CN112129805A - 一种双向拉伸尼龙膜热收缩的测试方法 - Google Patents
一种双向拉伸尼龙膜热收缩的测试方法 Download PDFInfo
- Publication number
- CN112129805A CN112129805A CN202011013679.XA CN202011013679A CN112129805A CN 112129805 A CN112129805 A CN 112129805A CN 202011013679 A CN202011013679 A CN 202011013679A CN 112129805 A CN112129805 A CN 112129805A
- Authority
- CN
- China
- Prior art keywords
- nylon film
- sample
- biaxially oriented
- testing
- oriented nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种双向拉伸尼龙膜热收缩的测试方法，包括如下步骤：在尼龙膜上裁切试样；在所述试样上画出标线，所述标线包括横向线和纵向线；加热所述画有标线的试样；测量所述试样上的标线长度，计算所述对应各标线延伸方向的收缩率。其特征在于：所述标线还包括两根彼此垂直的斜45°线。本发明的测试方法相比国标测试方法增加了两根斜45°的标线，能够更准确，全面的测量尼龙膜在各个方向下的热收缩率，方便下游厂商对尼龙膜进行精确加工，避免、减少尼龙膜在加工使用时出现“翘角”现象。
Description
技术领域
本发明涉及尼龙工业领域，尤其涉及一种双向拉伸尼龙膜热收缩的测试方法。
背景技术
目前国内按照GB/T 12027-2004标准对尼龙膜的热收缩率进行测定。这种测定方式存在以下的缺陷：GB/T 12027-2004标准仅测试尼龙膜横向和纵向两个方向下的热收缩率，而对于采用双向拉伸工艺制造的尼龙膜，其分子链会存在一定的取向性，各个方向下的收缩率不一致，目前的国标测试方法不能完全体现热缩程度对薄膜加工使用的影响，无法贴合实际的加工，导致尼龙膜产品在加工使用时容易出现“翘角”的现象。
发明内容
本发明所要解决的技术问题是提供新型的双向拉伸尼龙膜热收缩的测试方法，能够更加全面准确地测量尼龙膜的热收缩率。
本发明通过如下方式解决该技术问题：
一种双向拉伸尼龙膜热收缩的测试方法，包括如下步骤：
在尼龙膜上裁切试样；
在所述试样上画出标线，所述标线包括横向线和纵向线；
加热所述画有标线的试样；
测量所述试样上的标线长度，计算所述对应各标线延伸方向的收缩率；
其特征在于：所述标线还包括两根彼此垂直的斜45°线。
本发明的测试方法相比国标测试方法增加了两根斜45°的标线，能够更准确，全面的测量尼龙膜在各个方向下的热收缩率，方便下游厂商对尼龙膜进行精确加工，避免、减少尼龙膜在加工使用时出现“翘角”现象。
作为本发明的一种优选实施方式，所述对应各标线延伸方向的收缩率通过如下公式计算：HS＝L-L0/L0X100％，其中，HS为收缩率，L0为标线的初始长度，L为加热后的标线长度。
作为本发明的一种优选实施方式，在所述尼龙膜中部和两端各裁切一块所述试样，所述试样为宽度为200mm-300mm的正方形。
作为本发明的一种优选实施方式，所述试样的裁切位置离所述尼龙膜边缘的间距大于50mm。
作为本发明的一种优选实施方式，分别计算三块试样相应的收缩率，取算术平均值，以使得到的收缩率数据更为精准。
作为本发明的一种优选实施方式，所述横向线、纵向线和两根斜45°线彼此相交于一点，该相交点位于所述试样的中心，形成一个星形图案。
作为本发明的一种优选实施方式，将所述试样在100℃的水槽中加热25-50分钟。
作为本发明的一种优选实施方式，将所述试样在100℃-160℃的高温蒸汽中加热25-50分钟。以契合不同下游厂家的使用场景，使测量数据更精确，更具有针对性。
作为本发明的一种优选实施方式，所述试样的加热时间为45分钟。
综合以上，本发明能够更为准确、全面地测量双向拉伸尼龙膜的热收缩率，相比现有的国标测试方法具有显著的进步。
附图说明
下面结合附图来对本发明进行进一步的说明：
图1为本发明中试样的示意图；
其中：100-试样，200-标线，201-横向线，202-纵向线，203-斜45°线。
具体实施方式
以下通过具体实施例来对本发明进行进一步阐述：
如图1所示，一种双向拉伸尼龙膜热收缩的测试方法，包括以下步骤：
第一步：从尼龙膜的中部和两端各裁取一块宽度为200mm-300mm的正方形试样100。该试样100的取样位置应相距尼龙膜的边缘至少50mm，以保证试样的均匀度。
第二步：用笔在每块试样100上画出长度为150mm-200mm的标线200，标线包括横向线201、纵向线202和两根彼此垂直的斜45°线203，优选使各标线200相交于一点，且相交点位于试样100的中心，由此构成一个星形图案。
第三步：将试样100在100℃的水槽中加热25-50分钟，优选加热时间为45分钟。
第四步：记录下各标线200的长度，计算尼龙膜对应各标线延伸方向下的收缩率HS，其计算公式如下：
HS＝L-L0/L0X100％，其中，HS为单个试样所测出的收缩率，L0为标线的初始长度，L为加热后的标线长度，分别计算三块试样的收缩率HS并取算术平均值，即可得到最终的收缩率HS。
本发明的测试方法相比国标测试方法增加了两根斜45°的标线，能够更准确，全面的测量尼龙膜在各个方向下的热收缩率，方便下游厂商对尼龙膜进行精确加工，避免、减少尼龙膜在加工使用时出现“翘角”现象。
另外，对试样100的加热还可以在100℃-160℃的高温蒸汽下进行，加热时间为25-50分钟，优选为45分钟。以契合不同下游厂家的使用场景，使测量数据更精确，更具有针对性。
综合以上，本发明能够更为准确、全面地测量双向拉伸尼龙膜的热收缩率，相比现有的国标测试方法具有显著的进步。
但是，本技术领域中的普通技术人员应当认识到，以上的实施例仅是用说明本发明，而并非用作为对本发明的限定，只要在本发明的实质精神范围内，对以上所述实施例的变化、变型都将落在本发明的权利要求书范围内。
Claims (9)
1.一种双向拉伸尼龙膜热收缩的测试方法，包括如下步骤：
在尼龙膜上裁切试样(100)；
在所述试样(100)上画出等长的标线(200)，所述标线(200)包括横向线(201)和纵向线(202)；
加热所述画有标线(200)的试样(100)；
测量所述试样(100)上的标线(200)长度，计算所述对应各标线(200)延伸方向的收缩率；
其特征在于：所述标线(200)还包括两根彼此垂直的斜45°线(203)。
2.按照权利要求1所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：所述对应各标线(200)延伸方向的收缩率通过如下公式计算：HS＝L-L0/L0X100％，其中，HS为收缩率，L0为标线(200)的初始长度，L为加热后的标线(200)长度。
3.按照权利要求2所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：在所述尼龙膜中部和两端各裁切一块所述试样(100)，所述试样(100)为宽度为200mm-300mm的正方形。
4.按照权利要求3所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：所述试样(100)的裁切位置离所述尼龙膜边缘的间距大于50mm。
5.按照权利要求3所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：分别计算三块所述试样(100)的收缩率，取算术平均值。
6.按照权利要求3所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：所述横向线(201)、纵向线(202)和两根斜45°线(203)彼此相交于一点，该相交点位于所述试样(100)的中心，由此构成一个星形图案。
7.按照权利要求1所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：将所述试样(100)在100℃的水槽中加热25-50分钟。
8.按照权利要求1所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：将所述试样(100)在100℃-160℃的高温蒸汽中加热25-50分钟。
9.按照权利要求7或8所述的双向拉伸尼龙膜热收缩的测试方法，其特征在于：所述试样(100)的加热时间为45分钟。