CN112144678A - Waterproof material for settlement and expansion joints of buildings - Google Patents
Waterproof material for settlement and expansion joints of buildings Download PDFInfo
- Publication number
- CN112144678A CN112144678A CN202010957996.0A CN202010957996A CN112144678A CN 112144678 A CN112144678 A CN 112144678A CN 202010957996 A CN202010957996 A CN 202010957996A CN 112144678 A CN112144678 A CN 112144678A
- Authority
- CN
- China
- Prior art keywords
- parts
- asphalt
- settlement
- waterproof
- wood wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of sewage treatment, and discloses a waterproof material for settlement and expansion joints of buildings, which comprises 40-45 parts of wood wool boards, 10-20 parts of asphalt, 20-25 parts of acrylic waterproof coating, 20-30 parts of epoxy resin, 10-16 parts of polyacrylic acid, 20-30 parts of synthetic rubber, 8-16 parts of emulsifying agent, 5-8 parts of improved latex, 5-12 parts of cement, 10-18 parts of ethyl foam strips and 15-25 parts of synthetic polymer waterproof coiled materials. According to the invention, the acrylic waterproof coating and the synthetic rubber are mixed and stirred, so that the corrosion resistance of the filler is improved, rainwater in rainy season can be prevented from corroding the building settlement and the waterproof material in the expansion joint, and the service life is prolonged.
Description
Technical Field
The invention relates to the technical field of sewage treatment, in particular to a waterproof material for settlement and expansion joints of buildings.
Background
At present, settlement and expansion joints are generally combined and arranged, collectively called settlement expansion joints, the settlement expansion joints are specially arranged according to the difference of the wall height and the property of the foundation so as to avoid wall body cracking caused by uneven settlement of the foundation, the joints are specially arranged from the wall top to form a base, the joint width is 2-3 cm, soil foundation is arranged at intervals of 10-25 m, the distance between rock foundations can be properly increased, in the building wall body construction process, the settlement and expansion joints of a building need to be filled with building materials, the settlement and the water seepage at the joint of the expansion joints are prevented, water seeps into a base layer below a concrete slab or below a leakage slab, the bearing capacity of the foundation is reduced, the strength is uneven, or the water seepage of a laminate is caused, and the water icing, the uneven frost heaving and the like are.
The waterproof material has the advantages of low cost, availability of old materials and strong folding resistance, and the manufacturing method of the waterproof material has the advantages of capability of generating coiled materials with low cost and strong folding resistance and also has the advantage of simple operation, but when the waterproof material is used for building settlement and expansion joints, the waterproof material has the problems of poor corrosion resistance, short service life, high operation difficulty during filling and long construction time.
Therefore, the waterproof material for the settlement and expansion joints of the building is provided, the corrosion resistance of the waterproof material for the settlement and expansion joints is favorably improved, the service life of the material is mostly prolonged, workers are favorably filled in the settlement and expansion joints, and the construction time is shortened.
Disclosure of Invention
The invention aims to provide a waterproof material for settlement and expansion joints of buildings, which solves the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a waterproof material for settlement and expansion joints of buildings comprises 40-45 parts of wood wool boards, 10-20 parts of asphalt, 20-25 parts of acrylic waterproof paint, 20-30 parts of epoxy resin, 10-16 parts of polyacrylic acid, 20-30 parts of synthetic rubber, 8-16 parts of emulsifying agent, 5-8 parts of improved latex, 5-12 parts of daub, 10-18 parts of ethyl foam strips and 15-25 parts of synthetic polymer waterproof coiled materials.
The waterproof coating comprises 40 parts of wood wool boards, 10 parts of asphalt, 20 parts of acrylic waterproof coating, 20 parts of epoxy resin, 10 parts of polyacrylic acid, 20 parts of synthetic rubber, 8 parts of emulsifier, 5 parts of modified latex, 5 parts of daub, 10 parts of foam strips and 15 parts of synthetic polymer waterproof coiled materials.
In a preferred embodiment of the invention, the waterproof coating comprises 42 parts of wood wool boards, 12 parts of asphalt, 22 parts of acrylic waterproof coating, 25 parts of epoxy resin, 13 parts of polyacrylic acid, 25 parts of synthetic rubber, 12 parts of emulsifier, 6 parts of modified latex, 8 parts of daub, 14 parts of ethylene foam strips and 20 parts of synthetic polymer waterproof coiled materials.
45 parts of wood wool boards, 20 parts of asphalt, 25 parts of acrylic waterproof coating, 30 parts of epoxy resin, 16 parts of polyacrylic acid, 30 parts of synthetic rubber, 6 parts of emulsifier, 8 parts of modified latex, 12 parts of daub, 18 parts of ethylene foam strips and 25 parts of synthetic polymer waterproof coiled materials.
In a preferred embodiment of the present invention, the waterproof material for settlement and expansion joints of buildings as claimed in any one of claims 1 to 4 is used, and the production method of the waterproof material for settlement and expansion joints of buildings comprises the following steps.
S1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.
Compared with the prior art, the invention has the following beneficial effects:
1. according to the invention, the acrylic waterproof coating and the synthetic rubber are arranged, and the acrylic waterproof coating and the synthetic rubber are mixed and stirred, so that the corrosion resistance of the filler is improved, rainwater in rainy season is prevented from corroding waterproof materials in building settlement and expansion joints, and the service life is prolonged.
2. The asphalt, the wood wool board and the synthetic polymer waterproof coiled material are arranged, the asphalt is coated on the outer wall of the wood wool board, and the synthetic polymer waterproof coiled material is bonded with the outer wall of the asphalt to form a filler main body, the plate-shaped filler is convenient for workers to construct and fill and place, and is supplemented with the mixture to complete filling, so that the filling of the settlement and expansion joints by the workers is facilitated, and the construction time is reduced.
Drawings
Other features, objects and advantages of the invention will become more apparent upon reading of the detailed description of non-limiting embodiments with reference to the following drawings:
FIG. 1 is a schematic view of the construction of a waterproof material for settlement and expansion joints of buildings according to the present invention;
Detailed Description
In order to make the technical means, the creation characteristics, the achievement purposes and the effects of the invention easy to understand, the invention is further described with the specific embodiments.
In the description of the present invention, it is to be understood that the terms "upper", "lower", "front", "rear", "left", "right", "top", "bottom", "inner", "outer", and the like, indicate orientations or positional relationships based on the orientations or positional relationships shown in the drawings, are only for convenience in describing the present invention and simplifying the description, and do not indicate or imply that the device or element referred to must have a particular orientation, be constructed in a particular orientation, and be operated, and thus, should not be construed as limiting the present invention; in the description of the present invention, it should be noted that unless otherwise explicitly stated or limited, the terms "mounted," "connected," and "disposed" are to be construed broadly and can, for example, be fixedly connected, disposed, detachably connected, disposed, or integrally connected and disposed. The specific meanings of the above terms in the present invention can be understood in specific cases to those skilled in the art.
Referring to fig. 1, the present invention provides a technical solution: a waterproof material for settlement and expansion joints of buildings comprises 40-45 parts of wood wool boards, 10-20 parts of asphalt, 20-25 parts of acrylic waterproof paint, 20-30 parts of epoxy resin, 10-16 parts of polyacrylic acid, 20-30 parts of synthetic rubber, 8-16 parts of emulsifying agent, 5-8 parts of improved latex, 5-12 parts of daub, 10-18 parts of ethyl foam strips and 15-25 parts of synthetic polymer waterproof coiled materials.
In the embodiment, 40 parts of wood wool boards, 10 parts of asphalt, 20 parts of acrylic waterproof coating, 20 parts of epoxy resin, 10 parts of polyacrylic acid, 20 parts of synthetic rubber, 8 parts of emulsifier, 5 parts of improved latex, 5 parts of clay, 10 parts of ethyl foam strips and 15 parts of synthetic polymer waterproof coiled materials.
In the embodiment, 42 parts of wood wool board, 12 parts of asphalt, 22 parts of acrylic waterproof coating, 25 parts of epoxy resin, 13 parts of polyacrylic acid, 25 parts of synthetic rubber, 12 parts of emulsifier, 6 parts of improved latex, 8 parts of daub, 14 parts of ethylene foam strip and 20 parts of synthetic polymer waterproof coiled material.
In the embodiment, the waterproof coating comprises 45 parts of wood wool boards, 20 parts of asphalt, 25 parts of acrylic waterproof coating, 30 parts of epoxy resin, 16 parts of polyacrylic acid, 30 parts of synthetic rubber, 6 parts of emulsifier, 8 parts of improved latex, 12 parts of clay, 18 parts of ethylene foam strips and 25 parts of synthetic polymer waterproof coiled materials.
The invention also discloses a solid impurity sewage treatment method, which comprises the following steps of by means of waterproof materials of building settlement and expansion joints:
s1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.
Example one
The waterproof material for settlement and expansion joints of buildings comprises the following raw materials in parts by weight: 40 parts of wood wool board, 10 parts of asphalt, 20 parts of acrylic waterproof coating, 20 parts of epoxy resin, 10 parts of polyacrylic acid, 20 parts of synthetic rubber, 8 parts of emulsifier, 5 parts of improved latex, 5 parts of clay, 10 parts of foam strip B and 15 parts of synthetic polymer waterproof coiled material.
The preparation steps are as follows:
s1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.
Example two
The waterproof material for settlement and expansion joints of buildings comprises the following raw materials in parts by weight: 42 parts of wood wool board, 12 parts of asphalt, 22 parts of acrylic waterproof coating, 25 parts of epoxy resin, 13 parts of polyacrylic acid, 25 parts of synthetic rubber, 12 parts of emulsifier, 6 parts of improved latex, 8 parts of clay, 14 parts of ethyl foam strip and 20 parts of synthetic polymer waterproof coiled material.
The preparation steps are as follows:
s1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.
EXAMPLE III
The waterproof material for settlement and expansion joints of buildings comprises the following raw materials in parts by weight: 45 parts of wood wool board, 20 parts of asphalt, 25 parts of acrylic waterproof coating, 30 parts of epoxy resin, 16 parts of polyacrylic acid, 30 parts of synthetic rubber, 6 parts of emulsifier, 8 parts of improved latex, 12 parts of clay, 18 parts of ethyl foam strip and 25 parts of synthetic polymer waterproof coiled material.
The preparation steps are as follows:
s1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.
The data parameters of the waterproof material for settlement and expansion joints of the traditional building are shown in the table 1 as follows:
test items | Water resistance | Corrosion resistance | Service life | Difficulty of construction |
Parameter index | Good effect | Is poor | In general | Are cumbersome |
In the first embodiment, the data parameters of the waterproof material for settlement and expansion joints of the building are as follows:
test items | Water resistance | Corrosion resistance | Service life | Difficulty of construction |
Parameter index | Is excellent in | In general | Is longer | Simple and easy |
In the first embodiment, the data parameters of the waterproof material for settlement and expansion joints of the building are as follows:
test items | Water resistance | Corrosion resistance | Service life | Difficulty of construction |
Parameter index | Is excellent in | Excellence in | Is longer | Simple and easy |
The data parameters of the waterproof material for settlement and expansion joints of a building in the embodiment are as follows:
test items | Water resistance | Corrosion resistance | Service life | Difficulty of construction |
Parameter index | Excellence in | Is excellent in | Is longer | Simple and easy |
In summary, referring to the data comparison of tables 1, 2, 3 and 4, the present invention was achieved by applying asphalt to the outer wall of a wood wool board, the synthetic polymer waterproof coiled material is bonded with the outer wall of the asphalt to form a filler main body, the platy filler is convenient for workers to construct and place the filler, the acrylic waterproof coating and the synthetic rubber are mixed and stirred to improve the corrosion resistance of the filler, can effectively prevent rainwater from corroding in plum rain, the epoxy resin and the polyacrylic acid can also have the dispersing effect on soil, corrosion products and other amorphous substances, are dispersing agents, are mixed with synthetic rubber to improve the heat resistance, the cold resistance and the corrosion resistance of the filler, the adhesive is less affected by environmental factors, the adhesion degree among various materials is improved by mixing the emulsifier, improving the latex and the daub, and finally the height drop is generated after the filling and the packing of the foam B strip are condensed.
While there have been shown and described what are at present considered the fundamental principles and essential features of the invention and its advantages, it will be apparent to those skilled in the art that the invention is not limited to the details of the foregoing exemplary embodiments, but is capable of other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein. Any reference sign in a claim should not be construed as limiting the claim concerned.
Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.
Claims (5)
1. The utility model provides a building subsides, waterproof material at expansion joint which characterized in that: 40-45 parts of wood wool board, 10-20 parts of asphalt, 20-25 parts of acrylic waterproof coating, 20-30 parts of epoxy resin, 10-16 parts of polyacrylic acid, 20-30 parts of synthetic rubber, 8-16 parts of emulsifier, 5-8 parts of improved latex, 5-12 parts of clay, 10-18 parts of ethylene foam strip and 15-25 parts of synthetic polymer waterproof coiled material.
2. The waterproof material for settlement and expansion joints of buildings as claimed in claim 1, wherein: 40 parts of wood wool board, 10 parts of asphalt, 20 parts of acrylic waterproof coating, 20 parts of epoxy resin, 10 parts of polyacrylic acid, 20 parts of synthetic rubber, 8 parts of emulsifier, 5 parts of improved latex, 5 parts of clay, 10 parts of foam strip B and 15 parts of synthetic polymer waterproof coiled material.
3. The waterproof material for settlement and expansion joints of buildings as claimed in claim 1, wherein: 42 parts of wood wool board, 12 parts of asphalt, 22 parts of acrylic waterproof coating, 25 parts of epoxy resin, 13 parts of polyacrylic acid, 25 parts of synthetic rubber, 12 parts of emulsifier, 6 parts of improved latex, 8 parts of clay, 14 parts of ethyl foam strip and 20 parts of synthetic polymer waterproof coiled material.
4. The waterproof material for settlement and expansion joints of buildings as claimed in claim 1, wherein: 45 parts of wood wool board, 20 parts of asphalt, 25 parts of acrylic waterproof coating, 30 parts of epoxy resin, 16 parts of polyacrylic acid, 30 parts of synthetic rubber, 6 parts of emulsifier, 8 parts of improved latex, 12 parts of clay, 18 parts of ethyl foam strip and 25 parts of synthetic polymer waterproof coiled material.
5. The waterproof material for settlement and expansion joints of buildings as claimed in claim 1, wherein: the waterproof material for settlement and expansion joints of buildings as claimed in any one of claims 1 to 4 is produced by the following steps.
S1: adding asphalt into a heating device for heating to soften the asphalt;
s2: uniformly coating softened asphalt on the outer wall of the wood wool board, then attaching the synthetic polymer waterproof coiled material to the outer wall of the asphalt, and waiting for the external cooling;
s3: adding the acrylic waterproof coating, the epoxy resin and the polyacrylic acid into a stirring device, heating, stirring and mixing for 30-40min, adding the synthetic rubber, continuously stirring, stirring for 10min, adding the emulsifier, improving the latex and the cement, and taking out for later use;
s4: placing the cooled wood wool board coated with the asphalt in a corresponding settlement and expansion joint, and filling the mixture generated in the S3 in the settlement and expansion joint;
s5: and after the filler is condensed, filling and settling the foam strips and the height drop of the filler in the expansion joint.