是：PE膜抗静电，透光性好，拉伸率提高了，对大肠杆菌、革兰氏阳性菌、金黄色葡萄球菌和肠道沙门氏菌有抗菌效果（杀菌率98%以上）。
对照例1
由重量份LLDPE50份、HDPE35份、LDPE 8份组成；
将对照例1配方原料进行充分的搅拌混合，送至吹膜机，加热至180℃再吹成塑料薄膜。
对照例2
由重量份LLDPE 60份、HDPE 30份、LDPE 5份组成；
将对照例2配方原料进行充分的搅拌混合，送至吹膜机，加热至170℃再吹成塑料薄膜。
通过下表，对本发明实施例与对照例进行性能对比。
Figure DEST_PATH_IMAGE001
由上表可知，本发明实施例的手套膜静电性能、维卡软化温度、热合强度、手套抗菌试验结果，均优于对照例。

Claims (5)

1.一种PE手套膜，其特征在于：包括以下重量组分：LLDPE 50-60份、HDPE 30-35份、LDPE 5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份。
2.根据权利要求 1 所述的一种PE手套膜，其特征在于：所述成核剂在二苄叉山梨醇、松香酸、硬脂酸钙或月桂醇磷酸酯钾中任选一种或一种以上的组合。
3.根据权利要求 1 所述的一种PE手套膜，其特征在于：所述抗静电剂在三羟甲基丙烷三端氨基聚环氧丙烷醚、乙氧基化烷基硫酸铵、乙氧基月桂酸胺、硬脂酸甘油酯或乙氧基椰油烷基胺中任选一种或一种以上的组合。
4.根据权利要求 1 所述的一种PE手套膜，其特征在于：所述抗菌剂在绿原酸、咖啡酸、对甲基苄基三甲基氯化铵、二癸基二甲基氯化铵、三丁基十四烷基氯化鏻或聚b-氨基酸中任选一种或一种以上的组合。
5.一种如权利要求1所述的一种PE手套膜的制备方法，其特征在于：包括如下步骤：
（1）按重量份将LLDPE 50-60份、HDPE 30-35份、LDPE 5-8份、成核剂0.05-1份、抗静电剂0.1-3份、抗菌剂0.001-0.01份混合均匀形成PE物料；
（2）将步骤（1）混合均匀的PE物料，送至吹膜机，加热至170℃~190℃，吹成薄膜。
CN202010946129.7A 2020-09-10 2020-09-10 一种pe手套膜及制备方法 Pending CN112159562A (zh)