CN112144142A - 一种抗菌阻燃涤纶面料及其制备方法 - Google Patents
一种抗菌阻燃涤纶面料及其制备方法 Download PDFInfo
- Publication number
- CN112144142A CN112144142A CN202010782353.7A CN202010782353A CN112144142A CN 112144142 A CN112144142 A CN 112144142A CN 202010782353 A CN202010782353 A CN 202010782353A CN 112144142 A CN112144142 A CN 112144142A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- retardant polyester
- flame
- antibacterial flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：聚对苯二甲酸乙二醇酯85～95份、聚己二酰己二胺5～8份、有机硅改性聚氨酯弹性体3.5～5份、抗菌剂3～4份、阻燃剂2～3份、玻璃纤维2～3份、轻质纳米碳酸钙3～4份；纳米二氧化硅1～1.5份、氧化聚乙烯蜡2～3份。本发明通过精选原料组成，并优化各原料含量，事制得的抗菌阻燃涤纶面料具有良好的抗菌抑菌效果，不易发霉发臭；具有良好的阻燃性能；且透气率高，透气性能好；(经向)拉伸强度和顶破强度高，力学性能好，耐用性好；各项性能指标优良，综合使用性能好，使用寿命长。
Description
技术领域
本发明涉及纺织面料技术领域，具体涉及一种抗菌阻燃涤纶面料及其制备方法。
背景技术
当今社会，面料已不再只是服装的一种简单材质，而渐渐演化成为服装的一个主体灵魂支柱。随着人们生活水平的提高，对服装面料的舒适性、健康性、安全性和环保性等要求越来越高，对安全高效抗菌服饰的功能需求越来越多。在生活中，人们不可避免的接触到各种各样的细菌、真菌等微生物，这些微生物在合适的外界条件下，会迅速繁殖，并通过接触等方式传播疾病，影响人们的身体健康和正常的工作、学习和生活。可见，研制抗菌面料显得十分有必要。
抗菌面料具有阻断疾病传播、保洁卫生、面料自身性能维护等优点，具有广阔的应用前景。获得优良抗菌性能的面料，其关键在于选择优良的抗菌剂。无机抗菌剂有缓释长效性、耐热性、安全性、广泛性和可加工性等优势，因此越来越受到人们的青睐，然而，现有技术中的无机抗菌剂虽具有良好的抗菌性能，但可能并不适用于肌肤敏感人群，在贴身穿着时感觉生硬，且有可能引起过敏；且由于抗菌剂与面料基材之间的相容性不好，在长期使用过程中易从面料基材中外渗，导致面料抗菌性能稳定性不佳。
纳米抗菌面料是在面料基材中添加纳米抗菌剂而形成的一种功能性面料，由于纳米抗菌剂具有量子效应、小尺寸效应和具有极大的比表面积，使得达到纳米抗菌面料具有传统添加无机抗菌剂的抗菌面料所无法比拟的优良抗菌效果，且它们持久性、耐热性优异，对皮肤无刺激、安全性极高。然而，现有技术中的纳米抗菌面料普遍采用的是单一纳米抗菌技术，不具有抗菌广谱性且杀菌效果有限，且纳米抗菌剂存在易团聚的问题，存在抗菌性能不均一、性能稳定性不佳的缺陷。除此之外，市面上的纳米抗菌面料还或多或少存在着抗紫外老化性能和阻燃性差，穿着舒适性有待进一步提高的缺陷。
申请号为201610712919.2的中国发明专利公开了一种纳米抗菌面料，包括：氟丙烯酸酯聚合物、纳米氧化锌、纳米玉石粉、竹炭纤维、甲壳素纤维、纳米银离子纤维、乙氧基喹啉、聚六亚甲基双胍盐酸盐、醋酸纤维，所述的纳米抗菌面料按照质量百分比计算，包括以下重量份：氟丙烯酸酯聚合物1-4份、纳米氧化锌2-5份、纳米玉石粉3-6份、竹炭纤维2-4份、甲壳素纤维5-10份、纳米银离子纤维1-7份、乙氧基喹啉2-5份、聚六亚甲基双胍盐酸盐3-6份、醋酸纤维1-5份。该发明提供的纳米抗菌面料，环保无污染、成本低廉、柔软滑爽，悬垂性好，透气保暖，保暖性好。然而，纳米材料与面料基材相容性不佳，面料抗菌性能稳定性不佳，且使用的纳米银离子纤维价格较高。
基于上述情况，本发明提出了一种抗菌阻燃涤纶面料及其制备方法，可有效解决以上问题。
发明内容
本发明的目的在于提供一种抗菌阻燃涤纶面料及其制备方法。本发明通过精选原料组成，并优化各原料含量，事制得的抗菌阻燃涤纶面料具有良好的抗菌抑菌效果，不易发霉发臭；具有良好的阻燃性能；且透气率高，透气性能好；(经向)拉伸强度和顶破强度高，力学性能好，耐用性好；各项性能指标优良，综合使用性能好，使用寿命长。
为解决以上技术问题，本发明提供的技术方案是：
一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯85～95份、
聚己二酰己二胺5～8份、
有机硅改性聚氨酯弹性体3.5～5份、
抗菌剂3～4份、
阻燃剂2～3份、
玻璃纤维2～3份、
轻质纳米碳酸钙3～4份；
纳米二氧化硅1～1.5份、
氧化聚乙烯蜡2～3份。
优选的，所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯90份、
聚己二酰己二胺6.5份、
有机硅改性聚氨酯弹性体4.2份、
抗菌剂3.5份、
阻燃剂2.5份、
玻璃纤维2.5份、
轻质纳米碳酸钙3.5份；
纳米二氧化硅1.25份、
氧化聚乙烯蜡2.5份；
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
本发明通过精选原料组成，并优化各原料含量，事制得的抗菌阻燃涤纶面料具有良好的抗菌抑菌效果，不易发霉发臭；具有良好的阻燃性能；且透气率高，透气性能好；(经向)拉伸强度和顶破强度高，力学性能好，耐用性好；各项性能指标优良，综合使用性能好，使用寿命长。
优选的，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂2～3份。
优选的，所述抗氧剂为抗氧剂PEP-36。
可更好地改善本发明制得的抗菌阻燃涤纶面料的抗氧老化性能。
优选的，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：2～3份。
优选的，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
可更好地改善本发明制得的抗菌阻燃涤纶面料的坑紫外老化性能。
本发明还提供一种所述的抗菌阻燃涤纶面料的制备方法，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。
本发明与现有技术相比，具有以下优点及有益效果：
本发明通过精选原料组成，并优化各原料含量，事制得的抗菌阻燃涤纶面料具有良好的抗菌抑菌效果，不易发霉发臭；具有良好的阻燃性能；且透气率高，透气性能好；(经向)拉伸强度和顶破强度高，力学性能好，耐用性好；各项性能指标优良，综合使用性能好，使用寿命长。
具体实施方式
为了使本领域的技术人员更好地理解本发明的技术方案，下面结合具体实施例对本发明的优选实施方案进行描述，但是不能理解为对本专利的限制。
下述实施例中所述试验方法或测试方法，如无特殊说明，均为常规方法；所述试剂和材料，如无特殊说明，均从常规商业途径获得，或以常规方法制备。
实施例1：
一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯85～95份、
聚己二酰己二胺5～8份、
有机硅改性聚氨酯弹性体3.5～5份、
抗菌剂3～4份、
阻燃剂2～3份、
玻璃纤维2～3份、
轻质纳米碳酸钙3～4份；
纳米二氧化硅1～1.5份、
氧化聚乙烯蜡2～3份。
优选的，所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯90份、
聚己二酰己二胺6.5份、
有机硅改性聚氨酯弹性体4.2份、
抗菌剂3.5份、
阻燃剂2.5份、
玻璃纤维2.5份、
轻质纳米碳酸钙3.5份；
纳米二氧化硅1.25份、
氧化聚乙烯蜡2.5份；
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
优选的，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂2～3份。
优选的，所述抗氧剂为抗氧剂PEP-36。
优选的，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：2～3份。
优选的，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
本发明还提供一种所述的抗菌阻燃涤纶面料的制备方法，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。
实施例2：
一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯85份、
聚己二酰己二胺5份、
有机硅改性聚氨酯弹性体3.5份、
抗菌剂3份、
阻燃剂2份、
玻璃纤维2份、
轻质纳米碳酸钙3份；
纳米二氧化硅1份、
氧化聚乙烯蜡2份。
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂2份。
在本实施例中，所述抗氧剂为抗氧剂PEP-36。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：2份。
在本实施例中，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
在本实施例中，所述的抗菌阻燃涤纶面料的制备方法，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。
实施例3：
一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯95份、
聚己二酰己二胺8份、
有机硅改性聚氨酯弹性体5份、
抗菌剂4份、
阻燃剂3份、
玻璃纤维3份、
轻质纳米碳酸钙4份；
纳米二氧化硅1.5份、
氧化聚乙烯蜡3份。
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂3份。
在本实施例中，所述抗氧剂为抗氧剂PEP-36。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：3份。
在本实施例中，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
在本实施例中，所述的抗菌阻燃涤纶面料的制备方法，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。
实施例4：
一种抗菌阻燃涤纶面料，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
聚对苯二甲酸乙二醇酯90份、
聚己二酰己二胺6.5份、
有机硅改性聚氨酯弹性体4.2份、
抗菌剂3.5份、
阻燃剂2.5份、
玻璃纤维2.5份、
轻质纳米碳酸钙3.5份；
纳米二氧化硅1.25份、
氧化聚乙烯蜡2.5份；
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂2.5份。
在本实施例中，所述抗氧剂为抗氧剂PEP-36。
在本实施例中，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：2.5份。
在本实施例中，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
在本实施例中，所述的抗菌阻燃涤纶面料的制备方法，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。
以上仅是本发明的优选实施方式，应当指出的是，上述优选实施方式不应视为对本发明的限制，本发明的保护范围应当以权利要求所限定的范围为准。对于本技术领域的普通技术人员来说，在不脱离本发明的精神和范围内，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (7)
1.一种抗菌阻燃涤纶面料，其特征在于，所述抗菌阻燃涤纶面料由抗菌阻燃涤纶长丝经针织或机织工艺制得；
所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯85～95份、
聚己二酰己二胺5～8份、
有机硅改性聚氨酯弹性体3.5～5份、
抗菌剂3～4份、
阻燃剂2～3份、
玻璃纤维2～3份、
轻质纳米碳酸钙3～4份；
纳米二氧化硅1～1.5份、
氧化聚乙烯蜡2～3份。
2.根据权利要求1所述的抗菌阻燃涤纶面料，其特征在于，所述抗菌阻燃涤纶长丝由包括以下重量份的原料制成：
聚对苯二甲酸乙二醇酯90份、
聚己二酰己二胺6.5份、
有机硅改性聚氨酯弹性体4.2份、
抗菌剂3.5份、
阻燃剂2.5份、
玻璃纤维2.5份、
轻质纳米碳酸钙3.5份；
纳米二氧化硅1.25份、
氧化聚乙烯蜡2.5份；
所述抗菌剂为纺织防霉抗菌剂KP-MJ150；
所述耐水洗纺织阻燃剂FT-6501。
3.根据权利要求2所述的抗菌阻燃涤纶面料，其特征在于，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗氧剂2～3份。
4.根据权利要求3所述的抗菌阻燃涤纶面料，其特征在于，所述抗氧剂为抗氧剂PEP-36。
5.根据权利要求4所述的抗菌阻燃涤纶面料，其特征在于，所述抗菌阻燃涤纶长丝还包括以下重量份的原料：抗紫外光剂：2～3份。
6.根据权利要求5所述的抗菌阻燃涤纶面料，其特征在于，所述抗紫外光剂为2'-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯苯并三唑。
7.一种如权利要求1至7任一项所述的抗菌阻燃涤纶面料的制备方法，其特征在于，包括下列步骤：
A、按重量份分别称取所述抗菌阻燃涤纶长丝的各原料；
B、通过熔融纺丝工艺得到所述抗菌阻燃涤纶长丝；
C、抗菌阻燃涤纶长丝经针织或机织工艺制得所述抗菌阻燃涤纶面料。